CN114206747B - 用于蒸煮应用的防沾污包装膜 - Google Patents
用于蒸煮应用的防沾污包装膜 Download PDFInfo
- Publication number
- CN114206747B CN114206747B CN202080055234.XA CN202080055234A CN114206747B CN 114206747 B CN114206747 B CN 114206747B CN 202080055234 A CN202080055234 A CN 202080055234A CN 114206747 B CN114206747 B CN 114206747B
- Authority
- CN
- China
- Prior art keywords
- white
- region
- packaging film
- film
- multilayer film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
为了减少在食品产品的包装内蒸煮加工期间发生的沾污的量,使用包装膜,该包装膜包括白色多层膜,该白色多层膜具有在该包装膜的暴露表面上的密封区域、含有白色颜料的白色区域和位于该白色区域与该密封区域之间的阻挡区域,其中该密封区域和该阻挡区域的组合厚度是该白色多层膜的厚度的至少70%。
Description
技术领域
本披露涉及用于包装蒸煮应用中的食品的膜结构、具体地白色膜结构。本文所述的层压物表现出减少的来自食品产品的沾污。
背景技术
蒸煮操作用于热加工食品和灭菌初级包装部件。将包装在可蒸煮容器中的食品转移至高压灭菌器单元中,在该高压灭菌器单元中使其经受包括潮湿或湿润环境、通常超过水的沸点的温度和升高的压力的蒸煮条件持续特定时间段。因此,可蒸煮容器被设计成耐受蒸煮条件。
使用多层柔性高阻隔膜包装蒸煮灭菌的食物是常见的。例如,柔性膜可以被热密封成立式袋的形式、填充有食品产品并且气密地密封,然后蒸煮加工。用于蒸煮加工的另一种常见的包装形式是聚合物或金属托盘,将柔性盖热密封至其上以气密地包封食品产品。多种多样的食品产品可以包封在蒸煮包装内,包括汤、蔬菜或带有酱汁的意大利面食。
常常,包装膜印刷有适于零售销售食品产品的图形。作为图形的背景,膜的一部分通常是白色着色的。这典型地通过包括连同图形一起的纯白色油墨层,或者通过将在印刷图形后面的膜的聚合物层之一着色进行。
当使用白色着色膜时,膜可能在蒸煮过程期间被食品产品沾污。沾污可能是不均匀和黄色的,从而为包装提供不希望的外观。在一些情况下,白色着色膜可以使用含有聚合物诸如聚酰胺或乙烯乙烯醇共聚物(EVOH)的阻挡层。这些聚合物可以防止食品成分沾污白色膜。然而,在一些情况下,希望避免使用聚酰胺和/或EVOH,因为它们增加了成本和结构的复杂性以及产生更难以回收的整体膜结构。
发明内容
本文披露了用于蒸煮加工的包装膜,这些包装膜防止可能由于食品产品成分而发生的沾污。这些包装膜含有白色多层膜,该白色多层膜具有a)密封区域,该密封区域位于该包装膜的暴露表面上,b)白色区域,该白色区域包含按重量计从3.5%至35%的量的白色颜料和基于丙烯的聚合物,以及c)阻挡区域,该阻挡区域位于该密封区域与该白色区域之间。该密封区域和该阻挡区域各自含有基于丙烯的聚合物并且各自基本上不含该白色颜料。该密封区域和该阻挡区域的组合厚度是白色多层膜厚度的至少70%。包装食品产品可以使用该包装膜生产,并且该多层膜的该白色区域将比类似的常规包装膜沾污更少。
