CN114381929A - 一种涤纶布的柔化处理工艺 - Google Patents
一种涤纶布的柔化处理工艺 Download PDFInfo
- Publication number
- CN114381929A CN114381929A CN202210097173.4A CN202210097173A CN114381929A CN 114381929 A CN114381929 A CN 114381929A CN 202210097173 A CN202210097173 A CN 202210097173A CN 114381929 A CN114381929 A CN 114381929A
- Authority
- CN
- China
- Prior art keywords
- polyester fabric
- treatment process
- softening treatment
- soaking
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种涤纶布的柔化处理工艺，包括如下步骤：S1：将涤纶布放置在浸泡溶液里浸泡，浸泡时间为T1；S2：将浸泡后的涤纶布进行清洗，清洗时间为T2；S3：将清洗后的涤纶布进行灭菌处理，灭菌时间为T3，灭菌温度为TE1；S4：将灭菌后的涤纶布进行烘干，烘干时间为T4。本发明公开的涤纶布的柔化处理工艺，方法简单，可以提高涤纶布的柔软度，具有良好的抗菌作用和耐变黄性能。此涤纶布制成的产品具有较好的柔和度和舒适度，有效的提高了产品的舒适性。
Description
技术领域
本发明涉及布料加工技术领域，具体地是涉及一种涤纶布的柔化处理工艺。
背景技术
聚酯纤维，俗称“涤纶”。是由有机二元酸和二元醇缩聚而成的聚酯经纺丝所得的合成纤维，简称PET纤维，属于高分子化合物。于1941年发明，是当前合成纤维的第一大品种。涤纶布是日常生活中用的比较广泛的一种化纤服装面料，它的优点抗皱性和保持性都很好，尤其耐磨性非常好。它的缺点则是不柔和导致涤纶布制作的产品使用时不柔软和不舒适。现有技术中的柔化处理工艺复杂，且柔软性难以满足人们越来越高的需求。
因此，本发明的发明人亟需构思一种新技术以改善其问题。
发明内容
本发明旨在提供一种涤纶布的柔化处理工艺，其方法简单，并且可以有效增加涤纶布的柔软性。
为解决上述技术问题，本发明的技术方案是：
一种涤纶布的柔化处理工艺，包括如下步骤：
S1：将涤纶布放置在浸泡溶液里浸泡，浸泡时间为T1；
S2：将浸泡后的涤纶布进行清洗，清洗时间为T2；
S3：将清洗后的涤纶布进行灭菌处理，灭菌时间为T3，灭菌温度为TE1；
S4：将灭菌后的涤纶布进行烘干，烘干时间为T4。
优选的，所述步骤S1中的浸泡时间T1在25-35min之间。
优选的，所述步骤S2中的清洗时间T2在10-25min之间。
优选的，所述步骤S3中的灭菌时间T3在15-30min之间。
优选的，所述步骤S4中的灭菌时间T4在25-35min之间。
优选的，所述步骤S1中的浸泡溶液为84消毒液与水按照一定比例混合。
优选的，所述步骤S1中的浸泡溶液为84消毒液与水按照1:6的比例混合。
优选的，所述步骤S2中将浸泡后的涤纶布放入洗衣机中进行清洗。
优选的，所述步骤S3中将清洗后的涤纶布放置于压力灭菌柜中进行灭菌处理。
优选的，所述步骤S4中将灭菌后的涤纶布放入洗衣机中进行烘干。
采用上述技术方案，本发明至少包括如下有益效果：
本发明所述的涤纶布的柔化处理工艺，方法简单，可以提高涤纶布的柔软度，具有良好的抗菌作用和耐变黄性能。此涤纶布制成的产品具有较好的柔和度和舒适度，有效的提高了产品的舒适性。
附图说明
图1为本发明所述的涤纶布的柔化处理工艺的流程图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
如图1所示，为符合本发明的一种涤纶布的柔化处理工艺，包括如下步骤：
S1：将涤纶布放置在浸泡溶液里浸泡，浸泡时间为T1；
S2：将浸泡后的涤纶布进行清洗，清洗时间为T2；
S3：将清洗后的涤纶布进行灭菌处理，灭菌时间为T3，灭菌温度为TE1；
S4：将灭菌后的涤纶布进行烘干，烘干时间为T4。
优选的，所述步骤S1中的浸泡时间T1在25-35min之间。
优选的，所述步骤S2中的清洗时间T2在10-25min之间。
优选的，所述步骤S3中的灭菌时间T3在15-30min之间。
优选的，所述步骤S4中的灭菌时间T4在25-35min之间。
优选的，所述步骤S1中的浸泡溶液为84消毒液与水按照一定比例混合。
优选的，所述步骤S1中的浸泡溶液为84消毒液与水按照1:6的比例混合。
优选的，所述步骤S2中将浸泡后的涤纶布放入洗衣机中进行清洗。
优选的，所述步骤S3中将清洗后的涤纶布放置于压力灭菌柜中进行灭菌处理。
优选的，所述步骤S4中将灭菌后的涤纶布放入洗衣机中进行烘干。
优选的，所述步骤S3中的灭菌温度TE1在115℃-130℃之间。更为优选的灭菌温度TE1为121℃。
下面结合附图和实施例来具体描述本发明。下述实施例中所用的试剂、材料等，如无特殊说明，均可以从商业途径获得。
实施例1
一种涤纶布的柔化处理工艺，包括以下步骤：
1.将涤纶布放置浸泡溶液(84消毒液与水配比1:6)里浸泡25min。
2.将浸泡后的涤纶布放置洗衣机中清洗10min。
3.将清洗后的涤纶布放置于压力灭菌柜中15min，设置温度为121℃。
