CN1590342A - 一种将废玻璃再生为隔热保温瓷化砖的方法 - Google Patents

一种将废玻璃再生为隔热保温瓷化砖的方法 Download PDF

Info

Publication number
CN1590342A
CN1590342A CN 03155930 CN03155930A CN1590342A CN 1590342 A CN1590342 A CN 1590342A CN 03155930 CN03155930 CN 03155930 CN 03155930 A CN03155930 A CN 03155930A CN 1590342 A CN1590342 A CN 1590342A
Authority
CN
China
Prior art keywords
heat
ceramic tile
cullet
insulation
regenerated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 03155930
Other languages
English (en)
Other versions
CN1319904C (zh
Inventor
秦文隆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB031559301A priority Critical patent/CN1319904C/zh
Publication of CN1590342A publication Critical patent/CN1590342A/zh
Application granted granted Critical
Publication of CN1319904C publication Critical patent/CN1319904C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种废弃物资源化处理技术，特别是一种将废玻璃再生为具有隔热保温功效的瓷化砖的方法。包括如下步骤：废玻璃材料的预处理；添加黏土材料、发泡剂，密闭混合研磨，干燥造粒；用成型机利用模具制成各种尺寸的砖胚；发泡烧制，徐冷退火，出窑。若需要精致加工，可再彩饰上釉或经切、磨等特殊的工序加工。本发明产品比重小，但又无损其结构强度，吸水率在1％以下，具有隔热保温功效，原料来源广泛，成本低廉，可以直接利用生产瓷砖原设备、生产线。

