CN115521230A - 一种含硅单体、光固化组合物、封装薄膜及包含其的有机电致发光器件 - Google Patents

一种含硅单体、光固化组合物、封装薄膜及包含其的有机电致发光器件 Download PDF

Info

Publication number
CN115521230A
CN115521230A CN202211268976.8A CN202211268976A CN115521230A CN 115521230 A CN115521230 A CN 115521230A CN 202211268976 A CN202211268976 A CN 202211268976A CN 115521230 A CN115521230 A CN 115521230A
Authority
CN
China
Prior art keywords
bis
diene
acid
ethane
meth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202211268976.8A
Other languages
English (en)
Inventor
于哲
尹恩心
秦翠英
石卓
马晓宇
王辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jilin Optical and Electronic Materials Co Ltd
Original Assignee
Jilin Optical and Electronic Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jilin Optical and Electronic Materials Co Ltd filed Critical Jilin Optical and Electronic Materials Co Ltd
Priority to CN202211268976.8A priority Critical patent/CN115521230A/zh
Publication of CN115521230A publication Critical patent/CN115521230A/zh
Pending legal-status Critical Current

Abstract

本发明涉及光固化材料及薄膜封装技术领域，具体涉及一种含硅单体、光固化组合物、封装薄膜及包含其的有机电致发光器件。本发明公开的光固化组合物包括含硅单体、光固化单体和光交联引发剂。本发明提供的含硅单体，含有刚性基团的芳环和Si原子，相比于不含苯环和硅原子的单体具有更好的耐热性、透明性，更低的水汽透过率和氧气透过率，另一方面也减少了封装组合物在固化时所产生过多的收缩体积，将其用于OLED器件的薄膜封装，能够有效阻隔水和氧气，提高了可靠性，且进一步延长了OLED器件的使用寿命。

Description

一种含硅单体、光固化组合物、封装薄膜及包含其的有机电致 发光器件
技术领域
本发明涉及光固化材料及薄膜封装技术领域，具体涉及一种含硅单体、光固化组合物、封装薄膜及包含其的有机电致发光器件。
背景技术
OLED又称为有机电激光显示、有机发光半导体。OLED属于一种电流型的有机发光显示装置，是通过载流子的注入和复合而致发光的现象，发光强度与注入的电流成正比。OLED在电场的作用下，阳极产生的空穴和阴极产生的电子就会发生移动，分别向空穴传输层和电子传输层注入，迁移到发光层。当二者在发光层相遇时，产生能量激子，从而激发发光分子最终产生可见光。有机发光显示装置包含了由空穴注入电极(阳极)、有机发光层以及电子注入电极(阴极)组成的有机发光器件(OLED)。这个有机发光器件通常是提供在玻璃基板上，为了防止受到从外部流入水分或氧导致劣化，用另外一张基板覆盖住。目前，包括有机发光显示装置在内的显示装置在消费者的需求下日渐变薄，有机发光装置方面也为了满足此需求将薄膜封装适用在有机发光装置的覆盖上。
薄膜封装结构是在基板显示范围内将形成的有机发光器件上方分别将无机膜与有机膜一层以上交替叠层从而覆盖住显示范围来保护有机发光器件的结构，通常将叠层的无机膜与有机膜称为薄膜封装层。具有此薄膜封装层的有机发光显示设备与具有柔性的基板一起优化设备的柔韧性。另外，此有机发光显示设备使设备的多样设计成为了可能，最重要的是让薄型化成为了可能。