4.将灭菌后的涤纶布放置洗衣机烘干25min。
实施例2
一种涤纶布的柔化处理工艺，包括以下步骤：
1.将涤纶布放置浸泡溶液(84消毒液与水配比1:6)里浸泡30min。
2.将浸泡后的涤纶布放置洗衣机清洗15min。
3.将清洗后的涤纶布放置于压力灭菌柜中20min，设置温度为121℃。
4.将灭菌后的涤纶布放置洗衣机烘干30min。
实施例3
一种涤纶布的柔化处理工艺，包括以下步骤：
1.将涤纶布放置浸泡溶液(84消毒液与水配比1:6)里浸泡30min。
2.将浸泡后的涤纶布放置洗衣机清洗20min。
3.将清洗后的涤纶布放置于压力灭菌柜中25min，设置温度为115℃。
4.将灭菌后的涤纶布放置洗衣机烘干35min。
实施例4
一种涤纶布的柔化处理工艺，包括以下步骤：
1.将涤纶布放置浸泡溶液(84消毒液与水配比1:6)里浸泡35min。
2.将浸泡后的涤纶布放置洗衣机清洗25min。
3.将清洗后的涤纶布放置于压力灭菌柜中30min，设置温度为130℃。
4.将灭菌后的涤纶布放置洗衣机烘干35min。
对比例1：申请号为CN201610543114.X，发明名称为“一种棉纤维的柔化处理工艺”中公开了一种柔化处理步骤，具体如下：
A、预处理：将棉纤维在pH为7-8的碱性溶液中煮沸，降低温度至40-50℃，加入碱性果胶酶进行脱胶10-15min，再煮沸使酶失活；
B、漂白：将水温降低至30-40℃，加入5-10g/L的25％双氧水、3-5g/L的漂白稳定剂、3-5g/L的壳聚糖，保温25-35min；
C、染色：将棉面料取出并简单冲洗后，放入天然染料染液中进行染色，其中天然染料的加入量为5-15g/L，匀染剂1-2g/L，浴比为1:20-45，浸泡20-30min；
D、柔化处理：用柔化剂溶液浸泡棉纤维，所述的柔化剂溶液包括9-11g/L有机硅柔软剂、60-80g/L丙三醇、3-5g/L润湿剂、2-5g/L EDTA、0.2-0.5g/L桑叶粉，浴比为1:20-30，温度50-55℃，处理时间90-120min，然后以0.5-0.8℃/min的速度升温至80℃；
E、将棉纤维烘干到含水率8-10％；对棉纤维进行开清棉、梳棉、精梳、纺粗纱、纺细纱，得到高强度柔化纱线产品。
经检测，经过实施例1-4和对比例1所述的工艺处理的样品柔软度测试结果详见如下表格1(参考标准GB/T 18318.3-2009)。
表格1
经检测，首先经过本发明工艺处理的样品其柔软度明显优于对比例1，其次经过本发明工艺处理的样品其对黄金葡萄球菌、大肠杆菌、白色念珠球菌的抑菌率达到95％以上，其优于对比例1中的85％。再次经过本发明工艺处理的样品，水洗60次以后，未发现明显的黄变现象，其耐黄变性能也明显优于对比例1。最后本发明的柔化处理工艺简单易行，工业用料较少，在保证质量的前提下有利于控制企业的生产加工成本，提高生产效益，具有较好的市场应用前景。
本发明所述的涤纶布柔化处理工艺方法简单，可以提高涤纶布的柔软度，具有良好的抗菌作用和耐变黄性能。此涤纶布制成的产品具有较好的柔和度和舒适度，有效的提高了产品的舒适性。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (10)
1.一种涤纶布的柔化处理工艺，其特征在于，包括如下步骤：
S1：将涤纶布放置在浸泡溶液里浸泡，浸泡时间为T1；
S2：将浸泡后的涤纶布进行清洗，清洗时间为T2；
S3：将清洗后的涤纶布进行灭菌处理，灭菌时间为T3，灭菌温度为TE1；
S4：将灭菌后的涤纶布进行烘干，烘干时间为T4。
2.如权利要求1所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S1中的浸泡时间T1在25-35min之间。
3.如权利要求1或2所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S2中的清洗时间T2在10-25min之间。
4.如权利要求1-3任一所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S3中的灭菌时间T3在15-30min之间。
5.如权利要求1-4任一所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S4中的灭菌时间T4在25-35min之间。
6.如权利要求1-5任一所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S1中的浸泡溶液为84消毒液与水按照一定比例混合。
7.如权利要求1-6任一所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S1中的浸泡溶液为84消毒液与水按照1:6的比例混合。
8.如权利要求1-7任一所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S2中将浸泡后的涤纶布放入洗衣机中进行清洗。
9.如权利要求1-8任一所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S3中将清洗后的涤纶布放置于压力灭菌柜中进行灭菌处理。
10.如权利要求1-9任一所述的涤纶布的柔化处理工艺，其特征在于：所述步骤S4中将灭菌后的涤纶布放入洗衣机中进行烘干。