用于蒸煮加工的防沾污包装膜的另一个实施例可以包括白色多层膜,该白色多层膜具有a)密封区域,该密封区域位于该包装膜的暴露表面上,b)白色区域,以及c)阻挡区域,该阻挡区域位于该密封区域与该白色区域之间。该白色区域包含基于丙烯的聚合物和按重量计从3.5%至35%的量的白色颜料,该密封区域和该阻挡区域各自含有基于丙烯的聚合物并且各自基本上不含该白色颜料,并且该密封区域和该阻挡区域的组合厚度是至少2.7密耳(68.6微米)。
用于蒸煮加工的防沾污包装膜的另一个实施例具有外部抗损伤层(abuselayer)、阻隔层和白色多层膜,该白色多层膜具有第一主表面和第二主表面。该白色多层膜具有:具有基于聚丙烯的聚合物的密封区域,该密封区域位于该白色多层膜的该第一主表面上并且位于该包装膜的暴露表面上;和白色区域,该白色区域具有的厚度为白色多层膜厚度的30%或更少,并且位于该白色多层膜的该第二主表面上。该阻隔层在该外部抗损伤层与该白色多层膜之间,该白色区域包含按重量计在3.5%与35%之间的白色颜料,并且该白色多层膜另外基本上不含白色颜料。
附图说明
结合附图考虑以下对本披露的各实施例的详细描述,可以更全面地理解本披露,其中:
图1A和1B是使用防沾污包装膜的示例性包装产品的平面图;
图2是示例性防沾污包装膜的截面视图;
图3是可以用于防沾污包装膜中的示例性白色多层膜的截面视图;以及
图4是示例性防沾污包装膜的另一截面视图。
附图示出了一些但并非所有的实施例。附图中描绘的元件是说明性的并且不一定按比例绘制,并且相同的(或类似的)附图标记在整个附图中代表相同的(或类似的)特征。
具体实施方式
本文描述了防沾污包装膜,这些防沾污包装膜包括白色多层膜、适用于蒸煮过程。包装膜可以用于构造填充有食品产品的包装。然后将包装气密地密封且然后蒸煮加工。本文所述的膜在蒸煮加工之后表现出减少的沾污并且具有改善的外观。
防沾污包装膜可以用于多种多样的包装产品中。包装可以具有任何合适的形式,包括但不限于图1A和1B所示的那些。图1A是具有如对于多种零售食品产品来说典型的立式袋形式的包装产品10。立式袋具有前面片和后面片以及角撑片,其中至少一个由本文披露的防沾污包装膜制成。如所示,至少前面片包括防沾污包装膜20,因为前面可能对于具有最佳视觉外观并具有最少化产品沾污是最至关重要的。将立式袋的片通过热密封22连接,从而在其中容纳产品30。图1B是具有成形杯或托盘40的形式的包装产品10,其中作为盖的防沾污包装膜20通过热密封22附接至杯或托盘40上。将防沾污包装膜通过膜的密封区域热密封至其自身、另一种防沾污包装膜或另一种包装部件。虽然本文所述的包装通过热密封形成进行描述,但本发明的包装不限于热密封并且可以通过其他密封工艺(诸如超声密封)进行组装。
可以包装在蒸煮包装中的食品产品包括但不限于带有酱汁、豆类、肉汁或汤类的米或意大利面食。特别容易沾污包装并且将最受益于防沾污包装膜的食品产品是具有高脂肪或油含量的那些和具有强烈颜色的那些。
本文所述的防沾污包装膜使用已经白色着色的特定白色多层膜。将白色颜料添加至特定层中,并且禁止于特定层中,以帮助限制膜的沾污。除了白色多层膜,包装膜的一些实施例具有外部抗损伤层和阻隔层。
如本文所用,术语“层”是指作为单一材料类型或材料的均匀共混物的结构的膜的结构单元。层可以是单一聚合物,单一聚合物类型的材料的共混物或各种聚合物的共混物,可以含有金属材料并可以具有添加剂。层可以与膜连续或可以是不连续或图案化的。层具有与长度和宽度相比显著小的厚度,并且因此定义为具有两个主表面,其面积由层的长度和宽度限定。外部层是仅在主表面之一处连接至另一个层的层。换句话说,外部层的一个主表面是暴露的。内部层是在两个主表面处连接至另一个层的层。换句话说,该层在两个其他层之间。
