CN1863873A - 阻燃聚酰胺模塑材料及其用途 - Google Patents
阻燃聚酰胺模塑材料及其用途 Download PDFInfo
- Publication number
- CN1863873A CN1863873A CNA2004800292945A CN200480029294A CN1863873A CN 1863873 A CN1863873 A CN 1863873A CN A2004800292945 A CNA2004800292945 A CN A2004800292945A CN 200480029294 A CN200480029294 A CN 200480029294A CN 1863873 A CN1863873 A CN 1863873A
- Authority
- CN
- China
- Prior art keywords
- moulding compound
- polyamide
- weight
- polymeric amide
- polyamide moulding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及基于脂肪族和部分芳香族聚酰胺混合物的无卤阻燃模塑材料,其含有膦酸盐作为阻燃剂。本发明还涉及本发明的聚酰胺模塑材料用于生产模制品、尤其是电气和电子工业用组件的用途。
Description
本发明涉及基于脂肪族和部分芳香族聚酰胺混合物的无卤阻燃模塑料,其含有膦酸盐作为阻燃剂。此外,本发明涉及根据本发明的聚酰胺模塑料用于生产模制品、尤其是电气和电子工业用组件的用途。
基于脂肪族聚酰胺的模塑料由于其出色的性能特征而在多个应用领域中用于生产模制品。对于电气和电子工业用组件来说尤其需要具有阻燃性能的聚酰胺模塑料,以确保充分防火。
聚酰胺通常通过加入卤素化合物而提供阻燃处理。含卤素的聚酰胺模塑料由于在焚烧处理过程中释放含卤素物质,因此除了其它缺点之外其在毒理学上也是成问题的。为此,已经开发了一些用于聚酰胺的无卤阻燃体系。
DE 1 931 387描述将红磷加入到聚酰胺中。这种模塑料具有固有的暗色,这限制了用于着色的可能性。此外,在生产和加工含有红磷作为阻燃剂的聚酰胺模塑料的过程中,由于形成有毒的膦而需要相当多的安全防护。
由DE 195 25 873已知无机阻燃剂例如氢氧化镁的用途。为得到足够的阻燃性需要高填充量,这导致模塑料具有下降的强度和高脆性。
在EP 0 614 933中尤其描述了含氮阻燃剂例如氰尿酸三聚氰胺。在聚酰胺中,尤其是在玻璃纤维增强配方中,其效果有限。
对于玻璃纤维增强聚酰胺模塑料,在EP 0 782 599中尤其提出含磷/氮阻燃体系,例如三聚氰胺多磷酸盐。对于根据UL94的V0阻燃级别,需要至少25重量%的填充量,这使得模塑料的断裂伸长率低而不足以适用于各种应用。
磷化合物被提出作为另一组无卤阻燃剂。因而,EP 0 792 912描述了膦酸和二膦酸的钙和铝盐作为阻燃剂用于聚酰胺的用途。提及聚酰胺6和聚酰胺66是特别适用的聚酰胺。由此生产的具有30重量%填充量的模塑料在试样厚1.2mm时达到根据UL94的的V0阻燃级别。在EP 1 0241 67 A1中也证明了这些膦酸盐的较高用量的必要性。从EP 1 024 167的表1中可推导出对于玻璃纤维增强聚酰胺6需要远大于20重量%、对于玻璃纤维增强聚酰胺66需要30重量%以上的膦酸铝,以达到UL94的V0级别。这种高填充量对于机械性能具有不利影响。如果模塑料由于低断裂伸长率而呈脆性,这会导致一些问题,例如在具有咬合连接的组件的情况下在电气工业中常产生的问题。所述组件通常在通过注射成型生产的短时间内被组装,即没有调湿,其中如果这些咬合连接由于材料脆性而断裂,则发生明显破坏。为了防止出现这种情况,对于这些应用,要求模塑料在新的模塑状态下具有至少2%的断裂伸长率。
