CN116075560A - 锚涂剂及使用其的柔性版印刷物的制造方法 - Google Patents
锚涂剂及使用其的柔性版印刷物的制造方法 Download PDFInfo
- Publication number
- CN116075560A CN116075560A CN202180057415.0A CN202180057415A CN116075560A CN 116075560 A CN116075560 A CN 116075560A CN 202180057415 A CN202180057415 A CN 202180057415A CN 116075560 A CN116075560 A CN 116075560A
- Authority
- CN
- China
- Prior art keywords
- anchor
- coating agent
- mass
- anchor coating
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种锚涂剂,所述锚涂剂具有适当的粘度,由其能够抑制飞墨现象、能够对印刷介质均匀地转移所需量并且能够得到涂膜耐受性优异的涂膜。本发明涉及一种包含乳液、纤维素醚和/或聚乙烯醇以及水性介质的锚涂剂。
Description
技术领域
本发明涉及一种锚涂剂以及使用该锚涂剂的柔性版印刷物的制造方法。
背景技术
在包装容器的领域中通常使用柔性版印刷方式。
近年,即使在包装容器的领域中,从提高附加价值的观点出发,针对能够再现高质量的设计的喷墨印刷方式的关注度正在高涨。
在利用喷墨印刷方式进行印刷时,作为其预处理已知的是将包含水溶性多价金属盐的锚涂剂涂布到印刷介质上。
例如,在专利文献1中公开了一种锚涂剂,其是被涂布到挂面纸板(裱衬原纸)或瓦楞纸板上用于柔性版印刷,其特征在于包含解离性多价金属盐、乳液以及水性介质。
专利文献1中公开的锚涂剂因粘度低而存在印刷过程中发生喷雾状飞散的飞墨(misting)现象的情况,另外伴随飞墨现象存在无法针对印刷介质均匀地转移所需量这样的问题。
另外,对于专利文献1中公开的锚涂剂,虽然通过添加增粘剂能够使粘度上升,但是存在发生由增粘剂导致的飞墨现象的情况,尚有进一步改善的余地。
现有技术文献
专利文献
专利文献1:日本特开2015-134914号公报
发明内容
发明要解决的问题
本发明的目的在于提供一种具有适当的粘度、能够抑制飞墨现象、能够对印刷介质均匀地转移所需量、能够得到涂膜耐受性优异的涂膜的锚涂剂。
用于解决问题的手段
本发明人鉴于上述的问题反复专心研究的结果,发现了通过包含乳液、纤维素醚和/或聚乙烯醇以及水性介质,能够获得一种具有适当的粘度、能够抑制飞墨现象、能够对印刷介质均匀地转移所需量并且能够形成涂膜耐受性优异的涂膜的锚涂剂,由此完成本发明。
即,本发明的锚涂剂的特征在于包含:乳液,纤维素醚和/或聚乙烯醇,以及水性介质。
在本发明的锚涂剂中,优选上述纤维素醚是选自羟丙基甲基纤维素和羟乙基甲基纤维素中的一种以上。
另外,优选上述乳液的酸值小于50mgKOH/g。
另外,以锚涂剂的质量为基准,优选上述乳液的含量以固体成分计为5~65质量%。
另外,优选本发明的锚涂剂还包含离子盐。
另外,优选上述离子盐是钙盐类。
