CN116496706A - 一种3d曲屏用的保护膜及其制备方法 - Google Patents
一种3d曲屏用的保护膜及其制备方法 Download PDFInfo
- Publication number
- CN116496706A CN116496706A CN202310307164.8A CN202310307164A CN116496706A CN 116496706 A CN116496706 A CN 116496706A CN 202310307164 A CN202310307164 A CN 202310307164A CN 116496706 A CN116496706 A CN 116496706A
- Authority
- CN
- China
- Prior art keywords
- base film
- pet
- protective film
- curved screen
- steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种3D曲屏用的保护膜及其制备方法,通过在PET基膜表面涂覆十七氟癸基三乙氧基硅烷,进而在PET基膜表面形成一层氟层,在另一面涂抹胶水,再在胶水面覆盖PET离型膜制得,PET基膜表面含有大量氟和氨基,在环氧基与氨基反应过程产生羟基,使得在PET基膜表面涂覆十七氟癸基三乙氧基硅烷时,十七氟癸基三乙氧基硅烷能够水解并与表面的羟基接枝,使得氟层能够稳定的吸附在PET基膜表面,使得预处理基膜表面形成双层氟层,PET基膜中的抗静电剂能够降低保护膜的表面电阻,进而防止在使用过程中保护膜产生静电吸附,同时保护膜表面具有很好的疏水疏油效果,能够减少指纹或污渍的附着,进而保证了3D曲屏的使用效果。
Description
技术领域
本发明涉及显示屏保护膜制备技术领域,具体涉及一种3D曲屏用的保护膜及其制备方法。
背景技术
随着科技的发展,特别是智能手机的更新换代,显示屏幕不再局限于平面屏幕,曲面屏幕因其更好的观看舒适度、观感效果而越来越受到消费者的喜爱,广大电子厂商也相继推出具有曲面显示屏的电子产品,曲面显示屏保护膜也因此应运而生,PET树脂为聚对苯二甲酸乙二醇酯塑料,俗称涤纶树脂,它是对苯二甲酸与乙二醇的缩聚物,与PBT一起统称为热塑性聚酯,或饱和聚酯,PET树脂分子结构高度对称,具有一定的结晶取向能力,故而具有较高的成膜性,PET树脂具有很好的耐候性,另外PET树脂具有优良的耐磨耗摩擦性和尺寸稳定性及电绝缘性PET做成的瓶具有强度大、无毒、防渗透、质量轻、生产效率高等因而受到了广泛的应用。
发明内容
本发明的目的在于提供一种3D曲屏用的保护膜及其制备方法,解决了现阶段保护膜易出现灰尘吸附,且长时间使用后会在表面残留指纹印记的问题。
本发明的目的可以通过以下技术方案实现:
一种3D曲屏用的保护膜的制备方法,具体包括如下步骤:
步骤S1:将PET基膜浸泡在去离子水中,取出保持表面湿润,向PET基膜一面涂抹十七氟癸基三乙氧基硅烷,在温度为20-30℃的条件下,保温处理1-1.5h,制得预处理基膜;
步骤S2:向预处理基膜为涂抹十七氟癸基三乙氧基硅烷的一面涂抹胶水,再在胶水面覆盖PET离型膜,制得3D曲屏用的保护膜。
进一步,所述的PET基膜由如下步骤制成:
步骤A1:将3-缩水甘油醚氧丙基四基二甲氧基硅烷和三氟丙基甲基二氯硅烷加入去离子水中,在转速为200-300r/min,温度为25-30℃的条件下,搅拌20-30min后,加入四氢呋喃和浓硫酸,升温至55-65℃,保温5-10min,加入1,1,3,3-四甲基二硅氧烷,进行反应3-5h,制得中间体1;
步骤A2:将中间体1和丙烯醇的苯溶液混合,在转速为200-300r/min,温度为50-60℃的条件下,搅拌并加入氯铂酸,加入完毕后升温至60-65℃,进行反应3-4h,制得中间体2,将对苯二甲酸、中间体2、乙二醇、乙二醇锑、磷酸混合均匀,通入氮气保护,在转速为60-120r/min,温度为230-250℃,压强为0.3-0.5MPa的条件下,进行反应2-3h后,再在温度为280-285℃,压强为50-60Pa的条件下,保温30-40min,制得预处理PET;
