CN1186027A - 磁性显示用分散组合物 - Google Patents

磁性显示用分散组合物 Download PDF

Info

Publication number
CN1186027A
CN1186027A CN97114198A CN97114198A CN1186027A CN 1186027 A CN1186027 A CN 1186027A CN 97114198 A CN97114198 A CN 97114198A CN 97114198 A CN97114198 A CN 97114198A CN 1186027 A CN1186027 A CN 1186027A
Authority
CN
China
Prior art keywords
magnetic
magnetic display
distributing composition
composition
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN97114198A
Other languages
English (en)
Other versions
CN1097517C (zh
Inventor
田崎博司
小松崎明広
野照明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
K K PILOT
Original Assignee
K K PIRATE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by K K PIRATE filed Critical K K PIRATE
Publication of CN1186027A publication Critical patent/CN1186027A/zh
Application granted granted Critical
Publication of CN1097517C publication Critical patent/CN1097517C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供了防止静电影响的磁性显示用分散组合物。这种磁性显示用分散组合物由10—30重量%的粒径为10—150μm的磁性粒子、0.01—0.5重量%的防带电剂、1—10重量%的有机增稠剂、0.1—10重量%的着色材料以及作为重量其余部分的有机类分散介质组成。

Description

磁性显示用分散组合物
本发明涉及利用磁性来显示清晰的记录且又能消去该记录的磁性显示用分散组合物。
历来，人们就知道利用磁力使磁性粒子泳动来显示磁性，以及由磁性粒子、分散介质、增稠剂和能获得所希望颜色的着色材料即可组成磁性显示用分散组合物。
使用磁性显示用分散组合物可以显示所记录的内容，也可消去所记录的内容。利用配备了磁性显示用分散组合物的记录用盘的外侧基板上配置了磁性笔或电磁铁的尖端进行记录时，被磁性笔、电磁铁等的磁力吸引的磁性粒子就会从内侧泳动出来，根据分散液体和磁性粉末之间的色差对比，就能够显示出记录的内容。而且，如果内侧基板的消磁器产生了磁力，被吸引到外侧基板的磁性粒子就能被吸引到内侧基板而消去已显示的记录。
一般，磁性显示用分散组合物被用于制造分散系的磁性粒子被磁性笔吸引而显示出所记录的文字、图形等的记录板等，例如应用于玩具以及文具等领域。它在使用时不受环境的影响，在温度、湿度有变化的日常生活环境下就能使用。
但是，对于以前的磁性显示用分散组合物，由于上述使用形式中的显示盘的基板主要使用的是氯乙烯薄板或聚酯薄板，所以在象冬天那样气温较低、空气干燥的气候条件下，易产生静电，发生带电现象。而且，除了冬天以外的其他季节，如使磁性显示用分散组合物的磁性笔移动，记录下文字或图形时，由于磁性粒子的移动以及磁性粒子之间的碰撞、或磁性笔的磁头和外侧基板表面之间的摩擦、以及消磁器和内侧基板表面之间的摩擦而引起的静电，都会使外侧或内侧基板上带上大量的电荷。另外，用手握住磁性笔进行记录时，由于磁性显示用分散组合物的外侧基板表面和手之间的摩擦，也会引起静电。