另外,以锚涂剂的质量为基准,优选上述离子盐的含量为0.1~40质量%。
另外,优选本发明的锚涂剂用于柔性版印刷。
另外,本发明的柔性版印刷物的制造方法,其是通过柔性版印刷机印刷的柔性版印刷物的制造方法,其特征在于包括将本发明的锚涂剂涂布到印刷介质上的工序。
另外,在本发明的柔性版印刷物的制造方法中,优选上述锚涂剂的涂布量为0.1~10g/m2,更优选为0.1~2g/m2。
下面,对本发明的锚涂剂以及使用该锚涂剂的柔性版印刷物的制造方法详细地进行说明。
<锚涂剂>
本发明的锚涂剂,其特征在于包含乳液、纤维素醚和/或聚乙烯醇以及水性介质。
(乳液)
本发明的锚涂剂包含乳液。
作为上述乳液,可以举出丙烯酸系树脂、聚酯系树脂、聚氨酯系树脂、聚醋酸乙烯酯系树脂、聚氯乙烯系树脂、聚苯乙烯系树脂、聚丁二烯系树脂等的乳液。
其中,从锚涂剂的涂膜的凝聚性优异、适当地赋予涂膜耐受性的观点出发,优选为丙烯酸系树脂的乳液。
上述乳液可以单独使用或者组合使用两种以上。
优选为,上述乳液的酸值小于50mgKOH/g。
若上述乳液的酸值为50mgKOH/g以上,则在包含锚涂剂中的后述的离子盐的情况下,与上述乳液之间发生相互作用,存在盐析效果降低的倾向,存在喷墨印刷适应性降低的情况。另外,还存在与后述的离子盐的相容性降低、无法充分赋予保存稳定性的情况。
上述乳液的酸值更优选为30mgKOH/g以下,从更合适地赋予保存稳定性的观点出发,进一步优选为20mgKOH/g以下。
上述乳液的酸值可以使用电位差滴定法进行测量。
例如,可以根据JIS K0070:1992“化学产品的酸值、皂化值、酯值、碘值、羟值以及不皂化物的试验方法”等进行。作为这样的电位差滴定装置,例如可以举出电位差自动滴定装置AT610(京都电子工业株式会社制)。
上述乳液的玻璃化转变温度优选为70℃以下,从适当地赋予保存稳定性的观点出发,更优选为40℃以下,从更适当地赋予涂膜耐受性的观点出发,进一步优选为20℃以下。
另外,上述乳液的玻璃化转变温度的下限优选为-10℃以上,从更适当地赋予保存稳定性的观点出发,更优选为0℃以上。
上述乳液的玻璃化转变温度例如可以通过按照JIS K7121:2012“塑料的转变温度测量方法”等的示差扫描量热测量(DSC)进行。
以锚涂剂的质量为基准,优选上述乳液的含量以固体成分计为5~65质量%。
若上述乳液的含量以固体成分计小于5质量%,则存在锚涂剂的涂膜的凝聚力降低、涂膜耐受性降低的情况。另一方面,若上述乳液的含量以固体成分计超过65质量%,则配合其它成分的余地减少,存在发明的效果变得不充分的情况。
从适当地赋予涂膜耐受性的观点出发,以锚涂剂的质量为基准,上述乳液的含量以固体成分计更优选为6质量%以上,进一步优选为7质量%以上。另外,从适当地赋予保存稳定性的观点出发,以固体成分计更优选为小于30质量%,进一步优选为15质量%以下,特别优选为10质量%以下,最优选为9质量%以下。
作为上述乳液,可以举出使用低分子的乳化剂将上述例示过的树脂在后述的水性介质中乳化得到的乳液,使用高分子的乳化剂在后述的水性介质中乳化得到的乳液,通过自乳化在后述的水性介质中乳化得到的乳液等。