步骤A3:将预处理PET溶于六氟异丙醇中,加入抗静电剂,在转速为200-300r/min,温度为30-40℃,pH值为10-11的条件下,进行反应6-8h后,蒸馏去除六氟异丙醇,将底物在温度为260-270℃的条件下,挤出压片,再拉伸成膜制得PET基膜。
进一步,步骤A1所述的3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷、去离子水和1,1,3,3-四甲基二硅氧烷的用量比为8mmol:15mmol:2mL:10mmol,浓硫酸的用量为3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷和1,1,3,3-四甲基二硅氧烷质量和的10%。
进一步,步骤A2所述的中间体1和丙烯醇的摩尔比为1:2,氯铂酸在中间体1和氯乙烯的苯溶液中的浓度为20-30ppm,对苯二甲酸、中间体2、乙二醇、乙二醇锑和磷酸的质量比为10:9:6:0.015:0.3。
进一步,步骤A3所述的预处理PET上的环氧基和抗静电剂上的氨基摩尔比为2:1。
进一步,所述的抗静电剂由如下步骤制成:
步骤B1:将二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯混合,在转速为150-200r/min,温度为100-110℃的条件下,进行反应4-6h,制得中间体3,将中间体3、乙腈和对苯二酚混合均匀,在转速为200-300r/min,温度为45-50℃的条件下,搅拌并滴加溴代十二烷,进行反应10-15h,制得中间体4;
步骤B2:将中间体4、对氨基苯乙烯和乙醇混合均匀,在转速为200-300r/min的条件下,搅拌并加入偶氮二异丁腈,升温至75-80℃,进行反应5-7h,蒸馏去除乙醇,将底物溶于甲苯中,加入浓盐酸和双氰胺,在转速为200-300r/min,温度为90-95℃的条件下,进行反应3-4h,制得抗静电剂。
进一步,步骤B1所述的二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯的用量比为0.5mol:1.5mol:4mmol:30mmol,中间体3、乙腈、对苯二酚和溴代十二烷的用量比为55mmol:30mmol:4mL:50mmol。
进一步,步骤B2所述的中间体4、对氨基苯乙烯、乙醇、偶氮二异丁腈、浓盐酸和双氰胺的用量比为100mmol:50mmol:120mL:0.4g:110mmol:140mmol。
本发明的有益效果:本发明制备的一种3D曲屏用的保护膜,通过在PET基膜表面涂覆十七氟癸基三乙氧基硅烷,进而在PET基膜表面形成一层氟层,在另一面涂抹胶水,再在胶水面覆盖PET离型膜制得,PET基膜以3-缩水甘油醚氧丙基四基二甲氧基硅烷和三氟丙基甲基二氯硅烷为原料,先水解再与1,1,3,3-四甲基二硅氧烷聚合,形成端氢键聚硅烷,制得中间体1,将中间体1与丙烯醇在氯铂酸的作用下,使得丙烯醇上的双键与中间体上的Si-H键反应形成Si-C键,制得中间体2,将对苯二甲酸、中间体2和乙二醇先进行酯化再缩聚,制得预处理PET,将预处理PET和抗静电剂反应,使得预处理PET上的环氧基与抗静电剂上的氨基反应,制得PET基膜,PET基膜表面含有大量氟和氨基,在环氧基与氨基反应过程产生羟基,使得在PET基膜表面涂覆十七氟癸基三乙氧基硅烷时,十七氟癸基三乙氧基硅烷能够水解并与表面的羟基接枝,使得氟层能够稳定的吸附在PET基膜表面,进而在预处理基膜表面形成双层氟层,抗静电剂以二甲氨基乙醇和甲基丙烯酸甲酯为原料,进行酯交换反应,制得中间体3,将中间体3与溴代十二烷反应,使得中间体3上的二甲氨基与溴代十二烷上的溴原子位点反应,形成季铵盐,制得中间体4,将中间体4和对氨基苯乙烯在偶氮二异丁腈的作用下聚合,再与双氰胺反应,使得组合物分子侧链上的氨基与双氰胺上的氰基反应,制得抗静电剂,该抗静电剂能够降低保护膜的表面电阻,进而防止在使用过程中保护膜产生静电吸附,同时保护膜表面具有很好的疏水疏油效果,能够减少保护膜表面指纹或污渍的附着,进而保证了3D曲屏的使用效果。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
