CN113045702A - 一种硼酸衍生物改性的粘结剂及含有该粘结剂的锂离子电池 - Google Patents
一种硼酸衍生物改性的粘结剂及含有该粘结剂的锂离子电池 Download PDFInfo
- Publication number
- CN113045702A CN113045702A CN202110278031.3A CN202110278031A CN113045702A CN 113045702 A CN113045702 A CN 113045702A CN 202110278031 A CN202110278031 A CN 202110278031A CN 113045702 A CN113045702 A CN 113045702A
- Authority
- CN
- China
- Prior art keywords
- copolymer
- binder
- meth
- formula
- lithium ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种硼酸衍生物改性的粘结剂及含有该粘结剂的锂离子电池,所述粘结剂的乳液胶粒的表面带有丰富的硼酸基团(‑B(OH)2)。当应用到电池极片中时,在极片干燥的过程中硼酸基团与分散剂羧甲基纤维素钠中的‑OH或者功能单体中的‑OH可以发生脱水缩合反应,形成三维网络,增加粘结力,大幅提升了极片的剥离强度。所述粘结剂还能明显改善锂离子电池的循环性能,从而延长了锂离子电池的循环寿命;与常规的粘结剂相比,使用本发明的粘结剂的锂离子电池的循环容量保持率更高,且循环后锂离子电池的膨胀率更低,由此能够显著抑制锂离子电池长期使用之后的膨胀率,且使用本发明的粘结剂的锂离子电池低温性能也同时得到明显的改进。
Description
技术领域
本发明涉及一种硼酸衍生物改性的粘结剂及含有该粘结剂的锂离子电池,属于锂离子电池技术领域,具体属于锂离子电池粘结剂技术领域。
背景技术
锂离子电池中的粘结剂作为一种聚合物,既起到活性材料层间的粘结作用,又可以用于活性材料层与极片基材之间的粘结,在电池的制造和性能方面起重要作用,电池的重要组成之一。
目前业内使用最多的乳液型粘结剂有苯乙烯与丁二烯的共聚物形成的SBR乳液、苯乙烯与丙烯酸酯共聚形成的苯丙乳液。这些乳液所形成的胶膜都是不同交联度的弹性体,能起到粘结作用。但是这类乳液中的微粒之间仅存在范德华作用力,没有化学相互作用,所以在使用过程中不能形成有效的三维粘结网络,这样在电池循环过程中,对电池的膨胀抑制能力欠佳。因此,急需开发功能化的乳液型粘结剂,使其在使用过程中能形成有效的三维粘结网络,提高电池的性能。
发明内容
为了解决现有粘结剂的粘结性能差等问题,本发明提供一种硼酸衍生物改性的粘结剂及含有该粘结剂的锂离子电池,所述硼酸衍生物改性的粘结剂的粘结性能较现有的粘结剂有大幅提高,且制备成膜的机械稳定性也有所提升。
本发明是通过如下技术方案实现的:
一种共聚物,所述共聚物为基体单体与式(1)所示共聚单体的共聚物;
式(1)中,R1选自-C1-6亚烷基-、-C6-12亚芳基-、-C(=O)-O-C6-12亚芳基-;R2选自-H、-C1-6烷基;R3选自-H、-C1-6烷基。
根据本发明,所述基体单体选自式(2)和式(3)所示化合物中的至少一种;
H2C=CH-R4 式(2)
H2C=C(CH3)-R4 式(3)
式(2)和式(3)中,R4选自-C(R5)=C(R5)2、-C6-12芳基、-C(=O)-O-R6;其中,R5相同或不同,彼此独立地选自-H、-C1-6烷基;R6选自取代或未取代的-C1-6烷基,取代基选自羟基。
根据本发明,所述式(1)所示共聚单体具体选自如下式(1-1)、式(1-2)、式(1-3)、式(1-4)和式(1-5)所示的化合物中的至少一种:
根据本发明,所述共聚物为基体单体、式(1)所示共聚单体和功能单体的共聚物,所述功能单体选自丙烯腈、(甲基)丙烯酰胺、(甲基)丙烯酸、衣康酸、2-丙烯酰胺基-2-甲基丙磺酸、烯丙基磺酸、N-羟甲基(甲基)丙烯酰胺、N,N-二甲基丙烯酰胺、对苯乙烯磺酸钠、乙烯基磺酸钠、烯丙基磺酸钠、2-甲基烯丙基磺酸钠、甲基丙烯酸乙酯磺酸钠、(甲基)丙烯酸羟乙酯、(甲基)丙烯酸羟丙酯或二甲基二烯丙基氯化铵中的至少一种。所述功能单体的引入有利于提升所述共聚物的性能,如共聚物形成的乳液在水中的分散稳定性及对活性物质的粘附力。
根据本发明,所述基体单体选自丁二烯和苯乙烯;或者,所述基体单体选自(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种;或者,所述基体单体选自苯乙烯和下述化合物中的至少一种:(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯。
根据本发明,当所述基体单体选自丁二烯和苯乙烯时,所述共聚物例如为式(1)所示共聚单体(硼酸衍生物)、丁二烯和苯乙烯的共聚物,或者为式(1)所示共聚单体(硼酸衍生物)、丁二烯、苯乙烯和功能单体的共聚物。
根据本发明,当所述基体单体选自(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种时,所述共聚物例如为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种与式(1)所示共聚单体(硼酸衍生物)的共聚物,或者为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)与功能单体的共聚物。
根据本发明,当所述基体单体包括苯乙烯和下述化合物中的至少一种时:(甲基)丙烯酸烷基酯、(甲基)丙烯酸羟烷基酯,所述共聚物例如为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)与苯乙烯的共聚物,或者为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)、苯乙烯与功能单体的共聚物。
根据本发明,所述式(I)所示共聚单体占所述共聚物总质量的0.1~10wt%。优选地,所述式(I)所示共聚单体占所述共聚物总质量的1~5wt%。
根据本发明,所述基体单体占所述共聚物总质量的90~99.9wt%。优选地,所述基体单体占所述共聚物总质量的95~99wt%。
根据本发明,所述功能单体占所述共聚物总质量的0~10wt%。优选地,所述功能单体占所述共聚物总质量的0.1~5wt%。
根据本发明,所述共聚物的玻璃化转变温度为-20℃~80℃。
本发明还提供一种粘结剂,所述粘结剂包括上述的共聚物。
根据本发明,所述粘结剂为乳液型粘结剂。
其中,所述乳液型粘结剂的粒径为100~800nm,优选为100~300nm。
其中,所述乳液型粘结剂的PDI不大于0.3,优选为不大于0.1。
其中,所述乳液型粘结剂的粘度为10~500mPa·s,优选为50~250mPa·s。
其中,所述乳液型粘结剂的固含量为1~70wt%,例如为5~65wt%,还例如为10~60wt%,进一步例如为20~60wt%,再例如为30~60wt%,优选为40~60wt%。
本发明提供了一种极片,所述极片包括集流体和位于集流体至少一侧表面的活性物质层,所述活性物质层包括上述粘结剂,所述粘结剂的质量占活性物质层总质量的0.5~5wt%,例如0.8~2.5wt%,又如1.5~2.5wt%。
本发明提供了一种锂离子电池,所述锂离子电池包括上述的粘结剂和/或上述极片。
本发明的有益效果:
本发明提供了一种硼酸衍生物改性的粘结剂及含有该粘结剂的锂离子电池,所述粘结剂的乳液胶粒的表面带有丰富的硼酸基团(-B(OH)2)。当应用到电池极片中时,在极片干燥的过程中硼酸基团与分散剂羧甲基纤维素钠中的-OH或者功能单体中的-OH可以发生脱水缩合反应,形成三维网络,增加粘结力,大幅提升了极片的剥离强度。所述粘结剂还能明显改善锂离子电池的常温和低温条件下的循环性能,从而延长了锂离子电池的循环寿命;与常规的粘结剂相比,使用本发明的粘结剂的锂离子电池的循环容量保持率更高,且循环后锂离子电池的膨胀率更低,由此能够显著抑制锂离子电池长期使用之后的膨胀率,且使用本发明的粘结剂的锂离子电池低温性能也同时得到明显的改进。