现阶段的OLED最大的问题之一是使用寿命较短，其容易失效。其中，影响OLED寿命的主要因素之一是长时间使用OLED器件的内部会存在水汽和氧气。因此，为了提高OLED的使用寿命，改善OLED的封装工艺是最直接且有效的方法。
现有用于封装OLED的结构一般采用玻璃或金属材料的封装盖板与OLED基板通过环氧树脂进行粘接形成的，其虽然可以起到一定的阻隔作用，但是仍然存在水蒸气透过率角度以及透光率较低等问题。因此解决此问题迫在眉睫。
发明内容
有鉴于此，为了实现上述目的，本发明的第一个目的在于提供一种含硅单体。
采用如下技术方案：
一种含硅单体，具有式1所示结构：
A1-R3-Y2-R2-L1-X-L2-R1-Y1-R4-A2
式1，
其中，
X独立选自O、N、S；
L1、L2各自独立地选自单键、C1-C20烷基、C1-C20烷氧基、C1-C10烯基、C1-C10炔基、C6-C30芳基、C3-C20环烷基或4元-30元杂芳基；且L1和L2至少有一个是芳基或杂芳基；
R1、R2独立地选自氢，取代或未取代的C1-C10烷基，取代或未取代的C3-C20环烷基，取代或未取代的C1-C10羟烷基，取代的或未取代的C6-C20芳基，取代或未取代的2元-20元杂芳基，取代或未取代的C2-C10链烯基，取代或未取代的C1-C10烷氧基；且R1、R2不能同时为氢；
R3、R4为取代或未取代的C1-C10烷基，取代或未取代的C3-C20环烷基，取代或未取代的C1-C10羟烷基，取代的或未取代的C6-C20芳基，取代或未取代的2元-20元杂芳基，取代或未取代的C2-C10链烯基，取代或未取代的C1-C10烷氧基；
Y1、Y2独立地选自单键、氧、被烷基取代或未取代的氨基或硫；
A1、A2独立地选自取代的丙烯酸酯基或未取代的丙烯酸酯基，其结构通式为式5：
Figure BDA0003894336760000031
其中，“*”为连接位置，Z选自H原子、取代或者未取代的碳原子小于20的烷基、碳原子小于20的烷氧基。
本发明公开提供的含硅单体，含有刚性基团的芳环和Si原子，相比于不含苯环和硅原子的单体具有更好的耐热性、透明性，更低的水汽透过率和氧气透过率，另一方面也减少了封装组合物在固化时所产生过多的收缩体积，将其用于OLED器件的薄膜封装，能够有效阻隔水和氧气，提高了可靠性，且进一步延长了OLED器件的使用寿命。
进一步的，Y1、Y2独立地选自如下列化学结构式2至式4中的任意一种：
Figure BDA0003894336760000041
其中，
Figure BDA0003894336760000042
为连接位置。
进一步的，所述式1的具体结构为F-01～F-85中的任意一种：
Figure BDA0003894336760000051
Figure BDA0003894336760000061
Figure BDA0003894336760000071
Figure BDA0003894336760000081
本发明的第二个目的在于提供一种光固化组合物。
采用如下技术方案：
一种光固化组合物，包括以下质量分数的组分：
9.5～90wt％的含硅单体、9.5～90wt％的光固化单体和0.5～10wt％的光交联引发剂。
进一步的，所述光交联引发剂至少为苯乙酮系化合物、二苯甲酮系化合物、噻吨酮系化合物、苯偶姻系化合物、三嗪系化合物中的一种。
更进一步的，所述苯乙酮系化合物为2,2'-二乙氧基苯乙酮，2,2'-二丁氧基苯乙酮，2-羟基-2-甲基苯乙酮，对丁基三氯苯乙酮，叔丁基二氯苯乙酮，4-氯苯乙酮，2,2'-二氯-4-苯氧基苯乙酮，2-甲基-1-(4-(甲硫基)苯基)-2-吗啉代丙烷-1-酮，2-苄基-2-二甲基氨基-1-(4-吗啉代苯基)-丁丹-1-酮中的一种或几种。