实施例
一种3D曲屏用的保护膜的制备方法,具体包括如下步骤:
步骤S1:将PET基膜浸泡在去离子水中,取出保持表面湿润,向PET基膜一面涂抹十七氟癸基三乙氧基硅烷,在温度为20℃的条件下,保温处理1h,制得预处理基膜;
步骤S2:向预处理基膜为涂抹十七氟癸基三乙氧基硅烷的一面涂抹KL-9302高透硅胶胶水,再在胶水面覆盖PET离型膜,制得3D曲屏用的保护膜。
所述的PET基膜由如下步骤制成:
步骤A1:将3-缩水甘油醚氧丙基四基二甲氧基硅烷和三氟丙基甲基二氯硅烷加入去离子水中,在转速为200r/min,温度为25℃的条件下,搅拌20min后,加入四氢呋喃和浓硫酸,升温至55℃,保温5min,加入1,1,3,3-四甲基二硅氧烷,进行反应3h,制得中间体1;
步骤A2:将中间体1和丙烯醇的苯溶液混合,在转速为200r/min,温度为50℃的条件下,搅拌并加入氯铂酸,加入完毕后升温至60℃,进行反应3h,制得中间体2,将对苯二甲酸、中间体2、乙二醇、乙二醇锑、磷酸混合均匀,通入氮气保护,在转速为60r/min,温度为230℃,压强为0.3MPa的条件下,进行反应2h后,再在温度为280℃,压强为50Pa的条件下,保温30min,制得预处理PET;
步骤A3:将预处理PET溶于六氟异丙醇中,加入抗静电剂,在转速为200r/min,温度为30℃,pH值为10的条件下,进行反应6h后,蒸馏去除六氟异丙醇,将底物在温度为260℃的条件下,挤出压片,再拉伸成膜制得PET基膜。
步骤A1所述的3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷、去离子水和1,1,3,3-四甲基二硅氧烷的用量比为8mmol:15mmol:2mL:10mmol,浓硫酸的用量为3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷和1,1,3,3-四甲基二硅氧烷质量和的10%。
步骤A2所述的中间体1和丙烯醇的摩尔比为1:2,氯铂酸在中间体1和氯乙烯的苯溶液中的浓度为20ppm,对苯二甲酸、中间体2、乙二醇、乙二醇锑和磷酸的质量比为10:9:6:0.015:0.3。
步骤A3所述的预处理PET上的环氧基和抗静电剂上的氨基摩尔比为2:1。
所述的抗静电剂由如下步骤制成:
步骤B1:将二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯混合,在转速为150r/min,温度为100℃的条件下,进行反应4h,制得中间体3,将中间体3、乙腈和对苯二酚混合均匀,在转速为200r/min,温度为45℃的条件下,搅拌并滴加溴代十二烷,进行反应10h,制得中间体4;
步骤B2:将中间体4、对氨基苯乙烯和乙醇混合均匀,在转速为200r/min的条件下,搅拌并加入偶氮二异丁腈,升温至75℃,进行反应5h,蒸馏去除乙醇,将底物溶于甲苯中,加入浓盐酸和双氰胺,在转速为200r/min,温度为90℃的条件下,进行反应3h,制得抗静电剂。
步骤B1所述的二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯的用量比为0.5mol:1.5mol:4mmol:30mmol,中间体3、乙腈、对苯二酚和溴代十二烷的用量比为55mmol:30mmol:4mL:50mmol。
