CN114761473A - 树脂发泡体 - Google Patents
树脂发泡体 Download PDFInfo
- Publication number
- CN114761473A CN114761473A CN202080081924.2A CN202080081924A CN114761473A CN 114761473 A CN114761473 A CN 114761473A CN 202080081924 A CN202080081924 A CN 202080081924A CN 114761473 A CN114761473 A CN 114761473A
- Authority
- CN
- China
- Prior art keywords
- resin foam
- resin
- polyolefin
- compression
- foam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供薄、冲击吸收性优异,并且在应用于图像显示装置时能够防止由按压导致的显示不均的树脂发泡体。本发明的树脂发泡体的50%压缩载荷为5N/cm2~30N/cm2、6小时后的压缩应力保持率为50%以上、12小时后的压缩应力保持率为50%以上,并且具有气泡结构。在一个实施方式中,上述树脂发泡体的50%压缩载荷为30N/cm2以下。在一个实施方式中,上述树脂发泡体的压缩模量为200kPa以上。
Description
技术领域
本发明涉及树脂发泡体。
背景技术
作为电子设备的画面保护、基板的保护等的缓冲材料,大多使用树脂发泡体。近年,与电子设备的薄型化倾向相适应,要求缓冲材料即使被配置于间隙窄的位置也能够发挥高冲击吸收性。
另外,在智能手机、移动终端等触摸面板式的液晶显示装置中,以使用者按压画面时产生的凹陷为主要原因,有时会发生液晶面板中的液晶分子的取向紊乱、显示不均(波纹状的渗色图案;所谓伸长图案(pulling))。这样的现象随着近年设备的薄型化倾向特别成为问题,
引用文献1公开了一种冲击吸收性良好、且能够使产生的伸长图案在早期消失的具有耐伸长图案特性的发泡片。然而,即使通过该技术,也难以防止伸长图案本身的产生。另外,专利文献2中公开了一种提高了应力分散性而不易发生面板的显示不均的发泡体,但其对于冲击吸收性没有任何公开。
现有技术文献
专利文献
专利文献1:日本特开2007-016070号公报
专利文献2:国际公开第WO12/133288号公报
发明内容
发明所要解决的问题
本发明的课题在于,提供薄、冲击吸收性优异,并且在应用于图像显示装置时能够防止由按压导致的显示不均的树脂发泡体。
解决问题的方法
本发明的树脂发泡体的50%压缩载荷为5N/cm2~30N/cm2、6小时后的压缩应力保持率为50%以上、12小时后的压缩应力保持率为50%以上,并且具有气泡结构。
在一个实施方式中,上述树脂发泡体的50%压缩载荷为10N/cm2~30N/cm2。
在一个实施方式中,上述树脂发泡体的压缩模量为200kPa以上。
在一个实施方式中,上述树脂发泡体的非发泡弯曲应力为5MPa以上。
在一个实施方式中,上述树脂发泡体的由反复压缩带来的厚度变化率为10%以下。
在一个实施方式中,上述树脂发泡体的表观密度为0.02g/cm3~0.50g/cm3。
在一个实施方式中,上述树脂发泡体的厚度恢复率为75%以上。
在一个实施方式中,上述树脂发泡体所具有的气泡的长径比为1.5以上。
在一个实施方式中,上述树脂发泡体的平均气泡直径为10μm~200μm。
在一个实施方式中,上述树脂发泡体的气泡率为30%以上。
在一个实施方式中,上述树脂发泡体的气泡直径的变动系数为0.5以下。
在一个实施方式中,上述树脂发泡体的气泡壁的厚度为0.1μm~10μm。
在一个实施方式中,上述树脂发泡体包含聚烯烃类树脂。
在一个实施方式中,上述聚烯烃类树脂为除聚烯烃类弹性体以外的聚烯烃与聚烯烃类弹性体的混合物。
在一个实施方式中,在上述树脂发泡体的一面或两面具有热熔融层。
根据本发明的另一方面,提供一种发泡构件,该发泡构件具有树脂发泡层、和配置于该树脂发泡层的至少一侧的粘合剂层,该树脂发泡层是上述树脂发泡体。
发明的效果
能够提供薄、冲击吸收性优异,并且在应用于图像显示装置时能够防止由按压导致的显示不均的树脂发泡体。
附图说明
图1是本发明的一个实施方式的发泡构件的剖面示意图。
图2是应力松弛试验机的剖面示意图。
符号说明
100 发泡构件
10 树脂发泡层
20 粘合剂层
1000 应力松弛试验机
A 铁制的支撑体
200 聚碳酸酯板
300 应力测定膜
400 树脂发泡结构体
500 双面粘接带
600 间隔件
700 ABS板
800 铁球
具体实施方式
A.树脂发泡体
本发明的树脂发泡体的50%压缩载荷为5N/cm2~30N/cm2、6小时后的压缩应力保持率为50%以上、12小时后的压缩应力保持率为50%以上。本发明的树脂发泡体具有气泡结构(气孔结构)。作为气泡结构(气孔结构),可列举独立气泡结构、连续气泡结构、半连续半独立气泡结构(混合存在有独立气泡结构和连续气泡结构的气泡结构)等。树脂发泡体的气泡结构优选为连续气泡结构、或半连续半独立气泡结构,更优选为半连续半独立气泡结构。本发明的树脂发泡体通过使树脂组合物发泡而得到。上述树脂组合物是至少含有构成树脂发泡体的树脂的组合物。
如上所述,本发明的树脂发泡体的50%压缩载荷为5N/cm2~30N/cm2。如果是这样的范围,则能够得到具有适度的硬度、即使在受到高冲击力时也不易发生压缩变形、冲击吸收性优异的树脂发泡体。另外,可以得到能够适度地抑制应用于间隙(特别是空隙窄的间隙)时的反弹力、能够防止对周边构件的不良影响的树脂发泡体。此外,如果50%压缩载荷为上述范围,则可以得到能够防止应用于图像显示装置时由按压导致的显示不均、例如能够在对液晶显示装置进行触摸操作时防止由液晶取向的紊乱导致的颜色不均的树脂发泡体。50%压缩载荷小于5N/cm2时,变得难以发生压缩变形,存在无法防止应用于图像显示装置时由按压导致的显示不均的担忧。树脂发泡体的50%压缩载荷优选为7N/cm2~30N/cm2、更优选为10N/cm2~30N/cm2、进一步优选为10N/cm2~25N/cm2、特别优选为10N/cm2~20N/cm2。如果是这样的范围,则上述效果变得显著。
如上所述,本发明的树脂发泡体的6小时后的压缩应力保持率为50%以上。如果是这样的范围,则能够得到不易变形、而且即使变形也能够理想地恢复的树脂发泡体。这样的树脂发泡体能够防止应用于图像显示装置时由按压导致的显示不均,例如能够防止在对液晶显示装置进行触摸操作时由液晶取向的紊乱导致的颜色不均。树脂发泡体的6小时后的压缩应力保持率优选为60%以上、更优选为70%以上、进一步优选为80%以上。如果是这样的范围,则上述效果变得显著。6小时后的压缩应力保持率的上限例如为95%(优选为98%)。根据以压缩速度10mm/min将30mm×30mm尺寸的试验片刚压缩至压缩率达到50%时的压缩应力(N1)、和保持6小时50%压缩后的压缩应力(N2)并通过式N2/N1×100求出6小时后的压缩应力保持率。
如上所述,本发明的树脂发泡体的12小时后的压缩应力保持率为50%以上。如果是这样的范围,则能够得到不易变形、而且即使变形也能够理想地恢复的树脂发泡体。这样的树脂发泡体能够防止应用于图像显示装置时由按压导致的显示不均,例如能够防止在对液晶显示装置进行触摸操作时由液晶取向的紊乱导致的颜色不均。树脂发泡体的12小时后的压缩应力保持率优选为60%以上、更优选为70%以上、进一步优选为80%以上。如果是这样的范围,则上述效果变得显著。12小时后的压缩应力保持率的上限例如为95%(优选为98%)。根据以压缩速度10mm/min将30mm×30mm尺寸的试验片刚压缩至压缩率达到50%时的压缩应力(N1)、和保持12小时50%压缩后的压缩应力(N2)并通过式N2/N1×100求出12小时后的压缩应力保持率。
本发明的树脂发泡体具有如下特征:通过使50%压缩载荷及压缩应力保持率为上述范围而具有给定的硬度,不易变形,即使变形也容易恢复。这样的树脂发泡体的冲击吸收性优异,并且能够防止对液晶显示装置进行触摸操作时由液晶取向的紊乱导致的颜色不均。