进一步的，所述光固化单体为可光固化的丙烯酸类化合物，且所述丙烯酸类化合物为2-苯氧乙基丙烯酸，2-苯氧乙基(甲基)丙烯酸，3-苯氧基丙基丙烯酸，3-苯氧基丙基(甲基)丙烯酸，4-苯氧基丁基丙烯酸，4-苯氧基丁基(甲基)丙烯酸，5-苯氧基戊基丙烯酸，5-苯氧基戊基(甲基)丙烯酸，6-苯氧基己基丙烯酸，6-苯氧基己基(甲基)丙烯酸，7-苯氧基庚基丙烯酸，7-苯氧基庚基(甲基)丙烯酸，8-苯氧基辛基丙烯酸，8-苯氧基辛基(甲基)丙烯酸，9-苯氧基壬基丙烯酸，9-苯氧基壬基(甲基)丙烯酸，10-苯氧基癸基丙烯酸，10-苯氧基癸基(甲基)丙烯酸，2-(苯硫基)乙基丙烯酸，2-(苯硫基)乙基(甲基)丙烯酸，3-(苯硫基)丙基丙烯酸，3-(苯硫基)丙基(甲基)丙烯酸，4-(苯硫基)丁基丙烯酸，4-(苯硫基)丁基(甲基)丙烯酸,5-(苯硫基)戊基丙烯酸，5-(苯硫基)戊基(甲基)丙烯酸，6-(苯硫基)己基丙烯酸，6-(苯硫基)己基(甲基)丙烯酸，7-(苯硫基)庚基丙烯酸，7-(苯硫基)庚基(甲基)丙烯酸，8-(苯硫基)辛基丙烯酸，8-(苯硫基)辛基(甲基)丙烯酸，9-(苯硫基)壬基丙烯酸，9-(苯硫基)壬基(甲基)丙烯酸，10-(苯硫基)癸基丙烯酸，10-(苯硫基)癸基(甲基)丙烯酸，2-(萘-2-基氧基)乙基丙烯酸，2-(萘-2-基氧基)乙基(甲基)丙烯酸，3-(萘-2-基氧基)丙基丙烯酸，3-(萘-2-基氧基)丙基(甲基)丙烯酸，4-(萘-2-基氧基)丁基丙烯酸，4-(萘-2-基氧基)丁基(甲基)丙烯酸，5-(萘-2-基氧基)戊基丙烯酸，5-(萘-2-基氧基)戊基(甲基)丙烯酸，6-(萘-2-基氧基)己基丙烯酸，6-(萘-2-基氧基)己基(甲基)丙烯酸，7-(萘-2-基氧基)庚基丙烯酸，7-(萘-2-基氧基)庚基(甲基)丙烯酸，8-(萘-2-基氧基)辛基丙烯酸，8-(萘-2-基氧基)辛基(甲基)丙烯酸，9-(萘-2-基氧基)壬基丙烯酸，9-(萘-2-基氧基)壬基(甲基)丙烯酸，10-(萘-2-基氧基)癸基丙烯酸，10-(萘-2-基氧基)癸基(甲基)丙烯酸，2-(萘-2-基硫代)乙基丙烯酸，2-(萘-2-基硫代)乙基(甲基)丙烯酸，3-(萘-2-基硫代)丙基丙烯酸，3-(萘-2-基硫代)丙基(甲基)丙烯酸，4-(萘-2-基硫代)丁基丙烯酸，4-(萘-2-基硫代)丁基(甲基)丙烯酸，5-(萘-2-基硫代)戊基丙烯酸，5-(萘-2-基硫代)戊基(甲基)丙烯酸，6-(萘-2-基硫代)己基丙烯酸，6-(萘-2-基硫代)己基(甲基)丙烯酸，7-(萘-2-基硫代)庚基，丙烯酸，7-(萘-2-基硫代)庚基(甲基)丙烯酸，8-(萘-2-基硫代)辛基丙烯酸，8-(萘-2-基硫代)辛基(甲基)丙烯酸，9-(萘-2-基硫代)壬基丙烯酸，9-(萘-2-基硫代)壬基(甲基)丙烯酸，10-(萘-2-基硫代)癸基丙烯酸，10-(萘-2-基硫代)癸基(甲基)丙烯酸，2-([1,1'-联苯基]-4-基氧基)乙基丙烯酸，2-([1,1'-联苯基]-4-基氧基)乙基(甲基)丙烯酸，3-([1,1'-联苯基]-4-基氧基)丙基丙烯酸，3-([1,1'-联苯基]-4-基氧基)丙基(甲基)丙烯酸，4-([1,1'-联苯基]-4-基氧基)丁基丙烯酸，4-([1,1'-联苯基]-4-基氧基)丁基(甲基)丙烯酸，5-([1,1'-联苯基]-4-基氧基)戊基丙烯酸，5-([1,1'-联苯基]-4-基氧基)戊基(甲基)丙烯酸，6-([1,1'-联苯基]-4-基氧基)己基丙烯酸，6-([1,1'-联苯基]-4-基氧基)己基(甲基)丙烯酸，7-([1,1'-联苯基]-4-基氧基)庚基丙烯酸，7-([1,1'-联苯基]-4-基氧基)庚基(甲基)丙烯酸，8-([1,1'-联苯基]-4-基氧基)辛基丙烯酸，8-([1,1'-联苯基]-4-基氧基)辛基(甲基)丙烯酸，9-([1,1'-联苯基]-4-基氧基)壬基丙烯酸，9-([1,1'-联苯基]-4-基氧基)壬基(甲基)丙烯酸，10-([1,1'-联苯基]-4-基氧基)癸基丙烯酸，10-([1,1'-联苯基]-4-基氧基)癸基(甲基)丙烯酸，2-([1,1'-联苯基]-4-基硫代)乙基丙烯酸，2-([1,1'-联苯基]-4-基硫代)乙基(甲基)丙烯酸，3-([1,1'-联苯基]-4-基硫代)丙基丙烯酸，3-([1,1'-联苯基]-4-基硫代)丙基(甲基)丙烯酸，4-([1,1'-联苯基]-4-基硫代)丁基丙烯酸，4-([1,1'-联苯基]-4-基硫代)丁基(甲基)丙烯酸，5-([1,1'-联苯基]-4-基硫代)戊基丙烯酸，5-([1,1'-联苯基]-4-基硫代)戊基(甲基)丙烯酸，6-([1,1'-联苯基]-4-基硫代)己基丙烯酸,6-([1,1'-联苯基]-4-基硫代)己基(甲基)丙烯酸，7-([1,1'-联苯基]-4-基硫代)庚基丙烯酸，7-([