发生了带电现象后，磁性粒子吸着在外侧或内侧基板上，使磁性显示用盘处于被污染的状态，这样在记录时就会使有笔迹部分和无笔迹部分的对比性降低，或消去笔迹时产生不能完全消去这样的消去不良等问题。而且，由于静电吸引力破坏了增稠剂和着色剂的分散系，所以发生了磁性粒子沉降和相分离的现象，造成磁性分散组合物的耐久性下降，无法清晰显示所记录的文字以及图形等问题。为了解决以上的问题，提出了预先在外侧基板表面涂上防带电剂；或在外侧基板表面铺上一层防带电的合成树脂薄膜，这样即使因为磁性笔移动或其他原因而引起静电时，也能使静电通过该防静电合成树脂薄膜快速放电以达到防止带电的目的等方法。
但是，上述历来防带电的方法之一的在外侧基板表面涂布防带电剂的方法，由于反复显示记录以及消去记录时磁性笔的磁头和基板表面之间有摩擦，所以出现了磨损、瑕疵等导致防带电剂脱落而不能维持耐久性的问题。此外，在外侧基板表面铺上一层非带电性合成树脂薄膜以防止带电的方法，由于基板上有一层不带电的合成树脂薄膜，所以造成了文字、图形等记录的显示清晰度下降的问题。而且在制造方面，由于增加了在外侧基板表面铺上该薄膜的步骤，所以成本就会有所提高。
本发明就是鉴于以上事实，进行改进后完成的。本发明提供了即使在象冬天那样易产生静电的苛刻条件下，有笔迹部分和无笔迹部分的对比也不会下降；不会发生笔迹消除不良而有残留等问题；能获得清晰的笔迹部分和具有良好掩蔽性的无笔迹部分；而且成本也较低的磁性显示用分散组合物。
本发明的第1项是关于由10-30重量％的粒径10-150μm的磁性粒子、0.01-0.5重量％的防带电剂、1-10重量％的有机增稠剂、0.1-10重量％的着色剂、以及作为重量其余部分的有机类分散介质组成的磁性显示用分散组合物。
本发明的第2项是关于第1项中记载的磁性显示用分散组合物，其中的有机类分散介质为异构链烷烃或锭子油或乙二醇。
本发明的第3项是关于第1项中记载的磁性显示用分散组合物，其中的有机类分散介质为异构链烷烃和锭子油的混合物。
本发明的第4项是关于第1项至第3项中的任何一项记载的磁性显示用分散组合物，其中的防带电剂可选自1种或2种以上的下列各种物质，如聚丁烯硫酸化物、脂肪族烷基季铵盐、氨基乙醇-环氧氯丙烷缩聚物、烷基苯磺酸、烷基水杨酸金属盐、丁二酸磺酸盐、二烷基丁二酸磺酸盐、十二烷基苯磺酸金属盐。
本发明的第5项是关于第1项至第3项中的任何一项记载的磁性显示用分散组合物，其中的防带电剂是聚丁烯硫酸化物、脂肪族烷基季铵盐、氨基乙醇-环氧氯丙烷缩聚物、烷基苯磺酸的混合物。
本发明的第6项是关于第1项至第3项中的任何一项记载的磁性显示用分散组合物，其中的防带电剂是烷基水杨酸铬盐、丁二酸磺酸钙盐、聚合物的混合物。
本发明的第7项是关于第1项至第6项中的任何一项记载的磁性显示用分散组合物，其中的防带电剂溶解并分散于和分散介质相溶的溶剂中。
本发明的第8项是关于第1项至第7项中的任何一项记载的磁性显示用分散组合物，其中的增稠剂可选自1种或2种以上的下列各种物质，如含有羟基的脂肪酸双酰胺、氢化蓖麻油、N-酰胺酸烷基酰胺。
本发明的磁性显示用分散组合物是由磁性粒子、分散介质、增稠剂、前述的防带电剂、能获得所希望颜色的着色剂等混合而成的。
本发明所用的防带电剂包括复合型、阴离子型、阳离子型、非离子型、高分子型等。
阴离子型防带电剂包括烷基苯磺酸、烷基苯磺酸盐、烷基磷酸盐、丁二酸二烷基酯磺酸钠盐、丁二酸磺酸钙盐、水杨酸类铬盐、水杨酸类铝盐；阳离子型防带电剂是指脂肪族烷基季铵盐；非离子型防带电剂包括聚环氧乙烷烷基醚、聚环氧乙烷烷基烯丙基醚、聚环氧乙烷烷基胺等聚环氧化物的衍生物以及山梨糖醇酐脂肪酸酯；高分子型防带电剂包括聚羧酸胺盐、氨基乙醇-环氧氯丙烷缩聚物。其他还包括烷基甜菜碱、磺基甜菜碱、聚丁烯硫酸化物。复合型防带电剂是从上述各种防带电剂组合中选用2种以上组合而成的。从上述的防带电剂中选择1种或2种以上，既可单独也可组合在一起加入分散液体中，用量为0.01-0.5重量％。
