DE19838017A1 - Schweißbare, korrosionsbeständige ALMg-Legierungen, insbesondere für die Verkehrstechnik - Google Patents

Schweißbare, korrosionsbeständige ALMg-Legierungen, insbesondere für die Verkehrstechnik

Info

Publication number
DE19838017A1
DE19838017A1 DE19838017A DE19838017A DE19838017A1 DE 19838017 A1 DE19838017 A1 DE 19838017A1 DE 19838017 A DE19838017 A DE 19838017A DE 19838017 A DE19838017 A DE 19838017A DE 19838017 A1 DE19838017 A1 DE 19838017A1
Authority
DE
Germany
Prior art keywords
weight
scandium
corrosion
weldable
alloy according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19838017A
Other languages
English (en)
Other versions
DE19838017C2 (de
Inventor
Blanka Lenczowski
Rainer Rauh
Dietrich Wieser
Gerhard Tempus
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Airbus Defence and Space GmbH
Original Assignee
DaimlerChrysler AG
Vereinigte Aluminium Werke AG
Vaw Aluminium AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to DE19838017A priority Critical patent/DE19838017C2/de
Application filed by DaimlerChrysler AG, Vereinigte Aluminium Werke AG, Vaw Aluminium AG filed Critical DaimlerChrysler AG
Priority to DE59907283T priority patent/DE59907283D1/de
Priority to CZ20001446A priority patent/CZ20001446A3/cs
Priority to PCT/DE1999/002549 priority patent/WO2000011229A2/de
Priority to CN99801414A priority patent/CN1103828C/zh
Priority to US09/530,068 priority patent/US6258318B1/en
Priority to RU2000112644/02A priority patent/RU2226566C2/ru
Priority to EP99952401A priority patent/EP1027466B1/de
Priority to JP2000566479A priority patent/JP2003526733A/ja
Priority to CA002306892A priority patent/CA2306892C/en
Publication of DE19838017A1 publication Critical patent/DE19838017A1/de
Application granted granted Critical
Publication of DE19838017C2 publication Critical patent/DE19838017C2/de
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Schweißbare, korrosionsbeständige Aluminium-Magnesium-Legierung, bestehend zumindest aus 3-5 Gew.-% Magnesium (Mg), 0,05-0,15 Gew.-% Zirkonium (Zr), 0,05-0,12 Gew.-% Mangan (Mn), 0,01-0,2 Gew.-% Titan (Ti), 0,05-0,5 Gew.-% eines oder mehrere Elemente der Scandiumgruppe und/oder Terbium (Tb), wobei zumindest Scandium enthalten ist sowie Aluminium und unvermeidbare Verunreinigungen mit max. 0,2 Gew.-% Silizium (Si).

