ES2068379T3 - Acero para trabajar en frio con una elevada resistencia a la compresion. - Google Patents

Acero para trabajar en frio con una elevada resistencia a la compresion.

Info

Publication number
ES2068379T3
ES2068379T3 ES90890280T ES90890280T ES2068379T3 ES 2068379 T3 ES2068379 T3 ES 2068379T3 ES 90890280 T ES90890280 T ES 90890280T ES 90890280 T ES90890280 T ES 90890280T ES 2068379 T3 ES2068379 T3 ES 2068379T3
Authority
ES
Spain
Prior art keywords
weight
steel
component
high compression
compression resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES90890280T
Other languages
English (en)
Inventor
Karl Dipl-Ing Leban
Herbert Schweiger
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Voestalpine Boehler Edelstahl GmbH
Original Assignee
Boehler Edelstahl GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Boehler Edelstahl GmbH filed Critical Boehler Edelstahl GmbH
Application granted granted Critical
Publication of ES2068379T3 publication Critical patent/ES2068379T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

LA INVENCION TRATA DE UN ACERO QUE SE AMECANIZA EN FRIO TIENE UNA ELEVADA RESESTENCIA A LA PRESION TANTO COMO COMPONENTE Y COMO HERRAMIENTA QUE SE SOMETE A GRANDES ESFUERZOS MECANICOS, SE EMPLEA COMO CAPA DE DESGASTE A ELEVADAS TEMPERATURAS PARA EL COMPONENTE DE LA HERRAMIENTA Y SE COMPONE POR LAS IMPUREZAS USUALES; UN 0,6 A 1,4 % EN PESO DE C; UN 0,2 A 1,6 EN PESO DE SI; 0,2 A 1,2 % EN PESO DE MN; UN 5 A 10 % EN PESO DE CR; UN 0 A 3,0 % EN PESO DE MO; UN O A 6,0 % EN PESO DE W; UN 0,3 A 1,5 % EN PESO DE V; UN 0,2 A 1,6 % EN PESO DE AL; UN 0 A 0,5 % EN PESO DE NB, UN 0 A 0,1 % EN PESO DE N; Y EL RESTO HIERRO. EL ACERO SE CARACTERIZA PORQUE TIENE UN CONTENIDO DE MO + W(2) ENTRE UN 1,0 A 3,0 % EN PESO.
ES90890280T 1989-10-23 1990-10-12 Acero para trabajar en frio con una elevada resistencia a la compresion. Expired - Lifetime ES2068379T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
AT2423/89A AT393387B (de) 1989-10-23 1989-10-23 Kaltarbeitsstahl mit hoher druckfestigkeit und verwendung dieses stahles

Publications (1)

Publication Number Publication Date
ES2068379T3 true ES2068379T3 (es) 1995-04-16

Family

ID=3534087

Family Applications (1)

Application Number Title Priority Date Filing Date
ES90890280T Expired - Lifetime ES2068379T3 (es) 1989-10-23 1990-10-12 Acero para trabajar en frio con una elevada resistencia a la compresion.

Country Status (12)

Country Link
US (1) US5160553A (es)
EP (1) EP0425471B1 (es)
JP (1) JP2794641B2 (es)
KR (1) KR0170386B1 (es)
AT (1) AT393387B (es)
AU (1) AU631690B2 (es)
BR (1) BR9005350A (es)
DE (1) DE59008009D1 (es)
DK (1) DK0425471T3 (es)
ES (1) ES2068379T3 (es)
TW (1) TW199910B (es)
ZA (1) ZA908467B (es)

Families Citing this family (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5445685A (en) * 1993-05-17 1995-08-29 The Regents Of The University Of California Transformation process for production of ultrahigh carbon steels and new alloys
GB2280865A (en) * 1993-08-13 1995-02-15 Mono Pumps Ltd Flexible drive shaft
AT403058B (de) * 1995-03-23 1997-11-25 Boehler Edelstahl Eisenbasislegierung zur verwendung bei erhöhter temperatur und werkzeug aus dieser legierung
FR2759092B1 (fr) * 1997-02-04 1999-04-16 Thyssen France Sa Acier pour le formage a froid
JP3284092B2 (ja) * 1997-12-05 2002-05-20 理研ダイヤモンド工業株式会社 切断破砕用カッター
SE511747C2 (sv) * 1998-03-27 1999-11-15 Uddeholm Tooling Ab Kallarbetsstål
US6093303A (en) 1998-08-12 2000-07-25 Swagelok Company Low temperature case hardening processes
JP4144094B2 (ja) * 1999-01-28 2008-09-03 日立金属株式会社 メタルバンドソー用刃材
AT407648B (de) * 1999-05-10 2001-05-25 Boehler Edelstahl Metallischer werkstoff mit hoher härte, hohem verschleisswiderstand und hoher zähigkeit
AT410448B (de) * 2001-04-11 2003-04-25 Boehler Edelstahl Kaltarbeitsstahllegierung zur pulvermetallurgischen herstellung von teilen
US20030155045A1 (en) * 2002-02-05 2003-08-21 Williams Peter C. Lubricated low temperature carburized stainless steel parts
US6723182B1 (en) * 2002-11-14 2004-04-20 Arthur J. Bahmiller Martensitic alloy steels having intermetallic compounds and precipitates as a substitute for cobalt
AT500728B8 (de) 2005-02-21 2007-02-15 Boehler Edelstahl Schneidwerkzeug
WO2008066438A1 (en) * 2006-11-27 2008-06-05 E2 Forestry Hb Wear resistant tool for wood chipping
AT507215B1 (de) * 2009-01-14 2010-03-15 Boehler Edelstahl Gmbh & Co Kg Verschleissbeständiger werkstoff
AT508591B1 (de) * 2009-03-12 2011-04-15 Boehler Edelstahl Gmbh & Co Kg Kaltarbeitsstahl-gegenstand
KR101599721B1 (ko) 2014-02-27 2016-03-04 김종선 원적외선 코팅층을 구비한 전기온돌판넬
CN105526437A (zh) * 2016-02-15 2016-04-27 海安欣凯富机械科技有限公司 金属软管

