CN1274742C - 低变黄烧焦抑制剂组合物 - Google Patents
低变黄烧焦抑制剂组合物 Download PDFInfo
- Publication number
- CN1274742C CN1274742C CNB038044757A CN03804475A CN1274742C CN 1274742 C CN1274742 C CN 1274742C CN B038044757 A CNB038044757 A CN B038044757A CN 03804475 A CN03804475 A CN 03804475A CN 1274742 C CN1274742 C CN 1274742C
- Authority
- CN
- China
- Prior art keywords
- tert
- composition
- butyl
- phenol
- butylphenol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
份数 | |
多元醇 | 100.00 |
蒸馏水 | 5.50 |
L5770硅氧烷(OSi) | 1.20 |
A127胺催化剂(OSi) | 0.47 |
Fyrol FR2(Akzo/Nobel) | 7.00 |
Dabco T9(航空产品) | 0.25 |
Mondur TD80 Grade A TDI(Bayer AG) | 70.80 |
添加剂 | 0.50 |
时间(小时) | 组合物1 | 比较组合物2 | Δb |
3 | 5.42 | 4.12 | -1.3 |
6 | 9.05 | 9.66 | 0.61 |
9.5 | 12.28 | 14.63 | 2.35 |
12 | 12.84 | 15.74 | 2.90 |
时间(小时) | 组合物1 | 比较组合物2 |
3 | -0.12 | -0.09 |
6 | -1.13 | -4.63 |
9.5 | -1.18 | -2.43 |
12 | -0.92 | -2.09 |
时间(天) | 组合物1 | 比较组合物2 |
12 | 7.14 | 9.46 |
时间(天) | 组合物1 | 比较组合物2 |
12 | 0.06 | -0.17 |
时间(小时) | 组合物1 | 比较组合物2 | Δb |
1 | 1.81 | 1.70 | -0.11 |
2 | 3.63 | 3.85 | 0.22 |
3 | 5.57 | 5.94 | 0.37 |
4 | 6.29 | 7.03 | 0.74 |
5 | 6.85 | 8.59 | 1.74 |
6 | 8.52 | 9.81 | 1.29 |
7 | 9.24 | 10.98 | 1.74 |
8 | 10.36 | 12.38 | 2.02 |
9 | 10.77 | 13.02 | 2.25 |
10 | 11.36 | 13.67 | 2.31 |
烧焦 | 6小时NOX气体 | 9小时NOX气体 | |
单独TBC | 淡黄 | 8.00 | 11.2 |
常规BHT/胺 | 金黄 | 10.00 | 16 |
常规BHT | 常规945 | PLX 976/232 | PLX 976/132 | |
6小时气体 | 5.67 | 8.80 | 6.31 | 6.26 |
9小时气体 | 11.97 | 14.67 | 9.19 | 8.90 |
常规945 | PLX 976 | 1135代替PLX 976中的ISONOX 132 | |
未照射b | -1.68 | -1.47 | -1.47 |
6天b | 11.53 | 6.04 | 6.17 |
13天b | 13.90 | 10.08 | 10.49 |
常规945 | PLX 976 | 1135代替PLX 976中的ISONOX 132 | |
未照射B | -1.50 | -1.30 | 1.58 |
3小时B | 11.09 | 6.19 | 5.53 |
6小时B | 13.30 | 8.75 | 8.21 |
9小时B | 14.82 | 11.29 | 11.42 |
VANOX 945 | PLX 976 | 1135代替PLX 976中的ISONOX 132 | |
0小时(b) | -1.78 | -1.61 | -1.69 |
4小时(b) | 7.56 | 5.73 | 6.97 |
8小时(b) | 13.43 | 8.53 | 12.36 |
NOX气体 | 荧光 | 紫外线 | ||||
3小时 | 6小时 | 10天 | 22天 | 1小时 | 2.5小时 | |
+PTZ | 7.64 | 9.67 | 7.15 | 11.51 | 2.46 | 4.9 |
无PTZ | 7.67 | 9.87 | 7.09 | 11.27 | 2.43 | 5.06 |
普通BHT | 9.52 | 13.72 | 11.92 | 15.96 | 5.45 | 9.76 |
普通945 | 12.16 | 14.95 | 12.38 | 14.66 | 6.02 | 9.22 |
氧化氮(NOX)气体 | 荧光 | 紫外光 | |||||||
6小时 | 18小时 | 24小时 | 6天 | 20天 | 35天 | 1小时 | 5小时 | 11小时 | |
PLX-976 | 4.39 | 10.76 | 12.5 | 4.73 | 10.18 | 13.04 | 1.7 | 7.12 | 12.9 |
BHT/976 | 3.36 | 11.24 | 13.4 | 4.64 | 13.44 | 15.28 | 1.42 | 7.02 | 13.54 |
232/976 | 7.4 | 14.29 | 15.8 | 4.87 | 10.69 | 13.39 | 1.78 | 7.48 | 13.2 |
1010/976 | 5.13 | 13.78 | 15.66 | 4.6 | 10.80 | 14.14 | 1.56 | 7.89 | 13.95 |
气室 | 荧光 | W-O-M | |||
7.0小时 | 11.5小时 | 3天 | 0.5小时 | 1.5小时 | |
不稳定组合物 | 5.44 | 8.01 | 5.63 | 0.93 | 5.34 |
PLX-976 | 6.58 | 9.54 | 4.87 | 1.70 | 5.71 |
常规混合物 | 4.93 | 10.53 | 7.84 | 1.83 | 7.12 |
常规945 | 10.21 | 14.60 | 10.40 | 5.68 | 10.49 |
AFC | 荧光 | W-O-M | ||||
2小时 | 4小时 | 1天 | 9天 | 2小时 | 4小时 | |
PLX-976(5000ppm) | 3.38 | 6.83 | 1.66 | 11.6 | 1.16 | 2.89 |
PLX-976(3500ppm) | 3.05 | 6.49 | 1.18 | 11.0 | 0.86 | 2.59 |
C2常规945 | C3PLX 976 | C31在976中的ANOX 70 | C32在976中的Lowinox AH25 | C33在976中的Lowinox TBM6 | C34在976中的Lowinox MD24 | |
未照射b | -1.69 | -1.56 | -1.49 | -1.28 | -1.01 | -1.31 |
2天b | 8.63 | 2.65 | 3.19 | 4.10 | 4.37 | 4.41 |
7天b | 12.82 | 7.89 | 8.28 | 9.90 | 9.42 | 10.70 |
C2常规945 | C3PLX 976 | C31在976中的ANOX 70 | C32在976中的Lowinox AH25 | C33在976中的Lowinox TBM6 | C34在976中的Lowinox MD24 | |
未照射b | -1.53 | -1.27 | -1.32 | -1.04 | -1.10 | -1.23 |
3小时b | 10.60 | 5.37 | 5.47 | 7.11 | 6.03 | 7.48 |
7小时b | 13.57 | 9.25 | 9.70 | 11.35 | 9.91 | 12.29 |
C2VANOX945 | C3PLX 976 | C31在976中的ANOX 70 | C32在976中的Lowinox AH25 | C33在976中的Lowinox TBM6 | C34在976中的Lowinox MD24 | |
未照射b | -1.62 | -1.60 | -1.57 | -1.24 | -1.19 | -1.52 |
3.5小时b | 12.78 | 7.78 | 9.69 | 7.36 | 8.96 | 8.99 |
5小时b | 14.79 | 8.80 | 11.49 | 8.00 | 9.80 | 10.00 |
11小时b | 18.43 | 11.09 | 14.78 | 10.16 | 11.78 | 12.45 |
Claims (15)