CS265599B1 - Double cadmium-magnesium cyclo-tetraphosphates and process for preparing them - Google Patents
Double cadmium-magnesium cyclo-tetraphosphates and process for preparing them Download PDFInfo
- Publication number
- CS265599B1 CS265599B1 CS884478A CS447888A CS265599B1 CS 265599 B1 CS265599 B1 CS 265599B1 CS 884478 A CS884478 A CS 884478A CS 447888 A CS447888 A CS 447888A CS 265599 B1 CS265599 B1 CS 265599B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- magnesium
- cadmium
- cyclo
- tetraphosphates
- double
- Prior art date
Abstract
Řešení se týká nových sloučenin typu podvojných cyklo-tetrafosforečnanů kademnato-hořečnatých vzorce c-Cd2-xMgxP40y2, kde x je v rozmezí od hodnot blížících se k nule až do hodnot blížících se dvěma. Připraví se krystalizací v suché atmosféře z taveniny o teplotě nad 800 °C, obsahující kationty kademnaté a hořečnaté ve vzájemném molárním poměru Cd/Mg odpovídajícím vztahu (2-x)/x a dále obsahující fosforečnanové anionty v množství odpovídajícím poměru P2O5/(Cd + Mg) rovným 0,96 až 1,1 při jejím tuhnutí.The present invention relates to novel compounds of the type cadmium-magnesium double-cyclo-tetraphosphates of formula c-Cd2-xMgxP40y2, where x is in the range of near zero up to values approaching two. Prepare with crystallization in dry atmosphere from a melt having a temperature above 800 ° C containing cadmium cations and magnesium cations molar ratio Cd / Mg corresponding to the relationship (2-x) / x and further containing phosphate anions in proportion to the ratio P2O5 / (Cd + Mg) equal to 0.96-1.1 at its value solidification.
Description
Vynález se týká nových sloučenin typu podvojných cyklo-tetrafosforečnanů kademnato-hořečnatýoh vzorce c-Cd2_xMgxP^O^2> kde x je v rozmezí od hodnot blížících se nule až do hodnot blížících se dvěma.The invention relates to novel cadmium-magnesium double cyclo-tetraphosphates of the formula c-Cd 2 x Mg x P 2 O 2 wherein x ranges from zero to two.
Ze sloučenin typu kondenzovaných fosforečnanů s jednim kationtem dvojmocného kovu a s molárním poměrem oxidu fosforečného (Ρ,Ο,.) k příslušnému kovu rovným jedné, jsou známy II většinou jednak cyklo-tetrafosforečnany (vzorce c-Me2 P^0^2) a 3e4nak vyšší lineární fosforečnany (vzorce Men/2H2Pn°3n+l^ toniu 3e také v případě kademnatých kondenzovaných fosforečnanů, kdy existuje jak cyklo-tetrafosforečnan dikademnatý (c-Cd2P^O^2), tak vyšší lineární fosforečnany kademnaté (c4ny2H2Pn°3n+l’ V P^-^padě hořečnatých sloučenin, kdy existují vyšší lineární fosforečnany (M9n/2H2Pn°3n+l’ Pr°4ukt s cyklickými tetrafosforečnanovými anionty (c-Mg2P^O^2). Na významu nabývají podvojné cyklo-tetrafosforečnany, obsahující hořečnaté kationty vedle jiných kationtů dvojmocných kovů. Tyto produkty nebyly dosud známy a pokud byla uvažována existence kondenzovaných fosforečnanů s dvojicemi těchto kationtů, pak pouze jako vyšší lineární fosforečnany. Tyto vyšší lineární fosforečnany dvojmocných kovů, at už s jedním kationtem či podvojné s více kationty, však mají některé vlastnosti, které jsou z hlediska jejich použití méně vhodné. Jsou to totiž látky amorfního, nekrystaliokého, sklovitého charakteru, které jsou křehké. Jsou také poměrně snadno rozpustné a některé mají dokonce sklony k navlhávání. Jejich termická stabilita je omezena teplotami rekrystalizaoe (500 až 800 °C). Vzhledem k ekologicky problematické roli kadmia, které bývá obsaženo v kyselině fosforečné jako výchozí surovině, je třeba znát možnosti a podmínky vzniku podvojných cyklo-tetrafosforečnanů kademnato-hořečnatých. Vazba kadmia do těchto obtížně rozpustných produktů by byla řešením jeho eliminace v reakčních směsích příprava kondenzovaných fosforečnanů