CN116406314A - 固态胺co2吸附剂及其制备方法 - Google Patents
固态胺co2吸附剂及其制备方法 Download PDFInfo
- Publication number
- CN116406314A CN116406314A CN202180069387.4A CN202180069387A CN116406314A CN 116406314 A CN116406314 A CN 116406314A CN 202180069387 A CN202180069387 A CN 202180069387A CN 116406314 A CN116406314 A CN 116406314A
- Authority
- CN
- China
- Prior art keywords
- solution
- boehmite
- pseudo
- sodium aluminate
- adsorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请涉及一种固态胺CO2吸附剂及其制备方法,所述制备方法包括:提供拟薄水铝石;对所述拟薄水铝石进行扩孔;将扩孔的拟薄水铝石进行焙烧,得到纳米氧化铝粉末;用有机胺溶液浸渍所述纳米氧化铝粉末,并进行干燥,得到所述固态胺CO2吸附剂。
Description
本申请涉及CO
2气体吸附净化技术领域,特别是涉及固态胺CO
2吸附剂及其制备方法。
为应对全球气候变暖导致的能源和环境危机,实现CO
2等温室气体的净零排放是控制全球升温低于1.5℃的重要举措。开展CO
2捕集和封存(CCS)技术能够从工业排放点源避免CO
2排放、减少大气中已有的CO
2,是实现“碳中和”目标的重要组成部分;特别对于水泥、钢铁和化工等行业的深度脱碳、低碳氢能的规模化生产、低碳电力供给、实现负排放等方面具有重要意义。CCS技术的核心在于CO
2捕集材料的开发,高效、廉价的CO
2捕集材料是降低CCS技术应用成本的关键。
固态胺材料因具有CO
2选择性高、再生能耗低、应用场景广等优点,成为目前最具发展前景的CO
2捕集技术。为了达到减排的目的,捕获得到的CO
2必须富集成高纯CO
2用于封存或利用,因此固态胺吸附剂需在实际CO
2气氛下解吸再生。然而目前固态胺材料在实际再生条件下大都会产生严重的尿素链化合物,导致严重的化学性失活,使得吸附能力急剧下降。因此,制备高CO
2吸附容量、抗尿素链的高循环稳定性且价格低廉的固态胺材料仍然是该领域内亟待解决的难题。
发明内容
基于此,有必要提供一种CO
2吸附容量高、抗尿素链性好且循环稳定性高的固态胺CO
2吸附剂。
一种固态胺CO
2吸附剂的制备方法,包括:
提供拟薄水铝石;
对所述拟薄水铝石进行扩孔;
将扩孔的拟薄水铝石进行焙烧,得到氧化铝粉末;
用有机胺溶液浸渍所述氧化铝粉末,并进行干燥,得到所述固态胺CO
2吸附剂。
在一个实施例中,所述拟薄水铝石采用在铝酸钠溶液中滴加H
2O
2溶液、或在铝酸钠溶液中通入CO
2、或使铝酸钠溶液与硫酸铝溶液混合制备而成。
在一个实施例中,在铝酸钠溶液中滴加H
2O
2溶液制备所述拟薄水铝石的步骤包括:
在室温下,将质量分数为5~20%的H
2O
2溶液滴加到浓度为20~200g/L的铝酸钠溶液中,滴加时间为10~60min,滴加完成后获得反应液;
将所述反应液静置30min,得到含有沉淀物的产液;以及
过滤出所述产液中的沉淀物,并对所述沉淀物进行洗涤,得到所述拟薄水铝石;
其中,所述铝酸钠溶液中的铝酸钠与所述H
2O
2溶液中的H
2O
2的摩尔比为1:1至1:5。
在一个实施例中,在铝酸钠溶液中通入CO
2制备所述拟薄水铝石的步骤包括:
在室温下,将含有10~50vol.%的CO
2的气体混合物通入浓度为10g/L~100g/L的铝酸钠溶液中,得到反应液;