附图说明
图1为实施例1和对比例1的粘结剂的红外光谱图。
图2为用于进行粘结剂的剥离强度测试装置的结构示意图。
具体实施方式
[共聚物]
如前所述,本发明提供一种共聚物,所述共聚物为基体单体与式(1)所示共聚单体的共聚物;
式(1)中,R1选自-C1-6亚烷基-、-C6-12亚芳基-、-C(=O)-O-C6-12亚芳基-;R2选自-H、-C1-6烷基;R3选自-H、-C1-6烷基。
在一个优选方案中,所述基体单体选自式(2)和式(3)所示化合物中的至少一种;
H2C=CH-R4 式(2)
H2C=C(CH3)-R4 式(3)
式(2)和式(3)中,R4选自-C(R5)=C(R5)2、-C6-12芳基、-C(=O)-O-R6;其中,R5相同或不同,彼此独立地选自-H、-C1-6烷基;R6选自取代或未取代的-C1-6烷基,取代基选自羟基。
示例性地,所述基体单体选自丁二烯、苯乙烯、(甲基)丙烯酸烷基酯、(甲基)丙烯酸羟烷基酯中的至少一种。
在一个优选方案中,R1选自-C1-3亚烷基-、-C6H4-、-C(=O)-O-C6H4-;R2选自-H、-C1-3烷基;R3选自-H、-C1-3烷基。
在一个优选方案中,R1选自-CH2-、-CH2CH2-、-CH2CH2CH2-、-CH2CH(CH3)-、-C6H4-、-C(=O)-O-C6H4-;R2选自-H、-CH3、-CH2CH3、-CH2CH2CH3、-CH(CH3)2;R3选自-H、-CH3、-CH2CH3、-CH2CH2CH3、-CH(CH3)2。
在一个优选方案中,所述式(1)所示共聚单体为带有不饱和键的硼酸衍生物,即式(1)所示共聚单体为硼酸衍生物。
在一个优选方案中,所述式(1)所示共聚单体具体选自如下式(1-1)、式(1-2)、式(1-3)、式(1-4)和式(1-5)所示的化合物中的至少一种:
在一个优选方案中,所述共聚物为基体单体、式(1)所示共聚单体和功能单体的共聚物。
在一个优选方案中,所述功能单体选自丙烯腈、(甲基)丙烯酰胺、(甲基)丙烯酸、衣康酸、2-丙烯酰胺基-2-甲基丙磺酸、烯丙基磺酸、N-羟甲基(甲基)丙烯酰胺、N,N-二甲基丙烯酰胺、对苯乙烯磺酸钠、乙烯基磺酸钠、烯丙基磺酸钠、2-甲基烯丙基磺酸钠、甲基丙烯酸乙酯磺酸钠、(甲基)丙烯酸羟乙酯、(甲基)丙烯酸羟丙酯或二甲基二烯丙基氯化铵中的至少一种。所述功能单体的引入有利于提升所述共聚物的性能,如共聚物形成的乳液在水中的分散稳定性及对活性物质的粘附力。
在一个优选方案中,所述基体单体选自丁二烯和苯乙烯;或者,所述基体单体选自(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种;或者,所述基体单体选自苯乙烯和下述化合物中的至少一种:(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯。
示例性的,所述的(甲基)丙烯酸烷基酯选自甲基丙烯酸丁酯、丙烯酸丁酯、甲基丙烯酸甲酯、丙烯酸甲酯、甲基丙烯酸乙酯、丙烯酸乙酯、甲基丙烯酸正辛酯、丙烯酸正辛酯、甲基丙烯酸异辛酯、丙烯酸异辛酯、甲基丙烯酸十二烷酯中的至少一种。
示例性的,所述的(甲基)丙烯酸羟烷基酯选自甲基丙烯酸羟乙酯、丙烯酸羟乙酯、甲基丙烯酸羟丙酯、丙烯酸羟丙酯中的至少一种。
在一个优选方案中,当所述基体单体选自丁二烯和苯乙烯时,所述共聚物例如为式(1)所示共聚单体(硼酸衍生物)、丁二烯和苯乙烯的共聚物,或者为式(1)所示共聚单体(硼酸衍生物)、丁二烯、苯乙烯和功能单体的共聚物。