由此出发,本发明的目的是提供一种新型聚酰胺模塑料,相对于现有技术、特别是相对于EP 1 024 167的聚酰胺模塑料,其机械性能尤其是断裂伸长率得到显著改善。所述聚酰胺化合物还应该在试样厚度最大为0.8mm时满足根据UL94的V0阻燃级别的要求。
上述目的通过本专利权利要求1的特征来实现。
令人惊奇的是,目前发现权利要求1所限定的模塑料使得可以生产具有改善的机械性能、尤其是在新模塑状态下断裂伸长率至少为2%的模制品。根据本发明的模塑料与现有技术的区别还在于可使用显著低填充量的膦酸盐作为阻燃剂,而且仍然达到根据UL94的V0阻燃级别。根据本发明,在本发明的基于脂肪族聚酰胺的模塑料的情况下,通过将一部分脂肪族聚酰胺替换为部分芳香族聚酰胺而明显达到上述效果。
因此,本发明的主题是阻燃聚酰胺模塑料,包含:
a)20-80重量%的一种或多种脂肪族聚酰胺;
b)1-40重量%的一种或多种部分芳香族聚酰胺;
c)1-30重量%的阻燃剂,所述阻燃剂包含式(1)的膦酸盐和/或式(2)的二膦酸盐和/或其聚合物;
其中,
R1、R2相同或不同,并且是指C1-C6的线型或支链烷基和/或芳基;
R3 指C1-C10的线型或支链亚烷基、C6-C10亚芳基、烷基亚芳基或芳基亚烷基;
M 指来自元素周期表第二或第三主族或副族的金属离子;
m 指2或3;
n 指1或3;
x 指1或2;
d)5-60重量%的纤维状或颗粒状填料或其混合物;
e)0.05-10重量%的常用添加剂,包括稳定剂、加工助剂、抗滴剂、着色剂、颜料等。
均聚酰胺和共聚酰胺可用作根据本发明的脂肪族聚酰胺(a),其重复单元来自脂肪族胺和脂肪族二羧酸或来自氨基羧酸,这些氨基羧酸也可以其内酰胺形式使用。典型实例有聚酰胺6、聚酰胺11、聚酰胺12、聚酰胺66、聚酰胺66/6、聚酰胺46。
均聚酰胺或者共聚酰胺可用作根据本发明的部分芳香族聚酰胺(b),其重复单元来自二羧酸和二胺以及来自氨基羧酸或分别来自相应的内酰胺。合适的二羧酸是芳香族和脂肪族二羧酸,例如对苯二酸、间苯二酸、己二酸、壬二酸、癸二酸、十四双酸和1,4-环己烷二羧酸。合适的二胺是脂肪族和环脂族二胺,例如六亚甲基二胺、壬二胺、癸二胺、十二甲撑二胺、2-甲基戊二胺、1,4-环已二胺、二(4-二氨基环己基)-甲烷、二(3-甲基-4-氨基环己基)-甲烷以及具有芳香基团的二胺,如间苯二甲胺和对苯二甲胺。合适的氨基羧酸是氨基己酸、氨基十一酸和氨基月桂酸。典型实例是聚酰胺6I、聚酰胺6T/6I、聚酰胺6T/6、聚酰胺6T/66、聚酰胺6T/6I/66、聚酰胺9T、聚酰胺10T、聚酰胺12T、聚酰胺6T/12、聚酰胺MXD6。
至于根据本发明的阻燃剂(c),涉及式(1)的膦酸盐和/或式(2)的二膦酸盐,
其中,
R1、R2相同或不同,并且是指C1-C6的线型或支链烷基和/或芳基;
R3 指C1-C10的线型或支链亚烷基、C6-C10亚芳基、烷基亚芳基或芳基亚烷基;
M 指来自元素周期表第二或第三主族或副族的金属离子;
m 指2或3;
n 指1或3;
x 指1或2;
和/或其聚合物。
用于生产根据本发明的膦酸盐的合适的膦酸例如二甲基膦酸、乙基甲基膦酸、二乙基膦酸、甲基正丙基膦酸、甲烷-二(甲基膦酸)、乙烷-1,2-二(甲基膦酸)、己烷-1,6-二(甲基膦酸)、苯-1,4-二(甲基膦酸)、甲基苯基膦酸、二苯基膦酸。