如本文所用,术语“区域”是指彼此直接相邻且彼此连接的一个或多个层。区域可以含有具有相同或不同的材料组成的层。
类似地,如本文所用,术语“膜”是指由层和/或区域和/或膜构建的幅材,其中全部彼此直接相邻且彼此连接。膜可以被描述为具有与膜的长度和宽度相比显著小的厚度。膜具有两个主表面,其面积由膜的长度和宽度限定。
示例性防沾污包装膜20的截面视图示出于图2中。包装膜20在暴露主表面24之一上具有外部抗损伤层100,并且在另一个暴露主表面24上具有白色多层膜300。阻隔层200在外部抗损伤层100与白色多层膜300之间。在所示的层与膜之间可以存在粘合剂或底漆。层和膜的结合可以通过熟悉膜转换的技术人员已知的任何方法进行。
外部抗损伤层可以具有任何组成。外部抗损伤层可以是取向膜,诸如双轴取向聚酰胺(BOPA)膜、双轴取向聚酯(OPET)膜或双轴取向聚丙烯(BOPP)膜,如典型地用于柔性包装膜中的。外部抗损伤层可以是涂覆的抗损伤漆。外部抗损伤层可以是多层膜中的单层。外部抗损伤层的厚度可以是从约1微米至约50微米,优选地在2微米与25微米之间。外部抗损伤层是透明的,使得可以通过外部抗损伤层观察到防沾污包装膜的任何印刷标记和白色多层膜部分。
防沾污包装膜的阻隔层确保膜具有低氧气和/或湿气透过率,并且包装产品将在保质期内保持高品质。一些蒸煮加工的包装产品可以在非冷藏条件下在延长的时间段(即超过一年)内保持稳定,只要包装具有足够的阻隔特性。阻隔层可以是已知在蒸煮包装中使用的任何材料,诸如无机氧化物涂层。无机氧化物涂层提供优异的阻隔性并且是透明的,从而允许通过阻隔层观察到白色多层膜。阻隔层可以是任何其他组成,只要它是透明的并且不与本文所述的包装膜的目的矛盾。
防沾污包装膜的阻隔层在外部抗损伤层与白色多层膜之间。在一些实施例中,阻隔层与外部抗损伤层直接相邻且连接至外部抗损伤层。在一些实施例中,阻隔层附接至另一个膜或层或者是另一个膜或层的一部分,并且整个复合材料位于外部抗损伤层与白色多层膜之间。
白色多层膜位于防沾污包装膜的主表面之一上,并且为膜提供白色外观和不透明度。白色多层膜的细节将在下面讨论。
另外,包装膜可以包括印刷标记的层。印刷标记典型地是置于层和/或膜之间的油墨颜料的不连续层,并且通过外部抗损伤层可观察到。这些印刷标记是在最终包装上看到的图形。
防沾污包装膜可以具有用于粘附功能的一个或多个层,诸如粘结层或粘合剂层。术语“粘结层”、“粘合剂”、“粘合剂层”或“粘合剂涂层”是指部分或整体地置于一个或多个层上以促进该层与另一个表面粘附的材料。“粘结层”是指为了在两个其他层之间提供粘附而与其他层共挤出的聚合物基材料。此类层被放置在两个膜、区域或层之间以将这两种材料保持在彼此相对的位置并且防止不希望的分层。
防沾污包装膜可以含有其他功能层,诸如但不限于主体层、用于刚度的层或另外的阻隔层,只要所含的这些层不损害膜的蒸煮性、防沾污性或整体功能性。防沾污包装膜的厚度可以是从约50微米至约500微米,优选地在50微米与200微米之间。
用于防沾污包装膜中的示例性白色多层膜的截面示出于图3中。在此实施例中,白色多层膜300由位于白色多层膜的主表面324之一上的密封区域330、位于相反的主表面324上的白色区域310和位于密封区域330与白色区域310之间的阻挡区域320组成。阻挡区域320还与其他两个层直接相邻且与其他两个层连接。图3中还示出了由标记为400的双头箭头指示的白色多层膜的厚度。类似地,箭头410和402分别指示白色区域的厚度以及密封区域和阻挡区域的组合厚度。