本发明的树脂发泡体的表观密度优选为0.02g/cm3~0.50g/cm3。如果是这样的范围,则能够得到柔软性及应力分散性优异的树脂发泡体。本发明的树脂发泡体的表观密度更优选为0.04g/cm3~0.4g/cm3、进一步优选为0.06g/cm3~0.3g/cm3、更进一步优选为0.08g/cm3~0.25g/cm3、特别优选为0.1g/cm3~0.2g/cm3、最优选为0.13g/cm3~0.2g/cm3。如果是这样的范围,则上述效果变得显著。表观密度的测定方法在后面叙述。
上述树脂发泡体的25%压缩载荷优选为3N/cm2以上。如果是这样的范围,则上述本发明的效果变得显著。树脂发泡体的25%压缩载荷优选为3.2N/cm2以上、更优选为3.5N/cm2以上、进一步优选为4N/cm2以上。树脂发泡体的25%压缩载荷的上限例如为10N/cm2(优选为20N/cm2)。25%压缩载荷的测定方法基于JIS K 6767中记载的发泡体的压缩硬度测定方法。
上述树脂发泡体的压缩模量优选为200kPa以上。如果是这样的范围,则能够得到即使在受到高冲击力时也不易发生压缩变形、不易破碎的树脂发泡体。树脂发泡体的压缩模量优选为220kPa以上、更优选为250kPa以上、进一步优选为300kPa以上。如果是这样的范围,则上述效果变得显著。树脂发泡体的压缩模量的上限优选为1000kPa、更优选为800kPa、进一步优选为600kPa。基于JIS K 6767的压缩试验一项测定树脂发泡体的压缩率(%)、压缩反弹力(kPa),分别读取压缩率5%时的压缩反弹力F(5%)和压缩率15%时的压缩时的反弹力F(15%),根据F(5%)、F(15%)并通过式(F(15%)-F(5%))/(15-5)×100计算出树脂发泡体的压缩模量。
本发明的树脂发泡体在压缩时的弹性应变能优选为10kPa以上。“压缩时的弹性应变能”是指使树脂发泡体压缩10%时的压缩反弹力的总量。具体而言,通过基于JIS K 6767的压缩试验(试验温度:23℃、样品尺寸:10mm×10mm、压缩速度:10mm/min)测定树脂发泡体的压缩率(%)及压缩反弹力(kPa)时,根据将x轴设为压缩率(%)并将y轴设为压缩反弹力(kPa)的压缩ss曲线求出“压缩时的弹性应变能”,该“压缩时的弹性应变能”是在压缩率为0%~10%的范围中、由该ss曲线和该x轴规定的区域的面积。如果树脂发泡体在压缩时的弹性应变能为上述范围,则能够得到冲击吸收性优异的树脂发泡体。更详细而言,具有上述范围的弹性应变能的树脂发泡体在施加冲击时,该树脂发泡体的变形会消耗大量的能量,因此,即使对于强冲击,也能够将其良好地吸收。本发明的树脂发泡体在压缩时的弹性应变能更优选为20kPa以上、进一步优选为30kPa以上、更进一步优选为50kPa以上、再进一步优选为60kPa以上、再进一步更优选为80kPa以上、特别优选为100kPa以上、最优选为150kPa以上。如果是这样的范围,则上述效果变得显著。本发明的树脂发泡体在压缩时的弹性应变能的上限例如为500kPa(优选为800kPa)。
本发明的树脂发泡体的非发泡弯曲应力优选为5MPa以上、更优选为6MPa以上、进一步优选为9MPa以上、特别优选为10MPa以上。如果是这样的范围,则使树脂发泡体的气泡壁(气孔壁)变形需要大的能量,能够得到具有优异的冲击吸收性的树脂发泡体。本发明的树脂发泡体通过适度降低以往在缓冲材料中被重视的柔软性、获取与其它特性的平衡,从而能够实现耐冲击性(冲击吸收性)的提高。通过这样地与以往不同的作用,展现冲击吸收性的本发明的树脂发泡体在冲击于窄范围传输这样的构成(冲击不易在面方向上扩散的构成)中特别有用,例如在应用于具有挠性的构件(例如,由树脂构成的构件)时特别有用。该非发泡弯曲应力的上限优选为20MPa、更优选为15MPa。如果是这样的范围,则能够得到柔软性及应力分散性更优异的树脂发泡体。“非发泡弯曲应力”是指,通过对树脂发泡体进行热压而恢复至无气泡的非发泡状态(块状)的树脂成型体a的弯曲应力。树脂成型体a的密度可以与由后述的树脂组合物形成的发泡前的树脂成型体b的密度同等。需要说明的是,树脂成型体a的弯曲应力(树脂发泡体的非发泡弯曲应力)可以与树脂成型体b同等。弯曲应力的测定方法在后面叙述。
上述树脂发泡体的冲击吸收率优选为25%以上、更优选为30%以上、进一步优选为35%以上。冲击吸收率如以下所述地进行测定。
·在冲击力传感器上依次配置树脂发泡体、双面带(型号:No.5603W、日东电工制)、PET膜(型号:DIAFOIL MRF75、三菱树脂制),形成了试验体。使66g的铁球从PET膜上方50cm的高度落下至试验体,对冲击力F1进行了测定。
·另外,使铁球如上所述地直接落下至冲击力传感器,测定空白的冲击力F0。
·根据F1、F0并通过式(F0-F1)/F0×100计算出冲击吸收率(%)。
上述树脂发泡体的厚度恢复率优选为75%以上、更优选为80%以上、进一步优选为85%以上。需要说明的是,发泡层的厚度恢复率由下式来定义。该发泡层的厚度恢复率是以某种程度的面积对发泡片施加负载、将其压缩而测定的恢复率,与局部施加负载而仅使一部分凹陷而测定的所谓凹陷恢复率不同。
厚度恢复率(%)={(解除压缩状态起0.5秒钟后的厚度)/(初始厚度)}×100
初始厚度:施加负载前的树脂发泡体的厚度。
解除压缩状态起0.5秒钟后的厚度:在对树脂发泡体施加1000g/cm2的负载的状态下保持120秒钟,将压缩解除,解除压缩0.5秒钟后的树脂发泡体的厚度。
本发明的树脂发泡体的由反复压缩带来的厚度变化率优选为10%以下。如果是这样的范围,则可以得到不易破碎、作为缓冲材料使用时能够防止与周边构件的间隙、并且防尘性优异的树脂发泡体。树脂发泡体的由反复压缩带来的厚度变化率更优选为8%以下、进一步优选为5%以下、特别优选为3%以下、最优选为1%以下。如果是这样的范围,则上述效果变得显著。树脂发泡体的由反复压缩带来的厚度变化率越小越优选,但其下限例如为0.5%(优选为0.3%、更优选为0.1%、进一步优选为0.05%)。树脂发泡体的由反复压缩带来的厚度变化率是指:将前端平坦的圆盘夹具(接触面积:4.9cm2)按压至树脂发泡体并在进行了5000次50%压缩/10%压缩(厚度基准)循环时的厚度的变化率。通过式(试验前的厚度)-(试验后的厚度)}/(试验前的厚度)×100计算出该变化率。
上述树脂发泡体在23℃下的拉伸模量优选为0.6MPa以上、更优选为0.7MPa~5MPa、进一步优选为1MPa~4MPa。如果是这样的范围,则能够得到应力分散性优异、即使为薄膜也能够发挥优异的冲击吸收性的树脂发泡体。以卡盘间距离40mm固定样品(尺寸:10mm×80mm),得到以拉伸速度500mm/min进行拉伸试验而得到的拉伸应变-拉伸强度曲线,根据连结该曲线的原点与拉伸应变10%时的拉伸强度的直线的斜率求出上述拉伸模量。
上述树脂发泡体在25℃下的断裂伸长率优选为120%以下、更优选为110%以下、进一步优选为100%以下、特别优选为90%以下。如果是这样的范围,则能够得到柔软性及应力分散性优异的树脂发泡体。需要说明的是,若断裂伸长率较小,则在对树脂发泡体施加负载时,该树脂发泡体的气孔壁的变形变小,例如在添加了填充材料的情况下,在构成该树脂发泡体的树脂与该填充材料的界面容易发生滑动,能进一步缓和负载。另一方面,若断裂伸长率过大,则树脂发泡体的气孔壁的变形变大,存在变得难以缓和负载的担忧。断裂伸长率可以基于JIS K 6767来测定。
上述树脂发泡体的拉伸应力保持率优选为60%以上、更优选为63%~100%、进一步优选为63%~95%。如果是这样的范围,则能够得到应力分散性优异、即使为薄膜也能够发挥优异的冲击吸收性的树脂发泡体。在本说明书中,上述拉伸应力保持率是指,以300m/min的速度将树脂发泡体(宽10mm×长100mm)沿着长度方向拉伸20%,刚拉伸后的拉伸强度与拉伸后保持了12小时后的拉伸强度的比率(12小时后的拉伸强度/刚拉伸后的拉伸强度×100)。
上述树脂发泡体的厚度优选为30μm~5000μm、更优选为35μm~4000μm、进一步优选为40μm~3000μm、更进一步优选为45μm~2000μm、特别优选为50μm~1000μm、最优选为55μm~500μm。如上所述,本发明的树脂发泡体虽然是薄层,但发挥优异的耐冲击性。另外,如果树脂发泡体的厚度为上述范围内,则能够形成微细且均匀的气泡结构,在能够展现优异的冲击吸收性的方面是有利的。
