DE3211602A1 - Verfahren zur herstellung von perlglanzpigmenten mit verbesserten glanzeigenschaften - Google Patents
Verfahren zur herstellung von perlglanzpigmenten mit verbesserten glanzeigenschaftenInfo
- Publication number
- DE3211602A1 DE3211602A1 DE19823211602 DE3211602A DE3211602A1 DE 3211602 A1 DE3211602 A1 DE 3211602A1 DE 19823211602 DE19823211602 DE 19823211602 DE 3211602 A DE3211602 A DE 3211602A DE 3211602 A1 DE3211602 A1 DE 3211602A1
- Authority
- DE
- Germany
- Prior art keywords
- pigments
- layer
- pigment
- mica
- shine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Description
Merck Patent Gesellschaft
mit beschränkter Haftung
Darmstadt
mit beschränkter Haftung
Darmstadt
Verfahren zur Herstellung von Perlglanzpigmenten mit . verbesserten Glanzeigenschaften
Die Erfindung betrifft ein Verfahren zur Herstellung von Perlglanzpigmenten mit verbesserten Glanzeigenschäften
auf der Basis von mit Metalloxiden beschichteten Glimmerschuppen, wobei Glimmer in wäßriger
Suspension mit einer Titandioxidaguatschicht belegt und danach gewaschen, getrocknet und geglüht wird.
Intensität und Reinheit der Interferenzfarbe dieser Pigmente hängt entscheidend von der Ausbildung der
auf die Glimmerschuppen aufgefällten Metalloxidschicht ab. Neben einer homogenen Schichtdicke wird vor allem
gefordert, daß die Schicht rißfrei ausgebildet ist und eine möglichst geringe Lichtstreuung aufweist.
Es ist dabei bekannt, daß sowohl Risse, die insbesondere bei dickeren Schichten beim Glühen der Pigmente
auftreten können, als auch insbesondere die Größe der auf den Glimmer aufgefällten Metalloxidkristalle
eine entscheidende Rolle für das Ausmaß der Streuung spielen. Ebenfalls bekannt ist, daß
die Streuung in der Schicht im betrachteten Bereich um so größer ist je größer die Einzelkristalle des
aufgefällten Metalloxids ausgebildet sind.
GSPHA9 D-wo
Das an den Streuzentren in der Metalloxidschicht entstehende diffuse Licht mindert zum einen die Intensität
im Glanzwinkel des reflektierten Lichtanteils und damit die Farbsättigung, zum anderen bewirkt es eine
Verweißlichung der Interferenzfarbe. Bei zu großen
Kristallen verschwindet der Perlglanz und die Interferenzfarbe vollkommen.
Nach der älteren Anmeldung P 31 51 354 war gefunden worden, daß durch gleichzeitiges Ausfällen von SiO2
und ΑΙ,Ο, zusammen mit dem Titandioxidaquat sehr homogene
und stabile Fällungen erzielt werden, die nicht zu Rissebildung beim Glühen neigen. Diese Pigmente
weisen eine erhöhte Transparenz und Farbkraft auf und sind sehr vorteilhaft für alle üblichen Zwecke
einsetzbar. Durch das Mitausfällen von SiO2 und Al2O3,
die beide einen geringen Brechungsindex besitzen, wird jedoch der Brechungsindex der Metalloxidschicht gegenüber
einer reinen TiO2-Fällung deutlich herabgesetzt.
Dies führt dazu, daß der Anteil des an der Oberfläche dieser Pigmentteilchen reflektierten Lichtes geringer
ist als bei reinen TiO2/Glimmer-Pigmenten.
Obwohl der mit diesen älteren Pigmenten erzielte samtige Glanz für viele Anwendungen sehr gut geeignet ist,
besteht für andere Anwendungen ein Bedürfnis nach Pigmenten mit spitzem Glanz und lebhaftem Funkeln. Aufgabe
der vorliegenden Erfindung war es daher, Pigmente zu finden, die den lebhaften Glanz von Pigmenten mit
reiner TiO2-Beschichtung besitzen, daneben aber durch eine homogene und rissefreie Schicht ein vermindertes
Streulicht und eine höhere Farbsättigung aufweisen.
CJSPHA9 D-WO
Eine Kombination dieser Eigenschaften schien nicht erreichbar, da einerseits die Erhöhung des Brechungsindex
durch Verminderung des Anteils niedrigbrechender Bestandteile der Schicht, die Inhomogenität und Rissebildung
in der Schicht erhöht und andererseits aber die zur Vermeidung dieser Nachteile zugesetzten Bestandteile
den Brechungsindex wieder herabsetzen. Es wurde nun jedoch gefunden, daß diese Aufgabe überraschenderweise
durch eine zweistufige Beschichtung gelöst werden kann, wobei sich an eine entsprechend
der älteren Anmeldung P 31 51 354 vorgenommene Beschichtung eine Zweitbeschichtung in Gegenwart von
Titansulfat anschließt.