示例性防沾污包装膜的截面示出于图4中。在此实施例中,防沾污包装膜20具有位于暴露主表面24上的外部抗损伤层100、白色多层膜300和位于外部抗损伤层100与白色多层膜300之间的阻隔层200。白色多层膜300具有白色区域310和密封区域330。图4中还示出了由标记为400的双头箭头指示的白色多层膜的厚度、和白色层的厚度。
可以通过任何已知的手段在单一过程中或连续步骤中组装白色多层膜。理想地,通过吹塑膜挤出或流延挤出在单一加工步骤中完全共挤出白色多层膜。白色多层膜的总厚度可以是从约50微米至约450微米,优选地在50微米与175微米之间。
如所述,白色多层膜的一些实施例具有密封区域和白色区域。一些白色多层膜受益于密封区域与白色区域之间的另外的阻挡区域。白色多层膜的一些实施例由密封区域、阻挡区域和白色区域组成。如将讨论的,每个区域可以具有一个或多个层。理想地,白色多层膜不含(或基本上不含)含有聚酰胺和/或EVOH的层。含有聚酰胺或EVOH的膜固有地防沾污,因为这些材料有效地阻挡沾污组分通过至白色层。本文所述的解决方案适用于在白色多层膜外具有阻隔层(诸如本文所述的无机氧化物层)的防沾污包装膜。
如所述,白色多层膜的密封区域位于防沾污包装膜的暴露表面上,且因此也位于白色多层膜的主表面之一上。此层的功能是为包装提供良好的密封性。用于密封区域的适当配制品是已知在蒸煮加工中表现良好的那些,典型地掺入各种类型的基于丙烯的聚合物(诸如聚丙烯均聚物、聚丙烯抗冲共聚物、聚丙烯无规共聚物、多相聚丙烯共聚物)的共混物。理想地,密封区域含有基于丙烯的聚合物的共混物,该共混物包含按重量计高达约10%的量的聚丙烯均聚物。在一些实施例中,密封区域具有含有橡胶改性的聚丙烯共聚物和按重量计高达10%的聚丙烯均聚物的共混物。
密封区域可以由一个或多个层构成。密封区域的厚度应在约8微米与约50微米之间。当在包装产品中使用防沾污包装膜时,密封区域与产品和/或包装的顶部空间直接接触。理想地,密封区域不含有任何白色颜料。
防沾污包装膜的一些实施例具有阻挡区域,该阻挡区域位于白色区域与密封区域之间。此层可以更具体地配制以帮助阻挡沾污组分,因为此层没有必须执行密封功能的负担。阻挡区域可以含有包含聚丙烯均聚物的共混物。聚丙烯均聚物可以以按重量计从约30%至100%的水平存在于阻挡区域中。聚丙烯均聚物可以以按重量计至少20%的水平存在于阻挡区域中。可以根据阻挡区域的厚度改变阻挡区域中存在的聚丙烯均聚物的水平。较厚的阻挡区域可以含有较少的聚丙烯均聚物,并且仍然具有相同的沾污阻挡性能。防沾污包装膜的一些实施例具有含有丙烯-乙烯共聚物和聚丙烯均聚物的共混物的阻挡区域,其中均聚物以按重量计至少10%的水平存在。防沾污包装膜的一些实施例具有含有按重量计0%至10%的水平的橡胶改性的聚丙烯共聚物的阻挡区域。
一些基于丙烯的共聚物含有聚丙烯均聚物相,该相也可以有助于阻挡沾污组分。已经发现,使用最小化橡胶改性含量和/或最大化聚丙烯均聚物含量的基于丙烯的聚合物共混物大大减少了沾污组分从食品产品至白色集中区的转移(即阻挡了这些沾污组分)。除了此共混物考虑之外,阻挡层不含有任何白色颜料也是至关重要的。
阻挡区域可以含有多于一个层,并且每个层可以具有基于丙烯的聚合物的不同共混物。阻挡区域中的一些层可以不具有任何均聚物聚丙烯。理想地,阻挡区域不含有任何白色颜料。在防沾污包装膜的一些实施例中,白色区域和阻挡区域的组合厚度是白色多层膜的厚度的至少70%。在防沾污包装膜的一些实施例中,白色区域和阻挡区域的组合厚度是至少68.5微米。