上述树脂发泡体的平均气泡直径(平均气孔直径)优选为10μm~200μm、更优选为15μm~180μm、进一步优选为20μm~150μm、更进一步优选为23μm~120μm、特别优选为25μm~100μm、最优选为30μm~80μm。如果是这样的范围,则能够得到受到冲击时不会过度变形、而能够展现高冲击吸收性的树脂发泡体。另外,能够制成具有适度的硬度、适宜作为填埋间隙的缓冲材料的树脂发泡体。平均气泡直径的测定方法在后面叙述。
上述树脂发泡体所具有的气泡的长径比优选为1.5以上。如果是这样的范围,则能够得到厚度恢复性优异的树脂发泡体。构成上述树脂发泡体的气泡的长径比优选为2.0以上、更优选为2.5以上。如果是这样的范围,则上述效果变得显著。另外,构成上述树脂发泡体的气泡的长径比的上限优选为5、更优选为4、进一步优选为3.5。如果是这样的范围,则能够得到冲击吸收性优异的树脂发泡体。
需要说明的是,在本说明书中,“树脂发泡体所具有的气泡的长径比”是指,在随机选择的部位处的树脂发泡体剖面中的给定面积(3mm2)范围内存在的各个气泡的长径比的平均值。“树脂发泡体所具有的气泡的长径比”的具体求出方法如下所述。
·使用剃刀,将树脂发泡体沿着TD(与流动方向正交的方向)、且相对于树脂发泡体的主面垂直的方向(厚度方向)切断,以倍率100倍观察给定面积(3mm2)范围。测定一个气泡的厚度方向的长度和TD的长度。
·对给定面积内存在的全部气泡进行同样的测定。
·通过TD的长度÷厚度方向的长度计算出气泡的长径比,对全部气泡进行同样的计算,将其平均值作为“树脂发泡体所具有的气泡的长径比”。
本发明的树脂发泡体的气泡直径(气孔直径)的变动系数优选为0.5以下、更优选为0.48以下、进一步优选为0.45以下、特别优选为0.43以下、最优选小于0.4。如果是这样的范围,则由冲击导致的变形变得均匀,可防止局部的应力负荷,能够得到应力分散性优异、并且耐冲击性特别优异的树脂发泡体。该变动系数越小越优选,其下限例如为0.2(优选为0.15、更优选为0.1、进一步优选为0.01)。气泡直径的变动系数的测定方法在后面叙述。
本发明的树脂发泡体的气泡率(气孔率)优选为30%以上、更优选为50%以上。如果是这样的范围,则能够得到压缩时的排斥应力小的树脂发泡体。对于这样的树脂发泡体而言,在间隙窄的位置稍微进行压缩并应用上述树脂发泡体时,能够减小对其它构件施加的应力。例如,在将树脂发泡体用于显示构件的情况下,能够使对该显示构件施加的应力松弛/分散,因此,从颜色不均减少、构件保护的观点考虑是有用的。该气泡率的上限优选为99%以下、更优选为95%以下、进一步优选为90%以下。如果是这样的范围,则可以制成具有适度的硬度、受到冲击时的变形量小、因而具有高冲击吸收性的树脂发泡体。气泡率的测定方法在后面叙述。
本发明的树脂发泡体的气泡壁(气孔壁)的厚度优选为0.1μm~10μm、更优选为0.3μm~8μm、进一步优选为0.5μm~5μm、特别优选为0.7μm~4μm、最优选为1μm~3μm。如果是这样的范围,则能够得到受到冲击时不会过度变形、而能够展现高冲击吸收性的树脂发泡体。另外,能够制成具有适度的硬度、适宜作为填埋间隙的缓冲材料的树脂发泡体。气泡壁的厚度的测定方法在后面叙述。
在本发明的树脂发泡体的气泡结构为半连续半独立气泡结构的情况下,其中的独立气泡结构的比例优选为40%以下、更优选为30%以下。如果是这样的范围,则能够制成具有适度的硬度、适宜作为填埋间隙的缓冲材料的树脂发泡体。在本说明书中,树脂发泡体的独立气泡率例如如下所述地求出:在温度23℃、湿度50%的环境中,使测定对象沉入水分中,测定之后的质量,然后在80℃的烘箱中使其充分地干燥后,再次测定质量。另外,如果是连续气泡,则能够保持水分,因此,可作为连续气泡测定其质量而求出。
作为本发明的树脂发泡体的形状,可以根据目的采用任意适当的形状。作为这样的形状,代表性地为片状。
可以在本发明的树脂发泡体的一面或两面具有热熔融层。具有热熔融层的树脂发泡体例如能够通过使用加热至构成树脂发泡体的树脂组合物的熔融温度以上的一对加热辊对树脂发泡体(或树脂发泡体的前体)进行压延而得到。
在不损害本发明效果的范围内,本发明的树脂发泡体可以通过任意适当的方法形成。作为这样的方法,代表性地,可举出使包含树脂材料(聚合物)的树脂组合物发泡的方法。
A-1.树脂组合物
本发明的树脂发泡体代表性地可以使树脂组合物发泡而得到。树脂组合物包含任意适当的树脂材料(聚合物)。
作为上述聚合物,可列举例如:丙烯酸类树脂、有机硅类树脂、氨基甲酸酯类树脂、聚烯烃类树脂、酯类树脂、橡胶类树脂等。上述聚合物可以仅单独使用一种,也可以组合使用两种以上。
相对于树脂组合物100重量份,聚合物的含有比例优选为30重量份~95重量份、更优选为35重量份~90重量份、进一步优选为40重量份~80重量份、特别优选为40重量份~60重量份。如果是这样的范围,则能够得到柔软性及应力分散性更优异的树脂发泡体。
在一个实施方式中,作为上述聚合物,使用聚烯烃类树脂。
相对于上述聚合物100重量份,聚烯烃类树脂的含有比例优选为50重量份~100重量份、更优选为70重量份~100重量份、进一步优选为90重量份~100重量份、特别优选为95重量份~100重量份、最优选为100重量份。
作为聚烯烃类树脂,可优选列举选自聚烯烃及聚烯烃类弹性体中的至少一种,更优选将聚烯烃与聚烯烃类弹性体组合使用。聚烯烃及聚烯烃类弹性体分别可以仅单独使用一种,也可以组合使用两种以上。需要说明的是,在本说明书中,在称为“聚烯烃”的情况下,不包括“聚烯烃类弹性体”。
在将聚烯烃与聚烯烃类弹性体作为聚烯烃类树脂组合使用的情况下,聚烯烃与聚烯烃类弹性体的重量比率(聚烯烃/聚烯烃类弹性体)优选为1/99~99/1、更优选为10/90~90/10、进一步优选为20/80~80/20、特别优选为30/70~70/30。如果是这样的范围,则本发明的效果变得显著。
作为聚烯烃,可以在不损害本发明效果的范围内采用任意适当的聚烯烃。作为这样的聚烯烃,可列举例如:直链状的聚烯烃、支链状的(具有支链的)聚烯烃等。在一个实施方式中,作为聚烯烃类树脂,使用支链状的聚烯烃。在该实施方式中,作为聚烯烃,可以仅使用支化状的聚烯烃,也可以将支化状的聚烯烃和直链状的聚烯烃组合使用。通过使用支化状的聚烯烃,能够得到平均气泡直径小、耐冲击性优异的树脂发泡体。相对于聚烯烃100重量份,支化状的聚烯烃的含有比例优选为30重量份~100重量份、更优选为80重量份~120重量份。
作为上述聚烯烃,可举出例如:包含来自α-烯烃的结构单元的聚合物。聚烯烃可以仅由来自α-烯烃的结构单元构成,也可以由来自α-烯烃的结构单元和来自除α-烯烃以外的单体的结构单元构成。在聚烯烃为共聚物的情况下,作为其共聚方式,可采用任意适当的共聚方式。可列举例如:无规共聚物、嵌段共聚物等。
作为能够构成聚烯烃的α-烯烃,优选例如碳原子数2~8(优选为2~6、更优选为2~4)的α-烯烃(例如乙烯、丙烯、1-丁烯、1-戊烯、1-己烯、4-甲基-1-戊烯、1-庚烯、1-辛烯等)。α-烯烃可以仅为一种,也可以为两种以上。
作为构成聚烯烃的α-烯烃以外的单体,可列举例如:乙酸乙烯酯、丙烯酸、丙烯酸酯、甲基丙烯酸、甲基丙烯酸酯、乙烯醇等烯属不饱和单体。除α-烯烃以外的单体可以仅为一种,也可以为两种以上。
作为聚烯烃,具体可列举例如:低密度聚乙烯、中密度聚乙烯、高密度聚乙烯、直链状低密度聚乙烯、聚丙烯(丙烯均聚物)、乙烯与丙烯的共聚物、乙烯与乙烯以外的α-烯烃的共聚物、丙烯与丙烯以外的α-烯烃的共聚物、乙烯、丙烯及除乙烯和丙烯以外的α-烯烃的共聚物、丙烯与烯属不饱和单体的共聚物等。
在一个实施方式中,作为聚烯烃,使用具有来自丙烯的结构单元的聚丙烯类聚合物。作为聚丙烯类聚合物,可列举例如:聚丙烯(丙烯均聚物)、乙烯与丙烯的共聚物、丙烯与丙烯以外的α-烯烃的共聚物等,优选为聚丙烯(丙烯均聚物)。聚丙烯类聚合物可以仅单独使用一种,也可以组合使用两种以上。
