CN1322974C - 以木材为基体的表面金属镀膜的抗静电地板的制作方法 - Google Patents

以木材为基体的表面金属镀膜的抗静电地板的制作方法 Download PDF

Info

Publication number
CN1322974C
CN1322974C CNB2005100506688A CN200510050668A CN1322974C CN 1322974 C CN1322974 C CN 1322974C CN B2005100506688 A CNB2005100506688 A CN B2005100506688A CN 200510050668 A CN200510050668 A CN 200510050668A CN 1322974 C CN1322974 C CN 1322974C
Authority
CN
China
Prior art keywords
metal
wood
coating
timber
slab
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100506688A
Other languages
English (en)
Other versions
CN1709693A (zh
Inventor
邵千钧
黄金鹏
冯祖琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang A&F University ZAFU
Original Assignee
Zhejiang Forestry College
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Forestry College filed Critical Zhejiang Forestry College
Priority to CNB2005100506688A priority Critical patent/CN1322974C/zh
Publication of CN1709693A publication Critical patent/CN1709693A/zh
Application granted granted Critical
Publication of CN1322974C publication Critical patent/CN1322974C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及以木材为基体的表面金属镀膜的抗静电地板的制作方法。所要解决的技术问题是提供一种使材料既整体保持了原有木质材料的物理力学性能，又满足了抗静电的要求的抗静电地板的制作方法。本发明的制作方法是：原材料准备，包括用作基体的木质材料和用作表面镀膜的金属材料；干燥，使木材的含水率小于10%或绝干处理；加工板坯，加工好木质地板的板坯，并进行砂光处理；涂刷及烘干，采用树脂类涂料对木质地板板坯进行涂刷或喷涂，并进行烘干；蒸镀，将板坯送入真空镀膜装置中进行蒸镀，其真空度控制在5×10-2～10-5Pa之间，蒸镀时间在0.5～3小时，表面镀膜金属的厚度在0.2～20μm之间。本发明可用于装饰装璜领域。