白色多层膜应具有含有白色颜料的白色区域。用于膜中的白色颜料典型地是二氧化钛。应将白色颜料以按白色区域的重量计3.5%至35%的水平装载至白色区域中。可以通过使用含有基于丙烯的载体聚合物和高水平(即50%)的白色颜料的母料材料将白色颜料装载至白色区域中。
理想地,白色区域位于尽可能远离密封区域的位置。因此,白色区域理想地位于白色多层膜的与包括密封区域的表面相反的主表面上。在一些实施例中,与白色多层膜的总厚度相比,白色区域的厚度是32%、或30%或更少。
实例和数据
测试1/实例1
生产具有密封区域、阻挡区域和白色区域的实例1防沾污包装膜。首先,通过共挤出生产三层白色多层膜。白色多层膜的每个层对应于本文所述的防沾污包装膜的区域之一,并且在下表1中概述。将三层膜作为共挤出结构在吹塑膜线上运行,总厚度为约101.6微米。在实例1中,每个区域含有一个层。
然后将白色多层膜层压以产生(12微米的涂覆有氧化铝的OPET)/印刷物/粘合剂/60ga BON/(白色多层膜)的防沾污包装膜结构。此膜在蒸煮试验中具有良好的性能,与含有更靠近膜的密封表面的白色颜料的可比材料相比显示出显著更少的沾污。
表1:用于测试1的白色多层膜
-PP共聚物1是具有EP橡胶(具有10%-15%乙烯)的分散相和均聚物PP的连续相的多相聚丙烯共聚物
-PP共聚物2是具有EP橡胶的分散相和丙烯-乙烯无规共聚物的连续相的多相聚丙烯共聚物
-白色颜料母料是具有按重量计50%二氧化钛装载量的聚丙烯均聚物载体
测试2/实例2-4和对比实例A-B
通过吹塑膜工艺生产五种白色多层膜;实例2-4以及对比实例A和B。每种膜具有密封区域、阻挡区域和白色区域,每个区域是单层(即膜具有三个层),并且膜结构和层内含物的细节汇总于表2中。
将白色多层膜热密封成三侧密封袋,这些三侧密封袋在袋的内表面上具有接触产品的密封区域。装载至袋中的产品是番茄酱、橄榄油、黑胡椒和姜黄的共混物。将袋气密地密封并且在蒸煮室中加工。
表2:用于测试2的白色多层膜细节
-PP共聚物1是具有EP橡胶(具有10%-15%乙烯)的分散相和均聚物PP的连续相的多相聚丙烯共聚物
-PP共聚物2是具有EP橡胶的分散相和丙烯-乙烯无规共聚物的连续相的多相聚丙烯共聚物
-hPP是聚丙烯均聚物
-白色颜料MB是具有按重量计50%二氧化钛装载量的聚丙烯均聚物载体
在蒸煮加工之后,将袋排空并且评价其沾污性能。通过比较黄度指数(Yi)评价沾污的相对水平,该黄度指数根据ASTM D1925使用具有25mm孔径的爱色丽(X-Rite)Color i5型号分光光度计来测量。对于每种实例膜,记录六次测量值并且报告平均值。更高的黄度指数表明膜更黄并且因此被更高度地沾污。沾污测量值的结果给出于表3中。
表3:测试2的沾污结果
样品 | 平均黄度指数 |
对比实例A | 65 |
对比实例B | 40 |
实例2 | 34 |
实例3 | 31 |
实例4 | 29 |
实施例:
A.一种用于蒸煮加工的防沾污包装膜,该防沾污包装膜包括白色多层膜,该白色多层膜包括:
密封区域,该密封区域位于该包装膜的暴露表面上,
白色区域,该白色区域包含按重量计从3.5%至35%的量的白色颜料和基于丙烯的聚合物,以及
阻挡区域,该阻挡区域位于该密封区域与该白色区域之间,
其中
该密封区域和该阻挡区域各自包含基于丙烯的聚合物并且各自基本上不含该白色颜料,并且
该密封区域和该阻挡区域的组合厚度是白色多层膜厚度的至少70%。
B.根据任一前述实施例所述的防沾污包装膜,其中该阻挡区域包含丙烯-乙烯共聚物和按重量计至少10%的量的聚丙烯均聚物的共混物。
