CN1580170A - 制作粘带钎料用粘结剂 - Google Patents

制作粘带钎料用粘结剂 Download PDF

Info

Publication number
CN1580170A
CN1580170A CN 03133625 CN03133625A CN1580170A CN 1580170 A CN1580170 A CN 1580170A CN 03133625 CN03133625 CN 03133625 CN 03133625 A CN03133625 A CN 03133625A CN 1580170 A CN1580170 A CN 1580170A
Authority
CN
China
Prior art keywords
solder
binding agent
adhesive tape
adhesive
polymethylmethacrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 03133625
Other languages
English (en)
Other versions
CN1237138C (zh
Inventor
曹斌升
杜静
桓恒
孔庆吉
金莹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Liming Aero Engine Group Co Ltd
Original Assignee
Shenyang Liming Aero Engine Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Liming Aero Engine Group Co Ltd filed Critical Shenyang Liming Aero Engine Group Co Ltd
Priority to CN 03133625 priority Critical patent/CN1237138C/zh
Publication of CN1580170A publication Critical patent/CN1580170A/zh
Application granted granted Critical
Publication of CN1237138C publication Critical patent/CN1237138C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种制作粘带钎料用粘结剂，它是由聚甲基丙烯酸甲酯(有机玻璃)溶液、邻苯二甲酸二丁脂和甲基丙烯酸甲酯组成，该粘结剂与镍基粉末钎料混合，可制作成不同厚度的粘带钎料，用于蜂窝结构等零件的真空钎焊。

