DE255302C - - Google Patents
Info
- Publication number
- DE255302C DE255302C DENDAT255302D DE255302DA DE255302C DE 255302 C DE255302 C DE 255302C DE NDAT255302 D DENDAT255302 D DE NDAT255302D DE 255302D A DE255302D A DE 255302DA DE 255302 C DE255302 C DE 255302C
- Authority
- DE
- Germany
- Prior art keywords
- viscose
- cellulose
- content
- fabrics
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
KAISERLICHESIMPERIAL
PATENTAMT.PATENT OFFICE.
Das Appretieren bzw. Füllen oder Schlichten von baumwollenen Geweben mit Hilfe von Viskose (Zellulosexanthogenat) für sich oder im Gemisch mit anorganischen oder organisehen Füllstoffen oder Pigmenten oder Farbstoffen begegnet der Schwierigkeit, daß die aus der Viskose bei ihrer Zersetzung sich regenerierende Zellulose bzw. Hydrozellulose nicht genügend in die Faser selbst eindringtThe finishing, filling or sizing of cotton fabrics with the help of Viscose (cellulose xanthate) on its own or in a mixture with inorganic or organic substances Fillers or pigments or dyes encountered the difficulty that those from the viscose during their decomposition regenerating cellulose or hydrocellulose does not penetrate sufficiently into the fiber itself
ίο und demzufolge allzusehr auf der Oberfläche des Gewebes sichtbar ist und die Maschen des Gewebes ausfüllt. Dasselbe gilt von mit der Viskose in bisheriger Weise geschlichteten Fäden, bei denen sich die Zellulose ebenfalls mehr auf der Oberfläche als im Innern regeneriert. Die Folge davon ist, daß die in bisheriger Weise mit Viskose allein oder im Gemisch mit den oben genannten Substanzen appretierten Gewebe oder geschlichteten Fäden oder aus geschlichteten Fäden hergestellte Gewebe das Aussehen und den Griff der natürlichen, also nicht appretierten Gewebe zum Teil oder ganz verlieren. Dieser Schwierigkeit wird vorliegender Erfindung nach dadurch begegnet, daß man die zur Appretur oder Schlichte zu verwendende Viskose so reich an Ätzalkalien macht, daß ihr Gehalt an Ätzalkali zum mindesten so viel beträgt als ihr Gehalt an Zellulose bzw. Zellulosehydrat. Eine an Alkali sehr reiche Viskose dringt nach Beobachtungen des Erfinders sehr tief in die Gewebefaser ein, so daß mit ihr allein oder im Gemisch mit anderen Appreturbzw. Schlichtmitteln oder mit anorganischen oder organischen Füllstoffen oder Pigmenten oder Farbstoffen für sich oder im Gemisch untereinander appretierte Gewebe oder geschlichtete Fäden oder aus solchen geschlichteten Fäden hergestellte Gewebe bei einem außerordentlichen Gewinn an Griffigkeit, Festigkeit und Gewicht vom Aussehen natürlicher ' Gewebe bzw. Fäden nicht weit entfernt sind bzw. jenen gleichkommen. Es gelingt nach dem vorliegenden Verfahren, sehr große Mengen von Zellulose bzw. Zellulosehydrat in bzw. auf der Faser niederzuschlagen ohne erhebliche Bildung von oberflächlichen bzw. die Maschen ausfüllenden, das Gewebe verunstaltenden Schichten.ίο and therefore too much on the surface of the fabric is visible and fills the mesh of the fabric. The same is true of with the viscose in the previous way sized threads, in which the cellulose is also regenerated more on the surface than inside. The consequence of this is that the previous Woven fabrics or sized threads finished with viscose alone or in a mixture with the substances mentioned above or fabrics made from sized threads the look and feel of natural, So lose some or all of the unfinished tissue. This difficulty is countered according to the present invention by the fact that the viscose to be used for the finish or size is so makes it rich in caustic alkalis that their caustic alkali content is at least as much than their cellulose or cellulose hydrate content. A viscose very rich in alkali penetrates very deeply into the fabric fiber according to the inventor's observations, so that with it alone or in a mixture with other finishes Sizing agents or with inorganic ones or organic fillers or pigments or dyes alone or as a mixture fabrics or sized threads or threads that are sized from one another Fabrics made from threads with an extraordinary gain in grip and strength and weight are not far removed from the appearance of natural fabrics or threads or equal to those. The present process succeeds in producing very large quantities of cellulose or cellulose hydrate in or on the fiber without significant Formation of superficial or the mesh filling, disfiguring the tissue Layers.