作为上述低分子的乳化剂,可以举出:单糖或多糖的脂肪酸酯、聚甘油脂肪酸酯、有机酸单甘油酯、丙二醇脂肪酸酯、聚甘油缩合蓖麻油酸酯、山梨糖醇酐脂肪酸酯、聚氧乙烯山梨糖醇酐脂肪酸酯、聚氧乙烯烷基醚、烷基苯磺酸盐、烷烃磺酸盐、α-烯烃磺酸盐,聚氧乙烯烷基醚硫酸盐、烷基硫酸盐、聚氧乙烯烷基醚磷酸盐、烷基磷酸盐、四烷基铵盐、烷基苄基二甲基铵盐、脂肪酸酰胺基胺(fatty acid amidoamine)、烷基吡啶鎓盐、烷基甜菜碱、以及烷基胺氧化物等。
(纤维素醚和/或聚乙烯醇)
本发明的锚涂剂含有纤维素醚和/或聚乙烯醇。
从适当地赋予保存稳定性的观点出发,本发明的锚涂剂优选为含有纤维素醚。
通常认为本发明的锚涂剂通过含有纤维素醚来使分子内的许多环状结构以及许多羟基在气液界面成为确定的取向状态,由此通过降低在对锚涂剂进行柔性版印刷时产生雾化的带电性,能够减少飞墨现象,此外,使锚涂剂的流动特性良好,能够提高转移性。但是,本发明也可以不局限于该作用机理进行解释。
作为上述纤维素醚,可以举出:甲基纤维素、乙基纤维素、丙基纤维素等的烷基纤维素;羟乙基纤维素、羟丙基纤维素等羟基烷基纤维素;羟丙基甲基纤维素、羟乙基甲基纤维素等羟基烷基烷基纤维素;苄基纤维素,三苯甲基纤维素等芳烷基纤维素;氰基乙基纤维素等氰基烷基纤维素;羧基甲基纤维素、羧基乙基纤维素等羧基烷基纤维素;羧基甲基甲基纤维素、羧基甲基乙基纤维素等羧基烷基烷基纤维素;氨基乙基纤维素等氨基烷基纤维素等。
上述纤维素醚可以单独使用或者组合使用两种以上。
上述纤维素醚优选为选自羟丙基甲基纤维素和羟乙基甲基纤维素中的一种以上,更优选为羟丙基甲基纤维素。
通过使上述纤维素醚是选自羟丙基甲基纤维素和羟乙基甲基纤维素中的一种以上,能够适当地赋予相对于后述的水性介质的溶解性,能够更适当地赋予保存稳定性。另外,通过使用羟乙基甲基纤维素,能够更适当地赋予相对于后述的水性介质的溶解性以及保存稳定性。
从赋予适当的粘度、抑制飞墨现象的观点、适当地赋予相对于印刷介质均匀地转移所需量的转移性的观点出发,以锚涂剂的质量为基准,上述纤维素醚和/或聚乙烯醇的含量优选为0.1~10质量%,更优选为使用0.2~5质量%,进一步优选为使用1~3质量%。
在不损害本发明的效果的范围内,本发明的锚涂剂可以含有上述纤维素醚和/或聚乙烯醇以外的增粘剂。
作为上述纤维素醚和/或聚乙烯醇以外的增粘剂,例如可以举出聚丙烯酸、聚丙烯酸(部分)中和物、聚乙二醇(以及与其它的环氧烷烃(alkyleneoxide)的共聚物)、(在氮原子上具有取代基的)聚丙烯酰胺、聚乙烯亚胺、糊精、海藻酸钠、聚乙烯吡咯烷酮、聚环氧乙烷(以及与其它的环氧烷烃的共聚物)、纤维素、葡萄糖等各种糖类、乙烯-乙烯醇共聚物、乙烯-丙烯酸共聚物(以及其中和物)等。
从赋予适当的粘度、抑制飞墨现象的观点出发,相对于增粘剂(上述纤维素醚和/或聚乙烯醇与上述纤维素醚和/或聚乙烯醇以外的增粘剂)的合计质量,上述纤维素醚和/或聚乙烯醇的含量优选为80质量%以上,更优选为90质量%以上,进一步优选为95%质量以上,最优选为100质量%。
另外,本发明中的“适当的粘度”是使用赞恩杯(Zahn cup)(4号,株式会社离合社制)在液温23℃的条件下测量的情况下成为8~35秒的粘度。
(水性介质)
作为上述水性介质,可以举出水或水与水混和性溶剂的混合物。作为水混和性溶剂,例如可以举出:低级醇类、多元醇类、以及它们的烷基醚或烷基酯类等,具体地说,可以举出甲醇、乙醇、正丙醇、异丙醇、正丁醇、异丁醇、仲丁醇等低级醇类、乙二醇、丙二醇、二乙二醇、二丙二醇、甘油等多元醇类、乙二醇单甲醚、乙二醇单乙醚、乙二醇单乙酸酯、丙二醇单甲醚、丙二醇单乙醚、丙二醇单乙酸酯、二乙二醇单甲醚以及二丙二醇单甲醚等。