s užitím kyseliny fosforečné či jejich solí jako výchozích surovin.Of the compounds of the condensed phosphate type with one divalent metal cation and with a molar ratio of phosphorus pentoxide (Ρ, Ο,) to the corresponding metal equal to one, cyclo-tetraphosphates (formulas c-Me 2 P ^ 0 ^ 2 ) and 3 are known. e 4 to k higher linear phosphates (of the formula Me n / 2 H 2 P n ° 3n + 1- tium 3 e also in the case of cadmium condensed phosphates, where both dicadium cyclo-tetrafosphate (c-Cd 2 P 2 O 4) and higher linear cadmium phosphates ( c 4ny2 H 2 P n ° 3n + 1 ' In the case of magnesium compounds where higher linear phosphates exist ( M 9n / 2 H 2 P n ° 3n + 1' P r ° 4uct with cyclic tetrafosphate anions (c-Mg 2 P 2 O 2 ), double-cyclo-tetraphosphates containing magnesium cations, in addition to other divalent metal cations, are gaining in importance. However, these higher linear phosphates of divalent metals, whether single-cation or double-cation-double-cationic, have some properties which are less suitable for their use. They are substances of amorphous, non-crystalline, glassy character, which are fragile. They are also relatively easily soluble and some even tend to be moisturized. Their thermal stability is limited by recrystallization temperatures (500-800 ° C). Given the ecologically problematic role of cadmium, which is usually contained in phosphoric acid as a starting material, it is necessary to know the possibilities and conditions for the formation of cadmium-magnesium double cyclo-tetraphosphates. Binding of cadmium to these poorly soluble products would be a solution to its elimination in the reaction mixtures by the preparation of condensed phosphates using phosphoric acid or its salts as starting materials.
Podstata vynálezu spočívá v tom, že uvádí podvojné cyklo-tetrafosforečnany kademnato-hořečnaté jako nové sloučeniny vzorce C-C42_XM9XP4°42' kde x íe v rozmezí od hodnot blížících se k nule až do hodnot blížících se dvěma. Spodní i Korní hranice pro x vyplývá z toho, že hodnoty nula až dvě nelze použít, protože by se již nejednalo o produkt podvojný, ale o čistý, jednoduchý cyklo-tetrafosforečnan dikademnatý c-Cd2P^O^2, resp. o jednoduchý cyklo-tetrafosforečnan dihořečnatý o-Mg2P^0^2· Podvojné cyklo-tetrafosforečnany kademnato-hořečnaté jsou bílé (bezbarvé) látky, jejichž hustoty se pohybují podle poměru Cd/Mg v rozmezí 2,87 až 3,85 g/cm . Mají krystalovou strukturu v monoklinické soustavě s prostorovou grupou C 2/c. Její mřížkové parametry se podle poměru Cd/Mg pohybují v rozmezích 1,174 9 až 1,232 8 nm pro a, 0,827 8 až 0,863 9 nm pro b, 0,990 5 až 1,038 8 nm pro c, 118,46° až 119,33° pro úhel beta a objem elementární buňky se pohybuje v rozmezí 0,843 až 0,964 5 nm^. Podvojné cyklo-tetrafosforečnany kademnato-hořečnaté jsou chemicky a termicky velmi stabilní látky. Jsou nerozpustné've vodě, organických rozpouštědlech a ve zředěných minerálních kyselinách, jen pozvolna se rozpouštějí v roztocích louhů. Tají až při vysokých teplotách podle poměru Cd/Mg v rozmezí 800 °C až 1 160 °C, přičemž skupenské tepla tání se pohybují v rozmezí 130 až 305 J/g. Ve zcela suché atmosféře nebo ve vakuu tají kongruentně, v atmosféře obsahující alespoň stopy vodní páry tají nekongruentně.The invention consists in that it provides double-cyclo-tetraphosphate kademnato magnesium as novel compounds of Formula CC 42_X M P 9X 4 ° 42 'where x i e in the range from values approaching zero until two values close. The lower and lower bounds for x arise from the fact that values of zero to two cannot be used, since they would no longer be a double product, but a pure, simple dicademic cyclo-tetrafosphate c-Cd 2 P ^ O ^ 2 , respectively. o simple magnesium di-cyclo-tetraphosphate o-Mg 2 P ^ 0 ^ 2 · Cadmium-magnesium double -cyclo-tetraphosphates are white (colorless) substances whose densities range in the range of 2.87 to 3.85 g / Cd / Mg cm. They have a crystal structure in a monoclinic system with a spatial group C 2 / c. Its lattice parameters are in the range of 1.174 9 to 1.232 8 nm for a, 0.827 8 to 0.863 9 nm for b, 0.990 5 to 1.038 8 nm for c, 118.46 ° to 119.33 ° for angle beta, and the volume of the elemental cell ranges from 0.843 to 0.964 5 nm. The cadmium-magnesium double cyclo-tetraphosphates are chemically and thermally very stable substances. They are insoluble in water, organic solvents and dilute mineral acids, only slowly dissolve in lye solutions. It melts at high temperatures according to the Cd / Mg ratio in the range of 800 ° C to 1160 ° C, with the latent heats of melting in the range of 130 to 305 J / g. In a completely dry atmosphere or in vacuum, they melt congruently, in an atmosphere containing at least traces of water vapor they melt non-congruently.
Podstata vynálezu spočívá dále v tom, že podvojné cyklo-tetrafosforečnany kademnato-hořečnaté se připraví tím způsobem, že tavenina o teplotě nad 800 °C, s výhodou na 1 160 °C, obsahující kationty kademnaté a hořečnaté v molárním poměru Cd/Mg odpovídajícím vztahu (2-x)/x a dále obsahující fosforečnanové anionty v množství odpovídajícím molárnímu poměru P2O,j/(Cd + Mg) rovným 0,96 až 1,1, s výhodou 1 až 1,005, se ponechá ve zcela suché atmosféře ztuhnout chladnutím s výhodou rychlostí menší než 5 °C za vzniku produktu v podobě mikrokrystalků. Teplotu taveniny je třeba volit nad teplotou tání resp. tuhnuti produktů, které se pohybuje podle poměru Cd/Mg v rozmezí 800 až 1 160 °C. Vzájemný poměr kademnatých a hořečnatých kationtů v tavenině se volí podle požadavku na jejich obsah v produktu, přičemž množství hořečnatých kationtů se může pohybovat v rozmezí od hodnot blížících se nule až do hodnoty blížící se dvěma. Obsah fosforečnanových aniontů v tavenině musí odpovídat molárnímu poměru P205/(Cd + Mg) rovnému jedné, nebo hodnotám lišícím se jen málo od jedné, tak jak to odpovídá sumárnímu vzorci produktu c-Cd2_xMgxP^O^2, jinak by vznikaly vedlejší produkty v podobě jiných typů kondenzovaných fosforečnanů a podíl hlavního produktu by se výrazně snižoval. Krystalizaci produktu tuhnutím z chladnoucí taveniny je třeba vést ve zcela suché atmosféře (nebo ve vakuu), nebot přítomnost i jen stopových množství vodní páry by opět vedla ke vzniku kondenzovaných fosforečnanů s jinými anionty a nikoliv s anionty cyklo-tetrafosforečnanovými. Přitom je výhodné vést chladnuti teveniny rychlosti menší než 5 °C/min, nebot se tak možnost jiných nežádoucích kondenzačních produktů snižuje. Produkty lze případně podle vynálezu ještě vyčistit loužením kyselinou chlorovodíkovou, sírovou, dusičnou nebo fosforečnou, nebot podvojné cyklo-tetrafosforečnany tomuto loužení odolávají, přičemž ostatní případně vzniklé produkty přejdou do roztoku. Výhodná koncentrace kyselin pro loužení je 0,05 až 10 hmotnostních' %, kdy odloužení vedlejších produktů je dostatečně účinné a přitom nebezpečí atakování hlavního produktu je zanedbatelné.The invention furthermore consists in that cadmium-magnesium double cyclo-tetraphosphates are prepared in such a way that the melt at a temperature above 800 ° C, preferably at 1160 ° C, contains cadmium and magnesium cations in a Cd / Mg molar ratio corresponding to (2-x) / x and further comprising phosphate anions in an amount corresponding to a molar ratio of P 2 O, j / (Cd + Mg) of 0.96 to 1.1, preferably 1 to 1.005, is allowed to solidify in a completely dry atmosphere