CN115029019A - 一种钛白粉生产中有机包膜剂的添加工艺 - Google Patents

一种钛白粉生产中有机包膜剂的添加工艺 Download PDF

Info

Publication number
CN115029019A
CN115029019A CN202210816639.1A CN202210816639A CN115029019A CN 115029019 A CN115029019 A CN 115029019A CN 202210816639 A CN202210816639 A CN 202210816639A CN 115029019 A CN115029019 A CN 115029019A
Authority
CN
China
Prior art keywords
titanium dioxide
coating agent
organic coating
filter cake
organic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202210816639.1A
Other languages
English (en)
Inventor
朱左美
和奔流
赵波
刘红星
刘峰
何正波
邓吉周
许有保
杨春成
文张彪
代朝永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Longbai Lufeng Titanium Industry Co ltd
Original Assignee
Longbai Lufeng Titanium Industry Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Longbai Lufeng Titanium Industry Co ltd filed Critical Longbai Lufeng Titanium Industry Co ltd
Priority to CN202210816639.1A priority Critical patent/CN115029019A/zh
Publication of CN115029019A publication Critical patent/CN115029019A/zh
Pending legal-status Critical Current

Abstract

本发明属于钛白粉生产技术领域，具体涉及一种钛白粉生产中有机包膜剂的添加工艺。本发明在钛白粉滤饼上添加有机包膜剂进行预包膜，在汽粉工段后再进行一次包膜，经过两次包膜，可提高有机包膜的质量，避免因包膜剂添加不均匀导致部分钛白粉未进行到有机包膜，并且将钛白粉滤饼和有机包膜剂加入到进料罐中进行搅拌，利用搅拌将钛白粉滤饼与有机包膜剂充分混合搅拌均匀再进行干燥，干燥后的物料因为添加了有机硅油，可提高钛白粉在生产线上的流动性，解决了在输送过程中钛白粉物料容易在管道或者储存仓内堆积，堵塞管道影响生产的问题。

