CN1210324C - 聚氨酯弹性体 - Google Patents
聚氨酯弹性体 Download PDFInfo
- Publication number
- CN1210324C CN1210324C CNB961998962A CN96199896A CN1210324C CN 1210324 C CN1210324 C CN 1210324C CN B961998962 A CNB961998962 A CN B961998962A CN 96199896 A CN96199896 A CN 96199896A CN 1210324 C CN1210324 C CN 1210324C
- Authority
- CN
- China
- Prior art keywords
- weight
- elastomerics
- storage modulus
- loss tangent
- polyisocyanates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
1 | 2 | 3 | 4 | 比较1 | 比较2 | |
多异氰酸酯I | 36.4 | 42.7 | - | - | - | - |
多异氰酸酯II | - | - | 46.8 | - | - | 42.9 |
多异氰酸酯III | - | - | - | - | 109 | - |
多异氰酸酯IV | - | - | - | 100 | - | - |
多元醇A | 100.0 | 50.0 | - | - | - | - |
多元醇B | - | 50.0 | 100.0 | - | - | - |
多元醇C | - | - | - | - | 100.0 | - |
多元醇D | - | - | - | - | 28.3 | - |
多元醇E | - | - | - | - | - | 100.0 |
乙二醇 | 5.0 | 7.0 | 7.0 | 4.55 | 8.9 | 6.0 |
水 | 0.3 | 0.3 | 0.3 | 0.21 | 0.6 | 0.3 |
催化剂1 | 1.0 | 0.5 | 1.0 | 0.7 | 2.6 | 1.0 |
催化剂2 | - | - | - | - | 0.4 | - |
模制物密度(千克/立方米) | 450 | 440 | 440 | 580 | 490 | 585 |
硬度 | 46(Asker C) | 51(Asker C) | 41(Asker C) | 62(Asker C) | 47(肖耳A) | N.M.* |
E′(20℃)/E′(120℃)比例 | 0.95 | 1.01 | 0.98 | 0.86 | 1.69 | 2.19 |
tanδ(100℃) | 0.002 | 0.013 | 0.024 | 0.005 | 0.070 | 0.078 |
tanδMAX(于℃之温度) | -23 | -26 | -11 | -11 | -43 | -45 |
tanδMAX(值) | 1.08 | 0.86 | 1.01 | 1.22 | 0.42 | 0.37 |
Claims (15)