CN1322614C - 锂离子电池用正极材料大晶粒LiCoO2及其制备方法 - Google Patents

锂离子电池用正极材料大晶粒LiCoO2及其制备方法 Download PDF

Info

Publication number
CN1322614C
CN1322614C CNB2005100121219A CN200510012121A CN1322614C CN 1322614 C CN1322614 C CN 1322614C CN B2005100121219 A CNB2005100121219 A CN B2005100121219A CN 200510012121 A CN200510012121 A CN 200510012121A CN 1322614 C CN1322614 C CN 1322614C
Authority
CN
China
Prior art keywords
preparation
lithium ion
grain
licoo
prepared
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100121219A
Other languages
English (en)
Other versions
CN1719643A (zh
Inventor
曾照强
胡晓清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tsinghua University
Original Assignee
Tsinghua University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tsinghua University filed Critical Tsinghua University
Priority to CNB2005100121219A priority Critical patent/CN1322614C/zh
Publication of CN1719643A publication Critical patent/CN1719643A/zh
Application granted granted Critical
Publication of CN1322614C publication Critical patent/CN1322614C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种锂离子电池用正极材料大晶粒LiCoO2及其制备方法，属于电池材料制备技术领域。该材料以Li2CO3、纳米Co3O4和微米Co3O4为原料。其特征在于，所述材料的配方为：Li2CO3：1～1.05，纳米Co3O4：0.2～0.5，微米Co3O4：0.5～0.8，其比例为实际摩尔数；球磨混料，烘干，过筛；在850℃空气气氛中煅烧，保温，即得大晶粒钴酸锂粉料。利用本发明的配方和制备方法制备的粉料粒度均匀，平均晶粒度为6～10μm，容量高140～145mAh/g，振实密度高2.5～2.8g/cm3，500次衰减为1～4%。本制备方法工艺简单、低成本，适用于工业化生产。

Description

锂离子电池用正极材料大晶粒LiCoO2及其制备方法
技术领域
本发明涉及一种锂离子电池用正极材料大晶粒LiCoO2材料及其制备方法，属于电池材料制备技术领域。
背景技术
目前，商业化锂离子电池采用的正极材料是晶粒尺寸较小的LiCoO2。通常钴酸锂的制备中采用的是单一颗粒尺寸的Co3O4，制备出的LiCoO2晶粒尺寸较小，材料的性能；如振实密度、电化学性能不能很好发挥，影响了锂离子电池的整体性能。
发明内容
本发明的目的是提供一种价格低廉、利于环保的性能优良的锂离子电池用大晶粒钴酸锂正极材料。通过配比两种不同晶粒尺寸的Co3O4，小晶粒向大晶粒扩散，促进大晶粒生长的原理制备出晶粒尺寸较大的LiCoO2，从而获得性能优良的LiCoO2电池材料。
本发明提出的锂离子电池用正极材料大晶粒LiCoO2，其特征在于，该材料以Li2CO3、纳米Co3O4和微米Co3O4为原料，所述材料的配方为：Li2CO3：1～1.05，纳米Co3O4：0.2～0.5，微米Co3O4：0.5～0.8，其比例为实际摩尔数。
本发明提出的一种制备如权利要求1所述锂离子电池用正极材料大晶粒LiCoO2的方法，其特征在于，该方法依次按如下步骤进行：
(1)分别称量按摩尔比为Li2CO3：1～1.05，纳米Co3O4：0.2～0.5(颗粒尺寸小于0.5μm)，微米Co3O4：0.5～0.8进行配料；
(2)将所配制的粉料进行球磨混料；
(3)将混合好的料烘干，过筛；
(4)将过筛的料在空气气氛中850℃煅烧，10～25小时；
(5)粉碎、分级，制备出晶粒尺寸为6～10μm的LiCoO2；
在上述锂离子电池用大晶粒LiCoO2正极材料的制备方法中，步骤(1)所述纳米Co3O4颗粒尺寸小于0.5μm；步骤(1)所述微米Co3O4颗粒尺寸1～10μm。
利用本发明的配方和制备方法制备的粉料粒度均匀，平均晶粒尺寸为粒度为5～10μm，容量高，分布范围140～145mAh/g，振实密度高2.5～2.8g/cm3，500次衰减为1～4％。本制备方法工艺简单、低成本，适用于工业化生产。
具体实施方式
下面结合实施例对本发明做进一步说明：
实施例1
(1)称取Li2CO3 34％wt，纳米Co3O4 33％wt，Co3O4 33％wt，粒度分别为2μm、0.3μm、1μm；
(2)将所配制的粉料按比例为料∶水∶球＝1∶1.5∶2(重量)，进行球磨混料12小时；
(3)将混合好的料在100℃烘干12小时，过60目筛；
(4)将过筛的料在空气气氛中850℃煅烧，25小时；
(5)粉碎、分级，制备出晶粒尺寸为8～10μm的LiCoO2
实施例2
(1)称取Li2CO3 34％wt，纳米Co3O4 20％wt，Co3O4 46％wt，粒度分别为2μm、0.2μm、1μm；
(2)将所配制的粉料按比例为料∶水∶球＝1∶1.5∶2(重量)，进行球磨混料12小时；
(3)将混合好的料在100℃烘干12小时，过60目筛；
(4)将过筛的料在空气气氛中850℃煅烧，20小时；
(5)粉碎、分级，制备出晶粒尺寸为7～9μm的LiCoO2
实施例3
(1)称取Li2CO3 34％wt，纳米Co3O4 15％wt，Co3O4 51％wt，粒度分别为2μm、0.3μm、1μm；
(2)将所配制的粉料按比例为料∶水∶球＝1∶1.5∶2(重量)，进行球磨混料12小时；
(3)将混合好的料在100℃烘干12小时，过60目筛；
(4)将过筛的料在空气气氛中850℃煅烧，20小时；
(5)粉碎、分级，制备出晶粒尺寸为6～8μm的LiCoO2

Claims (2)

1、锂离子电池用正极材料大晶粒LiCoO2的制备方法，其特征在于，该方法依次按如下步骤进行：
(1)分别称量按摩尔比为Li2CO3：1～1.05，纳米Co3O4：0.2～0.5，颗粒尺寸小于0.5μm，微米Co3O4：0.5～0.8进行配料；
(2)将所配制的粉料进行球磨混料；
(3)将混合好的料烘干，过筛；
(4)将过筛的料在空气气氛中850℃煅烧10～25小时；
(5)粉碎、分级，制备出晶粒尺寸为6～10μm的LiCoO2。
2、按照权利要求1所述的锂离子电池用正极材料大晶粒LiCoO2的制备方法，其特征在于：步骤(1)所述纳米Co3O4颗粒尺寸小于0.5μm；步骤(1)所述微米Co3O4颗粒尺寸为1～10μm。
CNB2005100121219A 2005-07-08 2005-07-08 锂离子电池用正极材料大晶粒LiCoO2及其制备方法 Expired - Fee Related CN1322614C (zh)