从能够进一步展现本发明效果的方面考虑,聚烯烃在温度230℃下的熔体流动速率(MFR)优选为0.2g/10分~10g/10分、更优选为0.25g/10分~5g/10分、进一步优选为0.3g/10分~3g/10分、特别优选为0.35g/10分~1.5g/10分。需要说明的是,在本说明书中,上述熔体流动速率(MFR)是指基于ISO1133(JIS-K-7210)在温度230℃、负载2.16kgf的条件下测定的MFR。
在一个实施方式中,组合使用在温度230℃下的熔体流动速率(MFR)在上述的范围内的两种以上不同的聚烯烃。在该情况下,可以组合使用在温度230℃下的熔体流动速率(MFR)优选为0.2g/10分以上且小于0.7g/10分(更优选为0.2g/10分~0.65g/10分)的聚烯烃、与在温度230℃下的熔体流动速率(MFR)优选为0.7g/10分~10g/10分(更优选为0.7g/10分~5g/10分、进一步优选为0.7g/10分~3g/10分、特别优选为0.7g/10分~1.5g/10分、最优选为0.7g/10分~1.3g/10分)的聚烯烃。这样一来,能够得到平均气泡直径小、耐冲击性优异的树脂发泡体。
作为聚烯烃,在组合使用在温度230℃下的熔体流动速率(MFR)为上述的范围内的两种以上不同的聚烯烃的情况下,例如上述在温度230℃下的熔体流动速率(MFR)优选为0.2g/10分以上且小于0.7g/10分(更优选为0.2g/10分~0.65g/10分)的聚烯烃、与在温度230℃下的熔体流动速率(MFR)优选为0.7g/10分~10g/10分(更优选为0.7g/10分~5g/10分、进一步优选为0.7g/10分~3g/10分、特别优选为0.7g/10分~1.5g/10分、最优选为0.7g/10分~1.3g/10分)的聚烯烃的重量比率优选为1/99~99/1、更优选为10/90~90/10、进一步优选为20/80~80/20、特别优选为30/70~70/30、最优选为40/60~60/40。
作为聚烯烃,可以使用市售品,可列举例如:“E110G”(普瑞曼聚合物株式会社制)、“EA9”(日本聚丙烯株式会社制)、“EA9FT”(日本聚丙烯株式会社制)、“E-185G”(普瑞曼聚合物株式会社制)、“WB140HMS”(Borealis公司制)、“WB135HMS”(Borealis公司制)等。
作为聚烯烃类弹性体,可以在不损害本发明效果的范围内采用任意适当的聚烯烃类弹性体。作为这样的聚烯烃类弹性体,可列举例如:乙烯-丙烯共聚物、乙烯-丙烯-二烯共聚物、乙烯-乙酸乙烯酯共聚物、聚丁烯、聚异丁烯、氯化聚乙烯、使聚烯烃成分与橡胶成分物理分散而得到的弹性体、具有聚烯烃成分与橡胶成分发生了微相分离的结构的弹性体等所谓的非交联型的热塑性烯烃类弹性体(TPO);通过在存在交联剂的条件下对包含形成基体的树脂成分A(烯烃类树脂成分A)及形成域(domain)的橡胶成分B的混合物进行动态热处理而得到的动态交联型热塑性烯烃类弹性体(TPV);等等,该动态交联型热塑性烯烃类弹性体是具有在作为基体(海相)的树脂成分A中细密地分散有交联橡胶粒子作为域(岛相)的海岛结构的多相体系的聚合物。
聚烯烃类弹性体优选包含橡胶成分。作为这样的橡胶成分,可列举日本特开平08-302111号公报、日本特开2010-241934号公报、日本特开2008-024882号公报、日本特开2000-007858号公报、日本特开2006-052277号公报、日本特开2012-072306号公报、日本特开2012-057068号公报、日本特开2010-241897号公报、日本特开2009-067969号公报、日本再表03/002654号公报等中记载的橡胶成分。
作为具有聚烯烃成分与烯烃类橡胶成分发生了微相分离的结构的弹性体,具体可列举:由聚丙烯树脂(PP)和乙丙橡胶(EPM)形成的弹性体、由聚丙烯树脂(PP)和乙烯-丙烯-二烯橡胶(EPDM)形成的弹性体等。聚烯烃成分与烯烃类橡胶成分的重量比(聚烯烃成分/烯烃类橡胶)优选为90/10~10/90、更优选为80/20~20/80。
对于动态交联型热塑性烯烃类弹性体(TPV)而言,一般来说,与非交联型的热塑性烯烃类弹性体(TPO)相比,其弹性模量高,并且压缩永久应变也小。由此,回复性良好,在制成发泡体的情况下,能够显示出优异的回复性。
动态交联型热塑性烯烃类弹性体(TPV)是指,如上述那样通过在存在交联剂的条件下对包含形成基体的树脂成分A(烯烃类树脂成分A)及形成域的橡胶成分B的混合物进行动态热处理而得到的具有在作为基体(海相)的树脂成分A中细密地分散有交联橡胶粒子作为域(岛相)的海岛结构的多相体系的聚合物。
作为动态交联型热塑性烯烃类弹性体(TPV),可列举例如:日本特开2000-007858号公报、日本特开2006-052277号公报、日本特开2012-072306号公报、日本特开2012-057068号公报、日本特开2010-241897号公报、日本特开2009-067969号公报、日本再表03/002654号等中记载的动态交联型热塑性烯烃类弹性体。
作为动态交联型热塑性烯烃类弹性体(TPV),可使用市售品,可列举例如:“Zeotherm”(日本瑞翁株式会社制)、“THERMORUN”(三菱化学株式会社制)、“Sarlink3245D”(东洋纺织株式会社制)等。
聚烯烃类弹性体在温度230℃下的熔体流动速率(MFR)优选为2g/10分~15g/10分、更优选为3g/10分~10g/10分、进一步优选为3.5g/10分~9g/10分、特别优选为4g/10分~8g/10分、最优选为4.5g/10分~7.5g/10分。
聚烯烃类弹性体的熔融张力(190℃、断裂时)优选小于10cN、更优选为5cN~9.5cN。
聚烯烃类弹性体的JIS A硬度优选为30°~95°、更优选为35°~90°、进一步优选为40°~88°、特别优选为45°~85°、最优选为50°~83°。需要说明的是,JIS A硬度基于ISO7619(JIS K6253)测定。
在一个实施方式中,上述树脂发泡体(即树脂组合物)可以进一步包含填充材料。通过含有填充材料,能够形成需要大的能量使气泡壁(气孔壁)变形的树脂发泡体,该树脂发泡体发挥优异的冲击吸收性。另外,通过含有填充材料,能够形成微细且均匀的气泡结构,在能够展现优异的冲击吸收性这方面也是有利的。填充材料可以单独使用仅一种,也可以组合使用两种以上。
相对于构成树脂发泡体的聚合物100重量份,上述填充材料的含有比例优选为10重量份~150重量份、更优选为30重量份~130重量份、进一步优选为50重量份~100重量份。如果是这样的范围,则上述效果变得显著。
在一个实施方式中,上述填充材料为无机物。作为构成作为无机物的填充材料的材料,可列举例如:氢氧化铝、氢氧化镁、碳酸钙、碳酸镁、硅酸钙、硅酸镁、氧化钙、氧化镁、氧化铝、氮化铝、硼酸铝晶须、氮化硅、氮化硼、结晶二氧化硅、非晶质二氧化硅、金属(例如,金、银、铜、铝、镍)、碳、石墨等。
在一个实施方式中,上述填充材料为有机物。作为构成作为有机物的填充材料的材料,可列举例如:聚甲基丙烯酸甲酯(PMMA)、聚酰亚胺、聚酰胺酰亚胺、聚醚醚酮、聚醚酰亚胺、聚酯酰亚胺等。
作为上述填充材料,可使用阻燃剂。作为阻燃剂,可列举例如:溴类阻燃剂、氯类阻燃剂、磷类阻燃剂、锑类阻燃剂等。从安全性的观点考虑,优选使用无卤无锑类阻燃剂。
作为无卤无锑类阻燃剂,可列举例如:包含铝、镁、钙、镍、钴、锡、锌、铜、铁、钛、硼等的化合物。作为这样的化合物(无机化合物),可列举例如:氢氧化铝、氢氧化镁、氧化镁/氧化镍的水合物、氧化镁/氧化锌的水合物等水合金属化合物等。
可以对上述填充材料实施任意适当的表面处理。作为这样的表面处理,可列举例如:硅烷偶联处理、硬脂酸处理等。
上述填充材料的堆积密度优选为0.8g/cm3以下、更优选为0.6g/cm3以下、进一步优选为0.4g/cm3以下、特别优选为0.3g/cm3以下。如果是这样的范围,则能够以良好的分散性含有填充材料,即使减少填充材料的含量,也能够充分地发挥填充材料添加效果。填充材料的含量少的树脂发泡体在高发泡、柔软、且应力分散性及外观优异的方面是有利的。填充材料的堆积密度的下限值例如为0.01g/cm3、优选为0.05g/cm3、更优选为0.1g/cm3。
上述填充材料的数均粒径(初级粒径)优选为5μm以下、更优选为3μm以下、进一步优选为1μm以下。如果是这样的范围,则能够以良好的分散性含有填充材料,并且能够形成均匀的气泡结构。其结果是,能够得到应力分散性及外观优异的树脂发泡体。填充材料的数均粒径的下限值例如为0.1μm。填充材料的数均粒径可以将在水100g中混合填充剂1g而制备的悬浮液作为样品、并使用粒度分布计(MicrtracII、MICROTRAC BEL株式会社)来测定。