步骤B2所述的中间体4、对氨基苯乙烯、乙醇、偶氮二异丁腈、浓盐酸和双氰胺的用量比为100mmol:50mmol:120mL:0.4g:110mmol:140mmol。
实施例
一种3D曲屏用的保护膜的制备方法,具体包括如下步骤:
步骤S1:将PET基膜浸泡在去离子水中,取出保持表面湿润,向PET基膜一面涂抹十七氟癸基三乙氧基硅烷,在温度为25℃的条件下,保温处理1.3h,制得预处理基膜;
步骤S2:向预处理基膜为涂抹十七氟癸基三乙氧基硅烷的一面涂抹KL-9302高透硅胶胶水,再在胶水面覆盖PET离型膜,制得3D曲屏用的保护膜。
所述的PET基膜由如下步骤制成:
步骤A1:将3-缩水甘油醚氧丙基四基二甲氧基硅烷和三氟丙基甲基二氯硅烷加入去离子水中,在转速为200r/min,温度为30℃的条件下,搅拌25min后,加入四氢呋喃和浓硫酸,升温至60℃,保温8min,加入1,1,3,3-四甲基二硅氧烷,进行反应4h,制得中间体1;
步骤A2:将中间体1和丙烯醇的苯溶液混合,在转速为200r/min,温度为55℃的条件下,搅拌并加入氯铂酸,加入完毕后升温至65℃,进行反应3.5h,制得中间体2,将对苯二甲酸、中间体2、乙二醇、乙二醇锑、磷酸混合均匀,通入氮气保护,在转速为60r/min,温度为240℃,压强为0.4MPa的条件下,进行反应2.5h后,再在温度为285℃,压强为55Pa的条件下,保温35min,制得预处理PET;
步骤A3:将预处理PET溶于六氟异丙醇中,加入抗静电剂,在转速为200r/min,温度为35℃,pH值为10的条件下,进行反应7h后,蒸馏去除六氟异丙醇,将底物在温度为265℃的条件下,挤出压片,再拉伸成膜制得PET基膜。
步骤A1所述的3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷、去离子水和1,1,3,3-四甲基二硅氧烷的用量比为8mmol:15mmol:2mL:10mmol,浓硫酸的用量为3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷和1,1,3,3-四甲基二硅氧烷质量和的10%。
步骤A2所述的中间体1和丙烯醇的摩尔比为1:2,氯铂酸在中间体1和氯乙烯的苯溶液中的浓度为25ppm,对苯二甲酸、中间体2、乙二醇、乙二醇锑和磷酸的质量比为10:9:6:0.015:0.3。
步骤A3所述的预处理PET上的环氧基和抗静电剂上的氨基摩尔比为2:1。
所述的抗静电剂由如下步骤制成:
步骤B1:将二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯混合,在转速为150r/min,温度为105℃的条件下,进行反应5h,制得中间体3,将中间体3、乙腈和对苯二酚混合均匀,在转速为200r/min,温度为50℃的条件下,搅拌并滴加溴代十二烷,进行反应15h,制得中间体4;
步骤B2:将中间体4、对氨基苯乙烯和乙醇混合均匀,在转速为200r/min的条件下,搅拌并加入偶氮二异丁腈,升温至78℃,进行反应6h,蒸馏去除乙醇,将底物溶于甲苯中,加入浓盐酸和双氰胺,在转速为200r/min,温度为95℃的条件下,进行反应3.5h,制得抗静电剂。
步骤B1所述的二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯的用量比为0.5mol:1.5mol:4mmol:30mmol,中间体3、乙腈、对苯二酚和溴代十二烷的用量比为55mmol:30mmol:4mL:50mmol。
步骤B2所述的中间体4、对氨基苯乙烯、乙醇、偶氮二异丁腈、浓盐酸和双氰胺的用量比为100mmol:50mmol:120mL:0.4g:110mmol:140mmol。
实施例
一种3D曲屏用的保护膜的制备方法,具体包括如下步骤:
步骤S1:将PET基膜浸泡在去离子水中,取出保持表面湿润,向PET基膜一面涂抹十七氟癸基三乙氧基硅烷,在温度为30℃的条件下,保温处理1.5h,制得预处理基膜;
