DE1496055B2 - Halbkristalline glaeser mit hohem glanz und guter trans parenz sowie verfahren zu deren herstellung - Google Patents
Halbkristalline glaeser mit hohem glanz und guter trans parenz sowie verfahren zu deren herstellungInfo
- Publication number
- DE1496055B2 DE1496055B2 DE19651496055 DE1496055A DE1496055B2 DE 1496055 B2 DE1496055 B2 DE 1496055B2 DE 19651496055 DE19651496055 DE 19651496055 DE 1496055 A DE1496055 A DE 1496055A DE 1496055 B2 DE1496055 B2 DE 1496055B2
- Authority
- DE
- Germany
- Prior art keywords
- percent
- weight
- tio
- zro
- sno
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 239000011521 glass Substances 0.000 title claims description 38
- 238000004519 manufacturing process Methods 0.000 title claims description 5
- 238000000034 method Methods 0.000 title description 2
- 229910010413 TiO 2 Inorganic materials 0.000 claims description 16
- 229910006404 SnO 2 Inorganic materials 0.000 claims description 12
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims description 11
- 229910018068 Li 2 O Inorganic materials 0.000 claims description 10
- 229910004298 SiO 2 Inorganic materials 0.000 claims description 10
- 239000000203 mixture Substances 0.000 claims description 7
- 238000002425 crystallisation Methods 0.000 claims description 5
- 230000008025 crystallization Effects 0.000 claims description 5
- 230000004907 flux Effects 0.000 claims description 5
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N silicon dioxide Inorganic materials O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims description 4
- 239000000377 silicon dioxide Substances 0.000 claims description 3
- FUJCRWPEOMXPAD-UHFFFAOYSA-N lithium oxide Chemical compound [Li+].[Li+].[O-2] FUJCRWPEOMXPAD-UHFFFAOYSA-N 0.000 claims description 2
- 229910001947 lithium oxide Inorganic materials 0.000 claims description 2
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 claims 1
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 10
- 239000002667 nucleating agent Substances 0.000 description 10
- 239000013078 crystal Substances 0.000 description 7
- MCMNRKCIXSYSNV-UHFFFAOYSA-N ZrO2 Inorganic materials O=[Zr]=O MCMNRKCIXSYSNV-UHFFFAOYSA-N 0.000 description 6
- XOLBLPGZBRYERU-UHFFFAOYSA-N tin dioxide Chemical compound O=[Sn]=O XOLBLPGZBRYERU-UHFFFAOYSA-N 0.000 description 6
- 229910001887 tin oxide Inorganic materials 0.000 description 6
- RVTZCBVAJQQJTK-UHFFFAOYSA-N oxygen(2-);zirconium(4+) Chemical compound [O-2].[O-2].[Zr+4] RVTZCBVAJQQJTK-UHFFFAOYSA-N 0.000 description 5
- 239000004408 titanium dioxide Substances 0.000 description 5
- 230000000052 comparative effect Effects 0.000 description 3
- 229910052642 spodumene Inorganic materials 0.000 description 3
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N Iron oxide Chemical compound [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 description 2
- CSNNHWWHGAXBCP-UHFFFAOYSA-L Magnesium sulfate Chemical compound [Mg+2].[O-][S+2]([O-])([O-])[O-] CSNNHWWHGAXBCP-UHFFFAOYSA-L 0.000 description 2
- QCWXUUIWCKQGHC-UHFFFAOYSA-N Zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 description 2
- 239000004327 boric acid Substances 0.000 description 2
- 239000004927 clay Substances 0.000 description 2
- 238000002474 experimental method Methods 0.000 description 2
- 238000010438 heat treatment Methods 0.000 description 2
- 238000002844 melting Methods 0.000 description 2
- 230000008018 melting Effects 0.000 description 2
- FGIUAXJPYTZDNR-UHFFFAOYSA-N potassium nitrate Chemical compound [K+].[O-][N+]([O-])=O FGIUAXJPYTZDNR-UHFFFAOYSA-N 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 229910001928 zirconium oxide Inorganic materials 0.000 description 2
- 229940043774 zirconium oxide Drugs 0.000 description 2
- 235000008733 Citrus aurantifolia Nutrition 0.000 description 1
- 235000011941 Tilia x europaea Nutrition 0.000 description 1
- JVQAJHYYWVAKPP-UHFFFAOYSA-N [O-2].[Ti+4].[Sn+2]=O.[O-2].[O-2] Chemical compound [O-2].[Ti+4].[Sn+2]=O.[O-2].[O-2] JVQAJHYYWVAKPP-UHFFFAOYSA-N 0.000 description 1
- 238000005299 abrasion Methods 0.000 description 1
- 229910000272 alkali metal oxide Inorganic materials 0.000 description 1
- HEHRHMRHPUNLIR-UHFFFAOYSA-N aluminum;hydroxy-[hydroxy(oxo)silyl]oxy-oxosilane;lithium Chemical compound [Li].[Al].O[Si](=O)O[Si](O)=O.O[Si](=O)O[Si](O)=O HEHRHMRHPUNLIR-UHFFFAOYSA-N 0.000 description 1