1,1'-联苯基]-4-基硫代)庚基(甲基)丙烯酸，8-([1,1'-联苯基]-4-基硫代)辛基丙烯酸，8-([1,1'-联苯基]-4-基硫代)辛基(甲基)丙烯酸，9-([1,1'-联苯基]-4基硫代)壬基丙烯酸，9-([1,1'-联苯基]-4-基硫代)壬基(甲基)丙烯酸，10-([1,1'-联苯基]-4-基硫代)癸基丙烯酸，10-([1,1'-联苯基]-4-基硫代)癸基(甲基)丙烯酸，2-羟基-2-苯氧基乙基丙烯酸，2-羟基-2-苯氧基乙基(甲基)丙烯酸，2-羟基-2-(萘-2-基氧基)乙基丙烯酸，2-羟基-2-(萘-2-基氧基)乙基(甲基)丙烯酸，2-([1,1'-联苯基]-4-基氧基)乙基丙烯酸，2-([1,1'-联苯基]-4基氧基)乙基(甲基)丙烯酸，2-(2-苯氧基乙氧基)乙基丙烯酸，2-(2-苯氧基乙氧基)乙基(甲基)丙烯酸，2-(苯氧基甲氧基)乙基丙烯酸，2-(苯氧基甲氧基)乙基(甲基)丙烯酸，2-(([1,1'-联苯基]-4-基氧基)甲氧基)乙基丙烯酸，2-(([1,1'-联苯基]-4-基氧基)甲氧基)乙基(甲基)丙烯酸，2-((萘-2-基氧基)甲氧基)乙基丙烯酸，2-((萘-2-基氧基)甲氧基)乙基(甲基)丙烯酸，2-((苯硫基)甲氧基)乙基丙烯酸，2-((苯硫基)甲氧基)乙基(甲基)丙烯酸，2-((萘-2-基硫代)甲氧基)乙基丙烯酸，2-((萘-2-基硫代)甲氧基)乙基(甲基)丙烯酸，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1次苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(3,3'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸),2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸酯)，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，聚酯型氨基甲酸酯二丙烯酸脂，树丙烯二丙烯酸，聚酯型氨基甲酸酯，环氧基丙烯酸，苯硫基乙基(甲基)丙烯酸，丙烯酸异壬酯，苯氧基-2-甲基-(甲基)丙烯酸乙酯，丙烯酸苯氧基苄酯，3-戊氧基-2-甲基-乙基(甲基)丙烯酸，苯氧基苯甲醇，3-苯氧基-2-硬脂氧基(甲基)丙烯酸酯，2-1-萘基氧基乙基(甲基)丙烯酸，2-2-萘基氧基乙基(甲基)丙烯酸，2-1-乙二醇丙烯酸酯，2-2-乙二醇丙烯酸酯，三甲醇丙烷丙烯酸酯，1,12-十二烷二醇二甲基丙烯酸酯，1,6-乙烷二烯酸酯，1,10-癸二醇二丙烯酸酯，1,11-十一烷二醇二甲基丙烯酸酯中的一种或几种。
本发明的第三个目的在于提供一种封装薄膜。
采用如下技术方案：
一种封装薄膜，所述封装薄膜是通过无机层和有机层多次堆叠而成；其中，
所述有机层部分或全部包含上述的光固化组合物；
所述无机层的材料至少为氮化硅、氮氧化硅、氧化硅、氧化铝、氧化锆、氧化钛、氧化锌中的一种。
需要说明的是，有机层可通过喷墨打印的方式将光固化组合物沉积在待封装物上，然后通过紫外固化成膜；无机层可通过CVD方法沉积在有机膜表面。
本发明的第四个目的在于提高一种有机电致发光器件。
采用如下技术方案：
一种有机电致发光器件，包括：有机发光二极管和设置在所述有机发光二极管上的薄膜封装层；
所述薄膜封装层为如上所述的封装薄膜。
具体的，本发明提供的硅体单体和光固化组合物可用于柔性OLED显示器件的封装，所述的柔性OLED器件主要包含：有机发光二极管、封装所用无机层和有机层叠加而成。OLED器件装置包括基板ITO，形成于基板上的用于装置的器件(有机发光二级管)和形成于封装构件上并且包括无机阻挡层SiNx、有机阻挡层(光固化组合物)、无机阻挡层SiNX叠层而成。
与现有技术相比，本发明提供的含硅单体，含有刚性基团的芳环和Si原子，相比于不含苯环和硅原子的单体具有更好的耐热性、透明性，更低的水汽透过率和氧气透过率，另一方面也减少了封装组合物在固化时所产生过多的收缩体积，将其用于OLED器件的薄膜封装，能够有效阻隔水和氧气，提高了可靠性，且进一步延长了OLED器件的使用寿命。
具体实施方式
