CN1131649A - 远红外陶瓷粉及其制品 - Google Patents

远红外陶瓷粉及其制品 Download PDF

Info

Publication number
CN1131649A
CN1131649A CN 95102429 CN95102429A CN1131649A CN 1131649 A CN1131649 A CN 1131649A CN 95102429 CN95102429 CN 95102429 CN 95102429 A CN95102429 A CN 95102429A CN 1131649 A CN1131649 A CN 1131649A
Authority
CN
China
Prior art keywords
far infrared
ceramic powder
far
make
al2o3
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 95102429
Other languages
English (en)
Inventor
冯展
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 95102429 priority Critical patent/CN1131649A/zh
Publication of CN1131649A publication Critical patent/CN1131649A/zh
Pending legal-status Critical Current

Abstract

一种远红外陶瓷粉，主要以SiO2和Al2O3为主要原料，掺入MgO、TiO2或CaO、Ni2O3，制成远红外陶瓷粉，其在8-15μm波段范围内，法向光谱的比辐射率达85％以上。采用本发明的远红外陶瓷粉可以制成陶瓷球，陶瓷片，用于节油和节能装置，还可用于掺入塑料中，制成保鲜盒和塑料膜，用于保鲜，保健制品。

Description

远红外陶瓷粉及其制品
本发明涉及的是一种远红外陶瓷粉及其制品。
近年来，远红外陶瓷材料被广泛应用，而对远红外材料的研制也越来越被人们重视。目前，主要是远红外陶瓷，因为这种材料可以根据需要制造出能发射各种不同波段范围的远红外线，而8-15μm范围内的远红外线应用范围较广。日本公开特许昭62-30150中采用瑾青石或莫来石与Si3N4合成方法制备能发射远红外线的材料；中国专利申请91100014.3公开了一种远红外陶瓷，它是以Al2O3、SiO2，苏州土、滑石、Fe2O3、ZrO2等为原料，经多次烧结粉碎制得。上述专利制造工艺复杂，产品成本高，而且合成物的颜色较深，限制了一些产品的应用。
本发明的目的在于克服现有技术上存在的缺欠，提供一种成本低，工艺简单的远红外陶瓷及其应用。
本发明是采用如下方案进行实施的。以SiO2和Al2O3为基料，添加MgO、TiO2、CaO、Ni2O3。其组成为(重量百分数)SiO2、30-45、Al2O3 35-50、MgO 20-25、TiO28-14或CaO 4-10、Ni2O3 3-5。首先将SiO2和Al2O3经混合进行烧成，烧成温度为1100-1300℃，粉碎成微粉，然后将MgO、TiO2、CaO和Ni2O3掺入，再进行混合粉碎，制成远红外陶瓷粉，其在8-15μm波段范围内，法向光谱比辐射率达到85％以上。
以本发明的远红外陶瓷粉为原料，按照普通陶瓷工艺，制成远红外外陶瓷球，用于节油，节能系统，经试验，效果良好，特别是用于汽车节油系统，不仅节油，而且还可以减少汽车尾气有害气体的排放，减少环境污染，有利于环境保护。另外还可以将陶瓷粉添加在塑料、纤维中或涂在织物上，制成保健产品，保鲜和促熟制品等。
下面结合具体实例对本发明作进一步说明：
实例1
远红外陶瓷粉成份(重量百分数)
SiO2 32、Al2O3 37、MgO20、TiO2 8、NiO3 3
首先将SiO2和Al2O3混合，在1200℃进行烧成，然后粉碎，再掺入MgO、TiO2和Ni2O3，混合后再进行粉碎成微粉，制成远红外陶瓷粉。将远红外陶瓷料加入塑料中，可以制成保鲜盒，还可作成塑料膜，用于农作物地膜或保鲜袋等。
实例2
远红外陶瓷粉成份(重量百分数)
SiO2 33、Al2O3 36、MgO20、CaO3 8、Ni2O3 3
按实例1方法制成远红外陶瓷粉，然后采用普通陶瓷工艺制成陶瓷球或陶瓷片，用作节油、节能材料。
本发明与现有技术相比，制造工艺比较简单，成本低，在常温下有较强的发射率，应用范围广，用于食品保鲜，医疗保健，节油，节能等方面。

Claims (4)

1、一种远红外陶瓷粉，其特征是由经1100-1300℃烧成的SiO2和Al2O3为基料，掺入MgO、TiO2、CaO、Ni2O3，其组成为(重量百分数)SiO2 30-45、Al2O3 35-50、MgO20-25、TiO2 4-10或CaO 8-14、Ni2O3 3-5，经混合粉碎，制成远红外陶瓷粉。
2、以权利要求1的远红外陶瓷粉为原料制成远红外制品，其特征在于按陶瓷工艺制成陶瓷球、陶瓷片。
3、根据权利要求2所述远红外制品，其特征是将陶瓷粉掺入塑料中制成塑料保鲜盒，塑料膜。
4、根据权利要求2所述远红外制品，其特征是将陶瓷粉掺入纤维或涂在织物上，制成远红外保健制品。
CN 95102429 1995-03-20 1995-03-20 远红外陶瓷粉及其制品 Pending CN1131649A (zh)