持续通入所述气体混合物,直至所述反应液的pH下降到9.5-9.8,得到含有沉淀物的产液;以及
过滤出所述产液中的沉淀物,并对所述沉淀物进行洗涤,得到所述拟薄水铝石。
在一个实施例中,使铝酸钠溶液与硫酸铝混合制备所述拟薄水铝石的步骤包括:
将浓度为20~200g/L的铝酸钠溶液和浓度为20~200g/L的硫酸铝溶液按质量比1:1进行混合,得到反应液;
调节所述反应液的pH至8.0~10.0,并在25~80℃的温度下搅拌2-5小时,得到含有沉淀物的产液;
过滤出所述产液中的沉淀物,并对所述沉淀物进行洗涤,得到所述拟薄水铝石。
在一个实施例中,对所述拟薄水铝石进行扩孔的步骤包括:
将过滤出的洗涤后的所述沉淀物与有机醇按1:5至1:30的质量比混合,形成悬浮液;
将所述悬浮液的温度升高到水与有机醇的共沸点蒸发10~60min,再升温到有机醇的沸点回流30~90min,得到所述扩孔的拟薄水铝石。
在一个实施例中,所述有机醇包括乙醇、正丙醇、异丙醇、正丁醇、异丁醇和仲丁醇中的一种或者多种。
在一个实施例中,将扩孔的拟薄水铝石进行焙烧,得到氧化铝粉末的步骤包括:
在400~600℃的温度下焙烧所述扩孔的拟薄水铝石2~8小时,得到纳米氧化铝粉末。
在一个实施例中,在焙烧步骤之后,还包括对所述氧化铝粉末进行研磨以得到纳米氧化铝粉末的步骤。
在一个实施例中,所述有机胺溶液包括有机胺和溶剂,所述有机胺为聚乙烯亚胺、二乙烯三胺、四乙烯五胺和五乙撑六胺中的一种或多种,所述溶剂为甲醇和乙醇中的一种或多种。
在一个实施例中,所述有机胺溶液中有机胺与溶剂的质量比为1:10至1:100。
在一个实施例中,用有机胺溶液浸渍所述氧化铝粉末,干燥后得到所述固态胺CO
2吸附剂的步骤包括:
将所述氧化铝粉末分散在有机胺溶液中,得到分散液;以及
将所述分散液中的溶剂去除,从而获得所述固态胺CO
2吸附剂。
在一个实施例中,将所述分散液中的溶剂去除的步骤包括在室温下将所述溶剂蒸发掉,并且将剩余物在真空干燥箱中于60℃至80℃下干燥3h至6h。
本申请还提供一种固态胺CO
2吸附剂,其由上述制备方法制备而成。
本申请所提供的硅基固态胺CO
2吸附剂及其制备方法具有以下优点:
(1)制备大孔氧化铝基体的原料来源广泛,制备工艺简单、反应条件温和、操作容易控制、无需复杂设备,适合工业化生产;
(2)基体制备过程不需要添加任何表面活性剂、模板剂、扩孔剂,共沸蒸馏过程使用的有机溶剂是常见的有机醇,价格便宜,可回收重复使用,对环境污染小,具有经济优势;
(3)以大孔氧化铝基体制备得到的固态胺CO
2吸附剂能够负载高含量的有机胺,饱和负载量可达70%以上,CO
2吸附容量可达5mmol/g以上;
(4)制备得到的固态胺CO
2吸附剂具备优异的循环稳定性,在实际CO
2再生气氛下循环50次,其CO
2吸附容量依然维持在4.8mmol/g以上,衰减不到5%。
由于本申请的高性能CO
2吸附剂具备极高的CO
2吸附容量和优异的实际条件再生循环稳定性,且制备过程简单、绿色、价格低廉,可广泛应用于CO
2捕集和沼气纯化领域。
为了更清楚地说明本申请具体实施方式或现有技术中的技术方案,下面将对具体实施方式或现有技术描述中所需要使用的附图作简单地介绍,显而易见地,下面描述中的附图是本申请的一些实施方式,对于本领域普通技术人员来讲,在不付出创造性劳动的前提下,还可以根据这些附图获得其他的附图。
图1是本申请实施例1中合成的大孔纳米氧化铝的扫描电镜图;
图2是本申请实施例1中合成的大孔纳米氧化铝的N
2吸附曲线图;
图3是本申请实施例1中固态胺CO
2吸附剂的长期循环稳定性图。
为了使本申请的目的、技术方案及优点更加清楚明白,以下通过实施例,并结合附图,对本申请进行进一步详细说明。应当理解,此处所描述的具体实施例仅用以解释本申请,并不用于限定本申请。
本申请提供一种固态胺CO
2吸附剂的制备方法,所述制备方法包括:
S1,提供拟薄水铝石;
S2,对所述拟薄水铝石进行扩孔;
S3,将扩孔的拟薄水铝石进行焙烧,得到氧化铝粉末;
S4,用有机胺溶液浸渍所述氧化铝粉末,并进行干燥,得到所述固态胺CO
2吸附剂。
在本申请中,对拟薄水铝石进行扩孔和焙烧后可获得孔体积较大的氧化铝粉末,孔体积较大的氧化铝粉末能够负载高含量的有机胺,从而提高了固态胺CO
2吸附剂的CO
2吸附容量。另外,现有的固态胺材料采用CO
2吹扫气进行再生时,CO
2与活性胺中的伯胺官能团在高温下(大于130℃)容易转化为尿素链化合物,使得CO
2不能从吸附剂中脱附,导致固态胺吸附剂失活。本申请制备的纳米氧化铝由于具有丰富的路易斯酸性位点,能与活性胺发生交联反应,将活性胺中的伯胺官能团转化为肿胺官能团,从而避免尿素链化合物的形成。本申请的固态胺CO
2吸附剂具有抗尿素链性能和高循环稳定性,其在多次CO
2吸附-再生循环后仍能够维持高的CO
2吸附容量。
在步骤S1中,所述拟薄水铝石可以通过多种方法进行制备。
在一个实施例中,通过在铝酸钠溶液中滴加H
2O
2溶液来制备拟薄水铝石。
铝酸钠溶液和H
2O
2溶液可以在室温下进行反应并生成拟薄水铝石沉淀。在该实施例中,可以通过控制铝酸钠溶液的浓度、H
2O
2溶液的浓度、铝酸钠溶液与H
2O
2溶液的比例、H
2O
2溶液的滴加速度和反应时间等反应条件,来控制拟薄水铝石和后续制备的氧化铝粉末的形貌、比表面积和孔体积等性质。
为了得到高比表面积和大孔体积的拟薄水铝石和氧化铝粉末,铝酸钠溶液的浓度可以为20g/L至200g/L,例如50g/L至190g/L,50g/L至180g/L,70g/L至170g/L,例如80g/L,90g/L,100g/L,110g/L,120g/L,130g/L,140g/L,150g/L,160g/L。H
2O
2溶液的浓度可以为5wt%至20wt%,例如6wt%至18wt%,7wt%至16wt%,8wt%至14wt%,例如9wt%,10wt%,11wt%,12wt%和13wt%。在滴加完成的反应液中,铝酸钠溶液和H
2O
2溶液中的铝酸钠和H
2O
2的摩尔比可以为1:1至1:5,例如1:2,1:3,和1:4。滴加时间可以为10min至60min。滴加完成后,可将反应液静置10min至60min,从而形成含有拟薄水铝石沉淀的产液。对所述产液进行过滤和洗涤,得到拟薄水铝石滤饼。铝酸钠溶液和H
2O
2溶液都可以为水溶液。
在另一个实施例中,通过在铝酸钠溶液中通入CO
2来制备拟薄水铝石。
可以在室温下将含有CO
2的气体通入铝酸钠溶液中进行反应并生成拟薄水铝石沉淀。在该实施例中,可以通过控制铝酸钠溶液的浓度、气体中CO
2的浓度、含有CO
2的气体的流量、反应液的pH等反应条件,来控制拟薄水铝石和后续制备的氧化铝粉末的形貌、比表面积和孔体积等性质。
为了得到高比表面积和大孔体积的拟薄水铝石和氧化铝粉末,铝酸钠溶液的浓度可以为10g/L~100g/L,例如10g/L至90g/L,10g/L至80g/L,15g/L至65g/L,例如10g/L,20g/L,25g/L,30g/L,50g/L,70g/L,90g/L,100g/L。含有CO
2的气体中的CO
2的浓度可以为10 vol.%至50vol.%,例如10vol.%至40vol.%,10vol.%至30vol.%,例如15vol.%,20vol.%,和25vol.%。含有CO
2的气体的流量可以为每升铝酸钠溶液通入600mL/min至1000mL/min的CO
2,例如700mL/min,800mL/min,和900mL/min。最终产液的pH可以为9.5至9.8,例如9.5,9.6,9.7,和9.8。反应完成后,对产液进行过滤和洗涤,得到拟薄水铝石滤饼。铝酸钠溶液可以为水溶液。含有CO
2的气体中不含其它能够与铝酸钠溶液发生反应的气体。
