CN114436304A - 一种球形氧化铝载体的制备方法 - Google Patents
一种球形氧化铝载体的制备方法 Download PDFInfo
- Publication number
- CN114436304A CN114436304A CN202011114411.5A CN202011114411A CN114436304A CN 114436304 A CN114436304 A CN 114436304A CN 202011114411 A CN202011114411 A CN 202011114411A CN 114436304 A CN114436304 A CN 114436304A
- Authority
- CN
- China
- Prior art keywords
- mixing
- spherical
- alumina carrier
- carrier
- boehmite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 对比例1 | 对比例2 | 对比例3 | 对比例4 | 对比例5 | |
氧化铝载体 | S1 | S2 | S3 | S4 | S5 | S6 | S7 | S8 | S9 |
比表面积,m<sup>2</sup>/g | 254 | 273 | 221 | 234 | 263 | 269 | 258 | 187 | 262 |
孔容,mL/g | 0.96 | 0.99 | 0.92 | 0.93 | 0.97 | 0.96 | 0.95 | 0.84 | 0.96 |
孔分布,v% | |||||||||
10-20nm,% | 48 | 61 | 56 | 53 | 37 | 41 | 45 | 46 | 35 |
30-60nm,% | 13 | 15 | 17 | 15 | 7 | 12 | 9 | 12 | 7 |
项目 | |
密度(20℃),g/cm<sup>3</sup> | 0.98 |
S,wt% | 3.6 |
N,wt% | 0.31 |
Ni,µg/g | 51.4 |
V,µg/g | 81.2 |
催化剂编号 | Cat1 | Cat2 | Cat3 | Cat4 | Cat5 | Cat6 | Cat7 | Cat8 | Cat9 |
脱V+Ni率,wt% | 68.5 | 72.1 | 70.4 | 69.8 | 50.8 | 53.6 | 54.9 | 63.5 | 51.1 |
Claims (10)