上述填充材料的比表面积优选为2m2/g以上、更优选为4m2/g以上、进一步优选为6m2/g以上。如果是这样的范围,则能够以良好的分散性含有填充材料,并且能够形成均匀的气泡结构。其结果是,能够得到应力分散性及外观优异的树脂发泡体。填充材料的比表面积的上限值例如为20m2/g。填充材料的比表面积能够通过利用BET法来测定,即通过使吸附占有面积已知的分子在利用液氮的低温下吸附于填充材料表面,根据其吸附量来测定。
可以在不损害本发明效果的范围内在树脂组合物中包含任意适当的其它成分。这样的其它成分可以仅为一种,也可以为两种以上。作为这样的其它成分,可列举例如:橡胶、作为树脂材料配合的聚合物以外的树脂、软化剂、脂肪族类化合物、防老化剂、抗氧剂、光稳定剂、耐候剂、紫外线吸收剂、分散剂、增塑剂、碳、抗静电剂、表面活性剂、交联剂、增稠剂、防锈剂、有机硅类化合物、张力改性剂、防收缩剂、流动性改性剂、凝胶化剂、固化剂、加强剂、发泡剂、发泡成核剂、着色剂(颜料、染料等)、pH调节剂、溶剂(有机溶剂)、热聚合引发剂、光聚合引发剂、润滑剂、结晶成核剂、结晶化促进剂、硫化剂、表面处理剂、分散助剂等。
A-2.树脂发泡体的形成
本发明的树脂发泡体代表性地通过使树脂组合物发泡而得到。作为发泡的方法(气泡的形成方法),可采用物理方法、化学方法等发泡成型中通常利用的方法。即,本发明的树脂发泡体代表性地可以是通过物理方法进行发泡而形成的发泡体(物理发泡体),也可以是通过化学方法进行发泡而形成的发泡体(化学发泡体)。物理方法一般是通过使空气、氮等气体成分分散于聚合物溶液并通过机械混合形成气泡的方法(机械发泡体)。化学方法一般是通过利用添加于聚合物基体的发泡剂的热分解产生的气体形成气孔而得到发泡体的方法。
待实施发泡成型的树脂组合物例如可以通过用任意适当的熔融混炼装置、例如开放型的混合辊、非开放型的班伯里混合机、单螺杆挤出机、双螺杆挤出机、连续式混炼机、加压捏合机等任意适当的机构将构成成分混合而制备。
<形成本发明的树脂发泡体的实施方式1>
作为形成本发明的树脂发泡体的一个实施方式1,例如可列举以下方式:经过使乳液树脂组合物(包含树脂材料(聚合物)等的乳液)机械发泡而起泡化的工序(工序A)来形成树脂发泡体。作为起泡装置,可列举例如:高速剪切方式的装置、振动方式的装置、加压气体的喷出方式的装置等。这些起泡装置中,从气泡直径的微细化、大容量制作的观点考虑,优选高速剪切方式的装置。形成本发明的树脂发泡体的该一个实施方式1无论是在由哪种树脂组合物形成时均可以应用。
从成膜性的观点考虑,优选乳液的固体成分浓度高的情况。乳液的固体成分浓度优选为30重量%以上、更优选为40重量%以上、进一步优选为50重量%以上。
通过机械搅拌进行起泡时的气泡是气体进入到乳液中而成的。作为气体,只要对于乳液无活性,就可以在不损害本发明效果的范围内采用任意适当的气体。作为这样的气体,可列举例如:空气、氮气、二氧化碳等。
经过将通过上述方法起泡化后的乳液树脂组合物(含气泡乳液树脂组合物)涂敷于基材上并进行干燥的工序(工序B),能够得到本发明的树脂发泡体。作为基材,可列举例如:进行了剥离处理的塑料膜(进行了剥离处理的聚对苯二甲酸乙二醇酯膜等)、塑料膜(聚对苯二甲酸乙二醇酯膜等)等。
在工序B中,作为涂敷方法、干燥方法,可以在不损害本发明效果的范围内采用任意适当的方法。工序B优选包括:将涂布于基材上的含气泡乳液树脂组合物以50℃以上且小于125℃的温度干燥的预干燥工序B1;和之后进一步以125℃以上且200℃以下的温度进行干燥的正式干燥工序B2。
通过设置预干燥工序B1和正式干燥工序B2,能够防止由急剧的温度上升导致的气泡的合为一体化、气泡的破裂。特别是对于厚度小的发泡片而言,由于温度的急剧的上升,气泡会合为一体化、破裂,因此,设置预干燥工序B1的意义很大。预干燥工序B1中的温度优选为50℃~100℃。预干燥工序B1的时间优选为0.5分钟~30分钟、更优选为1分钟~15分钟。正式干燥工序B2中的温度优选为130℃~180℃、更优选为130℃~160℃。正式干燥工序B2的时间优选为0.5分钟~30分钟、更优选为1分钟~15分钟。
<形成本发明的树脂发泡体的实施方式2>
作为形成本发明的树脂发泡体的一个实施方式2,可举出利用发泡剂使树脂组合物发泡而形成发泡体的方式。作为发泡剂,可使用在发泡成型中通常使用的发泡剂,从环境保护及对于被发泡体的低污染性的观点考虑,优选使用高压的不活泼气体。
作为不活泼气体,只要对于树脂组合物无活性且能够浸渗,就可以采用任意适当的不活泼气体。作为这样的不活泼气体,可列举例如:二氧化碳、氮气、空气等。这些气体也可以混合使用。这些当中,从对于树脂材料(聚合物)的浸渗量多、浸渗速度快的观点考虑,优选二氧化碳。
不活泼气体优选为超临界状态。即,特别优选使用超临界状态的二氧化碳。在超临界状态下,不活泼气体对于树脂组合物的溶解度进一步增大,能够以高浓度混入不活泼气体,并且压力急剧下降时,不活泼气体成为高浓度,因此,气泡核的产生变多,即使气孔率相同,该气泡核成长而能够形成的气泡的密度与其它状态的情况相比也更大,因此,能够得到微细的气泡。需要说明的是,二氧化碳的临界温度为31℃、临界压力为7.4MPa。
作为通过在树脂组合物中浸渗高压的不活泼气体而形成发泡体的方法,可列举例如经过下述工序而形成的方法等:在高压下使包含树脂材料(聚合物)的树脂组合物中浸渗不活泼气体的气体浸渗工序;在该工序后降低压力而使树脂材料(聚合物)发泡的减压工序;以及根据需要进行的通过加热而使气泡生长的加热工序。在该情况下,可以使预先成型的未发泡成型体浸于不活泼气体中,另外也可以在加压状态下使不活泼气体浸渗于熔融的树脂组合物中之后在减压时实施成型。这些工序可以以间歇方式、连续方式中的任意方式进行。即,可以是预先将树脂组合物成型为片状等适宜的形状并制成未发泡树脂成型体后、在该未发泡树脂成型体中浸渗高压的气体并释放压力而发泡的间歇方式;也可以是在加压下将树脂组合物与高压的气体一起进行混炼、成型,同时释放压力而同时进行成型和发泡的连续方式。
以下示出以间歇方式制造发泡体的例子。例如,通过使用单螺杆挤出机、双螺杆挤出机等挤出机对树脂组合物进行挤出而制作发泡体成型用树脂片。或者使用辊、凸轮、捏合机、班伯里型等设置有叶片的混炼机预先对树脂组合物进行均匀混炼,再利用热板的加压等压制加工成给定的厚度从而制作未发泡树脂成型体。将这样得到的未发泡树脂成型体放入高压容器中,注入高压不活泼气体(超临界状态的二氧化碳等),在未发泡树脂成型体中浸渗不活泼气体。在充分地浸渗有不活泼气体的时刻,释放压力(通常至大气压),在树脂中产生气泡核。可以使气泡核直接在室温下成长,但根据情况,也可以通过加热使其成长。作为加热的方法,可采用水浴、油浴、热辊、热风烘箱、远红外线、近红外线、微波等公知、惯用的方法。如此地使气泡生长之后,通过冷水等急剧冷却并将形状固定化,由此可以得到发泡体。需要说明的是,供于发泡的未发泡树脂成型体不限于片状物,也可以根据用途使用各种形状的未发泡树脂成型体。另外,供于发泡的未发泡树脂成型体除了挤出成型、加压成型以外,也可以通过注塑成型等其它成型法来制作。
以下示出以连续方式制造发泡体的例子。例如,通过下述混炼浸渗工序、成型减压工序进行发泡成型,该混炼浸渗工序一边使用单螺杆挤出机、双螺杆挤出机等挤出机对树脂组合物进行混炼,一边注入(导入)高压的气体(特别是不活泼气体、进而为二氧化碳),使高压的气体充分地浸渗于树脂组合物中;该成型减压工序通过设置于挤出机的前端的模头等将树脂组合物挤出,由此释放压力(通常至大气压),同时进行成型和发泡。另外,以连续方式进行发泡成型时,可以根据需要设置通过加热而使气泡成长的加热工序。如此地使气泡成长之后,可以根据需要通过冷水等急剧地进行冷却将形状固定化。另外,高压的气体的导入可以连续地进行,也可以不连续地进行。此外,在混炼浸渗工序及成型减压工序中,可以使用例如挤出机、注塑成型机。需要说明的是,作为使气泡核成长时的加热方法,可列举水浴、油浴、热辊、热风烘箱、远红外线、近红外线、微波等任意适当的方法。作为发泡体的形状,可采用任意适当的形状。作为这样的形状,可列举例如:片状、棱柱状、圆筒状、异型形状等。