下面将结合本发明实施例对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本说明书中各个实施例采用递进的方式描述，每个实施例重点说明的都是与其他实施例的不同之处，各个实施例之间相同相似部分互相参见即可。对于实施例公开的装置而言，由于其与实施例公开的方法相对应，所以描述的比较简单，相关之处参见方法部分说明即可。
实施例1：一种封装薄膜的制备方法，包括以下步骤：
步骤S1：有机层材料的处理
其中含硅单体F-01、光固化单体7-(萘-2-基氧基)庚基丙烯酸，交联引发剂2,2'-二乙氧基苯乙酮；
称取20g的F-01、75g的7-(萘-2-基氧基)庚基丙烯酸以及5g的2,2'-二乙氧基苯乙酮混合到一起，在50℃的真空下搅拌80h，然后用针筒过滤器进行过滤，使用粒子计数器进行检测，当检测到粒径大于0.5μm的粒子数不多于50个时，得到处理后的有机层材料；
步骤S2：选用氮化硅作为无机层材料；
步骤S3：无机层的制备
通过CVD的方法将无机层材料涂装在待封装物表面形成无机层；
步骤S4：有机层的制备
将处理后的有机层材料用喷墨打印机进行无机层表面的喷涂，形成有机层，用100mW/cm2，每次10秒的紫外光照射促有机层使有机层硬化；
步骤S5：封装薄膜的形成
按照无机层和有机层…无机层交替的形式进行待封装物表面的沉积涂装，最终沉积涂装在待封装物表面的有无机层和有机层…无机层即为封装薄膜。
实施例2：一种封装薄膜的制备方法，包括以下步骤：
步骤S1中：其中含硅单体F-01换成F-02、光固化单体7-(萘-2-基氧基)庚基丙烯酸换成2-2-萘基氧基乙基(甲基)丙烯酸，交联引发剂2,2'-二乙氧基苯乙酮换成2-甲基-1-(4-(甲硫基)苯基)-2-吗啉代丙烷-1-酮，其他与实施例1相同。
实施例3-实施例10：
按照与实施例1-实施例2类似的方法制备化合物F-04、F-08、F-11、F-12、F-16、F-20、F-25、F-30，分别记为实施例3-实施例10。
实施例11：
步骤S1中：20g的含硅单体F-01替换成30g含硅单体F-01、75g的7-(萘-2-基氧基)庚基丙烯酸替换成65g的7-(萘-2-基氧基)庚基丙烯酸，其他与实施例1相同。
实施例12-实施例20：
按照与实施例11类似的方法制备化合物F-05、F-09、F-15、F-23、F-33、F-35、F-40、F-45，F-50分别记为实施例12-实施例20。
比较例1：
其将上述实施例1中的含硅单体F-01质量分数改为0g，光固化单体7-(萘-2-基氧基)庚基丙烯酸质量分数改为95g及引发剂2,2'-二乙氧基苯乙酮质量分数改为3g，混合到一起，在50℃的真空下搅拌80h，然后用针筒过滤器进行过滤，使用粒子计数器进行测，当检测到粒径大于0.5μm的粒子数不多于50个时，得到光固化组合物。
试验例1：
对实施例1-20及比较例1的封装薄膜进行水蒸气透过率检测，检测仪器：厂家为美国MOCON公司(美国膜康公司)，型号为AQUARAN2的高精度水蒸气透过率测试仪；检测条件：温度85℃，相对湿度85％；检测时长：24小时；
对实施例1-20及比较例1的封装薄膜进行透光率检测，检测仪器：透光率测试仪；检测条件：温度40℃，相对湿度85％；结果如表1所示。
表1
Figure BDA0003894336760000191
Figure BDA0003894336760000201
通过实施例1-20和比较例1中制备的封装薄膜进行了水蒸气透过率的检测，其中加入本发明实施例提供的含硅单体后的封装薄膜的水蒸气透过率较未加入含硅单体的封装薄膜水蒸气透过率明显降低；且通过对表1中各实施例的对比也可以说明以上问题，由此表明，通过以上的封装薄膜封装有机发光器件，能够有效隔绝水气，延长有机发光器件的实用寿命。
本发明还提供了一种显示装置，其封装由上述的封装薄膜。具体的，显示装置可以为有机发光二极管等有机发光器件，其可包括基板(可采用氧化铟锡等)、形成于基板上的有机发光二级管以及封装在有机发光二级管上的上述实施例所提供的封装薄膜。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。

Claims (9)

1.一种含硅单体，其特征在于，具有式1所示结构：
A1-R3-Y2-R2-L1-X-L2-R1-Y1-R4-A2
式1，
其中，
X独立选自O、N、S；