根据本发明的膦酸盐可以根据已知方法生产,例如EP 0 699 708中所述。由此在含有根据反应条件基本为单体也可以是聚合物的金属碳酸盐、金属氢氧化物或金属氧化物的水溶液中转化膦酸,生产膦酸盐。
根据式(1)和(2)的膦酸盐可含有来自周期表的第二或第三主族或副族的金属离子,优选膦酸的钙盐和铝盐。这些膦酸盐也可以其混合物形式使用。优选以粉末形式应用,以便在引入到聚合物中的过程中实现良好的分散。
根据本发明的模塑料含有1-30、优选2-25、尤其优选8-20重量%的作为组分(c)的式(1)的膦酸盐和/或式(2)的二膦酸盐和/或其聚合物。
至于组分(d),根据本发明的模塑料可含有5-60重量%的纤维状或颗粒状填料或其混合物。可作为纤维状填料、纤维状增强物质的实例提及的例如玻璃纤维、碳纤维、芳族聚酰胺纤维、钛酸钾晶须,优选玻璃纤维。在所述模塑料中引入玻璃纤维可采用无端线束(粗纱)形式或短切形式(短玻璃纤维)来实现。为了改善与聚酰胺的相容性,所用的玻璃纤维可提供有修饰剂和胶粘剂。常用玻璃纤维的直径为6-20μm。
其中,玻璃球、白垩、粉末石英、滑石、硅灰石、高岭土、云母适合作为颗粒状填料。
作为组分(e)的常用添加剂例如绝热材料、抗氧化剂、光稳定剂、润滑剂、脱模剂、成核剂、颜料、着色剂、抗滴剂。
根据本发明的阻燃聚酰胺模塑料可根据本身已知的方法生产。为此,将各组分在混合装置例如双螺杆挤出机中均化。通常的方法包括通过分立的定量配料装置将组分a)-e)单独或预先混合而引入混合装置中。根据部分芳香族聚酰胺的熔点,在200-350℃的温度下进行聚合物熔体的均化过程。所述熔体一般拉伸为线束、冷却并造粒。
根据本发明的模塑料适合用于根据注射成型方法生产模制品。
实施例中使用下列起始材料来生产根据本发明的模塑料:
组分a)
聚酰胺a1):聚酰胺6,相对粘度(H2SO4中1%)=2.7
聚酰胺a2):聚酰胺66,相对粘度(H2SO4中1%)=2.67
组分b)
聚酰胺b1:聚酰胺6I/6T,间苯二酸与对苯二酸之比为67∶33,相对粘度(间甲酚中0.5%)=1.72
聚酰胺b2:聚酰胺6T/66,对苯二酸与己二酸的摩尔比为55∶45,相对粘度(间甲酚中0.5%)=1.69
聚酰胺b3:聚酰胺6T/6I,对苯二酸与间苯二酸之比为70∶30,相对粘度(间甲酚中0.5%)=1.135
聚酰胺b4:聚酰胺MXD6,相对粘度(间甲酚中0.5%)=1.85
组分c)
二乙基膦酸铝
甲基丙基膦酸钙
组分d)
聚酰胺用标准玻璃纤维,纤维长度4.5mm,直径10μm
组分e)
Irganox 1098(Ciba Specialities)
硬脂酸钙
实施例
利用来自Werner & Pfleiderer的ZSK30双螺杆挤出机将起始材料混合成相应的模塑料,起始材料的量示于表1中并分别以重量%表示。组分a)、b)和e)预先混合,并因此将类似的组分c)通过进料平衡量表输送至挤出机的进料区。玻璃纤维通过侧进料器供应,各组分的均化在260-310℃的温度下实施。
所述模塑料作为线束排出,在水浴中冷却并随后造粒。将颗粒干燥至含水量低于0.08%并在注射成型机上加工成试样。随即进行以下测试:
根据UL-94对正常调湿之后的厚度为0.4、0.8或1.6mm的试样的阻燃性测试
根据ISO527的弹性模量,刚成型
根据ISO527的断裂伸长,刚成型
根据ISO527的破坏应力,刚成型
根据ISO179/1eU的23℃下的冲击强度,刚成型。
表1
对比实施例1 | 实施例1 | 实施例2 | ||