磁性粒子包括黑色磁铁矿、γ-赤铁矿、二氧化铬、铁氧体等氧化物磁性材料；钴、镍等合金类的金属磁性材料。它们以粉末或薄片的形式加入分散液体中，用量为10-30重量％。此外，为了调整大小、形状等，还可在造粒后再使用。可根据目的的不同，使用大小从细粉到粗大粒子的不同的磁性粒子，形状包括球状、柱状、块状、薄片状等。可在磁性粒子中混入各种着色材料，也可将各种材料覆盖在磁性粒子的表面，将磁性粒子调整成与其固有颜色不同的色调后再使用。而且，如果磁性粒子的大小互不相同则其泳动性也各不相同，所以磁性粒子的大小较均一则显示的清晰度就较高。
为使本发明的记录性、显示的保持性、清晰性、消去性等性能和一般的磁性盘具有同样的效果，可添加增稠剂，添加的量为1-10重量％。
增稠剂包括含有羟基的脂肪酸双酰胺，例如乙烯基双-1，2-羟基硬脂酸酰胺、氢化蓖麻油；或N-酰胺酸烷基酰胺，例如N-十二烷基-L-谷氨酸-α、γ-二丁酰胺等。从以上各种物质中选取增稠剂，在分散液体中可单独也可组合在一起使用。此外，还可将其他的有机增稠剂、无机增稠剂作为辅助的增稠剂，与以上的增稠剂一起使用。
分散介质包括油类、脂肪族碳氢化合物等非极性溶剂；乙二醇类、醇类等极性溶剂。较好的是异构链烷烃等脂肪族碳氢化合物。
具体地讲，有异构链烷烃、锭子油、乙二醇等。
着色材料包括白色颜料、其他染料或颜料。对于可塑性分散液体，添加量一般在10％以下，较好的是在3％以下，这样可增大可塑性分散液体和磁性粒子的对比，其结果是使显示清晰度更高。如果着色材料的添加量过多，则通过磁性粒子的显示就变得不清晰。
此外，使用在分散介质中分散性较差的防带电剂，例如水杨酸铬盐时，可先将其溶解在与分散介质相溶的溶剂如甲苯等溶剂中，然后再添加入分散介质中，这样就能得到良好的分散状态。这种分散方法也适用于在分散介质中分散性良好的防带电剂。
本发明的磁性显示用分散组合物是藏于多室构造的盘或小囊中进行显示的。以例1为例对该盘进行说明。该磁性显示用盘通过以下各步完成，首先在基板上形成多室构造的众多小室，在这些小室中填充前述的磁性显示用分散组合物，最后贴上另一块基板就得到了磁性显示用盘。
其他的方法包括在利用基板上形成的多个凹处而构成的小室中，填充入前述的磁性显示用分散组合物，最后贴上另一块基板就得到了磁性显示用盘。此外，还可以在基板的一侧或两侧设置凹处，然后合并在一起，在基板间形成独立的小室。
其他的密封磁性显示用分散组合物的方法还有将其藏在小囊中，再将这种小囊与粘合剂材料混合，涂布于基板上，干燥后就得到了显示盘。
实施例1
在85.2重量份的异构链烷烃溶剂(ISOPER-M、Esso化学株式会社制造)中，添加0.1重量份的防带电剂(STADIS-425、Du Pont公司制造的防带电剂)以及1.3重量份的氢化蓖麻油(THIXCIN R RHEOX，Inc)，加热溶解后冷却，得到分散液体。
利用特殊机化工业株式会社制造的湿式分散机(T.K.HOMOMIXER)，将86.6重量份的上述分散液体和1.1重量份的氧化钛(TIPAQUE CR-50、石原产业株式会社制造)进行混合分散，得到87.7重量份的白色分散液体。
然后，将80重量份的磁铁矿(TODA COLOR KN-320，户田工业株式会社制造)和50重量份的固体环氧树脂(EPOTOHTO YD-017、东都化成株式会社制造)的40％的甲基乙基甲酮溶液混合，干燥后将其粉碎，得到50重量份的10-150μm的黑色磁性粒子。
将12.3重量份的这种磁性粒子混合入87.7重量份的前述白色分散液体中，得到100重量份的磁性显示用分散组合物。
实施例2-10
