CN112391222B - 一种抗氧抗磨润滑油添加剂及其应用 - Google Patents

一种抗氧抗磨润滑油添加剂及其应用 Download PDF

Info

Publication number
CN112391222B
CN112391222B CN202011165680.4A CN202011165680A CN112391222B CN 112391222 B CN112391222 B CN 112391222B CN 202011165680 A CN202011165680 A CN 202011165680A CN 112391222 B CN112391222 B CN 112391222B
Authority
CN
China
Prior art keywords
parts
lubricating oil
antioxidant
additive
compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202011165680.4A
Other languages
English (en)
Other versions
CN112391222A (zh
Inventor
王鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hebei Jinpu Petroleum Technology Co ltd
Original Assignee
Hebei Jinpu Petroleum Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hebei Jinpu Petroleum Technology Co ltd filed Critical Hebei Jinpu Petroleum Technology Co ltd
Priority to CN202011165680.4A priority Critical patent/CN112391222B/zh
Publication of CN112391222A publication Critical patent/CN112391222A/zh
Application granted granted Critical
Publication of CN112391222B publication Critical patent/CN112391222B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗氧抗磨润滑油添加剂及其应用，包括以下重量份的组分：复合抗氧剂20‑60重量份、钝化剂1‑4重量份、磷酸酯类抗磨剂25‑65重量份和防锈剂1‑5份；所述磷酸酯类抗磨剂为(2‑丁基辛基)膦酸二乙酯和磷酸三甲酚酯的质量比为1‑2:1混合物。本发明的润滑油添加剂中添加有(2‑丁基辛基)膦酸二乙酯和磷酸三甲酚酯复配而成的磷酸酯类抗磨剂，同时还添加了甲基苯三唑类钝化剂和复合抗氧化剂，多种具有不同功能的组分协同，不仅可以提高润滑油的抗磨减摩性能，还能改善润滑油不耐高温的问题，提高润滑油的热稳定性和抗氧化性。