从能够得到高发泡的发泡体的方面考虑,对树脂组合物进行发泡成型时的气体的混合量例如相对于树脂组合物总量优选为2重量%~10重量%、更优选为2.5重量%~8重量%、进一步优选为3重量%~6重量%。
使不活泼气体在树脂组合物中浸渗时的压力可以考虑操作性等适宜选择。这样的压力例如优选为6MPa以上(例如为6MPa~100MPa)、更优选为8MPa以上(例如为8MPa~50MPa)。需要说明的是,从保持二氧化碳的超临界状态的观点考虑,在使用超临界状态的二氧化碳的情况下的压力优选为7.4MPa以上。在压力低于6MPa的情况下,发泡时的气泡成长显著,气泡直径变得过大,有时无法得到优选的平均气孔直径(平均气泡直径)。这是因为,压力低时,气体的浸渗量与高压时相比相对较少,气泡核形成速度降低,形成的气泡核数变少,所以平均每1个气泡的气体量反而增加,气泡直径变得极大。另外,在低于6MPa的压力区域内,浸渗压力仅仅稍有变化就会导致气泡直径、气泡密度大幅变化,因此,气泡直径及气泡密度的控制容易变得困难。
气体浸渗工序中的温度根据使用的不活泼气体、树脂组合物中的成分的种类等而不同,能够在宽范围内选择。在考虑了操作性等的情况下,优选为10℃~350℃。在未发泡成型体中浸渗不活泼气体时的浸渗温度在间歇式的情况下优选为10℃~250℃、更优选为40℃~230℃。另外,将浸渗有气体的熔融聚合物挤出并同时进行发泡和成型时的浸渗温度在连续式的情况下优选为60℃~350℃。需要说明的是,在使用二氧化碳作为不活泼气体的情况下,为了保持超临界状态,浸渗时的温度优选为32℃以上、更优选为40℃以上。
在减压工序中,作为减压速度,为了得到均匀的微细气泡,优选为5MPa/秒~300MPa/秒。
加热工序中的加热温度优选为40℃~250℃、更优选为60℃~250℃。
B.发泡构件
图1是本发明的一个实施方式的发泡构件的剖面示意图。发泡构件100具有树脂发泡层10、和配置于树脂发泡层10的至少一侧的粘合剂层20。树脂发泡层10由上述树脂发泡体构成。
粘合剂层的厚度优选为5μm~300μm、更优选为6μm~200μm、进一步优选为7μm~100μm、特别优选为8μm~50μm。通过使粘合剂层的厚度在上述范围内,本发明的发泡构件能够发挥优异的冲击吸收性。
作为粘合剂层,可采用由任意适当的粘合剂形成的层。作为构成粘合剂层的粘合剂,可列举例如:橡胶类粘合剂(合成橡胶类粘合剂、天然橡胶类粘合剂等)、氨基甲酸酯类粘合剂、丙烯酸氨基甲酸酯类粘合剂、丙烯酸类粘合剂、有机硅类粘合剂、聚酯类粘合剂、聚酰胺类粘合剂、环氧类粘合剂、乙烯基烷基醚类粘合剂、氟类粘合剂、橡胶类粘合剂等。作为构成粘合剂层的粘合剂,优选为选自丙烯酸类粘合剂、有机硅类粘合剂、橡胶类粘合剂中的至少一种。这样的粘合剂可以仅为一种,也可以为两种以上。粘合剂层可以为一层,也可以为两层以上。
作为粘合剂,如果以粘合方式进行分类,则可列举例如:乳液型粘合剂、溶剂型粘合剂、紫外线交联型(UV交联型)粘合剂、电子束交联型(EB交联型)粘合剂、热熔融型粘合剂(热熔型粘合剂)等。这样的粘合剂可以仅为一种,也可以为两种以上。
粘合剂层的水蒸气透湿度优选为50(g/(m2·24小时))以下、更优选为30(g/(m2·24小时))以下、进一步优选为20(g/(m2·24小时))以下、特别优选为10(g/(m2·24小时))以下。如果粘合剂层的水蒸气透湿度在上述范围内,则本发明的发泡片能够使冲击吸收性稳定化而不会受到由水分导致的影响。需要说明的是,水蒸气透湿度例如可以通过基于JIS Z0208的方法、在40℃、相对湿度92%的试验条件下测定。
可以在不损害本发明效果的范围内在构成粘合剂层的粘合剂中包含任意适当的其它成分。作为其它成分,可列举例如:其它聚合物成分、软化剂、防老化剂、固化剂、增塑剂、填充材料、抗氧剂、热聚合引发剂、光聚合引发剂、紫外线吸收剂、光稳定剂、着色剂(颜料、染料等)、溶剂(有机溶剂)、表面活性剂(例如,离子型表面活性剂、有机硅类表面活性剂、氟类表面活性剂等)、交联剂(例如多异氰酸酯类交联剂、有机硅类交联剂、环氧类交联剂、烷基醚化三聚氰胺类交联剂等)等。需要说明的是,热聚合引发剂、光聚合引发剂可以包含于用于形成聚合物成分的材料中。
本发明的发泡构件可以通过任意适当的方法来制造。本发明的发泡构件的制造方法例如可列举:将树脂发泡层与粘合剂层层叠而制造的方法;在将粘合剂层的形成材料与树脂发泡层层叠后通过固化反应等形成粘合剂层而制造的方法等。
实施例
以下,通过实施例对本发明进行具体说明,但本发明不受这些实施例的任何限定。需要说明的是,实施例等中的试验及评价方法如下所述。需要说明的是,在记载为“份”的情况下,只要没有特别说明,则是指“重量份”,在记载为“%”的情况下,只要没有特别说明,则是指“重量%”。
[评价方法]
<50%压缩载荷>
按照JIS K 6767中记载的发泡体的压缩硬度测定方法进行了测定。具体而言,将实施例/比较例中得到的树脂发泡体切出30mm×30mm尺寸,作为试验片,以压缩速度10mm/min压缩至压缩率达到50%,将此时的应力(N)换算成平均每单位面积(1cm2)的值,作为25%压缩载荷(N/cm2)、50%压缩载荷(N/cm2)。
<压缩应力保持率(6小时后、12小时后)>
使用精密万能试验机(Autograph AG-X plus、岛津制作所制),将在实施例/比较例中得到的树脂发泡体切出30mm×30mm尺寸,作为试验片,将以压缩速度10mm/min刚压缩至压缩率达到50%后的应力设为(N1),将达到压缩率为50%后保持位移并经过给定时间(6小时、12小时)后的应力设为(N2)。然后,通过式压缩应力保持率[%]=N2/N1×100进行计算。
<表观密度>
树脂发泡体的密度(表观密度)如下所述地进行计算。将实施例/比较例中得到的树脂发泡体冲裁成20mm×20mm尺寸,作为试验片,用卡尺测定试验片的尺寸,接下来,通过电子天平测定试验片的重量,并且通过下式进行计算。
表观密度(g/cm3)=试验片的重量/试验片的体积
<平均气泡直径(平均气孔直径)、气泡直径(气孔直径)的变动系数>
使用剃刀,将树脂发泡体沿着TD(与流动方向正交的方向)、且相对于树脂发泡体的主面垂直的方向(厚度方向)切断,作为计测器,使用数字显微镜(商品名“VHX-500”,Keyence株式会社制),导入树脂发泡体的气泡部的放大图像,使用相同计测器的解析软件,通过进行图像解析而求出数均气泡直径(平均气孔直径)(μm)。需要说明的是,导入的放大图像的气泡数为400个左右。另外,根据气孔直径的全部数据计算标准偏差,使用下式计算出变动系数。
变动系数=标准偏差/平均气泡直径(平均气孔直径)
<气泡的长径比>
作为计测器,使用数字显微镜(商品名“VHX-2000,Keyence株式会社制),通过下述的方法对实施例/比较例中得到的树脂发泡体所具有的气泡的长径比进行了测定。
·使用剃刀,将树脂发泡体沿着TD(与流动方向正交的方向)、且相对于树脂发泡体的主面垂直的方向(厚度方向)切断,使用(例如,Keyence制“VHX-2000”)显微镜以倍率100倍对切截面观察给定面积(3mm2)范围,测定一个气泡的厚度方向的长度和TD的长度。
·对在给定面积内存在的全部气泡进行同样的测定。
·通过TD的长度÷厚度方向的长度计算出气泡的长径比,对全部气泡进行同样的计算,将平均值作为“树脂发泡体所具有的气泡的长径比”。
<气泡率(气孔率)>
在温度23℃、湿度50%的环境中进行了测定。通过100mm×100mm的冲裁刀模(2片加工刀(商品名“NCA07”、厚度0.5mm、刀尖角度45°、株式会社NAKAYAMA制))对实施例/比较例中得到的树脂发泡体进行冲裁,测定了冲裁后的试样的尺寸。另外,用测定端子的直径(φ)为20mm的1/100千分尺测定了厚度。根据这些值计算出实施例/比较例中得到的树脂发泡体的体积。接下来,通过最小刻度0.01g以上的托盘天平测定了实施例/比较例中得到的树脂发泡体的重量。根据这些值计算出实施例/比较例中得到的树脂发泡体的气泡率(气孔率)。
<气泡壁(气孔壁)的厚度>