在又一个实施例中,通过混合铝酸钠溶液与硫酸铝溶液来制备拟薄水铝石。
铝酸钠溶液和硫酸铝溶液发生反应并生成拟薄水铝石沉淀。在该实施例中,可以通过控制铝酸钠溶液的浓度、硫酸铝溶液的浓度、铝酸钠溶液与硫酸铝溶液的比例、反应温度、pH和反应时间等反应条件,来控制拟薄水铝石和后续制备的氧化铝粉末的形貌、比表面积和孔体积等性质。
为了得到高比表面积和大孔体积的拟薄水铝石和氧化铝粉末,铝酸钠溶液的浓度可以为20g/L至200g/L,例如20g/L至150g/L,20g/L至120g/L,20g/L至80g/L,例如20g/L,30g/L,40g/L,50g/L,60g/L,70g/L,和80g/L。硫酸铝溶液的浓度可以为20g/L至200g/L,例如20g/L至150g/L,20g/L至100g/L,20g/L至50g/L,例如20g/L,25g/L,30g/L,35g/L,40g/L,45g/L,和50g/L。铝酸钠溶液与硫酸铝溶液的质量比可以为1:3至3:1,例如1:2至2:1,例如1:2,1:1,和2:1。铝酸钠溶液与硫酸铝溶液可以在搅拌的条件下进行反应。铝酸钠溶液与硫酸铝溶液的反应温度可以为25~90℃,例如60℃,70℃,和80℃。铝酸钠溶液与硫酸铝溶液的混合溶液的pH可以调节至8.0~10.0,例如调节至8.0,8.5,9.0,9.5,和10.0,再升温进行反应。铝酸钠溶液与硫酸铝溶液的反应时间可以为2-5小时。铝酸钠溶液与硫酸铝溶液可以都是水溶液。反应完成后,对产液进行过滤和洗涤,得到拟薄水铝石滤饼。
应当理解,其他方法也可以用于制备所述拟薄水铝石。
在步骤S2中,对所述拟薄水铝石进行扩孔的方法可以包括使所述拟薄水铝石滤饼与有机醇共沸扩孔。
在一个实施例中,对所述拟薄水铝石进行扩孔的方法具体包括:
S21,将拟薄水铝石滤饼与有机醇混合均匀,形成悬浊液;
S22,将悬浊液的温度升高到水与有机醇的共沸点蒸发10~60min,再升高到有机醇的沸点回流30~90min,得到扩孔的拟薄水铝石。
在步骤S21中,有机醇包括但不限于乙醇、正丙醇、异丙醇、正丁醇、异丁醇和仲丁醇中的一种或多种。拟薄水铝石滤饼与有机醇的质量比可以为1:5至1:30,例如1:5至1:20,1:5至1:15。
在步骤S3中,可以通过控制焙烧条件来控制氧化铝粉末的形貌、比表面积和孔体积等性 质。
为了得到高比表面积和大孔体积的氧化铝粉末,焙烧温度可以为400℃至600℃。焙烧时间可以为4小时至8小时。升温速率可以为2~30℃/min。
进一步地,在步骤S3之后,可以包括研磨氧化铝粉末的步骤,以进一步减小氧化铝粉末的粒径。在一实施例中,可以将氧化铝粉末研磨至200目以下。
在步骤S4中,有机胺溶液包括有机胺和溶剂。有机胺包括但不限于聚乙烯亚胺、二乙烯三胺、四乙烯五胺和五乙撑六胺中的一种或多种。所述溶剂可以溶解有机胺,并且易挥发。所述溶剂包括但不限于甲醇、乙醇、丙酮和醋酸丁酯中的一种或多种。
可以通过控制有机胺溶液的浓度来控制氧化铝粉末上的有机胺负载量和有机胺在氧化铝粉末上的均匀性。在一实施例中,为了得到有机胺负载量高且负载均匀的固态胺CO
2吸附剂,有机胺溶液中有机胺与溶剂的质量比可以为1:10至1:100,例如1:10至1:80,1:10至1:60,1:10至1:40。
在一实施例中,步骤S4可以包括:
S41,将所述氧化铝粉末分散在有机胺溶液中,得到分散液;以及
S42,将所述分散液中的溶剂去除,从而获得所述固态胺CO
2吸附剂。
将所述分散液中的溶剂去除的步骤可以包括在室温下将所述溶剂蒸发掉,并且将剩余物在真空干燥箱中于60℃至80℃下干燥3h至6h。
在一实施例中,固态胺CO
2吸附剂中有机胺负载量为10~80%。
在获得固态胺CO
2吸附剂之后,可以对硅基固态胺CO
2吸附剂的CO
2吸附量和吸附-脱附循环性能进行测量。在一个实施例中,CO
2吸附量测量的步骤包括:固态胺CO