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE739958C (de) * 1937-04-30 1943-10-08 Sandvikens Jernverks Ab Stahllegierung fuer durch Walzen oder aehnliche Verarbeitungsverfahren hergestellte korrosionsbestaendige, gehaertete Schneidwerkzeuge
CH585799A5 (en) * 1971-12-29 1977-03-15 Lenin Kohaszati Muvek High speed steel based on molybdenum - with good cutting props dependent on vanadium and niobium content
US4224060A (en) * 1977-12-29 1980-09-23 Acos Villares S.A. Hard alloys
JPS60427B2 (ja) * 1979-05-17 1985-01-08 大同特殊鋼株式会社 冷間鍛造性のすぐれた快削鋼
US4264380A (en) * 1979-11-16 1981-04-28 General Electric Company Nitride casehardening process and the nitrided product thereof
JPH0765141B2 (ja) * 1985-09-18 1995-07-12 日立金属株式会社 熱間加工用工具鋼
SE457356C (sv) * 1986-12-30 1989-10-31 Uddeholm Tooling Ab Verktygsstaal avsett foer kallbearbetning
EP0295111B1 (en) * 1987-06-11 1994-11-02 Aichi Steel Works, Ltd. A steel having good wear resistance
JP2756451B2 (ja) * 1987-07-29 1998-05-25 大同特殊鋼株式会社 冷間工具鋼の製造方法
JPH076663B2 (ja) * 1988-01-11 1995-01-30 ダイキン工業株式会社 空気調和装置

Also Published As

Publication number Publication date
AU631690B2 (en) 1992-12-03
ATA242389A (de) 1991-03-15
KR910008158A (ko) 1991-05-30
AU6492290A (en) 1991-04-26
KR0170386B1 (ko) 1999-02-18
TW199910B (es) 1993-02-11
BR9005350A (pt) 1991-09-17
DK0425471T3 (da) 1995-02-20
JPH03197649A (ja) 1991-08-29
DE59008009D1 (de) 1995-01-26
AT393387B (de) 1991-10-10
EP0425471A1 (de) 1991-05-02
JP2794641B2 (ja) 1998-09-10
ZA908467B (en) 1991-12-24
US5160553A (en) 1992-11-03
EP0425471B1 (de) 1994-12-14

Similar Documents

Publication Publication Date Title
ES2068379T3 (es) Acero para trabajar en frio con una elevada resistencia a la compresion.
ES2141446T3 (es) Acero y procedimiento para la fabricacion de piezas de alta resistencia a la abrasion.
BR0116678A (pt) Método para fazer um artigo ferroso e artigo obtido
BR9901764A (pt) Casquilho de mancal deslizante e processo para a sua fabricação
ES2109132B1 (es) Biela de acero forjado.
ES2159662T3 (es) Tubos para la fabricacion de estabilizadores y fabricacion de estabilizadores a partir de dichos tubos.
ES2148705T3 (es) Acero para la fabricacion de piezas mecanicas cortables y pieza obtenida.
ES2170216T3 (es) Acero para la fabricacion de forjados con estructura bainitica y procedimiento de produccion de partes forjadas.
BR9908846A (pt) Componente de construção de material sintético
HUP9802355A2 (hu) Porkohászati úton előállított gyorsacél
BR8807494A (pt) Elemento de construcao protendido,de estrutura composita,e metodo para fabricacao do elemento
ES2054582B1 (es) Empleo de un acero para cilindros laminadores en frio.
ES2190027T3 (es) Biela forjada para motores de pistones alternativos a base de acero al carbono con tapa de cojinete fracturada.
AR023265A1 (es) Material de acero de elevada resistencia para un pozo petrolero, excelente en el craqueo de la tension de sulfuros y metodo para producir un material deacero de elevada resistencia.
MX172566B (es) Conjunto de compuerta deslizable refractaria y metodo
BR0002268A (pt) Chapa de aço com baixo teor em alumìnio para embalagem
AR033220A1 (es) Acero de herramientas con tenacidad reforzada, procedimiento de fabricacion de piezas de este acero y piezas obtenidas
ES2066961T3 (es) Utilizacion de un acero para la fabricacion de tubos de refuerzo de puertas.
MX170074B (es) Barra de acero para maquinado libre de extraccion en frio incluyendo bismuto
AR034875A1 (es) Un procedimiento de fabricacion de una pieza mecanica de acero, y pieza mecanica asi obtenida
ES2041454T3 (es) Utilizacion de un acero resistente al calor para elementos de construccion resistentes a la corrosion, tales como instalaciones de gas de escape.
AR020905A1 (es) Composicion de acero de construccion susceptible de ser cementado, fabricacion de piezas cementadas y tratadas y piezas de acero
ES2530635T3 (es) Aleación basada en titanio-silicio, de alta resistencia y resistente al desgaste y a la oxidación
JPS5686609A (en) Manufacture of roll to be subjected to electric spark dulling work
ATE31555T1 (de) Baggerzaehne.

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 425471

Country of ref document: ES