Description

一种钛白粉生产中有机包膜剂的添加工艺
技术领域
本发明属于钛白粉生产技术领域，具体涉及一种钛白粉生产中有机包膜剂的添加工艺。
背景技术
钛白粉的包膜分为有机包膜和无机包膜，其中有机包膜一般在汽粉工序进行，在现有技术中进行有机包膜的过程在瞬间完成，并且只进行一次包膜，因此经常会出现包膜剂添加不够或者包不到的情况，最终影响产品质量。并且在钛白粉生产过程中，从闪蒸干燥工序开始物料变为干燥粉状，在输送过程中物料也容易在管道或者储存仓内堆积，堵塞管道影响生产。
发明内容
针对现有技术中的问题，本发明提供了一种钛白粉生产中有机包膜剂的添加工艺。
本发明采用的技术方案如下：
一种钛白粉生产中有机包膜剂的添加工艺，包括钛白粉的生产工艺，包括以下步骤：
步骤1：将钛白粉滤饼和有机包膜剂加入到进料罐中进行搅拌，通过搅拌将钛白粉滤饼打散，使钛白粉与有机包膜剂混合均匀对钛白粉进行第一次包膜；
步骤2：将步骤1得到的钛白粉输送到闪蒸干燥工段进行干燥；
步骤3：将步骤2得到的钛白粉输送到汽粉工段进行粉碎；
步骤4：通过管道将步骤3得到的钛白粉输送到下一工段，并在所述管道内添加有机包膜剂对钛白粉进行第二次包膜。
采用该技术方案后，将钛白粉滤饼和有机包膜剂加入到进料罐中进行搅拌，利用搅拌将钛白粉滤饼与有机包膜剂充分混合搅拌均匀再进行干燥，干燥后的物料因为添加了有机包膜剂，可提高钛白粉在生产线上的流动性，解决了在输送过程中钛白粉物料容易在管道或者储存仓内堆积，堵塞管道影响生产的问题，在钛白粉滤饼上添加有机硅油进行预包膜，在汽粉工段后再进行一次包膜，经过两次包膜，可提高有机包膜的质量，避免因包膜剂添加不均匀导致部分钛白粉未进行到有机包膜。
作为优选，步骤1中的有机包膜剂的添加量为钛白粉滤饼的质量的千分之一到千分之二。
作为优选，所述有机包膜剂为有机硅油。
作为优选，步骤2中钛白粉通过闪蒸干燥工段的干燥塔进行干燥。
作为优选，步骤3中钛白粉通过汽粉工段的汽粉粉碎机进行粉碎。
综上所述，由于采用了上述技术方案，本发明的有益效果是：
1.将钛白粉滤饼和有机包膜剂加入到进料罐中进行搅拌，利用搅拌将钛白粉滤饼与有机包膜剂充分混合搅拌均匀再进行干燥，干燥后的物料因为添加了有机硅油，可提高钛白粉在生产线上的流动性。
2.在钛白粉滤饼上添加有机硅油进行预包膜，在汽粉工段后再进行一次包膜，经过两次包膜，可提高有机包膜的质量，避免因包膜剂添加不均匀导致部分钛白粉未进行到有机包膜。
附图说明
图1为本发明的工艺流程图。
具体实施方式
为使本申请实施例的目的、技术方案和优点更加清楚，下面将结合本申请实施例中附图，对本申请实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本申请一部分实施例，而不是全部的实施例。因此，以下对在附图中提供的本申请的实施例的详细描述并非旨在限制要求保护的本申请的范围，而是仅仅表示本申请的选定实施例。基于本申请的实施例，本领域技术人员在没有做出创造性劳动的前提下所获得的所有其他实施例，都属于本申请保护的范围。
实施例1
参照图1，一种钛白粉生产中有机包膜剂的添加工艺，包括钛白粉的生产工艺，包括以下步骤：
步骤1：将钛白粉滤饼和有机硅油加入到进料罐中进行搅拌，有机包膜剂的添加量为钛白粉滤饼的质量的千分之一，通过搅拌将钛白粉滤饼打散，使钛白粉与有机包膜剂混合均匀对钛白粉进行第一次包膜；
步骤2：将步骤1得到的钛白粉输送到闪蒸干燥工段的干燥塔进行干燥；
步骤3：将步骤2得到的钛白粉输送到汽粉工段的汽粉粉碎机进行粉碎；
步骤4：通过管道将步骤3得到的钛白粉输送到下一工段，并在所述管道内添加有机硅油对钛白粉进行第二次包膜。
本实施例中，未记载的钛白粉的生产工艺均为现有技术，不为本发明的发明点所在，因此不再赘述。
实施例2
本实施例与实施例1的工艺步骤基本相同，不同之处在于，本实施例中有机包膜剂的添加量为钛白粉滤饼的质量的千分之二。
以上所述实施例仅表达了本申请的具体实施方式，其描述较为具体和详细，但并不能因此而理解为对本申请保护范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本申请技术方案构思的前提下，还可以做出若干变形和改进，这些都属于本申请的保护范围。

Claims (5)

1.一种钛白粉生产中有机包膜剂的添加工艺，包括钛白粉的生产工艺，其特征在于：包括以下步骤：
步骤1：将钛白粉滤饼和有机包膜剂加入到进料罐中进行搅拌，通过搅拌将钛白粉滤饼打散，使钛白粉与有机包膜剂混合均匀对钛白粉进行第一次包膜；
步骤2：将步骤1得到的钛白粉输送到闪蒸干燥工段进行干燥；
步骤3：将步骤2得到的钛白粉输送到汽粉工段进行粉碎；
步骤4：通过管道将步骤3得到的钛白粉输送到下一工段，并在所述管道内添加有机包膜剂对钛白粉进行第二次包膜。
2.根据权利要求1所述的一种钛白粉生产中有机包膜剂的添加工艺，其特征在于：步骤1中的有机包膜剂的添加量为钛白粉滤饼的质量的千分之一到千分之二。
3.根据权利要求1所述的一种钛白粉生产中有机包膜剂的添加工艺，其特征在于：所述有机包膜剂为有机硅油。
4.根据权利要求1所述的一种钛白粉生产中有机包膜剂的添加工艺，其特征在于：步骤2中钛白粉通过闪蒸干燥工段的干燥塔进行干燥。
5.根据权利要求1所述的一种钛白粉生产中有机包膜剂的添加工艺，其特征在于：步骤3中钛白粉通过汽粉工段的汽粉粉碎机进行粉碎。
CN202210816639.1A 2022-07-12 2022-07-12 一种钛白粉生产中有机包膜剂的添加工艺 Pending CN115029019A (zh)