by cooling preferably at a rate of less than 5 ° C to form a microcrystalline product. The melt temperature must be selected above the melting point or the melting point. solidification of products having a Cd / Mg ratio of 800 to 1,160 ° C. The ratio of cadmium and magnesium cations in the melt is chosen according to the requirement for their content in the product, and the amount of magnesium cations can range from values close to zero to values close to two. The content of phosphate anions in the melt must correspond to a molar ratio P 2 0 5 / (Cd + Mg) equal to one, or values differing only slightly from one, as corresponding to the c-Cd 2 x x Mg x P O ^ 2 , otherwise by-products would be formed in the form of other types of condensed phosphates and the proportion of the main product would be significantly reduced. Solidification crystallization of the product from cooling melt should be conducted in a completely dry atmosphere (or vacuum), since the presence of even trace amounts of water vapor would again lead to condensation phosphates with other anions and not with cyclotetrafosphate anions. In this connection, it is advantageous to cause the core to cool at a rate of less than 5 ° C / min, since the possibility of other undesired condensation products is reduced. Alternatively, the products can be further purified according to the invention by leaching with hydrochloric, sulfuric, nitric or phosphoric acid, since the double cyclo-tetraphosphates resist this leaching, while the other products formed eventually become dissolved. The preferred concentration of acids for leaching is 0.05 to 10% by weight, where by-product separation is sufficiently effective, while the risk of attacking the main product is negligible.
Výhody vynálezu^spočívají v tom, že uvádí existenci nových sloučenin, které dosud nebyly známy. Tyto sloučeniny kumulují výhodné vlastnosti fyzikálně-chemické i aplikační, které mají jednoduché cyklo-tetrafosforečnany dvojmocných kovů. Zvýrazňují se speciální pigmentové vlastnosti a ovlivňuje se dlouhodobá rozpustnost.The advantages of the invention are that it indicates the existence of novel compounds which have not been previously known. These compounds accumulate advantageous physicochemical and application properties having simple divalent metal cyclotetrophosphates. Special pigment properties are emphasized and long-term solubility is influenced.
PřikladlHe did
Tavenina připravená roztavením 100 g vyšších lineárních fosforečnanů kademnatých aMelt prepared by melting 100 g of higher linear cadmium phosphates and
67.4 g vyšších lineárních fosforečnanů hořečnatých při 1 200 °C byla ochlazena v suché atmosféře rychlosti 5 °C/min. Bylo získáno 167,4 g mikrokrystalického produktu, který obsahuje67.4 g of higher linear magnesium phosphates at 1200 ° C were cooled in a dry atmosphere at a rate of 5 ° C / min. 167.4 g of the microcrystalline product were obtained
99.4 hmot. % podvojného cyklo-tetrafosforečnanu kademnato-hořečnatého vzorce CdMgP4O12Bílé mikrokrystalky jsou v monoklinické soustavě, prostorová grupa C 2/c, jejíž mřížkové parametry jsou á = 1,200 4 nm, b = 0,854 5 nm, c = 0,994 2 nm, beta = 118,46° a objem elementární buňky 0,896 5 nm3. Jejich hustota je 3,35 g/cm3, teplota tání 885 °C a skupenské teplo tání 155 J/g.99.4 wt. % of double cadmium cyclo-tetrafosphate of formula CdMgP 4 O 12 White microcrystals are in a monoclinic system, spatial group C 2 / c, whose lattice parameters are λ = 1,200 4 nm, b = 0,854 5 nm, c = 0,994 2 nm, beta = 118.46 ° and the cell volume of 0.896 5 nm 3 . Their density is 3.35 g / cm 3 , the melting point is 885 ° C, and the heat of fusion is 155 J / g.
