CN1544337A - 纳米氧化铋的制备工艺 - Google Patents

纳米氧化铋的制备工艺 Download PDF

Info

Publication number
CN1544337A
CN1544337A CNA2003101105587A CN200310110558A CN1544337A CN 1544337 A CN1544337 A CN 1544337A CN A2003101105587 A CNA2003101105587 A CN A2003101105587A CN 200310110558 A CN200310110558 A CN 200310110558A CN 1544337 A CN1544337 A CN 1544337A
Authority
CN
China
Prior art keywords
bismuth oxide
bismuth
removing impurities
hydroxide solution
biocl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2003101105587A
Other languages
English (en)
Inventor
卫 李
李卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Central South University
Original Assignee
Central South University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Central South University filed Critical Central South University
Priority to CNA2003101105587A priority Critical patent/CN1544337A/zh
Publication of CN1544337A publication Critical patent/CN1544337A/zh
Pending legal-status Critical Current

Abstract

纳米氧化铋的制备工艺。本发明用盐酸对氯氧铋精矿进行浸出、除杂；浸液用水解法进行除杂；用氢氧化钠溶液将氯氧铋转化为Bi2O3进行除杂；用硝酸将Bi2O3溶解除杂；用氢氧化钠溶液沉淀硝酸铋溶液；生成的氧化铋用去离子活性水洗涤，过滤后，于真空干燥箱中干燥，即得纳米氧化铋产品。本发明具有流程短、成本低、环境友好的特点；生产成本较常规化学沉淀法低20－30％；环保达标，无常规化学沉淀法产生的氧化氮气体对环境造成的污染。

Description

纳米氧化铋的制备工艺
[技术领域]本发明涉及纳米氧化铋的一种生产工艺。
[背景技术]对于纳米氧化铋的制备，主要方法有：等离子体法、熔融喷雾氧化法、化学气相凝聚法、溶胶—凝胶法、化学沉淀法等，各种方法各有其特点，其中等离子体法具有流程短的优点，但需要特殊设备，一次性投资大，成本高；熔融喷雾氧化法流程短，但存在铋氧化不完全，喷嘴寿命短，操作环境危险等问题；化学气相凝聚法对设备材质要求比较高，工业化发展受限；溶胶—凝胶法制备超细氧化铋粉末，具有化学均匀性好，纯度高，颗粒细，可容纳不溶性组分或不沉淀组分等优越性，但存在粉体烧结性不好，干燥时收缩大等缺点；化学沉淀法采用化学手段制备超细氧化铋粉末，具有设备相对简单、粒度分布均匀、粉末活性好的优越性，但目前化学沉淀法制备氧化铋粉末都是以金属铋锭为原料，其用硝酸溶解产生的氧化氮气体对环境造成严重的污染，成本也较高。
[发明内容]本发明的目的在于克服常规化学法中的技术难点，而提供一种以氯氧铋精矿为原料，生产工艺简单，成本低，环保达标，产品活性高而平均粒度小于0.010μm的生产纳米氧化铋的方法。
具体的工艺过程为：用盐酸对氯氧铋精矿进行浸出、除杂；浸液用水解法进行除杂；用氢氧化钠溶液将氯氧铋转化为Bi2O3进行除杂；用硝酸将Bi2O3溶解除杂；用氢氧化钠溶液沉淀硝酸铋溶液；生产的氧化铋用去离子活性水洗涤，过滤后，于真空干燥箱中干燥，即得纳米氧化铋产品。
发生的化学反应主要有：
(1)
(2)
(3)
(4)
(5)
采用该法制备纳米氧化铋，具有流程短、成本低、环境友好的特点；由于原料直接采用铋精矿，试剂采用价廉的盐酸，生产成本较常规化学沉淀法低20-30％；环保达标，无常规化学沉淀法产生的氧化氮气体对环境造成的污染；通过添加少量分散剂的情况下，利用硝酸铋与氢氧化钠一步反应生成纳米氧化铋产品，省略了前驱体制备和锻烧、球磨工序。
[具体实施方式]
1.将100g BiOCl精矿(含Bi60％)，在温度80℃，时间1h，液固比为2∶1，酸耗为理论量1.75倍的条件下进行浸出后过滤，浸出液在水量与BiCl3溶液体积比为10∶1左右，温度95℃的条件下水解得到BiOCl，所得BiOCl在温度95℃，液固比为5∶1，时间2小时，NaOH溶液浓度为5％的条件下得到Bi2O3，，将所得Bi2O3的40℃左右用硝酸溶解，控制铋浓度300g/l，游离硝酸浓度80g/l，过滤，同时加入DBS分散剂，维持其浓度为0.1M，此时溶液总体积为200ml。将110g含量95％的NaOH溶于100ml去离子水中，备用。
在90℃搅拌的条件下，快速加入NaOH溶液于Bi(NO3)3溶液中，不断搅拌2h后，过滤，用去离子水洗涤至检验NO3 -根合格后，在60℃左右于干燥箱中干燥，即得纳米氧化铋产品。

Claims (1)

1.一种纳米氧化铋的制备工艺，其特征在于：本发明用盐酸对氯氧铋精矿进行浸出、除杂；浸液用水解法进行除杂；用氢氧化钠溶液将氯氧铋转化为Bi2O3进行除杂；用硝酸将Bi2O3溶解除杂；用氢氧化钠溶液沉淀硝酸铋溶液；生在的氧化铋用去离子活性水洗涤，过滤后干燥，即得纳米氧化铋产品。
CNA2003101105587A 2003-11-25 2003-11-25 纳米氧化铋的制备工艺 Pending CN1544337A (zh)