L1、L2各自独立地选自单键、C1-C20烷基、C1-C20烷氧基、C1-C10烯基、C1-C10炔基、C6-C30芳基、C3-C20环烷基或4元-30元杂芳基；且L1和L2至少有一个是芳基或杂芳基；
R1、R2独立地选自氢，取代或未取代的C1-C10烷基，取代或未取代的C3-C20环烷基，取代或未取代的C1-C10羟烷基，取代的或未取代的C6-C20芳基，取代或未取代的2元-20元杂芳基，取代或未取代的C2-C10链烯基，取代或未取代的C1-C10烷氧基；且R1、R2不能同时为氢；
R3、R4为取代或未取代的C1-C10烷基，取代或未取代的C3-C20环烷基，取代或未取代的C1-C10羟烷基，取代的或未取代的C6-C20芳基，取代或未取代的2元-20元杂芳基，取代或未取代的C2-C10链烯基，取代或未取代的C1-C10烷氧基；
Y1、Y2独立地选自单键、氧、被烷基取代或未取代的氨基或硫；
A1、A2独立地选自取代的丙烯酸酯基或未取代的丙烯酸酯基，其结构通式为式5：
Figure FDA0003894336750000011
其中，“*”为连接位置，Z选自H原子、取代或者未取代的碳原子小于20的烷基、碳原子小于20的烷氧基。
2.根据权利要求1所述的一种含硅单体，其特征在于，Y1、Y2独立地选自如下列化学结构式2至式4中的任意一种：
Figure FDA0003894336750000021
其中，
Figure FDA0003894336750000022
为连接位置。
3.根据权利要求1所述的一种含硅单体，其特征在于，所述式1的具体结构为F-01～F-85中的任意一种：
Figure FDA0003894336750000031
Figure FDA0003894336750000041
Figure FDA0003894336750000051
Figure FDA0003894336750000061
4.一种光固化组合物，其特征在于，包括以下质量分数的组分：
9.5～90wt％的含硅单体、9.5～90wt％的光固化单体和0.5～10wt％的光交联引发剂；其中，
所述含硅单体为权利要求1～3所述的含硅单体。
5.根据权利要求4所述的光固化组合物，其特征在于，所述光交联引发剂至少为苯乙酮系化合物、二苯甲酮系化合物、噻吨酮系化合物、苯偶姻系化合物、三嗪系化合物中的一种。
6.根据权利要求5所述的光固化组合物，其特征在于，所述苯乙酮系化合物为2,2'-二乙氧基苯乙酮，2,2'-二丁氧基苯乙酮，2-羟基-2-甲基苯乙酮，对丁基三氯苯乙酮，叔丁基二氯苯乙酮，4-氯苯乙酮，2,2'-二氯-4-苯氧基苯乙酮，2-甲基-1-(4-(甲硫基)苯基)-2-吗啉代丙烷-1-酮，2-苄基-2-二甲基氨基-1-(4-吗啉代苯基)-丁丹-1-酮中的一种或几种。
7.根据权利要求4所述的光固化组合物，其特征在于，所述光固化单体为可光固化的丙烯酸类化合物，且所述丙烯酸类化合物为2-苯氧乙基丙烯酸，2-苯氧乙基(甲基)丙烯酸，3-苯氧基丙基丙烯酸，3-苯氧基丙基(甲基)丙烯酸，4-苯氧基丁基丙烯酸，4-苯氧基丁基(甲基)丙烯酸，5-苯氧基戊基丙烯酸，5-苯氧基戊基(甲基)丙烯酸，6-苯氧基己基丙烯酸，6-苯氧基己基(甲基)丙烯酸，7-苯氧基庚基丙烯酸，7-苯氧基庚基(甲基)丙烯酸，8-苯氧基辛基丙烯酸，8-苯氧基辛基(甲基)丙烯酸，9-苯氧基壬基丙烯酸，9-苯氧基壬基(甲基)丙烯酸，10-苯氧基癸基丙烯酸，10-苯氧基癸基(甲基)丙烯酸，2-(苯硫基)乙基丙烯酸，2-(苯硫基)乙基(甲基)丙烯酸，3-(苯硫基)丙基丙烯酸，3-(苯硫基)丙基(甲基)丙烯酸，4-(苯硫基)丁基丙烯酸，4-(苯硫基)丁基(甲基)丙烯酸,5-(苯硫基)戊基丙烯酸，5-(苯硫基)戊基(甲基)丙烯酸，6-(苯硫基)己基丙烯酸，6-(苯硫基)己基(甲基)丙烯酸，7-(苯硫基)庚基丙烯酸，7-(苯硫基)庚基(甲基)丙烯酸，8-(苯硫基)辛基丙烯酸，8-(苯硫基)辛基(甲基)丙烯酸，9-(苯硫基)壬基丙烯酸，9-(苯硫基)壬基(甲基)丙烯酸，10-(苯硫基)癸基丙烯酸，10-(苯硫基)癸基(甲基)丙烯酸，2-(萘-2-基氧基)乙基丙烯酸，2-(萘-2-基氧基)乙基(甲基)丙烯酸，3-(萘-2-基氧基)丙基丙烯酸，3-(萘-2-基氧基)丙基(甲基)丙烯酸，4-(萘-2-基氧基)丁基丙烯酸，4-(萘-2-基氧基)丁基(