Příklad 2Example 2
Tavenina připravená roztavením 150 g vyšších lineárních fosforečnanů kademnatých a 33,7 g vyšších lineárních fosforečnanů hořečnatých při 1 165 °C byla ochlazena ve vakuu rychlostí 20 °C/min. Bylo získáno 188,6 g mikrokrystalického produktu, který obsahuje 99,1 hmot. i podvojného cyklo-tetrafosforečnanu kademnato-hořečnatého vzorce c-Cd^ 5M9q 5P4°12‘The melt prepared by melting 150 g of higher linear cadmium phosphates and 33.7 g of higher linear magnesium phosphates at 1165 ° C was cooled in vacuo at a rate of 20 ° C / min. 188.6 g of a microcrystalline product was obtained which contained 99.1 wt. of cadmium-magnesium double cyclo-tetraphosphate of formula c-Cd ^ 5 M 9q 5 P 4 ° 12 '
Bílé mikrokrystalky jsou v monoklinické soustavě, prostorová grupa C 2/c, jejíž mřížkové parametry jsou a = 1,218 9 nm, b = 0,857 4 nm, c = 1,021 1 nm, beta = 119,03° a objem elementární buňky 0,933 1 nm3. Jejich hustota je 3,60 g/cm3, teplota tání 920 °C a skupenské teplo tání 195 J/g.White microcrystals are in a monoclinic system, spatial group C 2 / c, whose lattice parameters are a = 1.218 9 nm, b = 0.857 4 nm, c = 1.021 1 nm, beta = 119.03 ° and elemental cell volume 0.933 1 nm 3 . Their density is 3.60 g / cm 3 , the melting point is 920 ° C, and the heat of fusion is 195 J / g.
Příklad 3Example 3
Tavenina připravená roztavením 50 g vyšších lineárních fosforečnanů kademnatých a 101,1 g vyšších lineárních fosforečnanů hořečnatých při 1 210 °C byla chlazena v suché atmosféře rychlostí 2 °C/min. Bylo získáno 151,1 g mikrokrystalického produktu, který obsahuje 99,6 hmot. % podvojného cyklo-tetrafosforečnanu kademnato-hořečnatého vzorce c-CdQ ^Mg^ 5Ρ4Οΐ2· Bílé mikrokrystalky jsou v monoklinické soustavě, prostorová grupa C 2/c, jejíž mřížkové parametry jsou a = 1,187 9 nm, b = 0,841 6 nm, c = 0,990 4 nm, beta = 118,61° a objem elementární buňky je 0,869 2 nm3. Jejich hustota je 3,10 g/cm3, teplota tání 1 090 °C a skupenské teplo tání 243 J/g. 'The melt prepared by melting 50 g of higher linear cadmium phosphates and 101.1 g of higher linear magnesium phosphates at 1,210 ° C was cooled in a dry atmosphere at a rate of 2 ° C / min. 151.1 g of a microcrystalline product was obtained, which contained 99.6 wt. c-Cd Q ^ Mg ^ 5 Ρ 4 Ο ΐ2 · White microcrystals are in a monoclinic system, spatial group C 2 / c, whose lattice parameters are a = 1.187 9 nm, b = 0.841 6 nm, c = 0.990 4 nm, beta = 118.61 ° and the volume of the elemental cell is 0.869 2 nm 3 . Their density is 3.10 g / cm 3 , the melting point is 1090 ° C, and the latent heat of fusion is 243 J / g. '
Claims (2)