上述水性介质可以单独使用或者组合使用两种以上。
从适当地赋予流动性的观点、对锚涂剂的涂膜适当地赋予耐磨损性的观点出发,以锚涂剂的质量为基准,优选上述水性介质为含有10~50质量%,更优选为含有20~40质量%。
另外,上述水性介质的含量是将上述乳液中包含的水性介质的含量与上述乳液中包含的水性介质以外的水性介质的含量合计得到的值。
(离子盐)
本发明的锚涂剂优选还包含离子盐。
通过使本发明的锚涂剂还包含离子盐,由于使用锚涂剂形成的涂膜包含离子盐,所以盐析作用适当地作用,即使进行喷墨印刷,墨液中包含的颜料、粘合剂树脂等成分也难以浸透原纸,因此喷墨印刷适应性优异。
作为上述离子盐,可以举出有机离子盐以及无机离子盐。
作为上述有机离子盐,可以举出脂肪族磺酸盐、高级醇硫酸酯盐、高级醇磷酸酯盐、高级醇环氧乙烷加成硫酸酯盐、高级醇环氧乙烷加成磷酸酯盐、季铵盐、甜菜碱等有机离子盐等。
作为上述无机离子盐,可以举出碱金属盐、碱土类金属盐等。其中,从适当地赋予喷墨印刷适应性的观点出发,优选为解离性多价金属盐。
作为上述解离性多价金属盐,可以举出钙、镁等的氯化物、硫酸盐、硝酸盐等无机盐类或醋酸盐、甲酸盐等有机酸盐等。
具体地说,可以举出醋酸钙、氯化钙、甲酸钙、硝酸钙、硫酸钙、醋酸镁、氯化镁、甲酸镁、硝酸镁以及硫酸镁等。
上述离子盐可以单独使用或者组合使用两种以上。
上述离子盐优选为钙盐类。
通过使上述离子盐为钙盐类,能够适当地赋予向后述的水性介质的溶解性。
上述离子盐更优选为氯化钙或硝酸钙,从盐析作用适当地起作用、能够更适当地赋予喷墨印刷适应性的观点出发,进一步优选为氯化钙。
从适当地赋予喷墨印刷适应性的观点出发,以锚涂剂的质量为基准,上述离子盐的含量优选为0.1~40质量%,更优选为使用2~20质量%,进一步优选为使用5~15质量%。
(其它)
从适当地赋予涂膜耐受性的观点出发,优选本发明的锚涂剂包含聚烯烃蜡。
作为上述聚烯烃蜡,例如可以举出从乙烯、丙烯、丁烯等烯烃或其衍生物制造的蜡及其共聚物。具体地说,可以举出聚乙烯系蜡、聚丙烯系蜡、聚丁烯系蜡等。
其中,从对锚涂剂的涂膜更适当地赋予涂膜耐受性的观点出发,优选为聚乙烯系蜡。
作为聚烯烃蜡,可以利用市售的聚烯烃蜡,例如可以使用Nopcote PEM17(圣诺普科公司制)、CHEMIPEARL W400、CHEMIPEARL W4005(三井化学株式会社制)、AQUACER515、AQUACER593(毕克化学日本株式会社制)等。
相对于锚涂剂的总质量,本发明的锚涂剂中包含的聚烯烃蜡优选为0.1~10质量%,更优选为0.2~5质量%。
除了上述所示的成分以外,根据需要,本发明的锚涂剂可以适当地选择使用分散剂、分散助剂、湿润剂、粘度调整剂、pH调整剂、消泡剂、杀菌剂(fungicide)、防锈剂、均化剂等众所周知的添加剂。
(锚涂剂的制造方法)
本发明的锚涂剂的制造方法没有特别的限定,例如可以通过根据需要向上述的各成分添加添加剂等并进行混匀(混炼)来制造。
<柔性版印刷物的制造方法>
本发明的柔性版印刷物的制造方法是通过柔性版印刷机印刷的柔性版印刷物的制造方法,其特征在于,具有将本发明的锚涂剂涂布到印刷介质上的工序。