Description

制作粘带钎料用粘结剂
技术领域：
本发明涉及一种制作粘带钎料用粘结剂，该粘结剂与镍基粉末钎料混合，可制作成不同厚度的粘带钎料，用于蜂窝结构等零件的真空钎焊。
背景技术：
众所周知，高温镍基钎料一般由镍、铬、硅、硼等元素组成，因钎料中含有较多的硅和硼，故钎料比较脆，一般以粉末状态供应。使用时通常将钎料粉末(-150～300目)与粘结剂混合制成膏状，用涂敷器将膏状钎料施加到待钎焊零件的接头处。对蜂窝结构而言，由于其结构的特殊性，膏状钎料无法涂敷到钎焊接头处，因此不适用。为了将钎料均匀地涂敷到蜂窝结构钎焊接头处，使用粘带钎料是一种比较好的选择。而普通用于制作膏状钎料的粘结剂不适于制作粘带钎料。制作粘带钎料用的粘结剂应满足以下要求；
(1)结剂在真空加热时，在钎料的固相线温度以下必须全部挥发掉，不能残留碳黑等物质；
(2)粘结剂不能与钎料发生任何化学反应；
(3)粘结剂要有适当的粘性，在粘带钎料制作过程中不粘轧辊；
(4)制成的粘带钎料既柔韧又有足够的强度，并能根据需要切割成边界整齐的各种形状；
(5)粘结剂及其挥发物应无腐蚀性和无毒性。
发明内容：
本发明的目的是提供一种工艺简便、稳定、适用的粘结剂，与镍基粉状钎料混合制作钎焊蜂窝结构用粘带钎料。
本发明的粘结剂采用了聚甲基丙烯酸甲酯(俗称有机玻璃)溶液、邻苯二甲酸二丁脂和甲基丙烯酸甲酯，其各组份的重量百分比为：
6～8％浓度的聚甲基丙烯酸甲酯溶液      50～70％
邻苯二甲酸二丁脂                      20～40％
甲基丙烯酸甲酯                        5～15％
聚甲基丙烯酸甲酯溶液是将聚甲基丙烯酸甲酯块或聚甲基丙烯酸甲酯粉用溶剂溶解而获得，它们的配制比例是(重量百分比)；
聚甲基丙烯酸甲酯块(或粉)              6～8％
溶剂                                  92～94％
其中的溶剂选自二氯乙烷、三氯甲烷、甲酸中的一种。
聚甲基丙烯酸甲酯块(或粉)与溶剂根据所需配制重量按比例称出，放入能密封的玻璃瓶中，放置24～48小时，待聚甲基丙烯酸甲酯充分溶解到溶剂中，变成粘稠的均匀的聚甲基丙烯酸甲酯溶液。在溶解过程中，视情况，可用不锈钢棒或玻璃棒搅拌，使其均匀一致。
上述原料中：
聚甲基丙烯酸甲酯：聚甲基丙烯酸甲酯是粘结剂的主体，对粉状钎料超粘结作用。它可以将-150目～-300目的粉末状钎料粘合在一起而不松散。
溶剂：即液态的二氯乙烷(或三氯甲烷、甲酸)可将固态的聚甲基丙烯酸甲酯溶解成具有粘性的稠状溶液。
邻苯二甲酸二丁脂：邻苯二甲酸二丁脂是一种增韧剂，加入它可使制成的粘带钎料具有足够的韧性和强度。
甲基丙烯酸甲酯：使粘结剂不易干燥并延长其保存寿命。
本发明的粘结剂制作粘带钎料的比例为(重量比)：
粉末状钎料             93～95％
粘结剂                 5～7％
使用本发明的粘结剂制作粘带钎料钎焊蜂窝结构，施加钎料工艺简便，能保证钎焊面各处钎料均匀一致，钎焊质量优良而稳定。
具体实施方式：
实施例1
将6g聚甲基丙烯酸甲酯粉与94g二氯乙烷放入密封的玻璃瓶中，过夜，制成粘稠的均匀的聚甲基丙烯酸甲酯溶液。
将上述聚甲基丙烯酸甲酯溶液36g、邻苯二甲酸二丁脂18g、甲基丙烯酸甲酯6g倒如入塑料容器内，混合搅拌均匀，制成粘结剂。
称取镍基粉末钎料940g，与上述粘结剂混合，并用金属棒搅拌均匀，在室温下放置30小时。
将钎料搓合成“面团”状，用轧辊碾压成所需宽度和厚度的粘带钎料1000g，用该粘带钎料钎焊蜂窝结构，能保证钎焊面各处钎料均匀一致，钎焊质量优良而稳定。
实施例2
将实施例1聚甲基丙烯酸甲酯溶液30g、邻苯二甲酸二丁脂24g、甲基丙烯酸甲酯6g倒如入塑料容器内，混合搅拌均匀，制成粘结剂。
称取镍基粉末钎料940g，与上述粘结剂混合，并用金属棒搅拌均匀，在室温下放置40小时。
将钎料搓合成“面团”状，用轧辊碾压成所需宽度和厚度的粘带钎料1000g，用该粘带钎料钎焊蜂窝结构，能保证钎焊面各处钎料均匀一致，钎焊质量优良而稳定。
实施例3
将8g聚甲基丙烯酸甲酯粉与92g三氯甲烷放入密封的玻璃瓶中，过夜，制成粘稠的均匀的聚甲基丙烯酸甲酯溶液。
将上述聚甲基丙烯酸甲酯溶液36g、邻苯二甲酸二丁脂18g、甲基丙烯酸甲酯6g倒如入塑料容器内，混合搅拌均匀，制成粘结剂。
称取镍基粉末钎料940g，与上述粘结剂混合，并用金属棒搅拌均匀，在室温下放置30小时。
将钎料搓合成“面团”状，用轧辊碾压成所需宽度和厚度的粘带钎料1000g，用该粘带钎料钎焊蜂窝结构，能保证钎焊面各处钎料均匀一致，钎焊质量优良而稳定。
实施例4
将实施例3聚甲基丙烯酸甲酯溶液49g、邻苯二甲酸二丁脂17.5g、甲基丙烯酸甲酯3.5g倒如入塑料容器内，混合搅拌均匀，制成粘结剂。
称取镍基粉末钎料930g，与上述粘结剂混合，并用金属棒搅拌均匀，在室温下放置30小时。
将钎料搓合成“面团”状，用轧辊碾压成所需宽度和厚度的粘带钎料1000g，用该粘带钎料钎焊蜂窝结构，能保证钎焊面各处钎料均匀一致，钎焊质量优良而稳定。
实施例5
将7g聚甲基丙烯酸甲酯粉与93g甲酸放入密封的玻璃瓶中，过夜，制成粘稠的均匀的聚甲基丙烯酸甲酯溶液。
将上述聚甲基丙烯酸甲酯溶液36g、邻苯二甲酸二丁脂21g、甲基丙烯酸甲酯3g倒如入塑料容器内，混合搅拌均匀，制成粘结剂。
称取镍基粉末钎料940g，与上述粘结剂混合，并用金属棒搅拌均匀，在室温下放置30小时。
将钎料搓合成“面团”状，用轧辊碾压成所需宽度和厚度的粘带钎料1000g，用该粘带钎料钎焊蜂窝结构，能保证钎焊面各处钎料均匀一致，钎焊质量优良而稳定。

Claims (2)

1、一种制作粘带钎料用粘结剂，其特征在于以聚甲基丙烯酸甲酯溶液、邻苯二甲酸二丁脂、甲基丙烯酸甲酯为主要成分，其各组份的重量百分比为：
6～8％浓度的聚甲基丙烯酸甲酯溶液      50～70％
邻苯二甲酸二丁脂                      20～40％
甲基丙烯酸甲酯                        5～15％
2、按照权利要求1所述制作粘带钎料用粘结剂，其特征在于所述聚甲基丙烯酸甲酯溶液是通过将聚甲基丙烯酸甲酯块或聚甲基丙烯酸甲酯粉用溶剂溶解获得，它们的配制比例是，重量百分比：
聚甲基丙烯酸甲酯块或粉                6～8％
溶剂                                  92～94％
其中的溶剂选自二氯乙烷、三氯甲烷、甲酸中的一种。
CN 03133625 2003-08-01 2003-08-01 制作粘带钎料用粘结剂 Expired - Fee Related CN1237138C (zh)