Gegenstand der Erfindung ist daher ein Verfahren zur Herstellung von Perlglanzpigmenten mit verbesserten
Glanzeigenschaften auf der Basis von mit Metalloxiden beschichteten Glimmerschuppen, wobei Glimmer in wäßriger
Suspension mit einer Titandioxidaguatschicht belegt und danach gewaschen, getrocknet und geglüht
wird, das dadurch gekennzeichnet ist, daß das Verfahren als Zweistufenverfahren durchgeführt wird,
wobei zunächst eine Titandioxidaquatschicht zusammen mijt Siliciumdioxid und Aluminiumhydroxid als einheitliche
Schicht aufgefällt wird, das so gewonnene Pigment nach Waschen, Trocknen und Glühen in einer titansulfathaltigen
Lösung suspendiert und durch langsames Erhitzen der Suspension erneut beschichtet wird.
Gegenstand der Erfindung sind auch die so gewonnenen Pigmente und ihre Verwendung.
GSPHA9 D-wo
Der Vorteil der erfindungsgemäßen Pigmente liegt darin, daß es mit dem erfindungsgemäßen Verfahren überraschenderweise
gelungen ist, sowohl hohe Transparenz und Farbkraft durch homogene rißfreie Schichten als auch
lebhaften Glanz durch hohen Brechungsindex in einem Pigment zu vereinigen. Dies war weder vorauszusehen
noch für möglich gehalten worden. Es mußte vielmehr angenommen werden, daß bestenfalls ein Kompromiß zwischen
beiden Eigenschaften möglich sein würde:
Die Herstellung der Pigmente erfolgt nach einem Zweistufenverfahren,
wobei die erste Stufe mit dem Verfahren nach der älteren Anmeldung P 31 51 354 identisch
ist. Dazu werden Glimmerschuppen, die in der Regel einen Durchmesser von etwa 5 - 200 μΐη und eine Dicke
von etwa 0,1 - 5 pm besitzen, in einer wäßrigen Lösung suspendiert, die mit einer geeigneten Säure, wie z.B.
Salzsäure oder Schwefelsäure, auf einen pH-Wert von etwa 0,5 - 5, insbesondere etwa 2,O - 3,0, gebracht
wird. Zu dieser auf etwa 50 - 100 0C, vorzugsweise etwa 70 - 80 0C, erhitzten Suspension wird dann eine
Titansalzlösung langsam zulaufen lassen, wobei durch gleichzeitige Zugabe einer Base der pH-Wert der Suspension
weitgehend konstant gehalten wird. Als Titansalz kann dabei jedes lösliche Titansalz verwendet werden.
Bevorzugt werden TiCl- oder Titanylsulfat verwendet.
Nach dem Verfahren der P 31 51 354 wird die Fällung des Titandioxidaquats in Gegenwart von Aluminiumionen
durchgeführt. Dabei ist es gleichgültig, ob die Aluminiumionen im Fällungsgefäß vorgelegt werden oder in
der Titansalzlösung enthalten sind. Im Prinzip können alle Aluminiumsalze verwendet werden, die in den entsprechenden
Titansalzlösungen löslich sind. Bevorzugt
wird jeweils das Aluminiumsalz mit einem dem Titansalz entsprechenden Anion verwendet, also insbesondere Aluminiumchlorid
oder Aluminiumsulfat. Der Zusatz von Aluminiumionen erfolgt in jedem Fall in der Weise,
daß ein Gewichtsverhältnis von TiCl4 : AlCl3 . 6 E^O
von etwa 50 : 1 bis etwa 2:1, vorzugsweise etwa 30 : 1 bis etwa 5:1, eingehalten wird bzw. entsprechende
Gewichtsverhältnisse beim Einsatz anderer Salze.
Das nach der P 31 51 354 gleichzeitig mit auszufällende si°2 w^rc* vorzugsweise der Base zugesetzt, die zur
Aufrechterhaltung des pH-Wertes der Fällungssuspension gleichzeitig mit der sauren Titansalzlösung zudosiert
wird. Als Base wird vorzugsweise eine Alkalilauge, insbesondere NaOH, verwendet, wobei das mit auszufällende
Siliciumdioxid bevorzugt in Form eines löslichen Alkalisilicate, z.B. als Natriumsilicat, darin
enthalten ist. Wird NaOH als Base verwendet, so wird in der Regel ein Gewichtsverhältnis von NaOH : SiO2
von 5 : 1 bis 400 : 1, vorzugsweise von 20 j I bis 200 : 1, eingehalten.