在一个优选方案中,当所述基体单体选自(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种时,所述共聚物例如为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种与式(1)所示共聚单体(硼酸衍生物)的共聚物,或者为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)与功能单体的共聚物。
在一个优选方案中,当所述基体单体包括苯乙烯和下述化合物中的至少一种时:(甲基)丙烯酸烷基酯、(甲基)丙烯酸羟烷基酯,所述共聚物例如为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)与苯乙烯的共聚物,或者为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)、苯乙烯与功能单体的共聚物。
本发明中,所述共聚物中的式(1)所示共聚单体(硼酸衍生物)的引入可以让所述共聚物的乳胶粒表面带有丰富的硼酸-B(OH)2基团,该基团在水乳液中稳定存在。当将其作为锂离子电池用粘结剂使用时,其在极片干燥过程中易与羟基(-OH)发生脱水反应,该-OH可以来源于临近乳液颗粒表面的-B(OH)2、锂离子电池常用的分散剂羧甲基纤维素钠中的-OH、功能单体中的-OH;实现化学交联后,形成三维的粘结网络,增加粘结强度,从而提高电池性能。
在一个优选方案中,所述式(I)所示共聚单体占所述共聚物总质量的0.1~10wt%。优选地,所述式(I)所示共聚单体占所述共聚物总质量的1~5wt%。例如,式(I)所示共聚单体占所述共聚物总质量的0.1wt%、0.3wt%、0.5wt%、0.8wt%、1wt%、2wt%、3wt%、4wt%、5wt%、8wt%、10wt%。
在一个优选方案中,所述基体单体占所述共聚物总质量的90~99.9wt%。优选地,所述基体单体占所述共聚物总质量的95~99wt%。例如,基体单体占所述共聚物总质量的90wt%、92wt%、95wt%、96wt%、97wt%、98wt%、99wt%、99.2wt%、99.5wt%、99.7wt%、99.9wt%。
在一个优选方案中,所述功能单体占所述共聚物总质量的0~10wt%。优选地,所述功能单体占所述共聚物总质量的0.1~5wt%。例如,所述功能单体占所述共聚物总质量的0wt%、0.1wt%、0.2wt%、0.3wt%、0.4wt%、0.5wt%、0.8wt%、1wt%、2wt%、3wt%、4wt%、5wt%。
在一个优选方案中,所述共聚物为无规共聚物或嵌段共聚物,优选为无规共聚物。
在一个优选方案中,所述共聚物的玻璃化转变温度为-20℃~80℃。
在一个优选方案中,所述共聚物的重均分子量为25万~150万。
[硼酸衍生物改性的粘结剂]
如前所述,本发明还提供一种粘结剂,所述粘结剂包括上述的共聚物。
在一个优选方案中,所述粘结剂是通过式(1)所示共聚单体(硼酸衍生物)、基体单体和任选地功能单体经聚合反应制备得到的。
在一个优选方案中,所述粘结剂为乳液型粘结剂,具体的,所述共聚物分散在分散介质(如水)中,得到乳液型粘结剂。
在一个优选方案中,当所述基体单体为丁二烯和苯乙烯时,制备得到的粘结剂为乳液型粘结剂。具体的,将式(1)所示共聚单体(硼酸衍生物)、丁二烯和苯乙烯的共聚物,或者将式(1)所示共聚单体(硼酸衍生物)、丁二烯、苯乙烯和功能单体的共聚物分散在分散介质(如水)中,制备得到乳液型粘结剂。
在一个优选方案中,当所述基体单体为苯乙烯和下述化合物中的至少一种:(甲基)丙烯酸烷基酯、(甲基)丙烯酸羟烷基酯时,制备得到的粘结剂为乳液型粘结剂。具体的,将(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)与苯乙烯的共聚物,或者将(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)、苯乙烯与功能单体的共聚物分散在分散介质(如水)中,制备得到乳液型粘结剂。