使用剃刀,将树脂发泡体沿着TD(与流动方向正交的方向)、且相对于树脂发泡体的主面垂直的方向(厚度方向)切断,作为计测器,使用数字显微镜(商品名“VHX-500”,Keyence株式会社制),导入树脂发泡体的气泡部的放大图像,使用相同计测器的解析软件,通过进行图像解析而求出气泡壁(气孔壁)的厚度(μm)。需要说明的是,导入的放大图像的气泡数为400个左右。
<非发泡弯曲应力>
使用真空加压成型机(IVM-70:岩城工业株式会社),以(熔点+70℃)的温度、15MPa的压力对树脂发泡体加压5分钟,由此得到了非发泡状态的树脂成型体a。
将树脂成型体a切出宽6mm、长50mm,作为样品,将该样品放置于支点间距离25mm的3点弯曲夹具上,在23℃×50%RH的环境中,以压入速度0.5mm/min进行压入试验(株式会社岛津制作所制、商品名“AG-Xplus”),将对该样品压入5mm压时的负载(g)作为非发泡弯曲应力。
<压缩模量>
基于JIS K 6767的压缩试验一项,测定树脂发泡体的压缩率(%)、压缩反弹力(kPa),分别读取压缩率5%时的压缩反弹力F(5%)和压缩率15%时的压缩反弹力F(15%),根据F(5%)、F(15%)并通过式(F(15%)-F(5%))/(15-5)×100计算出压缩模量。
<厚度恢复率>
对于树脂发泡体,在对树脂发泡体施加1000g/cm2的负载的状态下保持120秒钟,将压缩解除,测定解除压缩0.5秒钟后的树脂发泡体的厚度(解除压缩状态起0.5秒钟后的厚度)。根据“解除压缩状态起0.5秒钟后的厚度”、和施加负载前的树脂发泡体的厚度(初始厚度)并通过下式求出厚度恢复率。
厚度恢复率(%)={(解除压缩状态起0.5秒钟后的厚度)/(初始厚度)}×100
<由反复压缩带来的厚度变化率>
使用微型伺服机(MMT-250NV-10、岛津制作所制),使前端平坦的圆盘夹具(压缩用附件圆盘型压缩夹具PC-5040、接触面积:4.9cm2、株式会社IMADA)相对于发泡体以达到50%压缩、10%压缩的方式反复移位,进行了5000次反复压缩(初始负载0.15N、下降速度5min/mm、上升速度5min/mm)。使用数字显微镜(商品名“VHX-500”,Keyence株式会社制)对试验后的厚度进行了测定。将试验前的厚度设为Z0,将试验后的厚度设为Z1,根据式(Z0-Z1)/Zo×100计算出由反复压缩带来的厚度变化率。
<冲击吸收率>
在冲击力传感器上依次配置树脂发泡体、双面带(型号:No.5603W、日东电工制)、PET膜(型号:DIAFOIL MRF75、三菱树脂制),形成了试验体。使66g的铁球从PET膜上方50cm的高度落下至试验体,对冲击力F1进行了测定。
另外,使铁球如上所述地直接落下至冲击力传感器,测定空白的冲击力F0。
根据F1、F0并通过式(F0-F1)/F0×100计算出冲击吸收率(%)。
<应力分散性>
图2是示出在应力分散度的测定中使用的应力松弛试验机1000的剖面示意图。
如图2所示,在铁制的支撑体A上放置聚碳酸酯板(200mm×300mm×厚度1mm)200,在其上放置应力测定膜300(商品名“Prescale”(两片,微压用(4LW),富士较胶片株式会社制,具有加压的部分显色的面的片,50mm×50mm×厚度0.16mm)。接下来,在应力测定膜300上放置测定对象的实施例/比较例中得到的树脂发泡结构体(150mm×200mm×厚度0.5mm)400,在其上粘贴双面胶粘带(No.5603,日东电工制,厚度0.03mm)500,配置厚度0.05mm的间隔件600,在最上部放置ABS板(200mm×300mm×厚度3mm)700。组装后,12小时后,从其上在中心部放置钢球SUS304(φ25mm)800,施加了20N的负载1min。
然后,观察应力测定膜300的颜色的变化,将颜色不从应力测定膜300的中心展开而成为点状者设为C、将颜色从应力测定膜300的中心起展开至25mm者设为B、将颜色从应力测定膜300的中心起大幅展开至50mm端部者设为A。
〔实施例1〕
使用株式会社日本制钢所(JSW)制造的双螺杆混炼机将聚丙烯(熔体流动速率(MFR)(230℃):0.40g/10min)65重量份、聚烯烃类弹性体(熔体流动速率(MFR):6g/10min、JIS A硬度:79°)35重量份、氢氧化镁(商品名“KISUMA 5P”协和化学工业制)80重量份、碳(商品名“旭#35”旭碳株式会社制)10重量份、及硬脂酸单甘油酯1重量份在200℃的温度下混炼后,以线料状挤出,水冷后成型为颗粒状。将该颗粒投入株式会社日本制钢所制造的单螺杆挤出机,在220℃的气氛中以13MPa(注入后12MPa)的压力注入了二氧化碳气体。相对于树脂100重量份,以4.5重量份的比例注入了二氧化碳气体。使二氧化碳气体充分饱和后,冷却至适于发泡的温度后,从模头挤出,得到了片状成型体。使用切片机将该片状成型体薄片化,得到了厚度为0.3mm的发泡结构体a1。
进一步,使上述发泡结构体a1通过一个辊被加热至200℃的一对辊的辊间(辊与辊之间的间隙),得到了厚度为0.1mm的树脂发泡体A。需要说明的是,辊间的空隙(间隙)按照可得到厚度为0.1mm的树脂发泡体A的方式设定。
将得到的树脂发泡体A供于上述评价,将结果示于表1。
〔实施例2〕
使用株式会社日本制钢所(JSW)制造的双螺杆混炼机将聚丙烯(熔体流动速率(MFR)(230℃):0.40g/10min)65重量份、聚烯烃类弹性体(熔体流动速率(MFR):6g/10min、JIS A硬度:79°)35重量份、氢氧化镁(商品名“KISUMA 5P”协和化学工业制)100重量份、碳(商品名“旭#35”旭碳株式会社制)10重量份、及硬脂酸单甘油酯1重量份在200℃的温度下混炼后,以线料状挤出,水冷后成型为颗粒状。将该颗粒投入株式会社日本制钢所制造的单螺杆挤出机,在220℃的气氛中以13MPa(注入后12MPa)的压力注入了二氧化碳气体。相对于树脂100重量份,以3.5重量份的比例注入了二氧化碳气体。使二氧化碳气体充分饱和后,冷却至适于发泡的温度后,从模头挤出,得到了片状成型体。使用切片机将该片状成型体薄片化,得到了厚度为0.3mm的发泡结构体b1。
进一步,使上述发泡结构体b1通过一个辊被加热至200℃的一对辊的辊间(辊与辊之间的间隙),得到了厚度为0.1mm的树脂发泡体B。需要说明的是,辊间的空隙(间隙)按照可得到厚度为0.1mm的树脂发泡体B的方式设定。
将得到的树脂发泡体B供于上述评价,将结果示于表1。
〔实施例3〕
使用株式会社日本制钢所(JSW)制造的双螺杆混炼机将聚丙烯(熔体流动速率(MFR)(230℃):0.40g/10min)65重量份、聚烯烃类弹性体(熔体流动速率(MFR):6g/10min、JIS A硬度:79°)35重量份、氢氧化镁(商品名“KISUMA 5P”协和化学工业制)120重量份、碳(商品名“旭#35”旭碳株式会社制)10重量份、及硬脂酸单甘油酯1重量份在200℃的温度下混炼后,以线料状挤出,水冷后成型为颗粒状。将该颗粒投入株式会社日本制钢所制造的单螺杆挤出机,在220℃的气氛中以13MPa(注入后12MPa)的压力注入了二氧化碳气体。相对于树脂100重量份,以3.0重量份的比例注入了二氧化碳气体。使二氧化碳气体充分饱和后,冷却至适于发泡的温度后,从模头挤出,得到了片状成型体。使用切片机将该片状成型体薄片化,得到了厚度为0.3mm的发泡结构体c1。
进一步,使上述树脂发泡体c1通过一个辊被加热至200℃的一对辊的辊间(辊与辊之间的间隙),得到了厚度为0.1mm的树脂发泡体C。需要说明的是,辊间的空隙(间隙)按照可得到厚度为0.1mm的树脂发泡体C的方式设定。
将得到的树脂发泡体C供于上述评价,将结果示于表1。
〔实施例4〕
使用株式会社日本制钢所(JSW)制造的双螺杆混炼机将聚丙烯(熔体流动速率(MFR)(230℃):0.40g/10min)15重量份、聚丙烯(熔体流动速率(MFR)(230℃):1.1g/10min)15重量份、聚烯烃类弹性体(熔体流动速率(MFR):6g/10min、JIS A硬度:79°)75重量份、氢氧化镁(商品名“KISUMA 5P”协和化学工业制)80重量份、碳(商品名“旭#35”旭碳株式会社制)10重量份、及硬脂酸单甘油酯1重量份在200℃的温度下混炼后,以线料状挤出,水冷后成型为颗粒状。将该颗粒投入株式会社日本制钢所制造的单螺杆挤出机,在220℃的气氛中以13MPa(注入后12MPa)的压力注入了二氧化碳气体。相对于树脂100重量份,以2.8重量份的比例注入了二氧化碳气体。使二氧化碳气体充分饱和后,冷却至适于发泡的温度后,从模头挤出,得到了片状成型体。使用切片机将该片状成型体薄片化,得到了厚度为0.4mm的发泡结构体d1。