2吸附剂在30~110℃、4~100vol.%CO
2、0~20vol.%水蒸气的条件下吸附5~60min,然后测量CO
2吸附量。在一个实施例中,吸附剂的再生过程为在120~165℃、CO
2气流、0~40vol.%水蒸气的条件下加热5~30min。
实施例1
(1)将13.0g铝酸钠溶解在装有80mL去离子水的烧杯中,并将烧杯置于搅拌器中不断搅拌,并在常温下逐滴加入150mL质量分数为12%的H
2O
2溶液,控制滴加速度使得滴加时间为30min,反应结束后静止30min,取出洗涤过滤,得到未干燥的滤饼。
(2)将滤饼与丁醇按质量比1:10混合捣碎成悬浊状,置于旋转蒸馏仪中先升温到93℃蒸发30min,再升温到117℃回流60min,停止加热;将共沸后的产物冷却、分离得到的沉淀物置于80℃的烘箱中干燥12h,得到扩孔拟薄水铝石。
(3)将扩孔拟薄水铝石置于500℃的马弗炉中焙烧5h,取出冷却,研磨成粒度为200目以下的粉末,即制备得到大孔体积的纳米氧化铝粉末。用N
2吸脱附法测得BET比表面为 397.9m
2/g,孔体积为2.60cm
3/g,平均孔径为22.5nm。
(4)将3.1g聚乙烯亚胺加入到30mL甲醇溶液中,搅拌溶解,使得聚乙烯亚胺均匀分散,加入1g制备的大孔纳米氧化铝基体,在25℃下搅拌蒸发5h,然后置于真空干燥箱中于60℃下干燥5h,制备得到固态胺CO
2吸附剂。
(5)将20mg吸附剂置于热分析仪中的坩埚中,吸附剂先在纯Ar、120℃条件下脱气30min,然后降温到90℃,通入流量为50mL/min、浓度为95vol.%CO
2+5%水蒸气的混合气体进行吸附实验,吸附过程为30min,然后将气流切换成70vol.%CO
2+30%水蒸气,在135℃下再生10min,然后降温到90℃进行新的一次吸附-再生过程,重复吸附-再生过程50次。
实施例2
(1)将13.0g铝酸钠溶解在装有80mL去离子水的烧杯中,并将烧杯置于搅拌器中不断搅拌,并在常温下逐滴加入150mL质量浓度为12%的H
2O
2溶液,控制滴加速度使得滴加时间为30min,反应结束后静止30min,取出洗涤过滤,得到未干燥的滤饼。
(2)将滤饼与丁醇按质量比1:10混合捣碎成悬浊状,置于旋转蒸馏仪中先升温到93℃蒸发30min,再升温到117℃回流60min,停止加热;将共沸后的产物,冷却、分离得到的沉淀物置于80℃的烘箱中干燥12h,得到扩孔拟薄水铝石;
(3)将扩孔拟薄水铝石置于500℃的马弗炉中焙烧5h,取出冷却,研磨成粒度为200目以下的粉末,即制备得到大孔体积的纳米氧化铝粉末。用N
2吸脱附法测得BET比表面为397.9m
2/g,孔体积为2.60cm
3/g,平均孔径为22.5nm。
(4)将2.0g聚乙烯亚胺加入到30mL甲醇溶液中,搅拌溶解,使得聚乙烯亚胺均匀分散,加入1g制备的大孔纳米氧化铝基体,在25℃下搅拌蒸发5h,然后置于真空干燥箱中于60℃下干燥5h,制备得到固态胺CO
2吸附剂。
(5)将20mg吸附剂置于热分析仪中的坩埚中,吸附剂先在纯Ar、120℃条件下脱气30min,然后降温到90℃,通入流量为50mL/min、浓度为40vol.%CO
2+5%水蒸气+55vol.%CH
4的混合气体进行吸附实验,吸附过程为30min,然后将气流切换成70vol.%CO
2+30%水蒸气,在135℃下再生10min,然后降温到90℃进行新的一次吸附-再生过程,重复吸附-再生过程50次。
实施例3
(1)将2%质量浓度的铝酸钠溶液置于反应釜中,通入浓度为15vol.%、流量为每升溶液800mL/min的CO
2,在25℃下充分反应3.5h,pH下降至9.8以下,取出洗涤、过滤,得到未干燥的滤饼。
(2)将滤饼与丁醇按质量比1:10混合捣碎成悬浊状,置于旋转蒸馏仪中先升温到93℃ 蒸发30min,再升温到117℃回流60min,停止加热;将共沸后的产物,冷却、分离得到的沉淀物置于80℃的烘箱中干燥12h,得到扩孔拟薄水铝石;