Die beiden Lösungen werden langsam so zugegeben, das di,e in der Glimmersuspension durch Hydrolyse entstehenden
Hydroxide bzw. Oxidaguate sich jeweils vollständig auf der Glimmeroberfläche abscheiden, ohne dafi
wesentliche Mengen von frei in der Suspension beweglichen Nebenprodukten entstehen. Die dabei zur Anwendung
kommenden Zulaufgeschwindigkeiten sind so gewählt, daß pro Hinute und pro Quadratmeter zu belegender Oberfläche
etwa 0,01 - 20 . 10 mol an auszufällenden SaI-
3Q zen zugeführt wird. Je nach der gewünschten Dicke der
Beschichtung werden dabei Beschichtungszeiten von mehreren Stunden bis zu mehreren Tagen benötigt.
GSFHA9 D-WO
Nach Erreichen der gewünschten Schichtdicke bzw. der gewünschten Interferenzfarbe wird die Beschichtung
beendet und die Pigmente werden analog dem üblichen Verfahren abgetrennt, gewaschen, getrocknet und geglüht.
Zum Glühen werden Temperaturen von etwa 500 1000 0C, insbesondere von 700 - 1000 0C, angewendet,
wobei die gefällten Metallhydroxide bzw. Oxidaquate entwässert werden und in die entsprechenden Oxide
übergehen. In der Metalloxidschicht liegen Titan, ο Silicium und Aluminium in oxidischer Form und gegebenenfalls
auch als Verbindung, wie z.B. als AIuminiumsilicat, in homogener Verteilung nebeneinander
vor. Dabei hat das Silicium, berechnet als SiO2 und
bezogen auf die Metalloxidschicht, in der Regel einen Anteil von etwa 0,1 bis etwa 20 Gewichtsprozent, vorzugsweise
von etwa 1-10 Gewichtsprozent, und das Aluminium, berechnet als Al2O3 und bezogen auf die
Metalloxidschicht, einen Anteil von etwa 0,1 bis etwa 20 Gewichtsprozent, vorzugsweise von etwa 0,2 bis etwa
10 Gewichtsprozent. SiO2 und Al2O3 bilden zusammen in
der Regel 0,2 - 30 Gewichtsprozent, vorzugsweise etwa 2-20 Gewichtsprozent, der Metalloxidschicht.
Dap so gewonnene Rohpigment, das neben Zusätzen von
SiO2 und Al2O3 selbstverständlich auch weitere färbende
oder nicht färbende Metalloxide, wie z.B.
Chromoxid oder Eisenoxid, enthalten kann, wird dann einer zweiten Beschichtung unterworfen. Dazu wird
das Pigment erneut in Wasser suspendiert und mit einer Titansalzlösung versetzt. Wesentlich dabei
3Q ist, daß das Rohpigment mit der Titansalzlösung
in Berührung kommt, bevor die Hydrolyse zu Titandioxidaguat beginnt und daß danach erst durch geeignete
Maßnahmen die Hydrolyse in Gang gesetzt wird.
GSPHA9 D-WO
--- 32T1602
Dies kann z.B. dadurch geschehen, daß das Rohpigment mit der Titansalzlosung versetzt wird und danach die
Suspension langsam zum Sieden erhitzt wird, wobei die Hydrolyse einsetzt und Titandioxidaguat ausgefällt
wird.
Bei dieser Zweitbeschichtung passiert zweierlei. Zum einen wird durch die Änderung der Schichtdicke durch
zusätzlich aufgefälltes Titandioxidaguat die Interferenzfarbe des Rohpigments entsprechend der höheren
Schichtdicke verändert. Zum anderen wird der Brechungsindex des Pigments wesentlich erhöht. Ohne an eine
Theorie gebunden zu sein, kann vermutet werden, daß beim Suspendieren des Rohpigments in der Titansalzlösung
diese in die bereits aufgefällte Schicht eindringt und bei der dann folgenden Hydrolyse nicht nur
eine Fällung auf, sondern auch in der zuerst aufgefällten Schicht erfolgt und diese Schicht dabei zusätzlich
verdichtet wird.
Es kann dies jedoch nicht die alleinige Erklärung für die überraschende Vorteilhaftigkeit der nach dem
erfindungsgemäßen Verfahren gewonnenen Pigmente sein, denn es wurde gefunden, daß zwar für die Herstellung
des Rohpigments beliebige Titansalzlösungen, insbesondere das Chlorid oder das Sulfat, verwendet werden
können, nicht jedoch für die Zweitfällung. Überraschenderweise erhält man dann besonders vorteilhafte Pigmente,
wenn für die Zweitfällung eine Titanylsulfatlösung verwendet wird oder eine Titansalzlösung, die
zumindest eine gewisse Menge Sulfationen enthält. Diese Menge sollte vorzugsweise mindestens etwa das 0,5-2-fache
der st-röchiometrischen Menge betragen.