C.根据任一前述实施例所述的防沾污包装膜,其中该阻挡区域包含按重量计在0%与10%之间的量的橡胶改性的聚丙烯共聚物。
D.根据任一前述实施例所述的防沾污包装膜,其中该密封区域包含橡胶改性的聚丙烯共聚物和高达10%的均聚物聚丙烯的共混物。
E.根据任一前述实施例所述的防沾污包装膜,其中该白色多层膜厚度在50微米与500微米之间。
F.根据任一前述实施例所述的防沾污包装膜,该防沾污包装膜进一步包括印刷标记。
G.根据任一前述实施例所述的防沾污包装膜,其中该白色多层膜不含EVOH或聚酰胺。
H.根据任一前述实施例所述的防沾污包装膜,该防沾污包装膜进一步包括外部抗损伤层和阻隔层,该阻隔层位于该外部抗损伤层与该白色多层膜之间。
I.根据实施例H所述的防沾污包装膜,其中该阻隔层是无机氧化物涂层。
J.根据实施例H或I所述的防沾污包装膜,其中该外部抗损伤层和该阻隔层两者是透明的,并且该白色多层膜的该白色区域可以通过该外部抗损伤层观察到。
K.一种包装产品,该包装产品包括根据任一前述实施例所述的防沾污包装膜和食品产品,其中该多层膜的该白色区域已经在蒸煮灭菌过程期间被该食品产品沾污。
L.一种用于蒸煮加工的防沾污包装膜,该防沾污包装膜包括白色多层膜,该白色多层膜包括:
密封区域,该密封区域位于该包装膜的暴露表面上,
白色区域,以及
阻挡区域,该阻挡区域位于该密封区域与该白色区域之间,
其中
该白色区域包含基于丙烯的聚合物和按重量计从3.5%至35%的量的白色颜料,
该密封区域和该阻挡区域各自包含基于丙烯的聚合物并且各自基本上不含该白色颜料,并且
该密封区域和该阻挡区域的组合厚度是至少68.6微米。
M.根据实施例L所述的防沾污包装膜,其中该阻挡区域包含丙烯-乙烯共聚物和按重量计至少10%的量的聚丙烯均聚物的共混物。
N.根据实施例L所述的防沾污包装膜,其中该阻挡区域包含按重量计在0%与10%之间的量的橡胶改性的聚丙烯共聚物。
O.根据实施例L、M或N所述的防沾污包装膜,其中该密封区域包含橡胶改性的聚丙烯共聚物和高达10%的均聚物聚丙烯的共混物。
P.一种用于蒸煮加工的防沾污包装膜,该防沾污包装膜包括外部抗损伤层、阻隔层和白色多层膜,该白色多层膜包括第一主表面和第二主表面并且包括:
包含基于聚丙烯的聚合物的密封区域,该密封区域位于该白色多层膜的该第一主表面上并且位于该包装膜的暴露表面上,以及
白色区域,该白色区域包括为白色多层膜厚度的30%或更少的白色区域厚度,该白色区域位于该白色多层膜的该第二主表面上,
其中该阻隔层在该外部抗损伤层与该白色多层膜之间,其中该白色区域包含按重量计在3.5%与35%之间的白色颜料,并且其中该白色多层膜另外基本上不含白色颜料。
Q.根据实施例P所述的防沾污包装膜,该防沾污包装膜进一步包括阻挡区域,该阻挡区域位于该密封区域与该白色区域之间。
R.根据实施例Q所述的防沾污包装膜,其中该阻挡区域包含按重量计至少20%的量的聚丙烯均聚物。
S.根据实施例P、Q或R所述的防沾污包装膜,其中该白色多层膜不含EVOH或聚酰胺。
T.一种包装产品,该包装产品包括根据实施例L至S中任一项所述的防沾污包装膜和食品产品,其中该多层膜的该白色区域已经在蒸煮灭菌过程期间被该食品产品沾污。
Claims (19)
1.一种用于蒸煮加工的防沾污包装膜,该防沾污包装膜包括白色多层膜,该白色多层膜包括:
密封区域,该密封区域位于该包装膜的暴露表面上,
白色区域,该白色区域包含按重量计从3.5%至35%的量的白色颜料和基于丙烯的聚合物,以及
阻挡区域,该阻挡区域位于该密封区域与该白色区域之间,其中