- 229910052785 arsenic Inorganic materials 0.000 description 1
- RQNWIZPPADIBDY-UHFFFAOYSA-N arsenic atom Chemical compound [As] RQNWIZPPADIBDY-UHFFFAOYSA-N 0.000 description 1
- 230000003796 beauty Effects 0.000 description 1
- 238000005452 bending Methods 0.000 description 1
- 230000009286 beneficial effect Effects 0.000 description 1
- KGBXLFKZBHKPEV-UHFFFAOYSA-N boric acid Chemical compound OB(O)O KGBXLFKZBHKPEV-UHFFFAOYSA-N 0.000 description 1
- 229910052681 coesite Inorganic materials 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 229910052906 cristobalite Inorganic materials 0.000 description 1
- 239000012535 impurity Substances 0.000 description 1
- 238000009776 industrial production Methods 0.000 description 1
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 1
- 239000004571 lime Substances 0.000 description 1
- YQNQTEBHHUSESQ-UHFFFAOYSA-N lithium aluminate Chemical compound [Li+].[O-][Al]=O YQNQTEBHHUSESQ-UHFFFAOYSA-N 0.000 description 1
- 239000002932 luster Substances 0.000 description 1
- 239000001095 magnesium carbonate Substances 0.000 description 1
- ZLNQQNXFFQJAID-UHFFFAOYSA-L magnesium carbonate Chemical compound [Mg+2].[O-]C([O-])=O ZLNQQNXFFQJAID-UHFFFAOYSA-L 0.000 description 1
- 235000014380 magnesium carbonate Nutrition 0.000 description 1
- 229910000021 magnesium carbonate Inorganic materials 0.000 description 1
- 229910052943 magnesium sulfate Inorganic materials 0.000 description 1
- 235000019341 magnesium sulphate Nutrition 0.000 description 1
- 239000000463 material Substances 0.000 description 1
- 238000002156 mixing Methods 0.000 description 1
- 238000000465 moulding Methods 0.000 description 1
- 229910052670 petalite Inorganic materials 0.000 description 1
- 230000000704 physical effect Effects 0.000 description 1
- 239000004323 potassium nitrate Substances 0.000 description 1
- 235000010333 potassium nitrate Nutrition 0.000 description 1
- 238000010791 quenching Methods 0.000 description 1
- 230000000171 quenching effect Effects 0.000 description 1
- 239000002994 raw material Substances 0.000 description 1
- 239000005368 silicate glass Substances 0.000 description 1
- 235000012239 silicon dioxide Nutrition 0.000 description 1
- 239000007858 starting material Substances 0.000 description 1
- 229910052682 stishovite Inorganic materials 0.000 description 1
- 229910052905 tridymite Inorganic materials 0.000 description 1
- 238000010792 warming Methods 0.000 description 1
- 229910052845 zircon Inorganic materials 0.000 description 1
- 229910052726 zirconium Inorganic materials 0.000 description 1
- GFQYVLUOOAAOGM-UHFFFAOYSA-N zirconium(iv) silicate Chemical compound [Zr+4].[O-][Si]([O-])([O-])[O-] GFQYVLUOOAAOGM-UHFFFAOYSA-N 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C10/00—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition
- C03C10/0018—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition containing SiO2, Al2O3 and monovalent metal oxide as main constituents
- C03C10/0027—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition containing SiO2, Al2O3 and monovalent metal oxide as main constituents containing SiO2, Al2O3, Li2O as main constituents
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Crystallography & Structural Chemistry (AREA)
- Dispersion Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Glass Compositions (AREA)
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US39101764A | 1964-08-20 | 1964-08-20 |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| DE1496055A1 DE1496055A1 (de) | 1969-02-13 |
| DE1496055B2 true DE1496055B2 (de) | 1971-04-01 |
Family
ID=23544873
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| DE19651496055 Pending DE1496055B2 (de) | 1964-08-20 | 1965-06-16 | Halbkristalline glaeser mit hohem glanz und guter trans parenz sowie verfahren zu deren herstellung |
Country Status (6)
| Country | Link |
|---|---|
| BE (1) | BE658573A (enrdf_load_stackoverflow) |
| DE (1) | DE1496055B2 (enrdf_load_stackoverflow) |
| GB (1) | GB1095254A (enrdf_load_stackoverflow) |
| LU (1) | LU49066A1 (enrdf_load_stackoverflow) |
| NL (1) | NL6503036A (enrdf_load_stackoverflow) |
| SE (1) | SE317162B (enrdf_load_stackoverflow) |