在一个优选方案中,当所述基体单体为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种时,制备得到的粘结剂为乳液型粘结剂。具体的,将(甲基)丙烯酸烷基酯、(甲基)丙烯酸羟烷基酯中的至少一种与式(1)所示共聚单体(硼酸衍生物)的共聚物,或者为(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种、式(1)所示共聚单体(硼酸衍生物)与功能单体的共聚物时,制备得到乳液型粘结剂。
其中,所述乳液型粘结剂的粒径为100~800nm,优选为100~300nm。
其中,所述乳液型粘结剂的PDI不大于0.3,优选为不大于0.1。
其中,所述乳液型粘结剂的粘度为10~500mPa·s,优选为50~250mPa·s。
其中,所述乳液型粘结剂的固含量为1~70wt%,例如为5~65wt%,还例如为10~60wt%,进一步例如为20~60wt%,再例如为30~60wt%,优选为40~60wt%。
选择所述参数的乳液型粘结剂的分散稳定性好,粘结力稳定,使用过程中易于分散。
在一个优选方案中,选用水作为分散介质时,具有无溶剂释放,符合环境要求,不燃烧、成本低,使用安全等特点。
[共聚物的制备方法]
本发明还提供上述共聚物的制备方法,即通过乳液聚合的方法制备,所述方法包括如下步骤:
将式(1)所示共聚单体与基体单体以及任选地功能单体混合,通入惰性气体,反应,制备得到所述共聚物。
其中,式(1)所示共聚单体、基体单体和功能单体的定义如前所述。
在一个优选方案中,所述惰性气体为高纯氮气、高纯氩气中的一种。
在一个优选方案中,所述反应的温度为30~120℃,所述反应的时间为5~24h。
在一个优选方案中,根据基体单体以及任选地功能单体的不同,在反应过程中还可以加入助剂。示例性的,所述助剂包括引发剂、交联剂、乳化剂或缓冲剂中的至少一种。
例如,所述乳化剂选自阴离子型乳化剂、阳离子型乳化剂、两性型乳化剂和非离子型乳化剂中的一种或几种。示例性地,所述乳化剂选自SDS(十二烷基硫酸钠)、OP-10(聚氧乙烯辛基苯酚醚-10)、十二烷基三甲基溴化铵、十二烷基磺酸钠、SDBS(十二烷基苯磺酸钠)、琥珀酸二辛酯磺酸钠、对壬基酚聚氧化乙烯(n=4-40)醚、聚氧化乙烯单月桂酸酯中的一种或几种。
例如,所述引发剂选自过硫酸钾、过硫酸铵、4,4'-偶氮双(4-氰基戊酸)、2,2-偶氮二(2-甲基丙基咪)二盐酸盐、过硫酸钠、四价铈盐(例如硝酸铈铵)、高锰酸钾、过硫酸钠/亚硫酸氢钠、硫酸亚铁/双氧水、过硫酸铵/四甲基乙二胺、过硫酸铵/亚硫酸钠中的至少一种。其中,过硫酸钠/亚硫酸氢钠、硫酸亚铁/双氧水、过硫酸铵/四甲基乙二胺、以及过硫酸铵/亚硫酸钠分别代表组合使用的引发剂,在使用时可以相继加入。
例如,所述缓冲剂选自碳酸氢钠或十二水磷酸钠(Na3PO4·12H2O)。
例如,所述交联剂选自二乙烯基苯、N,N-亚甲基双丙烯酰胺、二丙烯酸乙二醇酯、乙二醇二甲基丙烯酸酯中的至少一种。
[粘结剂的制备方法]
本发明还提供上述粘结剂的制备方法,所述方法包括如下步骤:
将上述共聚物分散在分散介质(如水)中,制备得到所述粘结剂,优选为乳液型粘结剂。
[粘结剂的应用]
本发明还提供上述粘结剂在锂离子电池中的应用。
优选地,在锂离子电池的正极和/或负极中的应用,进一步优选用于负极用粘结剂。
[极片]
如前所述,本发明提供了一种极片,所述极片包括集流体和位于集流体至少一侧表面的活性物质层,所述活性物质层包括上述粘结剂。
在一个优选方案中,所述极片为正极极片或负极极片。
在一个优选方案中,所述集流体为正极集流体或负极集流体;其中,所述负极集流体选自单光面铜箔、双光面铜箔或多孔铜箔;所述正极集流体选自单光面铝箔、双光面铝箔或多孔铝箔。
在一个优选方案中,所述粘结剂的质量占活性物质层总质量的0.5~5wt%,例如0.8~2.5wt%,又如1.5~2.5wt%。
在一个优选方案中,所述活性物质层中还包括活性物质和添加剂。
在一个优选方案中,所述活性物质为正极活性物质或负极活性物质,所述负极活性物质包括人造石墨、天然石墨、中间相碳球和钛酸锂、氧化硅、纳米硅粉、氧化亚硅、硅碳的至少一种;所述正极活性物质包括磷酸铁锂、三元正极材料、钴酸锂中的至少一种。