组成重量%聚酰胺a1聚酰胺a2聚酰胺b1聚酰胺b2聚酰胺b3聚酰胺b4二乙基膦酸铝甲基丙基膦酸钙玻璃纤维Irganox 1098硬脂酸钙 | 39.430300.250.35 | 43.014.412300.250.35 | 47.4814300.250.35 | |
测试阻燃性测试UL-940.4mm0.8mm1.6mm弹性模量破坏应力断裂伸长率冲击强度 | 级别MPaMPa%kJ/m2 | n.k.V-2106001301.749 | V-0V-0109001473.152 | V-0V-0106001352.348 |
表2
对比实施例2 | 实施例3 | 实施例4 | ||
组成重量%聚酰胺a1聚酰胺a2聚酰胺b1聚酰胺b2聚酰胺b3聚酰胺b4二乙基膦酸铝甲基丙基膦酸钙玻璃纤维Irganox 1098硬脂酸钙 | 39.425350.250.35 | 40.01014350.250.35 | 18.718.71215350.250.35 | |
测试阻燃性测试UL-940.4mm0.8mm1.6mm弹性模量破坏应力断裂伸长率冲击强度 | 级别MPaMPa%kJ/m2 | n.k.V-1110001401.850 | V-0V-0109001522.952 | V-0V-0105001452.858 |
Claims (10)
1.阻燃聚酰胺模塑料,包含
a)20-80重量%的一种或多种脂肪族聚酰胺;
b)1-40重量%的一种或多种部分芳香族聚酰胺;
c)1-18重量%的阻燃剂,所述阻燃剂包含式(1)的膦酸盐和/或式(2)的二膦酸盐和/或其聚合物;
其中,
R1、R2相同或不同,并且是指C1-C6的线型或支链烷基和/或芳基;
R3指C1-C10的线型或支链亚烷基、C6-C10亚芳基、烷基亚芳基或芳基亚烷基;
M指来自元素周期表第二或第三主族或副族的金属离子;
m指2或3;
n指1或3;
x指1或2;
d)5-60重量%的纤维状或颗粒状填料或其混合物;
e)0.05-10重量%的添加剂,
a)-e)的比例之和为100重量%。
2.阻燃聚酰胺模塑料,其特征在于,所述模塑料含有5-15重量%的阻燃剂。
3.根据权利要求1或2的阻燃聚酰胺模塑料,其特征在于,所述脂肪族聚酰胺a)选自均聚和共聚的聚酰胺,其重复单元来自脂肪族胺、脂肪族二羧酸和/或脂肪族氨基羧酸,这些氨基羧酸也可以其内酰胺形式使用。
4.根据权利要求1-3中至少一项的阻燃聚酰胺模塑料,其特征在于,所述部分芳香族聚酰胺b)选自如下聚酰胺,其重复单元来自至少一种芳香族二羧酸,根据需要来自一种或多种脂肪族二羧酸,以及来自一种或多种脂肪族和/或环脂族二胺。
5.根据权利要求1-3中至少一项的阻燃聚酰胺模塑料,其特征在于,所述部分芳香族聚酰胺b)选自如下聚酰胺,其重复单元来自至少一种脂肪族二羧酸,根据需要来自一种或多种芳香族二羧酸,和对苯二甲胺和/或间苯二甲胺。
6.根据权利要求1-5中至少一项的阻燃聚酰胺模塑料,其特征在于,所述部分芳香族聚酰胺b)选自如下聚酰胺,其重复单元来自对苯二酸和/或间苯二酸,并且根据需要来自己二酸,以及六亚甲基二胺。
7.根据权利要求1-6中至少一项的阻燃聚酰胺模塑料,其特征在于,式(1)的膦酸盐和/或式(2)的二膦酸盐和/或其聚合物用作阻燃剂c),其中M表示钙或铝离子。
8.根据权利要求1-7中任一项的阻燃聚酰胺模塑料,其特征在于,所述添加剂选自稳定剂、加工助剂、抗滴剂、着色剂和/或颜料。
9.根据前述权利要求中任一项的阻燃模塑料的用途,用于生产模制品。
10.根据权利要求9的阻燃模塑料的用途,用于生产在试样厚度最大为0.8mm时满足根据UL94的V0阻燃级别的要求的模制品。