该密封区域和该阻挡区域各自包含基于丙烯的聚合物并且各自基本上不含该白色颜料,该阻挡区域含有包含聚丙烯均聚物的共混物,并且
该密封区域和该阻挡区域的组合厚度是白色多层膜厚度的至少70%。
2.根据权利要求1所述的防沾污包装膜,其中该阻挡区域包含丙烯-乙烯共聚物和按重量计至少10%的量的聚丙烯均聚物的共混物。
3.根据权利要求1所述的防沾污包装膜,其中该阻挡区域包含按重量计在0%与10%之间的量的橡胶改性的聚丙烯共聚物。
4.根据权利要求1所述的防沾污包装膜,其中该密封区域包含橡胶改性的聚丙烯共聚物和高达10%的均聚物聚丙烯的共混物。
5.根据权利要求1所述的防沾污包装膜,其中该白色多层膜厚度在50微米与500微米之间。
6.根据权利要求1所述的防沾污包装膜,该防沾污包装膜进一步包括印刷标记。
7.根据权利要求1所述的防沾污包装膜,其中该白色多层膜不含EVOH或聚酰胺。
8.根据权利要求1所述的防沾污包装膜,该防沾污包装膜进一步包括外部抗损伤层和阻隔层,该阻隔层位于该外部抗损伤层与该白色多层膜之间。
9.根据权利要求8所述的防沾污包装膜,其中该阻隔层是无机氧化物涂层。
10.根据权利要求8所述的防沾污包装膜,其中该外部抗损伤层和该阻隔层两者是透明的,并且该白色多层膜的该白色区域能够通过该外部抗损伤层观察到。
11.一种包装产品,该包装产品包括根据权利要求1所述的防沾污包装膜和食品产品,其中该多层膜的该白色区域已经在蒸煮灭菌过程期间被该食品产品沾污。
12.一种用于蒸煮加工的防沾污包装膜,该防沾污包装膜包括白色多层膜,该白色多层膜包括:
密封区域,该密封区域位于该包装膜的暴露表面上,
白色区域,以及
阻挡区域,该阻挡区域位于该密封区域与该白色区域之间,其中
该白色区域包含基于丙烯的聚合物和按重量计从3.5%至35%的量的白色颜料,
该密封区域和该阻挡区域各自包含基于丙烯的聚合物并且各自基本上不含该白色颜料,该阻挡区域含有包含聚丙烯均聚物的共混物,并且
该密封区域和该阻挡区域的组合厚度是至少68.6微米。
13.根据权利要求12所述的防沾污包装膜,其中该阻挡区域包含丙烯-乙烯共聚物和按重量计至少10%的量的聚丙烯均聚物的共混物。
14.根据权利要求12所述的防沾污包装膜,其中该阻挡区域包含按重量计在0%与10%之间的量的橡胶改性的聚丙烯共聚物。
15.根据权利要求12所述的防沾污包装膜,其中该密封区域包含橡胶改性的聚丙烯共聚物和高达10%的均聚物聚丙烯的共混物。
16.一种用于蒸煮加工的防沾污包装膜,该防沾污包装膜包括外部抗损伤层、阻隔层和白色多层膜,该白色多层膜包括第一主表面和第二主表面并且包括:
包含基于聚丙烯的聚合物的密封区域,该密封区域位于该白色多层膜的该第一主表面上并且位于该包装膜的暴露表面上,
白色区域,该白色区域包括为白色多层膜厚度的30%或更少的白色区域厚度,该白色区域位于该白色多层膜的该第二主表面上,以及
阻挡区域,该阻挡区域位于该密封区域与该白色区域之间,并且该阻挡区域含有包含聚丙烯均聚物的共混物,
其中该阻隔层在该外部抗损伤层与该白色多层膜之间,其中该白色区域包含按重量计在3.5%与35%之间的白色颜料,并且其中该白色多层膜另外基本上不含白色颜料。
17.根据权利要求16所述的防沾污包装膜,其中该阻挡区域包含按重量计至少20%的量的聚丙烯均聚物。
18.根据权利要求16所述的防沾污包装膜,其中该白色多层膜不含EVOH或聚酰胺。
19.一种包装产品,该包装产品包括根据权利要求16所述的防沾污包装膜和食品产品,其中该多层膜的该白色区域已经在蒸煮灭菌过程期间被该食品产品沾污。