CN1295185C - 复合型汉白玉雕刻艺术装饰品及其制造方法 - Google Patents

复合型汉白玉雕刻艺术装饰品及其制造方法 Download PDF

Info

Publication number
CN1295185C
CN1295185C CNB2004100235268A CN200410023526A CN1295185C CN 1295185 C CN1295185 C CN 1295185C CN B2004100235268 A CNB2004100235268 A CN B2004100235268A CN 200410023526 A CN200410023526 A CN 200410023526A CN 1295185 C CN1295185 C CN 1295185C
Authority
CN
China
Prior art keywords
white marble
marble
ornament
weight
crystal resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100235268A
Other languages
English (en)
Other versions
CN1640690A (zh
Inventor
陈祥麟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2004100235268A priority Critical patent/CN1295185C/zh
Publication of CN1640690A publication Critical patent/CN1640690A/zh
Application granted granted Critical
Publication of CN1295185C publication Critical patent/CN1295185C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种复合型汉白玉雕刻艺术装饰品及其制造方法，该装饰品本体的配方组成物主要是采用汉白玉大理石整料或边角料碎石料的粉碎料和水晶树脂为主原料，并配以由固化剂、催化剂组成的辅助剂所制成，各原料的重量份数分别为：汉白玉大理石粉碎料65-78，水晶树脂22-33，固化剂2-4，催化剂2-4。其加工方法包括备料，粉碎，加水晶树脂、固化剂和催化剂搅拌均匀，置入模具压实固化成型，脱模风干进行人工细致雕刻修饰和打磨。与现有技术比较，本装饰品能批量定型出品，大大降低制作成本，而材质与造型都与真石制品没有多大区别，成品整体强度好，硬度高，制造方便，而且有利环境保护，可作为现代居家宾馆饭店广场等建筑装饰的首选工艺制品。

Description

复合型汉白玉雕刻艺术装饰品及其制造方法
【技术领域】
本发明涉及一种人造石头雕刻艺术制品，尤其是一种人造复合型汉白玉雕刻艺术装饰品及其制造方法，可用于建筑装璜装修中的人造石头仿雕刻艺术装饰品。
【背景技术】
自古以来，用各种石头特别是用各种质地的上等名贵石材(石头)雕刻的艺术品，一直被认为是最高境界的手工艺术品的衡量标准，其中汉白玉大理石的石质刚柔合并，白如似玉，如一块上好材质的汉白玉大理石经高手精雕细琢，能够呈现出光彩夺目，形似逼真的高级艺术品，在西方各国广为收藏与使用(用作各种建筑物装饰品)。然而在我国，由于大量开采，这种原料矿石资源越来越少，用汉白玉大理石真石制作的工艺品价格极为昂贵，每件都需几万元，不为一般消费者所能承受负担。另，天然汉白玉大理石加工过程复杂，除了成本高外，加工剩下的大量矿渣碎石废料边角料，因无法回收利用造成了难以避免的环境污染。
【发明内容】
本发明的目的之一是要提供一种人造的复合型汉白玉雕刻艺术装饰品。
本发明的目的之二是要提供一种人造的复合型汉白玉雕刻艺术装饰品的制造方法。
本发明的目的之一是以如下技术方案实现的：该雕刻艺术装饰制品本体的配方组成物主要是以采用汉白玉大理石整料或作为废料的边角料碎石的粉碎料和水晶树脂为主原料，并配以由固化剂、催化剂(亦称促进剂)等组成的辅助剂所制成，上述配方组成物中各原料的重量份数分别为：汉白玉大理石粉碎料65-78，水晶树脂22-33，固化剂2-4，催化剂2-4。
本发明上述技术解决方案中，所述的作为主原料之一的汉白玉大理石粉碎料是由依建筑用料标准(或工业矿沙用料标准)所粉碎加工出的0号(60目～80目)重量百分比为41-61％的汉白玉(细)石粉和1号(10目～30目)重量百分比为41-61％的汉白玉(粗)石粉搭配组成，且0号汉白玉细石粉和1号汉白玉粗石粉重量百分比之和为百分之百。。
在具体实施时，本发明还可在前述配方原料的基础上再添加以下重量份数的辅助原料：定型剂1-3，增白剂1-3。
本发明的目的之二是以如下技术方案实现的：本发明以回收废弃的汉白玉大理石的边角料、碎石料的粉碎料(或汉白玉大理石整料的粉碎料)和水晶树脂为主要原料，配以固化剂、催化剂、定型剂等辅助剂进行制造时，其制造的方法步骤主要包括：按配方配比量备料，将汉白玉边角料碎石料清洗风干并粉碎，再按配比量将粉碎料和水晶树脂拌和，再加固化剂、催化剂、定型剂等助剂搅拌均匀，置入预先制好的模具中压实固化成型，脱模后再自然风干成半成品，再进行人工细致雕刻，修饰打磨等精细加工，检验馐即成品。
本发明的上述方法步骤还可用于浮雕、圆雕、空雕及各种利用汉白玉大理石粉碎为原料所制作的艺术装饰品的加工制作。
与现有技术比较，本发明能批量定型出品，能大大降低真石的制作成本，而材质、硬度、亮度乃至于手感都与真汉白玉相媲美，成品整体强度好，硬度高，不仅物美价廉，制造方便，而且可充分利用废弃的碎矿石和边角碎石料，做到物尽其用，有利环境保护，可作为现代居家宾馆饭店广场装饰的首选工艺制品。
【具体实施方式】
以下结合具体实施例对本发明作进一步详细说明。
该复合型汉白玉雕刻艺术装饰品本体的配方组成物主要是以采用汉白玉大理石整料或作为废料的边角料碎石的粉碎料和水晶树脂为主原料，并配以由固化剂、催化剂(亦称促进剂)等组成的辅助剂所制成，上述配方组成物中各原料的重量份数分别为：汉白玉大理石粉碎料65-78，水晶树脂22-33，固化剂2-4，催化剂2-4。其中作为主原料之一的汉白玉大理石粉碎料是由依建筑用料标准(或工业矿沙用料标准)所粉碎加工出的0号(60目～80目)重量百分比为41-61％的汉白玉(细)石粉和1号(10目～30目)重量百分比为41-61％的汉白玉(粗)石粉搭配组成，且0号汉白玉细石粉和1号汉白玉粗石粉重量百分比之和为百分之百。
在具体实施时，本发明还可在前述配方原料的基础上再添加以下重量份数的辅助原料：定型剂1-3，增白剂1-3。
上述复合型汉白玉雕刻艺术装饰品的制作方法如下所述。
1、备料。人造汉白玉大理石原料制作：回收上等的汉白玉大理石的边料、下角料、碎石料，经清水洗净风干后，用粉碎机按工业矿沙用料标准破碎为0号和1号的粉料各占50％；2、按配比量选用高密度水晶树脂与上述的汉白玉大理石粉碎料进行搅拌均匀(放入搅拌机内搅拌)，拌匀完毕即成主料，可进入翻模状态；3、再在主料中加入配比量规定的固化剂、催化剂(各占3％)，定型剂、增白剂(各占2％)，在搅拌机中继续搅拌至均匀；4、压实固化成型：将上述拌匀的配料快速铺放入预先制作的模具上(模具是按预先选定好的雕塑题材内容制作的)，压实(可用模压或液压压实或用橡皮锤进行锤击夯实)后放置通风处进行固化；5、脱模后再自然风干形成半成品；6、人工细致雕刻修饰，用各种雕刻修饰打磨工具对半成品进行全面的修饰打磨，直至达到产品精致完美的程度；7、打磨上光，检验包装即为成品。