进一步,使上述发泡结构体d1通过一个辊被加热至200℃的一对辊的辊间(辊与辊之间的间隙),得到了厚度为0.1mm的树脂发泡体D。需要说明的是,辊间的空隙(间隙)按照可得到厚度为0.1mm的树脂发泡体D的方式设定。
将得到的树脂发泡体D供于上述评价,将结果示于表1。
〔实施例5〕
使用株式会社日本制钢所(JSW)制造的双螺杆混炼机将聚丙烯(熔体流动速率(MFR)(230℃):0.40g/10min)15重量份、聚丙烯(熔体流动速率(MFR)(230℃):1.1g/10min)15重量份、聚烯烃类弹性体(熔体流动速率(MFR):6g/10min、JIS A硬度:79°)75重量份、氢氧化镁(商品名“KISUMA 5P”协和化学工业制)60重量份、碳(商品名“旭#35”旭碳株式会社制)10重量份、及硬脂酸单甘油酯1重量份在200℃的温度下混炼后,以线料状挤出,水冷后成型为颗粒状。将该颗粒投入株式会社日本制钢所制造的单螺杆挤出机,在220℃的气氛中以13MPa(注入后12MPa)的压力注入了二氧化碳气体。相对于树脂100重量份,以2.6重量份的比例注入了二氧化碳气体。使二氧化碳气体充分饱和后,冷却至适于发泡的温度后,从模头挤出,得到了片状成型体。使用切片机将该片状成型体薄片化,得到了厚度为0.4mm的发泡结构体e1。
进一步,使上述发泡结构体e1通过一个辊被加热至200℃的一对辊的辊间(辊与辊之间的间隙),得到了厚度为0.1mm的树脂发泡体E。需要说明的是,辊间的空隙(间隙)按照可得到厚度为0.1mm的树脂发泡体E的方式设定。
将得到的树脂发泡体E供于上述评价,将结果示于表1。
〔比较例1〕
使用株式会社日本制钢所(JSW)制造的双螺杆混炼机将聚丙烯(熔体流动速率(MFR)(230℃):0.40g/10min)45重量份、聚烯烃类弹性体(熔体流动速率(MFR):6g/10min、JIS A硬度:79°)55重量份、氢氧化镁(商品名“KISUMA 5P”协和化学工业制)10重量份、碳(商品名“旭#35”旭碳株式会社制)10重量份、及硬脂酸单甘油酯1重量份在200℃的温度下混炼后,以线料状挤出,水冷后成型为颗粒状。将该颗粒投入株式会社日本制钢所制造的单螺杆挤出机,在220℃的气氛中以13MPa(注入后12MPa)的压力注入了二氧化碳气体。相对于树脂100重量份,以5.5重量份的比例注入了二氧化碳气体。使二氧化碳气体充分饱和后,冷却至适于发泡的温度后,从模头挤出,得到了片状成型体。使用切片机将该片状成型体薄片化,得到了厚度为0.3mm的发泡结构体f1。
进一步,使上述发泡结构体f1通过一个辊被加热至200℃的一对辊的辊间(辊与辊之间的间隙),得到了厚度为0.1mm的树脂发泡体F。需要说明的是,辊间的空隙(间隙)按照可得到厚度为0.1mm的树脂发泡体F的方式设定。
将得到的树脂发泡体F供于上述评价,将结果示于表1。
〔比较例2〕
使用株式会社日本制钢所(JSW)制造的双螺杆混炼机将聚丙烯(熔体流动速率(MFR)(230℃):0.40g/10min)15重量份、聚丙烯(熔体流动速率(MFR)(230℃):1.1g/10min)15重量份、聚烯烃类弹性体(熔体流动速率(MFR):6g/10min、JIS A硬度:79°)75重量份、氢氧化镁(商品名“KISUMA 5P”协和化学工业制)80重量份、碳(商品名“旭#35”旭碳株式会社制)10重量份、及硬脂酸单甘油酯1重量份在200℃的温度下混炼后,以线料状挤出,水冷后成型为颗粒状。将该颗粒投入株式会社日本制钢所制造的单螺杆挤出机,在220℃的气氛中以13MPa(注入后12MPa)的压力注入了二氧化碳气体。相对于树脂100重量份,以2.8重量份的比例注入了二氧化碳气体。使二氧化碳气体充分饱和后,冷却至适于发泡的温度后,从模头挤出,得到了片状成型体。使用切片机将该片状成型体薄片化,得到了厚度为0.1mm的树脂发泡体G。
将得到的树脂发泡体G供于上述评价。将结果示于表1。
[表1]
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 比较例1 | 比较例2 | |
50%压缩载荷[N/cm<sup>2</sup>] | 12 | 20 | 15 | 10 | 10 | 2 | 3.8 |
6小时后的压缩应力保持率 | 85 | 84 | 83 | 85 | 84 | 44 | 82 |
12小时后的压缩应力保持率 | 84 | 82 | 80 | 83 | 82 | 42 | 80 |
表观密度[g/cm<sup>3</sup>] | 0.11 | 0.14 | 0.14 | 0.12 | 0.14 | 0.1 | 0.07 |
气泡直径[μm] | 40 | 70 | 80 | 100 | 95 | 75 | 100 |
气泡变动系数[-] | 0.35 | 0.32 | 0.3 | 0.4 | 0.42 | 0.4 | 0.4 |
气泡长径比 | 1.6 | 1.9 | 2.8 | 3.2 | 3.1 | 1.8 | 1.2 |
气泡率[%] | 90 | 88 | 85 | 88 | 86 | 90 | 93 |
气孔壁的厚度[μm] | 2 | 2.5 | 2.2 | 2.6 | 2.6 | 1 | 1 |
非发泡弯曲应力[MPa] | 13 | 13.5 | 10.2 | 9.4 | 6.5 | 3.5 | 40 |
压缩模量[kPa] | 265 | 300 | 370 | 220 | 205 | 22 | 500 |
厚度恢复率[%] | 92 | 90 | 88 | 91 | 92 | 70 | 75 |
由反复压缩带来的厚度变化率[%] | 1.2 | 1.1 | 1 | 0.8 | 0.8 | 7.3 | 1.1 |
冲击吸收率[%] | 40 | 45 | 40 | 30 | 30 | 20 | 24 |
应力分散性 | A | A | A | A | A | C | B |
如表1所示,本发明的树脂发泡体的“应力分散性”优异。这样的树脂发泡体在应用于图像显示装置时能够防止由按压导致的显示不均的方面是有利的。
工业实用性
本发明的树脂发泡体例如可以适宜地用作电子设备用的缓冲材料。
Claims (16)
1.一种树脂发泡体,其50%压缩载荷为5N/cm2~30N/cm2、6小时后的压缩应力保持率为50%以上、12小时后的压缩应力保持率为50%以上,并且具有气泡结构。
2.根据权利要求1所述的树脂发泡体,其50%压缩载荷为10N/cm2~30N/cm2。
3.根据权利要求1或2所述的树脂发泡体,其压缩模量为200kPa以上。
4.根据权利要求1~3中任一项所述的树脂发泡体,其非发泡弯曲应力为5MPa以上。
5.根据权利要求1~4中任一项所述的树脂发泡体,其由反复压缩带来的厚度变化率为10%以下。
6.根据权利要求1~5中任一项所述的树脂发泡体,其表观密度为0.02g/cm3~0.50g/cm3。
7.根据权利要求1~6中任一项所述的树脂发泡体,其厚度恢复率为75%以上。
8.根据权利要求1~7中任一项所述的树脂发泡体,其中,
所述树脂发泡体所具有的气泡的长径比为1.5以上。
9.根据权利要求1~8中任一项所述的树脂发泡体,其平均气泡直径为10μm~200μm。
10.根据权利要求1~9中任一项所述的树脂发泡体,其气泡率为30%以上。
11.根据权利要求1~10中任一项所述的树脂发泡体,其气泡直径的变动系数为0.5以下。
12.根据权利要求1~11中任一项所述的树脂发泡体,其气泡壁的厚度为0.1μm~10μm。
13.根据权利要求1~12中任一项所述的树脂发泡体,其包含聚烯烃类树脂。
14.根据权利要求13所述的树脂发泡体,其中,
所述聚烯烃类树脂为除聚烯烃类弹性体以外的聚烯烃与聚烯烃类弹性体的混合物。
15.根据权利要求1~14中任一项所述的树脂发泡体,其中,
在所述树脂发泡体的一面或两面具有热熔融层。
16.一种发泡构件,其具有树脂发泡层、和配置于该树脂发泡层的至少一侧的粘合剂层,
该树脂发泡层为权利要求1~15中任一项所述的树脂发泡体。