Description

一种将废玻璃再生为隔热保温瓷化砖的方法
技术领域
本发明涉及废弃物资源化处理技术领域，特别是涉及一种将废玻璃再生为具有隔热保温功效的瓷化壁砖、地砖的方法，以运用于各种建筑物。
背景技术
对于废弃的玻璃产品，现在一般的回收处理方式是直接压碎后出售。随着电子业的发展，废弃的玻璃配件，包括显像管、电视机、电脑屏幕、灯管灯泡等污染越来越严重。因为这些玻璃配件含有重金属氧化物镀膜，污染严重，所以既无法回收供玻璃业生产中使用，也不能丢弃或掩埋或当沙砾用于铺路。目前尚无有效的解决办法。再者，随着对建材抗震性要求的提高，要求其比重越小越好。
发明内容
本发明的目的在于提供一种将废玻璃再生为具有隔热保温功效的瓷化砖的方法。
本发明将废玻璃再生为具有隔热保温功效的瓷化砖的方法，包括有如下步骤：
a.废玻璃材料的预处理：玻璃材料可以是废家电、显像管、显示器、废灯管、废灯泡、废玻璃容器等；
破碎：用破碎机将废玻璃破碎为0.2-1mm的颗粒；
筛选：由于破碎后颗粒大小不一，经筛选将粒径大于1mm的玻璃颗粒筛选出来，回到前一程序再次破碎直到可以通过1mm筛；
粉碎：将经过筛选的玻璃颗粒粉碎；
搓磨：由于有的废玻璃如废显像管等表面有一层深色镀膜，因此在破碎以前使用搓磨机进行表面搓磨处理，使其表面镀膜脱离，没有镀膜的玻璃材料可省略此步骤；
b.添加黏土材料：为了提高成品的隔热保温性能，可按照实际需求添加重量比5-20％黏土材料。例如，净水厂沉淀后淤泥、水库淤泥等；
c.添加发泡剂：添加重量比1-5％发泡剂：
d.密闭混合研磨：将玻璃粉料、黏土材料添加发泡剂后混合研磨为粉料，并干燥造粒；
e.成型：以成型机利用模具压制成各种尺寸的砖胚，并视实际需要在砖胚表面上彩饰釉药；
f.发泡烧成：按事先设定的烧成曲线在窑炉中发泡烧成；
g.徐冷退火：按事先设定的徐冷曲线徐冷退火，冷却后出窑即成具隔热保温功效的瓷化壁砖、地砖；
h.加工处理：可再经彩饰上釉或切、磨边(面)成特殊的装饰图案。
前述搓磨及破碎过程中可以用集尘设备收集粉尘，收集的粉尘可提供密闭混合研磨过程使用。
本发明具有如下优点：
1.本发明制成的产品比重约为0.3-1吨/米3，可减轻建筑物整体重量，但无损其结构强度。主要原因在于废玻璃材质与陶瓷主要原料长石非常接近，不同种类的显像管经添加其他原料作配方调整后，即可做成本发明的产品；
2.本发明产品吸水率在1％以下，可以显著降低建筑材料重量。通常用瓷砖吸水率为1％-5％；
3.本发明所采用的原料来源广泛，成本低廉，还可以解决环保问题；
4.本发明可以直接利用生产瓷砖原设备、生产线，投资小，见效快；
5.用该瓷砖贴于外墙或屋顶时，夏天可阻挡太阳热能被混泥土吸收，冬天可以阻断热流流失，从而降低能量的消耗。
具体实施方式
下面结合实施例具体说明本发明将废玻璃再生为具有隔热保温功效的瓷化砖的方法。
实施例1
a.废玻璃材料的预处理：以电子工业中产生的各种废显像管、显示器为原料，使用搓磨机进行表面搓磨处理，使其表面镀膜脱离，用破碎机将废玻璃破碎，经筛选将粒径大于1mm的玻璃颗粒筛选出来，经粉碎机再次破碎直到可以通过1mm筛，粉碎成粉料；
b.添加黏土材料：为了提高成品的隔热保温性能，在经过预处理的废玻璃材料中添加重量比为5％的黏土材料，黏土材料是净水厂沉淀后的淤泥；
c.添加发泡剂：添加重量比1％发泡剂；
d.密闭混合研磨：将玻璃粉料、黏土材料添加发泡剂后混合研磨为粉料，并干燥造粒；
e.成型：以成型机利用模具压制成各种尺寸的瓷化壁砖砖胚，并在砖胚表面上彩饰釉药；
f.发泡烧成：按事先设定的烧成曲线在窑炉中发泡烧成；
g.徐冷退火：按事先设定的徐冷曲线徐冷退火，冷却后出窑成具隔热保温功效的瓷化壁砖；
h.加工处理：可再经彩饰上釉或切、磨成特殊的装饰图案。
通过以上步骤即可利用废玻璃材料制造出具有隔热保温功效的瓷化壁砖。
实施例2
重复实施例1的步骤，添加重量比为20％的黏土材料、5％的发泡剂，其他与实施例1相同。
实施例3
重复实施例1的步骤，添加重量比为15％的黏土材料、3％的发泡剂，其他与实施例1相同。

Claims (4)

1.一种将废玻璃再生为隔热保温瓷化砖的方法，其特征在于包括如下步骤：
a.玻璃材料的预处理：将废玻璃材料破碎，筛选，粉碎成粉料；
b.添加黏土材料：添加重量比为5-20％的黏土材料；
c.添加发泡剂：添加重量比为1-5％的发泡剂；
d.密闭混合研磨：将玻璃粉料、黏土材料添加发泡剂后混合研磨成粉料，并干燥造粒；
e.成型：用成型机利用模具制成各种尺寸的砖胚；
f.发泡烧成：按事先设定的烧成曲线在窑炉中发泡烧成；
g.徐冷退火：按事先设定的徐冷曲线徐冷退火，冷却后出窑。
2.根据权利要求1所述的将废玻璃再生为隔热保温瓷化砖的方法，其特征在于将玻璃材料进行预处理前进行搓磨处理。
3.根据权利要求1或2所述的将废玻璃再生为隔热保温瓷化砖的方法，其特征在于用成型机利用模具制成各种尺寸的砖胚后，在砖胚表面上彩饰釉药。
4.根据权利要求1或2所述的将废玻璃再生为隔热保温瓷化砖的方法，其特征在于徐冷退火后，在瓷化砖表面上彩饰上釉或切、磨边。
CNB031559301A 2003-08-27 2003-08-27 一种将废玻璃再生为隔热保温瓷化砖的方法 Expired - Fee Related CN1319904C (zh)