Claims (6)

1、一种复合型汉白玉雕刻艺术装饰品，其特征是该装饰品本体的配方组成物主要是以采用汉白玉大理石整料或作为废料的边角料碎石料的粉碎料和水晶树脂为主原料，并配以由固化剂、催化剂组成的辅助剂所制成，上述配方组成物中各原料的重量份数分别为：汉白玉大理石粉碎料65-78，水晶树脂22-33，固化剂2-4，催化剂2-4。
2、根据权利要求1所述的复合型汉白玉雕刻艺术装饰品，其特征是所述的作为主原料之一的汉白玉大理石粉碎料，是由依建筑用料标准或工业矿沙用料标准所粉碎加工出的0号重量百分比为41-61％的汉白玉细石粉和1号重量百分比为41-61％的汉白玉粗石粉搭配组成，且0号汉白玉细石粉和1号汉白玉粗石粉重量百分比之和为百分之百。
3、根据权利要求1或2所述的复合型汉白玉雕刻艺术装饰品，其特征是在前述配方原料的基础上再添加以下重量份数的辅助原料：定型剂1-3，增白剂1-3。
4、一种如权利要求1所述的复合型汉白玉雕刻艺术装饰品的制造方法，其特征是以汉白玉大理石的粉碎料和水晶树脂为主要原料，配以固化剂、催化剂、定型剂进行制造，其制造的方法步骤主要包括：按配方配比量备料，将汉白玉边角料碎石料清洗风干并粉碎，再按配方配比量加水晶树脂拌和，再加固化剂、催化剂、定型剂，以及增白剂搅拌均匀，置入预先制好的模具中压实固化成型，脱模后再自然风干制成半成品，再进行人工细致雕刻、修饰打磨，检验包装成品。
5、根据权利要求4所述的复合型汉白玉雕刻艺术装饰品的制造方法，其特征是上述的方法步骤还可用于浮雕、圆雕、空雕及各种利用汉白玉大理石粉碎料为原料所制作的艺术饰品的加工制作。
6、根据权利要求4所述的复合型汉白玉雕刻艺术装饰品的制造方法，其特征是上述配方组成物中各原料的重量份数分别为：汉白玉大理石粉碎料65-78，水晶树脂22-33，固化剂2-4，催化剂2-4，定型剂1-3，增白剂1-3。
CNB2004100235268A 2004-01-14 2004-01-14 复合型汉白玉雕刻艺术装饰品及其制造方法 Expired - Fee Related CN1295185C (zh)