在一个优选方案中,所述添加剂包括导电剂和/或分散剂;优选地,所述导电剂选自石墨、炭黑、乙炔黑、石墨烯、碳纳米管中的至少一种;所述分散剂选自羧甲基纤维素钠或羧甲基纤维素锂。
其中,所述导电剂和/或分散剂的用量为本领域已知用量。
[极片的制备方法]
本发明还提供上述极片的制备方法,包括如下步骤:
在集流体至少一侧表面涂覆含有上述粘结剂的浆料,制备得到所述极片。
在一个优选方案中,所述负极极片的制备方法包括如下步骤:
(1)将负极活性物质、导电剂、分散剂、上述的粘结剂混合均匀,得到负极浆料;
(2)将所述负极浆料涂覆在集流体的表面,烘烤后即得到所述负极极片。
在一个优选方案中,所述正极极片由包括如下步骤的方法制备得到:
(1)将正极活性物质、导电剂和正极粘结剂混合均匀,得到正极浆料;
(2)将所述正极浆料涂覆在集流体的表面,烘烤后即得到正极极片。
其中,所述正极粘结剂可以为上述的粘结剂、PVDF、聚丙烯酸酯和聚丙烯酸中的至少一种,优选为PVDF。
[极片的应用]
本发明还提供上述极片在锂离子电池中的应用。
[锂离子电池]
如前所述,本发明提供了一种锂离子电池,所述锂离子电池包括上述的粘结剂和/或上述极片。
在一个优选方案中,所述锂离子电池包括正极极片、负极极片、隔膜和电解液。
在一个优选方案中,所述锂离子电池由正极极片、隔膜、负极极片和电解液组装得到。例如,将正极极片、负极极片和隔膜通过行业内通用的卷绕或者叠片式组装成电芯,再通过铝塑膜进行封装,再依次经过烘烤、注入电解液、化成、二封工序即得到锂离子电池。
下文将结合具体实施例对本发明的制备方法做更进一步的详细说明。应当理解,下列实施例仅为示例性地说明和解释本发明,而不应被解释为对本发明保护范围的限制。凡基于本发明上述内容所实现的技术均涵盖在本发明旨在保护的范围内。
下述实施例中所使用的实验方法如无特殊说明,均为常规方法;下述实施例中所用的试剂、材料等,如无特殊说明,均可从商业途径得到。
下述实施例和对比例中涉及到的剥离强度是采用如下方法测试得到的:
将负极浆料涂覆于集流体铜箔表面,经过干燥、冷压制成极片,将制备完成的极片裁剪为20×100mm尺寸的测试试样,备用;将极片用双面胶粘接需要测试的那一面,并用压辊压实,使之与极片完全贴合;试样的双面胶的另外一面粘贴于不锈钢表面,将试样一端反向弯曲,弯曲角度为180°;采用高铁拉力机测试,将不锈钢一端固定于拉力机下方夹具,试样弯曲末端固定于上方夹具,调整试样角度,保证上下端位于垂直位置,然后以50mm/min的速度拉伸试样,直到负极浆料全部从基板剥离,记录过程中的位移和作用力,认为受力平衡时的力为极片的剥离强度,装置示意图如图2所示。
下述实施例中的乳液胶粒粒径及PDI数据由激光粒度仪(马尔文公司的ZatasizerNano ZS90)测试得到。
下述实施例和对比例中涉及到的粘度是利用数显式旋转粘度计(上海三诺NDJ-5S)在室温(20~25℃)条件下测量得到的。
下述实施例和对比例中涉及到的玻璃化转变温度是由差示扫描量热仪(DSC),型号为910s(美国TA Instruments公司)测试得到。
实施例1
在反应釜中依次加入30份(质量份,同下)苯乙烯、70份丁二烯、0.4份丙烯酸、0.1份二乙烯基苯、2份对乙烯基苯硼酸(式1-1所示)、200份水、4.5份硬脂酸钠、0.5份分子量调节剂十二硫醇,通入氮气保护,搅拌300rpm,升温至65℃。继续搅拌20分钟后,加入0.31份过硫酸钾,60℃保温,冷凝,持续300rpm搅拌,反应7h,反应结束后,用氨水调节pH值,用200目的纱网过滤其中的凝胶物,得到对乙烯基苯硼酸改性的丁苯橡胶乳液型粘结剂,乳液型粘结剂的玻璃化转变温度为16℃,平均粒径为168nm,PDI为0.06,粘度为10~50mPa·s,固含量为40~42wt%,pH=6.5~7.5。