作为上述印刷介质,没有特别的限定,例如可以举出将化学浆、机械浆、废纸浆等一种或两种以上适当混合得到的挂面纸板(裱衬原纸)。此外,也可以使用将两层以上的纸浆层合层而成为多层结构的原纸等。
本发明的锚涂剂也可以利用众所周知的印刷方法进行印刷,但是优选为用于柔性版印刷。
本发明的锚涂剂能够适当地抑制在柔性版印刷时尤其容易产生的飞墨现象。
作为柔性版印刷,可以适当地选择利用众所周知的方法。
作为上述锚涂剂的涂布量,以固体成分计优选为0.1~20g/m2,从适当地赋予涂膜耐受性的观点出发,以固体成分计更优选为0.1~15g/m2。
若本发明的锚涂剂的涂布量小于0.1g/m2,则存在无法充分地得到本发明的效果的情况,若上述锚涂剂的涂布量超过20g/m2,则也存在容易发生逆套印(back trapping)、无法充分赋予涂膜耐受性的情况。
作为涂布了上述锚涂剂的涂布面的干燥方法,可以举出在该领域中使用的通常的干燥机,例如可以举出热风干燥机。另外,涂布有上述锚涂剂的涂布面可以是完全干燥状态,也可以是半干燥状态。
涂布上述锚涂剂形成的柔性版印刷物可以使用众所周知的墨液,通过众所周知的印刷方法形成印刷后的印刷层。
作为上述众所周知的印刷方法,例如可以举出凹版印刷、胶印印刷、柔性版印刷、丝网印刷以及喷墨印刷等印刷方式,优选为能够再现高质量的设计(图案)的喷墨印刷方式。
通过本发明的柔性版印刷物的制造方法制造的柔性版印刷物由于使用本发明的锚涂剂形成,所以涂膜耐受性优异。
发明效果
本发明能够提供一种具有适当的粘度、能够抑制飞墨现象、能够对印刷介质均匀转移所需量的锚涂剂,并且使用该锚涂剂形成的涂膜的涂膜耐受性优异。
具体实施方式
下面举出实施例对本发明更详细地进行说明,但本发明不仅仅局限于这些实施例。另外,除非另有说明,“%”的意思是指“质量%”,“份”的意思指“质量份”。
在实施例及比较例中使用的材料如下所述。
<离子盐>
二水氯化钙
四水硝酸钙
<乳液>
(丙烯酸树脂乳液-1)
(日本CARBIDE株式会社制,FX2043,酸值10mgKOH/g,玻璃化转变温度10℃,固体成分50质量%,水性介质为水)
按照以下的步骤合成了其它的丙烯酸树脂乳液。
(丙烯酸树脂乳液-2)
向由1.5质量份的丙烯酸、89.5质量份的甲基丙烯酸甲酯、9质量份的丙烯酸丁酯构成的单体的混合物添加3质量份的作为表面活性剂的Acualon HS-10(第一工业制药株式会社制),进一步添加将0.3质量份的过硫酸钾溶解到46质量份的蒸馏水中得到的水溶液,用搅拌机预先进行了乳化。向安装有搅拌机、冷凝管、温度计、氮气导入管的聚合容器添加20质量份的蒸馏水,进行氮气置换,当升温到80℃时用3小时滴加上述单体的乳化液,进而进行2小时的反应后结束聚合。但是,在聚合后期添加少量的过硫酸钾消耗掉残存的单体。向得到的乳液添加氢氧化钠将pH调整到7之后,以使固体成分浓度成为50质量%的方式添加蒸馏水,得到了丙烯酸树脂乳液-2(酸值10mgKOH/g,玻璃化转变温度70℃,固体成分50质量%,水性介质为水)。
(丙烯酸树脂乳液-3)
在上述丙烯酸树脂乳液-2的合成中,将丙烯酸变更为19.3质量份,将甲基丙烯酸甲酯变更为34.5质量份,将丙烯酸丁酯变更为46.2质量份,由此得到了丙烯酸树脂乳液-3(酸值150mgKOH/g,玻璃化转变温度10℃,固体成分50质量%,水性介质为水)。