Description

以木材为基体的表面金属镀膜的抗静电地板的制作方法
技术领域
本发明涉及一种以木材为基体的表面金属镀膜的抗静电地板的制作方法。适用于装饰装璜领域。
背景技术
木质地板具有比强度高、隔热隔音性能好、有良好的弹性等优点，广泛地用于室内装饰的各种场所。干燥的木材由于其电绝缘性能高，在使用过程中易产生静电积累，不适合用于防静电的生产或工作场所，如超净化环境、计算机或通讯设备机房、高粉尘的易燃易爆车间等。静电有可能导致吸尘严重难于净化而破坏超净化环境，从而影响产品外观或精密仪器的操作；静电放电会使各种精密仪器、电子元器件被击穿而报废，或导致设备主机故障；在炸药、煤矿、石油、化工、纺织等行业中，静电放电导致易燃易爆物起火或爆炸，造成巨大的恶性事故。所以抗静电地板在上述场所被广泛的应用。
目前的抗静电地板大体上分为三类：一是全部采用金属材料的全钢或全铝型地板；二是在刨花板和纤维板的基体上进行金属箔或导电塑料等防静电材料表面贴面的复合型地板；三是采用添加抗静电剂制备而成的PVC或橡胶地板。第一种的成本较高，金属材料的消耗量大；第二种表面与基体的结合强度不高；而第三种通常在强度或耐磨性方面有所欠缺。
发明内容
本发明要解决的技术问题是：提供一种以木材为基体的表面金属镀膜的抗静电地板的制作方法，旨在使材料既整体保持了原有木质材料的物理力学性能，同时满足了抗静电的要求，金属镀膜层具有很高的附着力，并且金属的消耗量很少，符合不可再生资源利用的集约化原则。
本发明所采用的技术方案是：
1)原材料准备
①用作基体的木质材料包括实木、刨花板、纤维板、胶合板、细木工板；
②用作表面镀膜的金属材料包括铝、铜、镍、铬、钛及其合金；
2)干燥
使木材的含水率小于1 0％或进行绝干处理；
3)加工板坯
加工好木质地板的板坯，并进行砂光处理；
4)涂刷及烘干
采用树脂类涂料对木质地板板坯进行涂刷或喷涂，并进行烘干；
5)蒸镀
将板坯送入真空镀膜装置中进行蒸镀，其真空度控制在5×10-2～10-5Pa之间，蒸镀时间控制在0.5～3小时，表面镀膜金属的厚度在0.2～20μm之间，可以根据需要通过镀膜工艺进行调整。
本发明的有益效果是：第一，使用真空镀膜的方式对木质地板表面进行金属化处理，金属用量少，其抗静电性能与全金属材料地板相当；第二，使用这种蒸镀方式在增加材料表面的抗静电性能的同时又不破坏木质材料固有的其它性能(如机械力学性能、隔热隔音性能等)；第三，该镀层的抗静电性能恒久稳定，不随湿度、时间的变化而变化；第四，该镀层的表面电阻率可以根据需要通过镀膜工艺进行适当的调节。
具体实施方式
本发明是一种以木质材料为基体的表面为镀膜金属的永久性抗静电地板，其表面镀膜金属的厚度为0.2～20μm，可以根据需要通过镀膜工艺进行调整。其镀层的抗静电性能稳定，抗剥离强度高，且金属材料消耗量小，同时不破坏木质地板原有的机械力学性能。
本发明涉及到的基材选用木质材料，可以为实木、刨花板、纤维板、胶合板、细木工板。
涉及的镀膜金属选用铝、铜、镍、铬、钛等，及其合金。
涉及的树脂类涂料可以为三聚氰胺涂料、聚氨酯涂料、醇酸树脂涂料，也可以是其改性产品。
镀层的表面电阻率与基材种类、基材表面粗糙度、镀层厚度等因素有关。随着镀层增厚，其表面电阻率随之减小，镀层的表面电阻率在100～105Ω之间。
本发明的制作方法按以下步骤：先进行干燥，使木材的含水率小于10％或进行绝干处理，加工好木质地板的板坯，并进行砂光处理，再采用树脂类涂料对木质地板板坯进行涂刷或喷涂，并进行烘干。然后送入真空镀膜装置中进行蒸镀，其真空度控制在5×10-2～10-5Pa之间，蒸镀时间控制在0.5～3小时。表面镀膜金属的厚度可达到0.2～20μm，可以根据需要通过镀膜工艺进行调整。
实施例1：实木地板表面镀铝膜
铝膜色泽银白，而且不易氧化，适合用于木质地板的表面镀膜处理。镀料选择99.99％的纯铝丝，工作真空度为1×10-2Pa，蒸镀时间为1小时，镀膜厚度为1.5μm。镀后既达到了抗静电效果，其表面还具有很好的光泽度，又达到了装饰效果。
实施例2：胶合板表面镀紫铜膜
紫铜膜具有良好的装饰效果，选择99％的紫铜丝作为镀料，工作真空为2×10-2Pa，蒸镀时间为0.6小时，镀膜厚度为0.5μm。镀后表面具有良好的抗静电效果，又达到了装饰效果。

Claims (1)

1、一种以木材为基体的表面金属镀膜的抗静电地板的制作方法，按以下步骤进行：
1)原材料准备
①用作基体的木质材料包括实木或刨花板或纤维板或胶合板或细木工板；
②用作表面镀膜的金属材料包括铝或铜或镍或铬或钛及其合金；
2)干燥
使木材的含水率小于10％或进行绝干处理；
3)加工板坯
加工好木质地板的板坯，并进行砂光处理；
4)封闭处理
采用树脂类涂料对木质地板板坯进行涂刷或喷涂，并进行烘干；
5)蒸镀
将板坯送入真空镀膜装置中进行蒸镀，其真空度控制在5×10-2～10-5Pa之间，蒸镀时间控制在0.5～3小时，表面镀膜金属的厚度在0.2～20μm之间。
CNB2005100506688A 2005-07-11 2005-07-11 以木材为基体的表面金属镀膜的抗静电地板的制作方法 Expired - Fee Related CN1322974C (zh)