甲基)丙烯酸，5-(萘-2-基氧基)戊基丙烯酸，5-(萘-2-基氧基)戊基(甲基)丙烯酸，6-(萘-2-基氧基)己基丙烯酸，6-(萘-2-基氧基)己基(甲基)丙烯酸，7-(萘-2-基氧基)庚基丙烯酸，7-(萘-2-基氧基)庚基(甲基)丙烯酸，8-(萘-2-基氧基)辛基丙烯酸，8-(萘-2-基氧基)辛基(甲基)丙烯酸，9-(萘-2-基氧基)壬基丙烯酸，9-(萘-2-基氧基)壬基(甲基)丙烯酸，10-(萘-2-基氧基)癸基丙烯酸，10-(萘-2-基氧基)癸基(甲基)丙烯酸，2-(萘-2-基硫代)乙基丙烯酸，2-(萘-2-基硫代)乙基(甲基)丙烯酸，3-(萘-2-基硫代)丙基丙烯酸，3-(萘-2-基硫代)丙基(甲基)丙烯酸，4-(萘-2-基硫代)丁基丙烯酸，4-(萘-2-基硫代)丁基(甲基)丙烯酸，5-(萘-2-基硫代)戊基丙烯酸，5-(萘-2-基硫代)戊基(甲基)丙烯酸，6-(萘-2-基硫代)己基丙烯酸，6-(萘-2-基硫代)己基(甲基)丙烯酸，7-(萘-2-基硫代)庚基，丙烯酸，7-(萘-2-基硫代)庚基(甲基)丙烯酸，8-(萘-2-基硫代)辛基丙烯酸，8-(萘-2-基硫代)辛基(甲基)丙烯酸，9-(萘-2-基硫代)壬基丙烯酸，9-(萘-2-基硫代)壬基(甲基)丙烯酸，10-(萘-2-基硫代)癸基丙烯酸，10-(萘-2-基硫代)癸基(甲基)丙烯酸，2-([1,1'-联苯基]-4-基氧基)乙基丙烯酸，2-([1,1'-联苯基]-4-基氧基)乙基(甲基)丙烯酸，3-([1,1'-联苯基]-4-基氧基)丙基丙烯酸，3-([1,1'-联苯基]-4-基氧基)丙基(甲基)丙烯酸，4-([1,1'-联苯基]-4-基氧基)丁基丙烯酸，4-([1,1'-联苯基]-4-基氧基)丁基(甲基)丙烯酸，5-([1,1'-联苯基]-4-基氧基)戊基丙烯酸，5-([1,1'-联苯基]-4-基氧基)戊基(甲基)丙烯酸，6-([1,1'-联苯基]-4-基氧基)己基丙烯酸，6-([1,1'-联苯基]-4-基氧基)己基(甲基)丙烯酸，7-([1,1'-联苯基]-4-基氧基)庚基丙烯酸，7-([1,1'-联苯基]-4-基氧基)庚基(甲基)丙烯酸，8-([1,1'-联苯基]-4-基氧基)辛基丙烯酸，8-([1,1'-联苯基]-4-基氧基)辛基(甲基)丙烯酸，9-([1,1'-联苯基]-4-基氧基)壬基丙烯酸，9-([1,1'-联苯基]-4-基氧基)壬基(甲基)丙烯酸，10-([1,1'-联苯基]-4-基氧基)癸基丙烯酸，10-([1,1'-联苯基]-4-基氧基)癸基(甲基)丙烯酸，2-([1,1'-联苯基]-4-基硫代)乙基丙烯酸，2-([1,1'-联苯基]-4-基硫代)乙基(甲基)丙烯酸，3-([1,1'-联苯基]-4-基硫代)丙基丙烯酸，3-([1,1'-联苯基]-4-基硫代)丙基(甲基)丙烯酸，4-([1,1'-联苯基]-4-基硫代)丁基丙烯酸，4-([1,1'-联苯基]-4-基硫代)丁基(甲基)丙烯酸，5-([1,1'-联苯基]-4-基硫代)戊基丙烯酸，5-([1,1'-联苯基]-4-基硫代)戊基(甲基)丙烯酸，6-([1,1'-联苯基]-4-基硫代)己基丙烯酸,6-([1,1'-联苯基]-4-基硫代)己基(甲基)丙烯酸，7-([1,1'-联苯基]-4-基硫代)庚基丙烯酸，7-([1,1'-联苯基]-4-基硫代)庚基(甲基)丙烯酸，8-([1,1'-联苯基]-4-基硫代)辛基丙烯酸，8-([1,1'-联苯基]-4-基硫代)辛基(甲基)丙烯酸，9-([1,1'-联苯基]-4基硫代)壬基丙烯酸，9-([1,1'-联苯基]-4-基硫代)壬基(甲基)丙烯酸，10-([1,1'-联苯基]-4-基硫代)癸基丙烯酸，10-([1,1'-联苯基]-4-基硫代)癸基(甲基)丙烯酸，2-羟基-2-苯氧基乙基丙烯酸，2-羟基-2-苯氧基乙基(甲基)丙烯酸，2-羟基-2-(萘-2-基氧基)乙基丙烯酸，2-羟基-2-(萘-2-基氧基)乙基(甲基)丙烯酸，2-([1,1'-联苯基]-4-基氧基)乙基丙烯酸，2-([1,1'-联苯基]-4基氧基)乙基(甲基)丙烯酸，2-(2-苯氧基乙氧基)乙基丙烯酸，2-(2-苯氧基乙氧基)乙基(甲基)丙烯酸，2-(苯氧基甲氧基)乙基丙烯酸，2-(苯氧基甲氧基)乙基(甲基)丙烯酸，2-(([1,1'-联苯基]-4-基氧基)甲氧基)乙基丙烯酸，2-(([1,1