利用与实施例1相同的表1中所示的各种物质，得到各实施例的磁性显示用分散组合物。
实施例11
利用与实施例1相同的表1中所示的各种物质，得到实施例11的磁性显示用分散组合物。
比较例1
在85.2重量份的异构链烷烃溶剂(ISOPER-M、Esso化学株式会社制造)中，添加1.3重量份的乙烯基双-1，2羟基硬脂酸酰胺(ITOH WAX J-530、伊藤制油株式会社制造)，加热溶解后冷却，得到分散液体。
利用T.K.HOMOMIXER(特殊机化工业株式会社制造的湿式分散机)，将86.5重量份的上述分散液体和1.3重量份的氧化钛(TIPAQUE CR-50、石原产业株式会社制造)进行混合分散，得到87.7重量份的白色分散液体。
然后，将80重量份的磁铁矿(TODA COLOR KN-320，户田工业株式会社制造)和50重量份的固体环氧树脂(EPOTOHTO YD-017、东都化成株式会社制造)的40％的甲基乙基甲酮溶液混合，干燥后将其粉碎，得到50重量份的10-150μm的黑色磁性粒子。
将12.3重量份的这种磁性粒子混合入87.7重量份的前述白色分散液体中，得到100重量份的磁性显示用分散组合物。
比较例2-3
利用与实施例1相同的表1中所示的各种物质，制造各比较例的磁性显示用分散组合物。
使用例1
首先，利用乙烯-乙酸乙烯类粘合剂，在作为外侧透明基板的约0.15mm的氯乙烯薄板上粘合上由厚约0.065mm的氯乙烯形成的1边约为2mm的类似正六角形、高约0.8mm的蜂窝状结构多室板，制成显示用盘的部件。然后，在多室构造的各个小室中填充入实施例1的磁性显示用分散组合物；作为内侧基板的是约0.08mm的透明氯乙烯薄板，利用环氧类粘合剂将其密封，制成磁性显示用盘(形式A)。
使用例2-10
与使用例1相同，填充实施例2-10的磁性显示用分散组合物，制成形式A的磁性显示用盘2-10。
使用例11
首先，利用真空成型模具，在作为内侧透明基板的约0.15mm的氯乙烯薄板上形成1边约2mm的类似正六角形、深约0.8mm的多个连续凹部。然后，在各凹部中填充实施例11的磁性显示用分散组合物，作为外侧基板的约0.08mm的透明氯乙烯薄板，利用环氧类粘合剂将其密封，制成磁性显示用盘(形式B)。
比较例的使用例1
与使用例1相同，填充比较例1的磁性显示用分散组合物，制成形式A的磁性显示用盘。
比较例2和3的使用例2-3
与使用例11相同，填充比较例2和3的磁性显示用分散组合物，制成形式B的磁性显示用盘。
                              表1
                                            实施例            比较例
    1     2     3     4     5     6     7     8     9     10     11     1     2     3
    添加物     防带电剂     L     0.1
    M     0.1
    N     0.1
    O     0.1
    P     0.1
    Q     0.1
    R     0.1
    S     0.1
    T     0.1
    U     0.1
    V     0.1
    增稠剂 乙烯基双-1，2-羟基硬脂酸酰胺     1.3     1.3     1.3     1.3     1.3     1.3     1.3     1.3     1.3     1.3
氢化蓖麻油     1.3     1.3
N-酰胺酸烷基酰胺     1.3     1.3
    分散介质 异构链烷烃溶剂     85.2     85.2     84.4     85.2     84.4     85.2     85.2     85.2     85.2     85.2