步骤S2:向预处理基膜为涂抹十七氟癸基三乙氧基硅烷的一面涂抹KL-9302高透硅胶胶水,再在胶水面覆盖PET离型膜,制得3D曲屏用的保护膜。
所述的PET基膜由如下步骤制成:
步骤A1:将3-缩水甘油醚氧丙基四基二甲氧基硅烷和三氟丙基甲基二氯硅烷加入去离子水中,在转速为300r/min,温度为30℃的条件下,搅拌30min后,加入四氢呋喃和浓硫酸,升温至65℃,保温10min,加入1,1,3,3-四甲基二硅氧烷,进行反应5h,制得中间体1;
步骤A2:将中间体1和丙烯醇的苯溶液混合,在转速为300r/min,温度为60℃的条件下,搅拌并加入氯铂酸,加入完毕后升温至65℃,进行反应4h,制得中间体2,将对苯二甲酸、中间体2、乙二醇、乙二醇锑、磷酸混合均匀,通入氮气保护,在转速为120r/min,温度为250℃,压强为0.5MPa的条件下,进行反应3h后,再在温度为285℃,压强为60Pa的条件下,保温40min,制得预处理PET;
步骤A3:将预处理PET溶于六氟异丙醇中,加入抗静电剂,在转速为300r/min,温度为40℃,pH值为11的条件下,进行反应8h后,蒸馏去除六氟异丙醇,将底物在温度为270℃的条件下,挤出压片,再拉伸成膜制得PET基膜。
步骤A1所述的3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷、去离子水和1,1,3,3-四甲基二硅氧烷的用量比为8mmol:15mmol:2mL:10mmol,浓硫酸的用量为3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷和1,1,3,3-四甲基二硅氧烷质量和的10%。
步骤A2所述的中间体1和丙烯醇的摩尔比为1:2,氯铂酸在中间体1和氯乙烯的苯溶液中的浓度为30ppm,对苯二甲酸、中间体2、乙二醇、乙二醇锑和磷酸的质量比为10:9:6:0.015:0.3。
步骤A3所述的预处理PET上的环氧基和抗静电剂上的氨基摩尔比为2:1。
所述的抗静电剂由如下步骤制成:
步骤B1:将二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯混合,在转速为200r/min,温度为110℃的条件下,进行反应6h,制得中间体3,将中间体3、乙腈和对苯二酚混合均匀,在转速为300r/min,温度为50℃的条件下,搅拌并滴加溴代十二烷,进行反应15h,制得中间体4;
步骤B2:将中间体4、对氨基苯乙烯和乙醇混合均匀,在转速为300r/min的条件下,搅拌并加入偶氮二异丁腈,升温至80℃,进行反应7h,蒸馏去除乙醇,将底物溶于甲苯中,加入浓盐酸和双氰胺,在转速为300r/min,温度为95℃的条件下,进行反应4h,制得抗静电剂。
步骤B1所述的二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯的用量比为0.5mol:1.5mol:4mmol:30mmol,中间体3、乙腈、对苯二酚和溴代十二烷的用量比为55mmol:30mmol:4mL:50mmol。
步骤B2所述的中间体4、对氨基苯乙烯、乙醇、偶氮二异丁腈、浓盐酸和双氰胺的用量比为100mmol:50mmol:120mL:0.4g:110mmol:140mmol。
对比例1
本对比例与实施例1相比未加入抗静电剂,其余步骤相同。
对比例2
本对比例与实施例1相比直接将对苯二甲酸、乙二醇、乙二醇锑、磷酸混合均匀,通入氮气保护,在转速为60r/min,温度为230℃,压强为0.3MPa的条件下,进行反应2h后,再在温度为280℃,压强为50Pa的条件下,保温30min,制得预处理PET,将预处理PET,在温度为260℃的条件下,挤出压片,再拉伸成膜制得PET基膜,其余步骤相同。
将实施例1-3和对比例1-2制得的保护膜依照GB/T30693-2014的标准检测表面水接触角,并用同样方法检测油接触角,依照GB/T1410-2006的标准检测保护膜的表面电阻,检测结果如下表所示。