GSPHA9 D-wo
Die Zweitbeschichtung wird so lange fortgesetzt, bis die für das Endprodukt erwünschte Interferenzfarbe
erreicht ist. Danach wird das Pigment auf übliche Weise abgetrennt, gewaschen, getrocknet und erneut
bei einer Temperatur zwischen 500 und 1000 0C geglüht. Die so erhaltenen Pigmente zeigen eine wesentlich erhöhte
Brillanz, einen meßbar höheren Glanz und eine hervorragende Farbkraft. Die Pigmente können wie die
bisher bekannten verwendet werden, also z.B. zur Pigmentierung von Kunststoffen, Farben und Lacken, insbesondere
auch in Körperpflegemitteln und Kosmetika.
A) Herstellung einer sulfathaltigen Titansalzlösung
Zu einer klaren Lösung von 36,25 g Na2SO4 in
125 ml Wasser werden 370 ml einer 20 %igen Lösung von TiCl4 in 5 %iger Salzsäure getropft,
danach die überschüssige Säure tropfenweise mit 22,5 ml 15 %iger Natronlauge neutralisiert
und die klare Lösung mit Wasser zu 1 1 aufgefüllt.
B) Herstellung des Rohpigments
Eine Suspension von 60 g Kaliglimmer der Kornfraktion 10 - 70 pm in 2 1 Wasser wird auf 75 0C
erhitzt und mit Salzsäure auf pH 2,6 eingestellt. Danach werden gleichzeitig eine Lösung, die 15
Gewichtsprozent TiCl4, 5 Gewichtsprozent HCl und pro 1 20 g AlCl3 . 6 H2O enthält und eine Lösung,
die 15 Gewichtsprozent NaOH und pro 1 3,3 g SiO2 (als Natriumsilicat) enthält, so zudosiert, daß
RSPHA9 D-wo
- ίο -
der pH-Wert bei 2,6 konstant gehalten wird. Nach Erreichen einer goldenen Interferenzfarbe wird
die Beschichtung abgebrochen, das Pigment abfiltriert, salzfrei gewaschen, bei 120 0C getrocknet
und 30 Minuten bei 800 0C geglüht.
C) Zweitbeschichtung
Eine Suspension von 100 g des Pigmentes nach Beispiel 1 B in 400 ml Titansalzlösung nach
Beispiel 1 A wird innerhalb von 30 Minuten auf 100 0C erhitzt und bei dieser Temperatur
so lange gehalten, bis sich die Interferenzfarbe, die langsam in Rotblau übergeht, nicht
mehr ändert, was nach etwa 2 Stunden der Fall ist. Danach wird das Pigment abgetrennt, gewaschen,
bei 120 0C getrocknet und 30 Minuten bei 800 0C geglüht. Man erhält ein Pigment mit
kräftiger rotblauer Interferenzfarbe und hoher
Brillanz.
Ein entsprechend Beispiel IB hergestelltes Pigment mit blauer Interferenzfarbe wird analog Beispiel 1 C
bei 100 0C beschichtet. Nach der üblichen Aufarbeitung wird ein Pigment erhalten, das eine kräftige grüne
Interferenzfarbe aufweist und hohe Brillanz besitzt.
In analoger Weise lassen sich Rohpigmente beliebiger Interferenz farben mit einer Zweitbeschichtung zur
Erhöhung der Farbkraft und der Brillanz versehen.
GSPHA9 D-wo
Claims (3)
1. Verfahren zur Herstellung von Perlglanzpigmenten mit verbesserten Glanzeigenschaften auf der Basis von
mit Metalloxiden beschichteten Glimmerschuppen, wobei Glimmer in wäßriger Suspension mit einer Titandioxidaguatschicht
belegt und danach gewaschen, getrocknet und geglüht wird, dadurch gekennzeichnet, daß das
Verfahren als Zweistufenverfahren durchgeführt wird, wobei zunächst eine Titandioxidaquatschicht zusammen
mit Siliciumdioxid und Aluminiumhydroxid als einheitliche Schicht aufgefällt wird, das so gewonnene
Pigment nach Waschen, Trocknen und Glühen in einer titansulfathaltigen Lösung suspendiert und durch langsames
Erhitzen der Suspension erneut beschichtet wird.
2. Perlglanzpigmente auf der Basis von mit Metalloxiden beschichteten Glimmerschuppen, dadurch gekennzeichnet,
daß sie nach dem Verfahren nach Anspruch 1 hergestellt sind.
3. Verwendung der Perlglanzpigmente nach Anspruch 2 zur Pigmentierung von Kunststoffen, Farben, Lacken und
Körperpflegemittel.