锭子油     84.4     85.2
乙二醇     85.2     85.2
甲苯     0.8     0.8     0.8
磁性粒子 磁铁矿     12.3     12.3     12.3     12.3     12.3     12.3     12.3     12.3     12.3     12.3     12.3     12.3     12.3     12.3
着色材料 氧化钛     1.1     1.1     1.1     1.1     1.1     1.1     1.1     1.1     1.1     1.1     1.1     1.2     1.2     1.1
盘的形式     A     A     A     A     A     A     A     A     A     A     B     A     B     B
(注)
L：4种成分(聚丁烯硫酸化物、脂肪族烷基季铵盐、氨基乙醇-环氧氯丙烷缩聚物、烷基苯磺酸)(E.I.du Pont de Nemours&Co.Inc、注册商标STADIS-425)
M：4种成分(聚丁烯硫酸化物、脂肪族烷基季铵盐、氨基乙醇-环氧氯丙烷缩聚物、烷基苯磺酸)(E.I.du Pont de Nemours&Co.Inc、注册商标STADIS-450)
N：3种成分(烷基水杨酸铬盐、丁二酸磺酸钙盐、聚合物)(Shell化学工业株式会社、注册商标ASA-3)
O：水杨酸类铬盐(Orient化学工业株式会社、注册商标BONTRON E-84)
P：水杨酸类铝盐(Orient化学工业株式会社、注册商标BONTRON E-88)
Q：丁二酸二烷基酯磺酸钠盐(日本乳化剂株式会社、注册商标NEW CALL291PG)
R：十二烷基苯磺酸钠盐(东京化成工业株式会社、注册商标FAW 01)
S：三甲基铵硬脂酰氯(花王株式会社、注册商标COATAMIN 86P CONC)
T：山梨糖醇单月桂酸酯(日本乳化剂株式会社、注册商标TECHSNOL SPT)
U：聚羧酸型高分子活性剂(花王株式会社、注册商标HOMOGENOL L-18)
V：聚羧酸型高分子活性剂(花王株式会社、注册商标HOMOGENOL L-1820)
试验方法以及评定
为了更清晰地显示使本发明的效果，对使用了实施例和比较例的磁性显示用盘的使用例的磁性显示用分散组合物进行下列各项的测试，并对其进行评定。
(1)耐久性(分散液体的寿命)
在圆盘试验机上安装磁性盘，使其连续反复地进行记录、消去操作，观察引起磁性盘状态变化(磁性粒子的沉降、液体的相分离)的次数。
下面对圆盘试验机作一下说明，圆盘试验机是由安装了磁性显示用盘的圆形板部分、使圆板旋转的驱动部分、记录用磁铁以及消去用磁铁构成的。该圆板部分是使用了板厚为1.5mm，直径为200mm的氧化铝材料的圆盘，该驱动部分使用了能控制转数以及速度的小型马达(ORIENTAL MOTOR制造的21 J3 GA-A2)，其旋转轴上安装有该圆板的中心部分。该记录用磁铁以放射状配置于离该圆板部分中心65mm处，而且当该磁性显示用盘安装在该圆板部分时，要在与该磁性显示用盘的外侧基板表面连接的位置上，沿圆周方向每72°配置5个大小为1mm的圆柱形电磁铁，在该圆板部分的内侧，要与记录用磁铁的位置错开，每72°配置5个消去用的圆柱形电磁铁。
试验内容是在该圆板部分上安装磁性显示用盘，使该磁性显示用盘以10rpm的速度旋转，通过该记录用磁铁的电磁铁磁头进行记录(记录速度为4m/分)，再用配置在该圆板部分内侧的，与记录用磁铁位置错开的消去用磁铁进行消去，连续反复进行，1分钟内进行50次记录和消去。而且，消去用磁铁使用了单面带磁性的各向异性橡胶磁铁(Mag-X株式会社制造的NT-5M-1504、长10×高10×厚5mm)。
(2)耐静电性(静电的影响)
