CN114188514A - 一种具有良好低温性能的正极浆料及制备方法和应用 - Google Patents
一种具有良好低温性能的正极浆料及制备方法和应用 Download PDFInfo
- Publication number
- CN114188514A CN114188514A CN202111370480.7A CN202111370480A CN114188514A CN 114188514 A CN114188514 A CN 114188514A CN 202111370480 A CN202111370480 A CN 202111370480A CN 114188514 A CN114188514 A CN 114188514A
- Authority
- CN
- China
- Prior art keywords
- positive electrode
- lithium
- slurry
- binder
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
示例 | 0.2C(%) | 0.5C(%) | 1C(%) |
实施例1 | 95.1 | 79.9 | 67.3 |
实施例2 | 98.2 | 84.5 | 75.6 |
实施例3 | 97.4 | 78.4 | 70.3 |
对比例1 | 90.00 | 71.0 | 50.0 |
对比例2 | 92.1 | 75.7 | 67.3 |
示例 | 循环圈数 | 首圈放电比容量(mAh/g) |
实施例1 | 2570 | 170.0 |
实施例2 | 2350 | 169.5 |
实施例3 | 2780 | 165.9 |
对比例1 | 2290 | 150.5 |
对比例2 | 2130 | 153.2 |
Claims (11)