<纤维素醚>
纤维素醚A(羟丙基甲基纤维素,信越化学株式会社制,METOLOSE90SH-100)
纤维素醚B(羟丙基甲基纤维素,信越化学株式会社制,METOLOSE60SH-400)
纤维素醚C(羧基甲基纤维素,株式会社大赛璐制,CMC1140)
纤维素醚D(羟乙基甲基纤维素,信越化学株式会社制,METOLOSE60SEB)
<聚乙烯醇>
聚乙烯醇(株式会社可乐丽制,PVA224)
<其它的增粘剂>
聚环氧乙烷(明成化学株式会社制,ALKOX R-400)
<水性介质>
纯化水
<其它>
聚乙烯蜡(三井化学株式会社制,CHEMIPEARL W-400)
均化剂(日信化学工业株式会社制,Surfynol 104)
消泡剂(陶氏东丽株式会社制,Antifoam 013A)
(实施例1~15,比较例1~3)
按照表1中记载的配合比,将各种材料进行混匀而制备了锚涂剂。
<粘度的测量>
使用赞恩杯(4号,株式会社离合社制),在液温23℃的条件下测量了粘度。其结果在表1中示出。
<转移性>
使用手持涂布器(HAND PULURFER)(360线)将在实施例以及比较例中制备出的锚涂剂以成为固体成分0.5g/m2的方式涂布到涂布纸板(联合株式会社(Rengo Co.,Ltd.)制,纸张定量230g/m2)上,用干燥机使涂布面干燥。
用目视确认了涂布面,按如下基准评价了锚涂剂的转移状态。其结果在表1中示出。
〇:均匀地进行了转移,对喷墨墨液的印刷没有影响;
△:存在转移不均匀的部分,但是对喷墨墨液的印刷没有影响;
×:转移不均匀或不是所需量,对喷墨墨液的印刷造成障碍。
<飞墨>
用堆叠式柔性版印刷机(ORIENT SOGYO CO.,LTD.制)将在实施例及比较例中制备出的锚涂剂以印刷速度150m/min的条件印刷到涂布纸板(联合株式会社制,纸张定量230g/m2)上。
用目视观测评价了上述柔性版印刷时的锚涂剂的飞散程度。其结果在表1中示出。
〇:完全没有飞散;
△:存在飞散但没有损害外观、没有对机器和材料造成影响的顾虑,因此无需停止印刷机器;
×:存在飞散,外观受损或者担心对机器和材料造成影响,因此需要停止印刷机器并进行清扫。
<涂膜耐受性>
使用手持涂布器(360线)将在实施例及比较例中制备出的锚涂剂以成为固体成分0.5g/m2的方式涂布到涂布纸板(联合株式会社制,纸张定量230g/m2)上,用干燥机使涂布面干燥。
使用学振型摩擦牢度试验机(株式会社东洋精机制作所制)根据下述的条件评价了涂膜耐受性。其结果在表1中示出。
评价条件:200g×2次,向面对上述纸板涂布面的摩擦布(细白布)滴下5滴水后进行试验
〇:涂膜没有被擦掉;
△:锚涂剂稍稍附着到摩擦布上;
×:锚涂剂附着到摩擦布的整面上。
<喷墨印刷适应性>
使用手持涂布器(360线)将在实施例及比较例中制备出的锚涂剂以成为固体成分0.5g/m2的方式涂布到涂布纸板(联合株式会社制,纸张定量230g/m2)上,用干燥机使涂布面干燥。
针对得到的涂布面,利用喷墨印刷用的打印机(爱普生株式会社制,PX105)使用喷墨用墨液(爱普生株式会社制,IC4CL69)印刷了0.3mm的细线。
用目视观察了印刷面,按如下基准评价了喷墨印刷适应性。其结果在表1中示出。