Zur Ausführung des Verfahrens wird rohe oder nach einem der bekannten Verfahren (d. h. durch Salze, schwache Säuren und Salze, Alkohole, schwache Säuren und Alkohole, andere wasserentziehende Mittel, Bisulfitlauge, schweflige Säure, Kohlensäure und andere schwache Säuren u. dgl.) gereinigte Viskose, die einen Alkaligehalt besitzt, welcher zum mindesten so viel beträgt als ihr Gehalt an Zellulose bzw. Zellulosehydrat, von Hand oder mittels entsprechender Maschinen auf die zu appretierenden Gewebe oder Gespinste aufgebracht bzw. jenen einverleibt. Diese Imprä-To carry out the process is raw or by one of the known methods (i.e. by salts, weak acids and salts, alcohols, weak acids and alcohols, other dehydrating agents, bisulphite lye, sulphurous acid, carbonic acid and others weak acids and the like.) Purified viscose, which has an alkali content, which for is at least as much as its cellulose or cellulose hydrate content, by hand or Applied to the fabric or web to be finished using appropriate machines or incorporated into them. This impres-
gnierung kann auch, um ein noch tieferes Eindringen in die Faser zu bewerkstelligen, im luftverdünnten Raum oder unter erhöhtem Druck geschehen. Das erforderliche Ätzalkali wird entweder schon bei der Herstellung der Viskose oder aber der fertigen Viskose zugesetzt. gnation can also be used to achieve even deeper penetration into the fiber, happen in an air-diluted room or under increased pressure. The required caustic alkali is either added to the viscose during manufacture or to the finished viscose.
Will man die durch den Alkaligehalt bedingte Schrumpfung der Gewebe bzw. Gespinste vermeiden, so empfiehlt sich, das Auswaschen oder die Trocknung unter Streckung der Gespinste oder Gewebe vorzunehmen.If you want the shrinkage of the fabrics or webs caused by the alkali content avoid, it is advisable to wash or dry while stretching the web or fabric.
Die Unlöslichmachung der Viskose (die Regeneration der Zellulose bzw. Hydrozellulose) und die Befreiung derselben von den Verunreinigungen geschieht zweckmäßig in bekannter Weise.The insolubilization of the viscose (the regeneration of the cellulose or hydrocellulose) and their liberation from impurities is expediently done in a known manner Way.
Aus führung s beispiele:Implementation examples:
i. 100 Gewichtsteile einer Rohviskose mit einem Zellulosegehalt von 10 bis 15 Prozent und einem Gehalt an Ätznatron von 3,5 bis 7 Prozent werden mit 30 bis 150 Gewichtsteilen einer Natronlauge von 50 ° Be. (50 Pro- zent) versetzt, und mit dieser Masse wird ein baumwollenes Gewebe auf einer entsprechenden Appreturmaschine appretiert oder ein Baumwollfaden auf einer entsprechenden Schlichtmaschine geschlichtet. Die Fertigstellung geschieht nach einem der bekannten Verfahren.i. 100 parts by weight of a raw viscose with a cellulose content of 10 to 15 percent and a content of caustic soda from 3.5 to 7 percent with 30 to 150 parts by weight of a sodium hydroxide solution of 50 ° Be. (50 pro cent), and with this mass a cotton fabric is placed on a corresponding Finishing machine finished or a cotton thread sized on a suitable sizing machine. Completion happens according to one of the known methods.
2. Zu der bei 1 beschriebenen Masse kommen noch 10 bis 20 Gewichtsteile Chinaclay oder Zinkweiß.2. 10 to 20 parts by weight of quinaclay are added to the mass described in 1 or zinc white.
3. Zu der bei 1 oder 2 beschriebenen Masse kommen noch 10 bis 20 Gewichtsteile eines weichmachenden Mittels, wie Glycerin, Türkischrotöl, Aluminiumoleat, Polyricinolsäure, Ricinusöl, Zucker; Sirup u. dgl. ■3. In addition to the mass described in 1 or 2, there are 10 to 20 parts by weight a softening agent such as glycerin, turkey red oil, aluminum oleate, polyricinoleic acid, Castor oil, sugar; Syrup and the like ■
4. Zu der unter 1 oder 2 oder 3 beschriebenen Masse kommen noch 10 bis 20 Gewichtsteile Stärke oder Leim in einer entsprechenden Wassermenge gelöst.4. In addition to the mass described under 1 or 2 or 3, there are 10 to 20 parts by weight of starch or glue in a corresponding one Amount of water dissolved.
5. Wie die Beispiele 1 bis 4, jedoch mit dem Unterschied, daß man an Stelle der Rohviskose eine denselben Zellulosegehalt aufweisende Lösung eines mit Hilfe von Kochsalz oder Ammonsulfat oder Chlorzink oder Alkohol aus alkoholischer oder mit einer schwachen Säure neutralisierter Rohviskose erzielten Niederschlages verwendet.5. As in Examples 1 to 4, but with the difference that instead of the raw viscose a solution having the same cellulose content with the aid of table salt or ammonium sulfate or zinc chloride or Alcohol from raw viscose that is alcoholic or neutralized with a weak acid obtained precipitation is used.
Claims (1)