(3)将扩孔拟薄水铝石置于500℃的马弗炉中焙烧5h,取出冷却,研磨成粒度为200目以下的粉末,即制备得到大孔体积的纳米氧化铝粉末。用N
2吸脱附法测得BET比表面为359.3m
2/g,孔体积为1.62cm
3/g,平均孔径为14.6nm。
(4)将2.0g聚乙烯亚胺加入到30mL甲醇溶液中,搅拌溶解,使得聚乙烯亚胺均匀分散,加入1g制备的大孔纳米氧化铝基体,在25℃下搅拌蒸发5h,然后置于真空干燥箱中于60℃下干燥5h,制备得到固态胺CO
2吸附剂。
(5)将20mg吸附剂置于热分析仪中的坩埚中,吸附剂先在纯Ar、120℃条件下脱气30min,然后降温到90℃,通入流量为50mL/min、浓度为40vol.%CO
2+5%水蒸气+55vol.%CH
4的混合气体进行吸附实验,吸附过程为30min,然后将气流切换成95vol.%CO
2+5%水蒸气,在165℃下再生10min,然后降温到90℃进行新的一次吸附-再生过程,重复吸附-再生过程50次。
实施例4
(1)将2%质量浓度的铝酸钠溶液置于反应釜中,通入浓度为15vol.%、流量为每升溶800mL/min的CO
2,在25℃下充分反应3.5h,pH下降至9.8以下,取出洗涤、过滤,得到未干燥的滤饼。
(2)将滤饼与丁醇按质量比1:10混合捣碎成悬浊状,置于旋转蒸馏仪中先升温到93℃蒸发30min,再升温到117℃回流60min,停止加热;将共沸后的产物,冷却、分离得到的沉淀物置于80℃的烘箱中干燥12h,得到扩孔拟薄水铝石;
(3)将扩孔拟薄水铝石置于600℃的马弗炉中焙烧5h,取出冷却,研磨成粒度为200目以下的粉末,即制备得到大孔体积的纳米氧化铝粉末。用N
2吸脱附法测得BET比表面为300.6m
2/g,孔体积为1.54cm
3/g,平均孔径为16.7nm。
(4)将2.0g聚乙烯亚胺加入到30mL甲醇溶液中,搅拌溶解,使得聚乙烯亚胺均匀分散,加入1g制备的大孔纳米氧化铝基体,在25℃下搅拌蒸发5h,然后置于真空干燥箱中于60℃下干燥5h,制备得到固态胺CO
2吸附剂。
(5)将20mg吸附剂置于热分析仪中的坩埚中,吸附剂先在纯Ar、120℃条件下脱气30min,然后降温到90℃,通入流量为50mL/min、浓度为4vol.%CO
2+20%水蒸气+76vol.%N
2的混合气体进行吸附实验,吸附过程为30min,然后将气流切换成100vol.%CO
2,在165℃下再生10min,然后降温到90℃进行新的一次吸附-再生过程,重复吸附-再生过程50次。
实施例5
(1)将2%质量浓度的铝酸钠溶液置于反应釜中,通入浓度为15vol.%、流量为每升溶液800mL/min的CO
2,在25℃下充分反应3.5h,pH下降至9.8以下,取出洗涤、过滤,得到未干燥的滤饼。
(2)将滤饼与乙醇按质量比1:10混合捣碎成悬浊状,置于旋转蒸馏仪中先升温到78.37℃蒸发30min,再升温到78.4℃回流60min,停止加热;将共沸后的产物,冷却、分离得到的沉淀物置于80℃的烘箱中干燥12h,得到扩孔拟薄水铝石;
(3)将扩孔拟薄水铝石置于500℃的马弗炉中焙烧5h,取出冷却,研磨成粒度为200目以下的粉末,即制备得到大孔体积的纳米氧化铝粉末。用N
2吸脱附法测得BET比表面为361.3m
2/g,孔体积为1.49cm
3/g,平均孔径为12.7nm。
(4)将2.0g聚乙烯亚胺加入到30mL甲醇溶液中,搅拌溶解,使得聚乙烯亚胺均匀分散,加入1g制备的大孔纳米氧化铝基体,在25℃下搅拌蒸发5h,然后置于真空干燥箱中于60℃下干燥5h,制备得到固态胺CO
2吸附剂。
(5)将20mg吸附剂置于热分析仪中的坩埚中,吸附剂先在纯Ar、120℃条件下脱气30min,然后降温到90℃,通入流量为50mL/min、浓度为40vol.%CO