使用静电障碍测试仪(三基电子株式会社制造的SET-30A型)，使磁性盘的表面带电，测定磁性粒子附着在外侧基板时的电压。
(3)清晰度(对比)
磁性盘产生静电时(外加电压为3KV时)，通过Macbeth浓度计(RD-915型)测定使用磁性笔记录时有笔迹部分和无笔迹部分的白度，求出记录部分和无记录部分的O.D.值的差。而且，记录时使用相当于JIS C2502 MPB380的永久磁铁作为记录的笔头。
各试验的评定结果如表2所示。
                            表2
    耐久性(次)     耐静电性KV     清晰度     综合
实施例1     30,000     4.0     0.75     ○
实施例2     30,000     4.5     0.75     ○
实施例3     32,500     6.5     0.75     ○
实施例4     30,000     3.5     0.75     ○
实施例5     27,500     4.0     0.75     ○
实施例6     30,000     4.0     0.75     ○
实施例7     20,000     4.0     0.75     ○
实施例8     30,000     3.5     0.75     ○
实施例9     27,500     4.0     0.75     ○
实施例10     32,500     3.5     0.75     ○
实施例11     25,000     4.0     0.75     ○
比较例1     15,000     2.5     0.57     ×
比较例2     15,000     2.5     0.57     ×
比较例3     15,000     2.5     0.57     ×
如上所述，利用本发明反复进行文字、图形等记录的显示以及消去时，即使由于磁性粒子的移动以及磁性粒子之间的碰撞；或由于磁性笔和外侧之间的摩擦；或由于温度、湿度等环境的变化而产生静电，也不会使其耐久性、耐静电性、清晰度下降。即以高对比性清晰地显示记录，而且能完全、干净地消去记录。

Claims (8)

1.一种磁性显示用分散组合物，其特征在于，由10-30重量％的粒径为10-150μm的磁性粒子、0.01-0.5重量％的防带电剂、1-10重量％的有机增稠剂、0.1-10重量％的着色材料以及作为重量其余部分的有机类分散介质组成。
2.如权利要求1所述的磁性显示用分散组合物，其中的有机类分散介质为异构链烷烃或锭子油或乙二醇。
3.如权利要求1所述的磁性显示用分散组合物，其中的有机类分散介质为异构链烷烃和锭子油的混合物。
4.如权利要求1-3的任何一项所述的磁性显示用分散组合物，其中的防带电剂可选自1种或2种以上的下列各种物质，如聚丁烯硫酸化物、脂肪族烷基季铵盐、氨基乙醇-环氧氯丙烷缩聚物、烷基苯磺酸、烷基水杨酸金属盐、丁二酸磺酸盐、二烷基丁二酸磺酸盐、十二烷基苯磺酸金属盐。
5.如权利要求1-3的任何一项所述的磁性显示用分散组合物，其中的防带电剂是聚丁烯硫酸化物、脂肪族烷基季铵盐、氨基乙醇-环氧氯丙烷缩聚物、烷基苯磺酸的混合物。
6.如权利要求1-3的任何一项所述的磁性显示用分散组合物，其中的防带电剂是烷基水杨酸铬盐、丁二酸磺酸钙盐、聚合物的混合物。
7.如权利要求1-6的任何一项所述的磁性显示用分散组合物，其中的防带电剂溶解并分散于和分散介质相溶的溶剂中。
8.如权利要求1-7的任何一项所述的磁性显示用分散组合物，其中的增稠剂可选自1种或2种以上的下列各种物质，如含有羟基的脂肪酸双酰胺、氢化蓖麻油、N-酰胺酸烷基酰胺。
CN97114198A 1996-12-11 1997-12-11 磁性显示用分散组合物 Expired - Fee Related CN1097517C (zh)