由上表可知实施例1-3制得的保护膜的水接触角为132.5-133.2°,油接触角为163.1-163.5°,表面电阻为106Ω,表明本发明具有很好的疏水疏油效果,且抗静电效果好,能够很好的避免保护表面吸附灰尘以及指纹残留。
以上内容仅仅是对本发明的构思所作的举例和说明,所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,只要不偏离发明的构思或者超越本权利要求书所定义的范围,均应属于本发明的保护范围。
Claims (9)
1.一种3D曲屏用的保护膜的制备方法,其特征在于:具体包括如下步骤:
步骤S1:将PET基膜浸泡在去离子水中,取出保持表面湿润,向PET基膜一面涂抹十七氟癸基三乙氧基硅烷,保温处理,制得预处理基膜;
步骤S2:向预处理基膜为涂抹十七氟癸基三乙氧基硅烷的一面涂抹胶水,再在胶水面覆盖PET离型膜,制得3D曲屏用的保护膜。
2.根据权利要求1所述的一种3D曲屏用的保护膜的制备方法,其特征在于:所述的PET基膜由如下步骤制成:
步骤A1:将3-缩水甘油醚氧丙基四基二甲氧基硅烷和三氟丙基甲基二氯硅烷加入去离子水中,搅拌处理后,加入四氢呋喃和浓硫酸,升温保温,加入1,1,3,3-四甲基二硅氧烷,进行反应,制得中间体1;
步骤A2:将中间体1和丙烯醇的苯溶液混合搅拌并加入氯铂酸,加入完毕后升温反应,制得中间体2,将对苯二甲酸、中间体2、乙二醇、乙二醇锑、磷酸混合反应,制得预处理PET;
步骤A3:将预处理PET溶于六氟异丙醇中,加入抗静电剂,进行反应后,蒸馏去除六氟异丙醇,将底物挤出压片,再拉伸成膜制得PET基膜。
3.根据权利要求2所述的一种3D曲屏用的保护膜的制备方法,其特征在于:步骤A1所述的3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷、去离子水和1,1,3,3-四甲基二硅氧烷的用量比为8mmol:15mmol:2mL:10mmol,浓硫酸的用量为3-缩水甘油醚氧丙基四基二甲氧基硅烷、三氟丙基甲基二氯硅烷和1,1,3,3-四甲基二硅氧烷质量和的10%。
4.根据权利要求2所述的一种3D曲屏用的保护膜的制备方法,其特征在于:步骤A2所述的中间体1和丙烯醇的摩尔比为1:2,氯铂酸在中间体1和氯乙烯的苯溶液中的浓度为20-30ppm,对苯二甲酸、中间体2、乙二醇、乙二醇锑和磷酸的质量比为10:9:6:0.015:0.3。
5.根据权利要求2所述的一种3D曲屏用的保护膜的制备方法,其特征在于:步骤A3所述的预处理PET上的环氧基和抗静电剂上的氨基摩尔比为2:1。
6.根据权利要求2所述的一种3D曲屏用的保护膜的制备方法,其特征在于:所述的抗静电剂由如下步骤制成:
步骤B1:将二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯混合,进行反应,制得中间体3,将中间体3、乙腈和对苯二酚混合搅拌并滴加溴代十二烷,进行反应,制得中间体4;
步骤B2:将中间体4、对氨基苯乙烯和乙醇混合搅拌并加入偶氮二异丁腈,升温反应后,蒸馏去除乙醇,将底物溶于甲苯中,加入浓盐酸和双氰胺,进行反应,制得抗静电剂。
7.根据权利要求6所述的一种3D曲屏用的保护膜的制备方法,其特征在于:步骤B1所述的二甲氨基乙醇、甲基丙烯酸甲酯、对苯二酚和钛酸四丁酯的用量比为0.5mol:1.5mol:4mmol:30mmol,中间体3、乙腈、对苯二酚和溴代十二烷的用量比为55mmol:30mmol:4mL:50mmol。
8.根据权利要求6所述的一种3D曲屏用的保护膜的制备方法,其特征在于:步骤B2所述的中间体4、对氨基苯乙烯、乙醇、偶氮二异丁腈、浓盐酸和双氰胺的用量比为100mmol:50mmol:120mL:0.4g:110mmol:140mmol。
9.一种3D曲屏用的保护膜,其特征在于:根据权利要求1-8任一所述的制备方法制备而成。