Families Citing this family (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP2364957A1 (en) | 2010-02-26 | 2011-09-14 | Corning Incorporated | Glass ceramics with bulk scattering properties and methods of making them |
| DE102016101066B3 (de) | 2016-01-21 | 2017-02-23 | Schott Ag | Verfahren zur Herstellung eines vorzugsweise nicht eingefärbten glaskeramischen Materials mit geringem Streulichtanteil sowie verfahrensgemäß hergestelltes glaskeramisches Material und dessen Verwendung |
| DE102016211065B4 (de) | 2016-06-21 | 2019-09-05 | Schott Ag | Transparenter, vorzugsweise eingefärbter Glaskeramikartikel mit geringem Streulichtanteil und hoher Festigkeit sowie Verfahren zu seiner Herstellung und seine Verwendung |
-
1965
- 1965-01-20 BE BE658573A patent/BE658573A/xx unknown
- 1965-03-10 NL NL6503036A patent/NL6503036A/xx unknown
- 1965-03-25 GB GB1276165A patent/GB1095254A/en not_active Expired
- 1965-06-16 DE DE19651496055 patent/DE1496055B2/de active Pending
- 1965-07-13 LU LU49066D patent/LU49066A1/xx unknown
- 1965-08-16 SE SE1068065A patent/SE317162B/xx unknown
Also Published As
| Publication number | Publication date |
|---|---|
| DE1496055A1 (de) | 1969-02-13 |
| SE317162B (enrdf_load_stackoverflow) | 1969-11-10 |
| BE658573A (enrdf_load_stackoverflow) | 1965-05-17 |
| LU49066A1 (enrdf_load_stackoverflow) | 1965-09-13 |
| GB1095254A (en) | 1967-12-13 |
| NL6503036A (enrdf_load_stackoverflow) | 1966-02-21 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| DE2404623C3 (de) | Entglasbares, in eine Glaskeramik umwandelbares Glas des Systems SiO2 -Al2 O3 - CaO - MgO - Na2 O und als Keimbildner TiO2, Verfahren zu seiner Herstellung und seine Verwendung | |
| DE1016908B (de) | Verfahren zum Herstellen von Glasgegenstaenden hoher mechanischer Festigkeit und danach hergestellte Glasgegenstaende | |
| DE1090829B (de) | Durchsichtige Glaskoerper, z. B. Mikroglaskugeln | |
| DE2263234A1 (de) | Verfahren zur herstellung von hochfesten und temperaturwechselbestaendigen glasgegenstaenden durch oberflaechenkristallisation | |
| DE1496497B2 (de) | Verfahren zur Herstellung transparenter kristalliner Gläser | |
| DE2208236A1 (de) | Glaskeramik mit Tetrakieselsäureglimmerstruktur | |
| DE2321008C3 (de) | Durch Schmelzen und Gießen hergestellte hochschmelzende Erzeugnisse mit Chromoxid | |
| DE2514226A1 (de) | Verfahren zum herstellen von kleinteiligem hydratiertem glas | |
| DE2236088A1 (de) | Glaskeramik und verfahren zu deren herstellung | |
| DE1496579B2 (de) | Verfahren zur Herstellung von weißen Glas-Kristall-Mischkörpern aus Hochofenschlakke | |
| DE1496488B2 (de) | Verfahren zur herstellung eines glas kirstall mischkoerpers optimaler festigkeit durch gesteuerte entglasung eines glases des systems li tief 2 0 si o tief 2 unter verwendung eines phosphats als keimbildner | |
| DE1496055B2 (de) | Halbkristalline glaeser mit hohem glanz und guter trans parenz sowie verfahren zu deren herstellung | |
| DE1596905A1 (de) | Verfahren zur Herstellung eines Keramikglases | |
| DE2633744A1 (de) | Vitrokeramische erzeugnisse mit hohem eisendioxid-gehalt und verfahren zu ihrer herstellung | |
| DE1496055C (de) | Halbkristalline Gläser mit hohem Glanz und guter Transparenz sowie Verfahren zu deren Herstellung | |
| DE1496052B2 (de) | Halbkristalline glaeser mit hohem glanz guter temperatur wechselbestaentigkeit und hoher festigkeit | |
| DE1950539A1 (de) | Glaskeramische Artikel | |
| DE2125898A1 (de) | Glaskeramisches Produkt und Verfahren zu seiner Herstellung | |
| DE1471337B2 (de) | Verfahren zur Herstellung von porzellanartigen Gegenständen | |
| DE1914982B2 (de) | Verwendung eines elektrogeschmolzenen feuerfesten Materials | |
| DE1421853B2 (de) | Glas, insbesondere für Glasperlen | |
| DE1496052C (de) | Halbkristalline Glaser mit hohem Glanz, guter Temperaturwechselbestandig keit und hoher Festigkeit | |
| DE1596726B1 (de) | Halbkristalline glasgegenstaende hoher festigkeit und minimaler deformation und verfahren zu ihrer herstellung insbesondere zur variierung des waermedehnungsverhaltens | |
| DE733503C (de) | Mittel zur Herstellung und Verbesserung von Emails, Glasuren u. dgl. | |
| DE2043572A1 (de) | Verglasbare Charge zur Herstellung von Natrium Calcium Silikat Glasern |