Description

Die Erfindung betrifft eine schweißbare, korrosionsbeständige Aluminium-Magnesium-Legierung, welche als wesentliche Komponente eine ternäre Aluminium-Scandium-Zirkonium-Phase enthält. Eine derartige Legierung ist beispielsweise aus der US 5,624,632 bekannt und ist aufgrund ihrer geringen Dichte, hohen Festigkeit und Korrosionsbeständigkeit vor allem für Anwendungen in der Luftfahrt von Interesse. Durch Zugabe von Elementen der seltenen Erden oder den seltenen Erden ähnlichen Elementen werden in der Aluminium-Magnesium-Legierung Dispersoide erzeugt, die gemäß dem o. g. US-Patent eine höhere Festigkeit und Korrosionsbeständigkeit erzeugen. Hinsichtlich der Schweißbarkeit einer derartigen Legierung kann dem o. g. US-Patent keine An­ gabe entnommen werden.
Es ist Aufgabe der vorliegenden Erfindung eine schweißbare, korrosionsbeständige Aluminium- Magnesium-Legierung zu schaffen, welche hinsichtlich Festigkeit und Korrosionsverhalten der bekannten Legierung zumindest nicht nachsteht und zusätzlich zu einer guten Schweißbarkeit, eine hohe Rekristallisationsschwelle aufweist. Diese Aufgabe wird durch eine Aluminium- Magnesium-Legierung gemäß Patentanspruch 1 gelöst.
Diese neue Legierung weist gegenüber der bekannten Legierung vor allem einen deutlich niedri­ geren Mangananteil auf, wobei sich überraschenderweise eine verbesserte Korrosionsbestän­ digkeit, vor allem im sensibilisierten Zustand der aus dieser Legierung hergestellten Teile zeigte, also beispielsweise, wenn kaltverformte Teile über längere Zeit einer erhöhten Temperatur aus­ gesetzt werden. Es wird vermutet, daß diese positiven Eigenschaften vor allem durch das Ver­ hältnis von Mangan zu Scandium bestimmt werden. So zeigt sich eine verbesserte Korrosions­ beständigkeit bei einem Verhältnis Mn : Sc < 2. Auch der im Unterschied zur bekannten Legie­ rung enthaltene Titananteil trägt, zusätzlich zur Wirkung als Kornfeinungsmittel, zur Festigkeits­ erhöhung bei, da Titan das Zirkonium in der ternären Al-Sc-Zr-Phase ersetzen kann, wobei die Löslichkeit von Titan jedoch niedriger als von Zirkonium ist.
Es hat sich weiterhin gezeigt, daß Scandium zumindest in gewissen Grenzen durch Terbium oder auch durch Cer ersetzt werden kann. Beim Ersatz durch Terbium ist jedoch zur Erzielung gleich­ bleibender Eigenschaften eine größere Zugabe als die des ersetzten Scandiums erforderlich.
Eine für Land-, See- oder Luftfahrzeuge besondere günstige Legierung enthält zumindest 0,15 Gew.-% Scandium. Die Zugabe von Lanthaniden bewegt sich vorteilhafterweise in einem Gew.-%- Bereich zwischen 0,05 und 0,35, wobei sich dieser Bereich bei Verwendung eines Lanthaniden­ gemisches auf das Gesamtgemisch bezieht. Die Legierung verträgt Verunreinigungen an Silizium bis zu 0,2 Gew.-%, darüber verschlechtern sich vornehmlich die dynamischen Eigenschaften.

Claims (5)

1. Schweißbare, korrosionsbeständige Aluminium-Magnesium-Legierung bestehend zumin­ dest aus 3-5 Gew.-% Magnesium (Mg), 0,05-0,15 Gew.-% Zirkonium (Zr), 0,05-0,012 Gew.-% Mangan (Mn), 0,01-0,2 Gew.-% Titan (Ti), 0,05-0,5 Gew.-% eines oder mehrere Elemente der Scandiumgruppe und/oder Terbium (Tb) wobei zumindest Scandium ent­ halten ist, sowie Aluminium und unvermeidbare Verunreinigungen mit max. 0,2 Gew.-% Silizium (Si).
2. AlMg-Legierung nach Anspruch 1, dadurch gekennzeichnet, daß das Verhältnis der Anteile von Mangan zu Scandium kleiner als zwei ist.
3. AlMg-Legierung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß zumindest 0,15 Gew.-% Scandium (Sc) enthalten ist.
4. AlMg-Legierung nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß 0,05-0,35 Gew.-% eines oder mehrerer Elemente der Lanthaniden, insbesondere Cer (Ce), Neodym (Nd), Europium (Eu), Gadolinium (Gd), Dysprosium (Dy), Holmium (Ho) oder Erbium (Er) enthalten ist.
5. Geschweißtes, gewalztes, stranggepreßtes oder geschmiedetes Bauteil für ein Luftfahr­ zeug, insbesondere für einen Flugzeugrumpf, für ein Seefahrzeug oder für ein Kraftfahr­ zeug bestehend aus einer AlMg-Legierung nach einem der Ansprüche 1 bis 4.
DE19838017A 1998-08-21 1998-08-21 Schweißbare, korrosionsbeständige AIMg-Legierungen, insbesondere für die Verkehrstechnik Expired - Lifetime DE19838017C2 (de)