'-联苯基]-4-基氧基)甲氧基)乙基(甲基)丙烯酸，2-((萘-2-基氧基)甲氧基)乙基丙烯酸，2-((萘-2-基氧基)甲氧基)乙基(甲基)丙烯酸，2-((苯硫基)甲氧基)乙基丙烯酸，2-((苯硫基)甲氧基)乙基(甲基)丙烯酸，2-((萘-2-基硫代)甲氧基)乙基丙烯酸，2-((萘-2-基硫代)甲氧基)乙基(甲基)丙烯酸，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1次苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)二丙烯酸，3,3'-(4,4'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(4,1-次苯基))双(氧基)双(丙烷-3,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(9H-芴-9,9-二烯)双(4,1-次苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,-1二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(3,3'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(3,3'-(4,4'-氧基双(4,1-亚苯基)双(二烯))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(3,3'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(丙烷-3,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸),2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(氧基)双(乙烷-2,1二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-(丙烷-2,2-二烯)双(4,1-亚苯基))双(二烯)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-氧基双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸酯)，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(氧基))双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)二丙烯酸，2,2'-(2,2'-(2,2'-(4,4'-硫代双(4,1-亚苯基)双(二烯))双(乙烷-2,1-二烯)双(氧基)双(乙烷-2,1-二烯))双(氧基)双(乙烷-2,1-二烯)双(2-甲基丙烯酸)，聚酯型氨基甲酸酯二丙烯酸脂，树丙烯二丙烯酸，聚酯型氨基甲酸酯，环氧基丙烯酸，苯硫基乙基(甲基)丙烯酸，丙烯酸异壬酯，苯氧基-2-甲基-(甲基)丙烯酸乙酯，丙烯酸苯氧基苄酯，3-戊氧基-2-甲基-乙基(甲基)丙烯酸，苯氧基苯甲醇，3-苯氧基-2-硬脂氧基(甲基)丙烯酸酯，2-1-萘基氧基乙基(甲基)丙烯酸，2-2-萘基氧基乙基(甲基)丙烯酸，2-1-乙二醇丙烯酸酯，2-2-乙二醇丙烯酸酯，三甲醇丙烷丙烯酸酯，1,12-十二烷二醇二甲基丙烯酸酯，1,6-乙烷二烯酸酯，1,10-癸二醇二丙烯酸酯，1,11-十一烷二醇二甲基丙烯酸酯中的一种或几种。
8.一种封装薄膜，其特征在于，所述封装薄膜是通过无机层和有机层多次堆叠而成；其中，
所述有机层部分或全部包含如权利要求4所述的光固化组合物；
所述无机层的材料至少为氮化硅、氮氧化硅、氧化硅、氧化铝、氧化锆、氧化钛、氧化锌中的一种。
9.一种有机电致发光器件，其特征在于，包括：有机发光二极管和设置在所述有机发光二极管上的薄膜封装层；
所述薄膜封装层为如权利要求8所述的封装薄膜。
CN202211268976.8A 2022-10-17 2022-10-17 一种含硅单体、光固化组合物、封装薄膜及包含其的有机电致发光器件 Pending CN115521230A (zh)