将正极活性物质钴酸锂、粘结剂PVDF和导电炭黑分散在N-甲基吡咯烷酮,搅拌后得到均匀分散的正极浆料,其中固体成分包括96.8wt%的钴酸锂、1.3wt%的PVDF和2wt%的导电炭黑,正极浆料的固体含量为67.5wt%,粘度为21745mPa·s。将正极浆料均匀地涂覆在铝箔两面,经过100~130℃干燥4h,利用辊压机对其压实,压实密度为2.6~3.2g/cm3,得到正极极片;
将石墨、上述乳液型粘结剂、分散剂CMC和导电剂导电炭黑混合分散于去离子水中,得到负极浆料,其中固体成分包括95.5wt%石墨、1.5wt%的CMC、1wt%的导电炭黑、2wt%的上述乳液型粘结剂,负极浆料的固体含量为44~46wt%,粘度为6561mPa·s。该浆料均匀地涂覆在铜箔两面,经过70~100℃干燥5h、辊压机压实,其中压实密度为1.4~1.7g/cm3,得到负极极片;
将正极片、负极片和隔膜(PP/PE/PP复合膜,厚度8μm,孔隙率为42%)卷绕并封装成电芯,然后注入电解液,化成、热压、二封后得到锂离子电池。
实施例2
在反应釜中依次加入33份苯乙烯、67份丁二烯、0.15份二乙烯基苯、3份式1-3所示的硼酸衍生物、155份水、2份丙烯酰胺、6份硬脂酸钠、0.6份分子量调节剂十二硫醇,通入氮气保护,搅拌300rpm,升温至60℃。继续搅拌20分钟后,加入0.3份过硫酸铵,65℃保温,冷凝,持续300rpm搅拌,反应6h,反应结束后,用氨水调节pH,并用200目的纱网过滤其中的凝胶物,得到碳硼酸衍生物改性的丁苯橡胶乳液型粘结剂,乳液型粘结剂的玻璃化转变温度为20℃,乳液型粘结剂的平均粒径为165nm,PDI为0.036,粘度为15~50mPa·s,固含量为39~41wt%,pH=7~8。
制作锂离子电池的方法流程与实施例1基本一致,不同之处为采用的粘结剂为本实施例中合成的乳液型粘结剂。
实施例3
以辛基酚聚氧乙烯醚(OP-10)和十二烷基硫酸钠(SDS)为乳化剂,质量比为1/1,共4份,丙烯酰胺1份,甲基丙烯酸甲酯33份,丙烯酸丁酯60份,丙烯酸羟乙酯2份,式1-2所示的硼酸衍生物3份,二丙烯酸乙二醇酯0.15份、过硫酸铵0.5份,亚硫酸氢钠0.5份,水200份。采用半连续法将乳化剂(OP-10/SDS)和去离子水加入到反应容器中,搅拌1h,混合均匀并使其乳化;然后升温至40℃,同时通入N2(排除体系中的O2),加入1/10份的混合单体和1/3份的引发剂,45℃反应1小时;随后分别向体系中同时滴加剩余的混合单体及引发剂(控制滴加速率),滴毕,继续反应5小时;降温至25℃,用氨水调节pH至7.0~8.0,即得目标的硼酸衍生物改性的丙烯酸酯乳液型粘结剂,乳液型粘结剂的玻璃化转变温度为25℃,乳液型粘结剂的平均粒径为185nm,PDI为0.03,粘度为10~70mPa·s,固含量为36~39wt%。
制作锂离子电池的方法流程与实施例1基本一致,不同之处为采用的乳液型粘结剂为本实施例中合成的乳液型粘结剂。
实施例4
以十二烷基硫酸钠(SDS)为乳化剂,0.05份,苯乙烯40份,丙烯酸丁酯60份,丙烯酰胺1份,N,N-亚甲基双丙烯酰胺0.1份,式1-4所示的硼酸衍生物2份,水200份。先将上述物料加入到反应容器中,搅拌,然后升温,同时通入N2(排除体系中的O2);待温度升至70℃后,加入0.35份过硫酸钾,继续反应8小时;降温至40℃,用氢氧化钠调节pH至7.0~8.0,冷却后即得目标的硼酸衍生物改性苯丙乳液粘结剂。乳液型粘结剂的玻璃化转变温度为10℃,乳液型粘结剂的平均粒径为175nm,PDI为0.043,粘度为10~60mPa·s,固含量为38~41wt%。
制作锂离子电池的方法流程与实施例1基本一致,不同之处为采用的粘结剂为本实施例中合成的乳液型粘结剂。
对比例1
与实施例1相比,不同之处在于没有加入硼酸衍生物单体,其他物质的含量及制备工艺与实施例1一致。
对比例2
与实施例2相比,不同之处在于没有加入硼酸衍生物单体,其他物质的含量及制备工艺与实施例2一致。
对比例3
与实施例3相比,不同之处在于没有加入硼酸衍生物单体,其他物质的含量及制备工艺与实施例3一致。