Description

一种抗氧抗磨润滑油添加剂及其应用
技术领域
本发明涉及润滑油技术领域，具体涉及一种具有抗氧抗磨性能的润滑油添加剂，以及该润滑油添加剂的应用。
背景技术
日常生活和工业生产中，机械损失大部分是由磨损造成的，润滑油可以减少金属直接接触，降低机械的磨损程度。润滑油主要是由基础油和添加剂组成，润滑油的基本性质由基础油决定，而添加剂按功效一般可以分为抗氧抗腐剂、清净分散剂、降凝剂、防锈剂和极压抗磨剂等。传统的润滑油添加剂虽然具有较好的抗磨减摩性能，但是使用时会分解产生含硫、氯等元素的化合物，增加环境污染，而且还易使设备发生腐蚀，加剧设备磨损。
发明内容
本发明提供一种抗氧抗磨润滑油添加剂，其能有效改善润滑油的抗磨减摩性能，还能提高润滑油的热稳定性和抗氧化性，进而改善润滑油的清洁性，延长润滑油的使用寿命。
本发明的第一方面提供了抗氧抗磨润滑油添加剂，包括以下重量份的组分：复合抗氧剂20-60重量份、钝化剂1-4重量份、磷酸酯类抗磨剂25-65重量份和防锈剂1-5份；所述磷酸酯类抗磨剂为(2-丁基辛基)膦酸二乙酯和磷酸三甲酚酯的质量比为1-2:1混合物。
特别优选地，磷酸酯类抗磨剂为(2-丁基辛基)膦酸二乙酯和磷酸三甲酚酯的质量比为1:1混合物。其中，(2-丁基辛基)膦酸二乙酯为2-丁基-1-辛烯和亚磷酸二乙酯通过自由基反应得到，该磷酸酯有优于磷酸三甲酚酯的抗磨性能，能够提高基础油的极压和减摩、抗磨性能。
优选地，还包括清净剂1-6重量份和分散剂1-7重量份；所述清净剂为磺酸盐或苯磺酸盐；所述分散剂为丁二酰亚胺类化合物。
进一步优选地，所述苯磺酸盐为低碱值合成烷基苯磺酸钙、高碱值合成二烷基苯磺酸钙、高碱值长链线型烷基苯磺酸钙中的一种或多种；所述磺酸盐为高碱值长链线型烷基磺酸镁；所述丁二酰亚胺类化合物为硼化高分子量聚异丁烯基丁二酰亚胺。磺酸盐或苯磺酸盐清净剂能够中和润滑油和燃料油氧化生成的含氧酸，阻止其进一步缩合，进而减少漆膜和油泥。丁二酰胺类化合物在改善低温油泥方面的效果显著，能有效地抑制发动机油粘度增长，还有一定的抗氧化和抗磨性能，其与金属清净剂复合还具有协同作用，不仅能够提高润滑油的使用性能，还能降低润滑油添加剂的使用剂量。
优选地，所述复合抗氧剂是对苯二酚、2-甲酸丁酯基-3-丁基苯酚的质量比为5-8：2-6的混合物。
优选地，所述钝化剂为甲基苯三唑类化合物，所述甲基苯三唑类化合物为甲基苯三唑和溴代脂肪族化合物反应而得。
进一步优选地，所述甲基苯三唑类化合物的制备方法包括步骤：将甲基苯并三唑溶于甲醇中，加入碳酸钾或碳酸氢钾，20-25℃的条件反应20-50min，缓慢滴加溴代脂肪族化合物，加热回流反应3-6h，萃取，纯化，即得。
具体地，上述反应中溴代试剂过量，以甲基苯并三唑计，优选为1.5-2.0当量。碳酸钾或碳酸氢钾与甲基苯并三唑的摩尔比为1:1。
具体地，上述溴代脂肪族化合物优选为C1-C16的直链烷烃，例如溴代乙烷、溴代丙烷、溴代癸烷和溴代十六烷。
优选地，所述防锈剂为烯基琥珀酸半酯。
优选地，所述抗氧抗磨润滑油添加剂包括以下重量份的组分：对苯二酚16重量份、2-甲酸丁酯基-3-丁基苯酚9重量份、甲基苯三唑类化合物2重量份、(2-丁基辛基)膦酸二乙酯20重量份、磷酸三甲酚酯15重量份、烯基琥珀酸半酯3重量份、高碱值长链线型烷基磺酸镁3重量份和硼化高分子量聚异丁烯基丁二酰亚胺1份。
本发明的第二方面提供了上述的抗氧抗磨润滑油添加剂在润滑油中作为添加剂的应用。
优选地，所述润滑油添加剂与基础油中的质量分数为1.6％-5.5％。具体地，基础油优选为500N基础油、150BS基础油、400SN基础油、PAO基础油。
本发明的有益效果体现在：
本发明的润滑油添加剂中添加有(2-丁基辛基)膦酸二乙酯和磷酸三甲酚酯复配而成的磷酸酯类抗磨剂，同时还添加了甲基苯三唑类钝化剂和复合抗氧化剂，多种具有不同功能的组分协同，不仅可以提高润滑油的抗磨减摩性能，还能改善润滑油不耐高温的问题，提高润滑油的热稳定性和抗氧化性。
具体实施方式
下面将对本发明技术方案的实施例进行详细的描述。以下实施例仅用于更加清楚地说明本发明的技术方案，因此只作为示例，而不能以此来限制本发明的保护范围。
需要注意的是，除非另有说明，本申请使用的技术术语或者科学术语应当为本发明所属领域技术人员所理解的通常意义。
实施例1
本实施例提供了一种抗氧抗磨润滑油添加剂，由以下重量份的组分组成：对苯二酚16重量份、2-甲酸丁酯基-3-丁基苯酚9重量份、甲基苯三唑类化合物2重量份、(2-丁基辛基)膦酸二乙酯20重量份、磷酸三甲酚酯15重量份、烯基琥珀酸半酯3重量份、高碱值长链线型烷基磺酸镁3重量份和硼化高分子量聚异丁烯基丁二酰亚胺1份。
具体地，甲基苯三唑类化合物的制备方法为：将甲基苯并三唑溶于甲醇中，加入碳酸钾或碳酸氢钾，25℃的条件反应30min，缓慢滴加溴代脂肪族化合物，加热回流反应5h，水和二氯甲烷萃取，过硅胶柱纯化，浓缩、干燥，即得。
需要说明的是，采用上述方法分离可得两种N-取代产物，经试验发现该两种甲基苯并唑作为抗磨剂的效果差别较小，故直接使用分离产物。
实施例2
本实施例提供了一种抗氧抗磨润滑油添加剂，由以下重量份的组分组成：对苯二酚25重量份、2-甲酸丁酯基-3-丁基苯酚10重量份、甲基苯三唑类化合物3重量份、(2-丁基辛基)膦酸二乙酯35重量份、磷酸三甲酚酯20重量份、烯基琥珀酸半酯1重量份、低碱值合成烷基苯磺酸钙1重量份和硼化高分子量聚异丁烯基丁二酰亚胺1份。
甲基苯三唑类化合物的制备方法同实施例1。
实施例3
本实施例提供了一种抗氧抗磨润滑油添加剂，由以下重量份的组分组成：对苯二酚32重量份、2-甲酸丁酯基-3-丁基苯酚24重量份、甲基苯三唑类化合物4重量份、(2-丁基辛基)膦酸二乙酯35重量份、磷酸三甲酚酯20重量份、烯基琥珀酸半酯4重量份、高碱值合成二烷基苯磺酸钙4重量份和硼化高分子量聚异丁烯基丁二酰亚胺2份。
甲基苯三唑类化合物的制备方法同实施例1。
实施例4
本实施例提供了一种抗氧抗磨润滑油添加剂，由以下重量份的组分组成：对苯二酚32重量份、2-甲酸丁酯基-3-丁基苯酚15重量份、甲基苯三唑类化合物2重量份、(2-丁基辛基)膦酸二乙酯20重量份、磷酸三甲酚酯15重量份、烯基琥珀酸半酯3重量份、低碱值合成烷基苯磺酸钙2重量份和硼化高分子量聚异丁烯基丁二酰亚胺1份。
甲基苯三唑类化合物的制备方法同实施例1。
对比例1
本对比例提供了一种抗氧抗磨润滑油添加剂，由以下重量份的组分组成：对苯二酚25重量份、2-甲酸丁酯基-3-丁基苯酚10重量份、甲基苯三唑类化合物3重量份、磷酸三甲酚酯45重量份、烯基琥珀酸半酯1重量份、低碱值合成烷基苯磺酸钙1重量份和硼化高分子量聚异丁烯基丁二酰亚胺1份。甲基苯三唑类化合物的制备方法同实施例1。
对比例2
本实施例提供了一种抗氧抗磨润滑油添加剂，由以下重量份的组分组成：对苯二酚25重量份、2-甲酸丁酯基-3-丁基苯酚10重量份、苯并三唑十八脂肪胺盐3重量份、(2-丁基辛基)膦酸二乙酯35重量份、磷酸三甲酚酯20重量份、烯基琥珀酸半酯1重量份、低碱值合成烷基苯磺酸钙1重量份和硼化高分子量聚异丁烯基丁二酰亚胺1份。
上述润滑油添加剂制备成润滑油的方法为：
1)取基础油，然后按照基础油质量的1.6％-5.5％称取润滑油添加剂的各组分；
2)将基础油加热至55-65℃，加入复合抗氧剂、钝化剂、磷酸酯类抗磨剂、防锈剂、清净剂和分散剂，搅拌0.5-2h，静置，过滤，即得润滑油。
本发明的润滑油添加剂适用的基础油优选为500N基础油、150BS基础油、400SN基础油、PAO基础油。
摩擦磨损性能测试
通过四球摩擦磨损试验机，将上述配方的润滑油添加剂添加至500N基础油中得到润滑油，并按照国家标准GB 3142-2019来测定油品的摩擦效果。
选用材质为GCR15、12.7mm的钢珠，硬度为63，试验条件：载荷为196N，温度为25℃、时间为60min、转速为1200r/min。通过测试得到添加剂在500N基础油中的平均摩擦系数和平均磨斑直径大小(将至少三次平行实验的平均值作为实验结果)，如表1所示。
表1润滑油添加剂在500N基础油中的减摩抗磨效果
Figure BDA0002745699900000051
Figure BDA0002745699900000061
由表1可知，本发明复配的润滑油添加剂有较佳的抗磨减摩效果，且在基础油中的溶解性良好。
最后应说明的是：以上各实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述各实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的范围，其均应涵盖在本发明的权利要求和说明书的范围当中。

