DE20220582U1 - Borosilicatglas - Google Patents
BorosilicatglasInfo
- Publication number
- DE20220582U1 DE20220582U1 DE20220582U DE20220582U DE20220582U1 DE 20220582 U1 DE20220582 U1 DE 20220582U1 DE 20220582 U DE20220582 U DE 20220582U DE 20220582 U DE20220582 U DE 20220582U DE 20220582 U1 DE20220582 U1 DE 20220582U1
- Authority
- DE
- Germany
- Prior art keywords
- borosilicate glass
- customary
- glass according
- oxide
- zro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Der Beschreibungstext wurde nicht elektronisch erfaßt
Claims (11)
1. Aluminiumfreies Borosilicatglas mit guter chemischer Beständigkeit,
mit einer Zusammensetzung (in Gew.-% auf Oxidbasis) von:
SiO2 65-77
B2O3 7-20
Li2O 0-2
Na2O 0-4
K2O 3-12
MgO 0-2
CaO 0-2
mit MgO + CaO 0-3
BaO 0-3
ZnO 0-2
ZrO2 0,8-12
TiO2 0-5
CeO2 0-1
F- 0-0,6
sowie ggf. übliche Läutermittel in üblichen Mengen
SiO2 65-77
B2O3 7-20
Li2O 0-2
Na2O 0-4
K2O 3-12
MgO 0-2
CaO 0-2
mit MgO + CaO 0-3
BaO 0-3
ZnO 0-2
ZrO2 0,8-12
TiO2 0-5
CeO2 0-1
F- 0-0,6
sowie ggf. übliche Läutermittel in üblichen Mengen
2. Borosilicatglas nach Anspruch 1,
gekennzeichnet durch
eine Zusammensetzung (in Gew.-% auf Oxidbasis) von:
SiO2 67-75
B2O3 9-18
Li2O 0-1
Na2O 0-3
K2O 5-10
mit Li2O + Na2O + K2O 5,5-13,5
CaO 0-1
BaO 0-1
ZnO 0-1
TiO2 0-1
ZrO2 0,8-10,5
CeO2 0-0,4
F- 0-0,6
sowie ggf. übliche Läutermittel in üblichen Mengen
SiO2 67-75
B2O3 9-18
Li2O 0-1
Na2O 0-3
K2O 5-10
mit Li2O + Na2O + K2O 5,5-13,5
CaO 0-1
BaO 0-1
ZnO 0-1
TiO2 0-1
ZrO2 0,8-10,5
CeO2 0-0,4
F- 0-0,6
sowie ggf. übliche Läutermittel in üblichen Mengen
3. Borosilicatglas nach Anspruch 1 oder 2,
gekennzeichnet durch
eine Zusammensetzung (in Gew.-% auf Oxidbasis) von:
SiO2 68-74
B2O3 9-13
Li2O 0-1
Na2O 0-3
K2O 5-10
mit Li2O + Na2O + K2O 5,5-13,5
ZrO2 3-7
CeO2 0-0,4
F- 0-0,6
sowie ggf. übliche Läutermittel in üblichen Mengen
SiO2 68-74
B2O3 9-13
Li2O 0-1
Na2O 0-3
K2O 5-10
mit Li2O + Na2O + K2O 5,5-13,5
ZrO2 3-7
CeO2 0-0,4
F- 0-0,6
sowie ggf. übliche Läutermittel in üblichen Mengen
4. Borosilicatglas nach wenigstens einem der Ansprüche 1 bis 3,
gekennzeichnet durch
eine Zusammensetzung (in Gew.-% auf Oxidbasis) von:
SiO2 71-74
B2O3 9-12
Li2O 0-1
Na2O 0-3
K2O 7-10
mit Li2O + Na2O + K2O 7-13,5
ZrO2 4-7
sowie ggf. übliche Läutermittel in üblichen Mengen
SiO2 71-74
B2O3 9-12
Li2O 0-1
Na2O 0-3
K2O 7-10
mit Li2O + Na2O + K2O 7-13,5
ZrO2 4-7
sowie ggf. übliche Läutermittel in üblichen Mengen
5. Borosilicatglas nach Anspruch 1 oder 2,
gekennzeichnet durch
eine Zusammensetzung (in Gew.-% auf Oxidbasis) von:
SiO2 68-71
B2O3 8-11
Li2O 0-1
Na2O 0-3
K2O 8-11
mit Li2O + Na2O + K2O 8-13,5
ZrO2 7,5-10,5
sowie ggf. übliche Läutermittel in üblichen Mengen
SiO2 68-71
B2O3 8-11
Li2O 0-1
Na2O 0-3
K2O 8-11
mit Li2O + Na2O + K2O 8-13,5
ZrO2 7,5-10,5
sowie ggf. übliche Läutermittel in üblichen Mengen
6. Borosilicatglas nach Anspruch 1 oder 2,
gekennzeichnet durch
eine Zusammensetzung (in Gew.-% auf Oxidbasis) von:
SiO2 70-75
B2O3 15-18
Li2O 0-1
Na2O 0-3
K2O 5-8
mit Li2O + Na2O + K2O 5,5-10,5
CaO 0-1
BaO 0-1
TiO2 0-1
ZrO2 0,8-5
sowie ggf. übliche Läutermittel in üblichen Mengen
SiO2 70-75
B2O3 15-18
Li2O 0-1
Na2O 0-3
K2O 5-8
mit Li2O + Na2O + K2O 5,5-10,5
CaO 0-1
BaO 0-1
TiO2 0-1
ZrO2 0,8-5
sowie ggf. übliche Läutermittel in üblichen Mengen
7. Borosilicatglas nach Anspruch 1 oder 2,
gekennzeichnet durch
eine Zusammensetzung (in Gew.-% auf Oxidbasis) von:
SiO2 67-70
B2O3 15-18
Li2O 0-1
Na2O 0-3
K2O 7-10
mit Li2O + Na2O + K2O 7-12,5
ZnO 0-1
ZrO2 2,5-6
sowie ggf. übliche Läutermittel in üblichen Mengen
SiO2 67-70
B2O3 15-18
Li2O 0-1
Na2O 0-3
K2O 7-10
mit Li2O + Na2O + K2O 7-12,5
ZnO 0-1
ZrO2 2,5-6
sowie ggf. übliche Läutermittel in üblichen Mengen
8. Borosilicatglas nach wenigstens einem der Ansprüche 1 bis 7,
dadurch gekennzeichnet,
dass das Glas wenigstens 0,2 Gew.-% Li2O enthält.
9. Borosilicatglas nach wenigstens einem der Ansprüche 1 bis 8,
dadurch gekennzeichnet,
dass das Glas wenigstens 0,5 Gew.-% Na2O enthält.
10. Borosilicatglas nach wenigstens einem der Ansprüche 1 bis 9,
dadurch gekennzeichnet,
dass es bis auf unvermeidliche Verunreinigungen frei ist von As2O3 und
Sb2O3.
11. Borosilicatglas nach wenigstens einem der Ansprüche 1 bis 10
mit einem thermischen Ausdehnungskoeffizienten α(20°C; 300°C) zwischen
3,7 × 10-6/K und 6 × 10-6/K und einer Verarbeitungstemperatur VA zwischen
1040°C und 1200°C.