对比例4
与实施例4相比,不同之处在于没有加入硼酸衍生物单体,其他物质的含量及制备工艺与实施例4一致。
测试例1
对实施例和对比例制备得到的电池进行性能测试,测试项目包括低温性能(0℃充电、-20℃放电)、循环保持率和常温循环膨胀率,测试过程如下:
(1)低温性能:-20℃放电:将电池置于0℃进行充电,然后将满电电池静置在-20℃的低温箱中,以0.2C放电,计算放电容量保持率。
(2)循环保持率:常温25℃下,以1C充放电循环250次,计算250次后的容量保持率。
(3)常温循环膨胀率:常温25℃下,以1C充放电循环250次,计算250次后的电池的厚度增加值与原始厚度的百分比。
上述实施例与对比例的电池通过电性能测试,结果如表1所示。
图1为实施例1和对比例1的粘结剂的红外光谱图。由图1可以看出,实施例1中通过引入硼酸衍生物结构,在1340cm-1及3200~3600cm-1波数处有B-O及O-H伸缩振动的特征吸收峰,而对比例1中此处均没有明显的吸收峰,由此可以判断硼酸衍生物单体参与了共聚,成功引入到了乳液胶粒中。
表1实施例与对比例的电池通过电性能测试结果
从表1中可以看出,添加了硼酸衍生物改性的粘结剂的电池性能与没有添加硼酸衍生物改性的粘结剂的电池性能相比,剥离强度、-20℃下0.2C放电容量保持率、常温1C充放电循环250T容量保持及常温膨胀率的性能方面均展现出优势。
以上,对本发明的实施方式进行了说明。但是,本发明不限定于上述实施方式。凡在本发明的精神和原则之内,所做的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (10)
2.根据权利要求1所述的共聚物,其中,所述基体单体选自式(2)和式(3)所示化合物中的至少一种;
H2C=CH-R4 式(2)
H2C=C(CH3)-R4 式(3)
式(2)和式(3)中,R4选自-C(R5)=C(R5)2、-C6-12芳基、-C(=O)-O-R6;其中,R5相同或不同,彼此独立地选自-H、-C1-6烷基;R6选自取代或未取代的-C1-6烷基,取代基选自羟基。
4.根据权利要求1所述的共聚物,其中,所述共聚物为基体单体、式(1)所示共聚单体和功能单体的共聚物,所述功能单体选自丙烯腈、(甲基)丙烯酰胺、(甲基)丙烯酸、衣康酸、2-丙烯酰胺基-2-甲基丙磺酸、烯丙基磺酸、N-羟甲基(甲基)丙烯酰胺、N,N-二甲基丙烯酰胺、对苯乙烯磺酸钠、乙烯基磺酸钠、烯丙基磺酸钠、2-甲基烯丙基磺酸钠、甲基丙烯酸乙酯磺酸钠、(甲基)丙烯酸羟乙酯、(甲基)丙烯酸羟丙酯或二甲基二烯丙基氯化铵中的至少一种;和/或,
所述基体单体选自丁二烯和苯乙烯;或者,所述基体单体选自(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯中的至少一种;或者,所述基体单体选自苯乙烯和下述化合物中的至少一种:(甲基)丙烯酸烷基酯和(甲基)丙烯酸羟烷基酯。
5.根据权利要求4所述的共聚物,其中,所述式(I)所示共聚单体占所述共聚物总质量的0.1-10wt%;所述基体单体占所述共聚物总质量的90-99.9wt%;所述功能单体占所述共聚物总质量的0-10wt%。
6.根据权利要求1-5任一项所述的共聚物,其中,所述共聚物的玻璃化转变温度为-20℃~80℃。
7.一种粘结剂,其中,所述粘结剂包括权利要求1-6任一项所述的共聚物。
8.根据权利要求7所述的粘结剂,其中,所述粘结剂为乳液型粘结剂,所述乳液型粘结剂的粒径为100~800nm;和/或,所述乳液型粘结剂的PDI不大于0.3;和/或,所述乳液型粘结剂的粘度为10~500mPa·s;和/或,所述乳液型粘结剂的固含量为1-70wt%。
9.一种锂离子电池,所述锂离子电池包括极片,所述极片包括集流体和位于集流体至少一侧表面的活性物质层,所述活性物质层包括权利要求7或8所述的粘结剂。
10.根据权利要求9所述的锂离子电池,其中,所述粘结剂的质量占活性物质层总质量的0.5~5wt%。