〇:印刷鲜明且完全没有洇渗;
△:印刷存在稍稍的洇渗,但是能够再现设计;
×:印刷存在大量洇渗,难以看到设计。
<溶解性>
为了使利用赞恩杯(4号,株式会社离合社制)测量出的液温23℃下的粘度为10秒以上,按如下基准评价了按表1中记载的质量比添加了各种材料时的溶解性。其结果在表1中示出。
〇:材料完全溶解,没有残渣;
△:稍微存在未溶解的材料,但是能够用过滤器(100目)去除;
×:材料的溶解性差,无法使粘度成为10秒以上,或者产生大量残渣且无法用过滤器(100目)去除。
<保存稳定性>
将在实施例及比较例中制备出的锚涂剂在密闭容器内在40℃下保存了7天,确认了有无增粘、分离以及沉淀(沉降),按如下基准进行了评价。其结果在表1中示出。
〇:未观察到增粘、分离、沉淀;
△:观察到增粘、分离或沉淀,但通过搅拌完全恢复;
×:观察到增粘、分离或沉淀,通过搅拌也没有完全恢复。
由此确认到实施例的锚涂剂具有适当的粘度、能够抑制飞墨现象、能够对印刷介质均匀地转移所需量、能够得到涂膜耐受性优异的涂膜。
根据实施例1与实施例11的比较,确认到能够通过包含离子盐来提高喷墨印刷适应性。
另外,根据实施例1与实施例12、14的比较,确认到能够通过使用羟丙基甲基纤维素来更适当地赋予溶解性以及保存稳定性。
另外,根据实施例1与实施例13的比较,确认到能够通过使乳液的酸值成为规定的范围来更适当地赋予溶解性以及保存稳定性。
另外,根据实施例15,确认到能够通过使用羟乙基甲基纤维素,来赋予适当的粘度、转移性优异、飞墨现象受到抑制、能够得到涂膜耐受性以及喷墨印刷适应性优异的涂膜。
另一方面,不包含增粘剂的比较例1的粘度不够,转移性也差。另外,不包含乳液的比较例2的涂膜耐受性差。另外,在使用聚环氧乙烷作为增粘剂的比较例3无法抑制飞墨现象。
工业实用性
本发明能够提供一种锚涂剂,其具有适当的粘度、能够抑制飞墨现象、能够对印刷介质均匀地转移所需量,作为使用该锚涂剂形成的涂膜的涂膜耐受性优异。
Claims (11)
1.一种锚涂剂,其包含:
乳液;
纤维素醚和/或聚乙烯醇;以及
水性介质。
2.如权利要求1所述的锚涂剂,其中,
所述纤维素醚是选自羟丙基甲基纤维素和羟乙基甲基纤维素中的一种以上。
3.如权利要求1或2所述的锚涂剂,其中,
所述乳液的酸值小于50mgKOH/g。
4.如权利要求1至3中任一项所述的锚涂剂,其中,
以锚涂剂的质量为基准,所述乳液的含量以固体成分计为5质量%~65质量%。
5.如权利要求1至4中任一项所述的锚涂剂,其中,
所述锚涂剂还包含离子盐。
6.如权利要求5所述的锚涂剂,其中,
所述离子盐是钙盐类。
7.如权利要求5或6所述的锚涂剂,其中,
以锚涂剂的质量为基准,所述离子盐的含量为0.1质量%~40质量%。
8.如权利要求1至7中任一项所述的锚涂剂,其中,
所述锚涂剂用于柔性版印刷。
9.一种柔性版印刷物的制造方法,其是通过柔性版印刷机印刷的柔性版印刷物的制造方法,其中,
所述制造方法包括将权利要求1至8中任一项所述的锚涂剂涂布到印刷介质上的工序。
10.如权利要求9所述的柔性版印刷物的制造方法,其中,
所述锚涂剂的涂布量以固体成分计为0.1g/m2~10g/m2。
11.如权利要求10所述的柔性版印刷物的制造方法,其中,
所述锚涂剂的涂布量以固体成分计为0.1g/m2~2g/m2。