CN1184703A - 一种多孔性含硅氧化铝载体小球及其制法 - Google Patents
一种多孔性含硅氧化铝载体小球及其制法 Download PDFInfo
- Publication number
- CN1184703A CN1184703A CN96120987A CN96120987A CN1184703A CN 1184703 A CN1184703 A CN 1184703A CN 96120987 A CN96120987 A CN 96120987A CN 96120987 A CN96120987 A CN 96120987A CN 1184703 A CN1184703 A CN 1184703A
- Authority
- CN
- China
- Prior art keywords
- pore volume
- time
- temperature
- described methods
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例 | 实施例1 | 实施例2 | 实施例3 | 比较例1 | |
孔容,ml/g | 0.71 | 0.67 | 0.75 | 0.58 | |
比表面,m2/g | 330 | 290 | 288 | 256 | |
颗粒直径,mm | 1.6 | 2.2 | 2.5 | 2.0 | |
孔分布% | 4.0nm | 4.9 | 5.0 | 3.8 | 4.9 |
4.0-10.0nm | 93.5 | 92.5 | 92.8 | 90.5 | |
10.0nm | 1.5 | 2.5 | 3.4 | 4.6 | |
平均孔径,nm | 9.6 | 9.9 | 9.8 | 9.1 | |
堆积密度,g/ml | 0.67 | 0.72 | 0.70 | 0.68 | |
机械强度,N/粒 | 98 | 103 | 82 | 95 | |
体积孔容,ml/ml | 0.467 | 0.492 | 0.480 | 0.394 | |
体积比表面,m2/ml | 221 | 209 | 202 | 174 | |
NH3化学吸附量,m·mol/g | 0.65 | 0.62 | 0.63 | 0.54 |
Claims (8)