ES2563229T3 - Policarbonato con fibras de vidrio - Google Patents

Policarbonato con fibras de vidrio Download PDF

Info

Publication number
ES2563229T3
ES2563229T3 ES12762625.7T ES12762625T ES2563229T3 ES 2563229 T3 ES2563229 T3 ES 2563229T3 ES 12762625 T ES12762625 T ES 12762625T ES 2563229 T3 ES2563229 T3 ES 2563229T3
Authority
ES
Spain
Prior art keywords
weight
parts
polycarbonate
glass fibers
flame retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
ES12762625.7T
Other languages
English (en)
Inventor
Gesa Dern
Birte SÄMISCH
Tanja Cassel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Covestro Deutschland AG
Original Assignee
Covestro Deutschland AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Covestro Deutschland AG filed Critical Covestro Deutschland AG
Application granted granted Critical
Publication of ES2563229T3 publication Critical patent/ES2563229T3/es
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Masas de moldeo termoplásticas ignífugas que contienen A) de 47,500 a 97,939 partes en peso al menos de un policarbonato aromático, B) de 0,001 a 1,000 partes en peso al menos de un agente ignífugo, C) de 0,01 a 0,50 partes en peso al menos de un terpolímero de alfa-olefina modificado con anhídrido y libre de caucho, D) de 2,0 a 40,0 partes en peso al menos de una carga inorgánica, E) de 0,05 partes en peso a 1,00 parte en peso al menos de un agente de desmoldeo, F) 0,0 - 10,0 partes en peso de otros aditivos habituales, en donde la suma de las partes en peso de los componentes A) a F) suman hasta 100 partes en peso.

Description

imagen1
imagen2
imagen3
imagen4
imagen5
imagen6
imagen7
imagen8
5
10
15
20
25
30
Componente D-3
MF 7980, fibras de vidrio molidas de la empresa Lanxess AG con un diámetro de fibra promedio de 14 m, una longitud de fibra promedio de 190 m. Componente D-4 Se usó harina de cuarzo de la empresa Quarzwerke GmbH (50226 Frechen, Alemania), que está disponible con el
nombre comercial Sikron SF 600 (d50= 3 m, d95 = 10 m, sin acabado). Componente E-1 Estearato de estearilo, un agente lubricante/de desmoldeo (Loxiol G32) de la empresa Emery Oleochemicals GmbH
con un punto de fusión de 54 -58 ºC, un índice de saponificación de 108 -114 mg de KOH/g. Componente E-2 Tetraestearato de pentaeritritol como agente lubricante/de desmoldeo Componente F-1 Estabilizador Irgafos® 168 (fosfito de tris-(2,4-di-terc-butil-fenilo)). La resistencia al choque según Charpy se midió según la norma ISO 179/leU en probetas inyectadas en un lado de
la dimensión 80 x 10 x 4 mm.
La medición de la resistencia al choque en la probeta entallada según Charpy se realiza según la norma ISO 179/leA en probetas de geometría 80 * 10 * 4 mm3. La temperatura Vicat B/120 como medida de la estabilidad de termomoldeo se determina de acuerdo con la norma
ISO 306 en probetas de dimensión 80 x 10 x 4 mm con una carga de punzón de 50 N y una velocidad de
calentamiento de 120 ºC/h. El tamaño de partícula promedio d50 es el diámetro por encima y por debajo del cual se encuentra respectivamente el 50 % en peso de las partículas.
El tamaño de partícula máximo d95 es el diámetro por debajo del cual se encuentra el 95 % en peso de las partículas. Los diámetros correspondientes se determinan mediante separación por aire.
El comportamiento frente a incendios se mide según la norma UL 94V en barras de dimensión 127 x 12,7 x 1,0 mm. El módulo E y el alargamiento de rotura se midieron de acuerdo con la norma ISO 527 en probetas inyectadas por un lado de dimensión 80 x 10 x 4 mm.
La determinación de la velocidad de fundido en volumen (MVR) se realiza según la norma ISO 1133 (a 300 ºC; 1,2 kg).
10
imagen9
imagen10
12
Tabla 3: carga de silicato
Ejemplo
26 27 28 29 30 31 32 33 34
A-1 % en peso
76,295 76,295 76,295 76,295 76,295 76,295 76,295 76,295 74,295
A-2 % en peso
3 2,895 2,89 2,85 2,8 2,7 2,4 1,9 2,9
B-1 % en peso
0,18 0,18 0,18 0,18 0,18 0,18 0,18 0,18 0,18
B-2 % en peso
0,2 0,2 0,2 0,2 0,2 0,2 0,2 0,2 0,2
C % en peso
0,005 0,01 0,05 0,1 0,2 0,5 1 2
D-4 % en peso
20 20 20 20 20 20 20 20 20
E-2 % en peso
0,35 0,35 0,35 0,35 0,35 0,35 0,35 0,35 0,35
F-1 % en peso
0,075 0,075 0,075 0,075 0,075 0,075 0,075 0,075 0,075
MVR [cm3/10 min]/6 min
14,1 14,0 14,4 14,6 14,4 14,9 14,9 15,4 15,0
VICAT [ºC]
145 145 144 145 144 144 143 143 142
resistencia al choque según Charpy [kJ/m2]
207 209 296 265 277 260 286 270
fragilidad (índice)
10 10 10 10 9 5 2 3
UL 94 (48 h)
94V-0 94V-0 94V-0 94V-0 94V-0 94V-0 94V-0 94V-0 no observado
tiempo de combustión posterior 48 h [s]
39 42 35 47 30 36 37 42 141
13

Claims (1)

  1. imagen1
ES12762625.7T 2011-09-28 2012-09-27 Policarbonato con fibras de vidrio Active ES2563229T3 (es)