2+5%水蒸气+55vol.%CH
4的混合气体进行吸附实验,吸附过程为30min,然后将气流切换成100vol.%CO
2,在120℃下再生10min,然后降温到90℃进行新的一次吸附-再生过程,重复吸附-再生过程50次。
实施例6
(1)在25℃的温度下,分别取100mL浓度为50g/L的铝酸钠溶液和浓度为35g/L硫酸铝溶液置于两烧杯中,在搅拌过程中快速将两溶液混合,滴加氨水和硫酸调节pH至8.5,然后在80℃下搅拌老化3h,取出洗涤、过滤,得到未干燥的滤饼。
(2)将滤饼与丁醇按质量比1:10混合捣碎成悬浊状,置于旋转蒸馏仪中先升温到93℃蒸发30min,再升温到117℃回流60min,停止加热;将共沸后的产物,冷却、分离得到的沉淀物置于80℃的烘箱中干燥12h,得到扩孔拟薄水铝石;
(3)将扩孔拟薄水铝石置于500℃的马弗炉中焙烧5h,取出冷却,研磨成粒度为200目以下的粉末,即制备得到大孔体积的纳米氧化铝粉末。用N
2吸脱附法测得BET比表面为343.5m
2/g,孔体积为2.13cm
3/g,平均孔径为23.8nm。
(4)将2.0g聚乙烯亚胺加入到30mL甲醇溶液中,搅拌溶解,使得聚乙烯亚胺均匀分散,加入1g制备的大孔纳米氧化铝基体,在25℃下搅拌蒸发5h,然后置于真空干燥箱中于60℃下干燥5h,制备得到固态胺CO
2吸附剂。
(5)将20mg吸附剂置于热分析仪中的坩埚中,吸附剂先在纯Ar、120℃条件下脱气 30min,然后降温到90℃,通入流量为50mL/min、浓度为40vol.%CO
2+5%水蒸气+55vol.%CH
4的混合气体进行吸附实验,吸附过程为30min,然后将气流切换成70vol.%CO
2+30%水蒸气,在135℃下再生10min,然后降温到90℃进行新的一次吸附-再生过程,重复吸附-再生过程50次。
在上述各实施例中,制备的高性能固态胺CO
2吸附剂的CO
2吸附能力和循环稳定性如表1和图2-3所示。实验实测结果表明,固态胺吸附剂的饱和CO
2吸附量可达5mmol/g以上,在实际CO
2再生气氛下的循环性能优异,50次循环后其依然维持着4.8mmol/g以上的吸附量,仅衰减不到5%。
表1实施例1~6中吸附剂的CO
2吸附能力对比
本申请还提供一种固态胺CO
2吸附剂,其由上述制备方法制备而成。
本申请所提供的硅基固态胺CO
2吸附剂及其制备方法具有以下优点:
(1)制备大孔纳米氧化铝基体的原料来源广泛,制备工艺简单、反应条件温和、操作容易控制、无需复杂设备,适合工业化生产;
(2)基体制备过程不需要添加任何表面活性剂、模板剂、扩孔剂,共沸蒸馏过程使用的有机溶剂是常见的有机醇,价格便宜,可回收重复使用,对环境污染小,具有经济优势;
(3)以大孔纳米氧化铝基体制备得到的固态胺CO
2吸附剂能够负载高含量的有机胺,饱和负载量可达70%以上,CO
2吸附容量可达5mmol/g以上;
(4)制备得到的固态胺CO
2吸附剂具备优异的循环稳定性,在实际CO
2再生气氛下循环50次,其CO
2吸附容量依然维持在4.8mmol/g以上,衰减不到5%。
由于本申请的高性能CO
2吸附剂具备极高的CO
2吸附容量和优异的实际条件再生循环稳定性,且制备过程简单、绿色、价格低廉,可广泛应用于CO
2捕集和沼气纯化领域。
以上所述实施例的各技术特征可以进行任意的组合,为使描述简洁,未对上述实施例中 的各个技术特征所有可能的组合都进行描述,然而,只要这些技术特征的组合不存在矛盾,都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本申请的几种实施方式,其描述较为具体和详细,但并不能因此而理解为对申请专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本申请构思的前提下,还可以做出若干变形和改进,这些都属于本申请的保护范围。因此,本申请专利的保护范围应以所附权利要求为准。