Claims (3)

1.抗氧抗磨润滑油添加剂，其特征在于，包括以下重量份的组分：对苯二酚16重量份、2-甲酸丁酯基-3-丁基苯酚9重量份、甲基苯三唑类化合物2重量份、(2-丁基辛基)膦酸二乙酯20重量份、磷酸三甲酚酯15重量份、烯基琥珀酸半酯3重量份、高碱值长链线型烷基磺酸镁3重量份和硼化高分子量聚异丁烯基丁二酰亚胺1份；所述甲基苯三唑类化合物为甲基苯三唑和溴代脂肪族化合物反应而得；所述甲基苯三唑类化合物的制备方法包括步骤：将甲基苯并三唑溶于甲醇中，加入碳酸钾或碳酸氢钾，20-25℃的条件反应20-50min，缓慢滴加溴代脂肪族化合物，加热回流反应3-6h，萃取，纯化，即得。
2.权利要求1所述的抗氧抗磨润滑油添加剂在润滑油中作为添加剂的应用。
3.根据权利要求2所述的应用，其特征在于，所述润滑油添加剂在基础油中的质量分数为1.6％-5.5％。
CN202011165680.4A 2020-10-27 2020-10-27 一种抗氧抗磨润滑油添加剂及其应用 Active CN112391222B (zh)