Claims (14)
- 一种固态胺CO 2吸附剂的制备方法,其特征在于,所述制备方法包括:提供拟薄水铝石;对所述拟薄水铝石进行扩孔;将扩孔的拟薄水铝石进行焙烧,得到氧化铝粉末;用有机胺溶液浸渍所述氧化铝粉末,并进行干燥,得到所述固态胺CO 2吸附剂。
- 根据权利要求1所述的制备方法,其特征在于,所述拟薄水铝石采用在铝酸钠溶液中滴加H 2O 2溶液、或在铝酸钠溶液中通入CO 2、或使铝酸钠溶液与硫酸铝溶液混合制备而成。
- 根据权利要求2所述的制备方法,其特征在于,在铝酸钠溶液中滴加H 2O 2溶液制备所述拟薄水铝石的步骤包括:在室温下,将质量分数为5~20%的H 2O 2溶液滴加到浓度为20~200g/L的铝酸钠溶液中,滴加时间为10~60min,滴加完成后获得反应液;将所述反应液静置30min,得到含有沉淀物的产液;以及过滤出所述产液中的沉淀物,并对所述沉淀物进行洗涤,得到所述拟薄水铝石;其中,所述铝酸钠溶液中的铝酸钠与所述H 2O 2溶液中的H 2O 2的摩尔比为1:1至1:5。
- 根据权利要求2所述的制备方法,其特征在于,在铝酸钠溶液中通入CO 2制备所述拟薄水铝石的步骤包括:在室温下,将含有10~50vol.%的CO 2的气体混合物通入浓度为10g/L~100g/L的铝酸钠溶液中,得到反应液;持续通入所述气体混合物,直至所述反应液的pH下降到9.5-9.8,得到含有沉淀物的产液;以及过滤出所述产液中的沉淀物,并对所述沉淀物进行洗涤,得到所述拟薄水铝石。
- 根据权利要求2所述的制备方法,其特征在于,使铝酸钠溶液与硫酸铝混合制备所述拟薄水铝石的步骤包括:将浓度为20~200g/L的铝酸钠溶液和浓度为20~200g/L的硫酸铝溶液按质量比1:1进行混合,得到反应液;调节所述反应液的pH至8.0~10.0,并在25~80℃的温度下搅拌2-5小时,得到含有沉淀物的产液;过滤出所述产液中的沉淀物,并对所述沉淀物进行洗涤,得到所述拟薄水铝石。
- 根据权利要求3至5中任一项所述的制备方法,其特征在于,对所述拟薄水铝石进行扩孔的步骤包括:将过滤出的洗涤后的所述沉淀物与有机醇按1:5至1:30的质量比混合,形成悬浮液;将所述悬浮液的温度升高到水与有机醇的共沸点蒸发10~60min,再升温到有机醇的沸点回流30~90min,得到所述扩孔的拟薄水铝石。
- 根据权利要求6所述的制备方法,其特征在于,所述有机醇包括乙醇、正丙醇、异丙醇、正丁醇、异丁醇和仲丁醇中的一种或者多种。
- 根据权利要求1所述的制备方法,其特征在于,将扩孔的拟薄水铝石进行焙烧,得到氧化铝粉末的步骤包括:在400~600℃的温度下焙烧所述扩孔的拟薄水铝石2~8小时,得到所述氧化铝粉末。
- 根据权利要求1所述的制备方法,其特征在于,在焙烧步骤之后,还包括对所述氧化铝粉末进行研磨,以形成纳米氧化铝粉末的步骤。
- 根据权利要求1所述的制备方法,其特征在于,所述有机胺溶液包括有机胺和溶剂,所述有机胺为聚乙烯亚胺、二乙烯三胺、四乙烯五胺和五乙撑六胺中的一种或多种,所述溶剂为甲醇、乙醇、丙酮和醋酸丁酯的一种或多种。
- 根据权利要求1所述的制备方法,其特征在于,所述有机胺溶液中有机胺与溶剂的质量比为1:10至1:100。
- 根据权利要求9所述的制备方法,其特征在于,用有机胺溶液浸渍所述氧化铝粉末,干燥后得到所述固态胺CO 2吸附剂的步骤包括:将所述氧化铝粉末分散在所述有机胺溶液中,得到分散液;以及将所述分散液中的溶剂去除,从而获得所述固态胺CO 2吸附剂。
- 根据权利要求12所述的制备方法,其特征在于,将所述分散液中的溶剂去除的步骤包括:在室温下将所述溶剂蒸发掉,并且将剩余物在真空干燥箱中于60℃至80℃下干燥3h至6h。
- 一种固态胺CO 2吸附剂,其由权利要求1所述的制备方法制备而成。