CN1117827C - 一种短时高效隔热涂料 - Google Patents

一种短时高效隔热涂料 Download PDF

Info

Publication number
CN1117827C
CN1117827C CN 98117687 CN98117687A CN1117827C CN 1117827 C CN1117827 C CN 1117827C CN 98117687 CN98117687 CN 98117687 CN 98117687 A CN98117687 A CN 98117687A CN 1117827 C CN1117827 C CN 1117827C
Authority
CN
China
Prior art keywords
coating
paint
filler
base
insulating paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 98117687
Other languages
English (en)
Other versions
CN1247215A (zh
Inventor
徐惠彬
刘福顺
宫声凯
王华明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beihang University
Beijing University of Aeronautics and Astronautics
Original Assignee
Beihang University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beihang University filed Critical Beihang University
Priority to CN 98117687 priority Critical patent/CN1117827C/zh
Publication of CN1247215A publication Critical patent/CN1247215A/zh
Application granted granted Critical
Publication of CN1117827C publication Critical patent/CN1117827C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种短时高效隔热涂料，该涂料的制备方法和步骤是：将基料和填料按2∶1的比例配置成涂料；其基料为有机硅树脂，填料为石棉粉、二氧化锆、硅酸铝粉、硅酸盐粉，其填料各成份的比例为(以涂料的重量为100%计)：15-25%石棉粉，6-10%二氧化锆，2-4%硅酸铝粉、2-4%硅酸盐粉(除硅酸铝外的其它硅酸盐)。然后将涂料搅拌均匀；采用喷涂或刷涂的方法将涂料涂覆在试件表面；将刷好涂料的试件在使用温度以上20℃～30℃烘烧0.5-1小时，涂料便在试件表面形成高效、保温、隔热涂层。

Description

一种短时高效隔热涂料
本发明为一种短时高效隔热涂料，属于化学涂料技术。
随着科学技术的发展，对材料的涂层要求也越来越高。为了提高涂层的耐热隔热性能，过去的研究工作大部分都集中在如何提高涂料中基料的热分解温度上。因此，有人设计使用无机材料，如水玻璃等，它的耐热性易满足要求，但耐介质性很差，易于吸潮，不利储存，脆性也大。采用有机防护涂层虽然其耐高温性较差，但它的韧性、附着力是无机材料难以相比的。无机材料的耐高温性很好，但热裂、脆性、抗热震，与基体的热匹配都很难做到隔热可靠的程度。而有机涂料的耐瞬时高温性能，尤其是在中等热流，较高温度下，材料的有效烧蚀热是相当高的。因此，作为隔热涂层是可取的。
本发明的目的是：提供一种适用于制备低散热发动机等热端部件，高温设备表面、各种金属零件表面、各种电气表面等要求短时、高效、保温隔热的涂层技术。
本发明的技术方案如下：
(一)涂料配比：
本发明涂料由有机硅树脂(organosil iconresin)作为基料，并以多种保温材料作为填料，其填料成份为(以涂料的重量为100％计)：15-25％石棉粉，6-10％二氧化锆，2-4％硅酸铝粉、2-4％硅酸盐粉(除硅酸铝外的其它硅酸盐)，基料和填料的配比为2∶1。
(二)本发明制备方法和步骤如下：
(1)将基料和填料按一定比例(2∶1)配置成涂料；
(2)将涂料搅拌均匀；
(3)采用喷涂或刷涂的方法涂覆在试件表面；
(4)在使用温度以上20℃～30℃烘烧0.5-1小时。
本发明的优点是：工艺简单、成本低、可广泛应用于各种高温设备表面。该涂料无毒、无腐蚀、耐潮湿、表面致密、耐高速气流冲刷、结合力好。该涂料耐热性好，可在300℃以下长期使用。在120秒时隔热效果可达180℃。
兹举实施例如下：
采用基料为66％，填料34％，其基料是有机硅树脂，填料包括有石棉粉、二氧化锆、硅酸铝粉，其填料各成份的比例是(以涂料的重量为100％计)：石棉粉20％、二氧化锆8％、硅酸铝粉3％、硅酸盐粉3％，然后将基料与填料混合搅拌均匀，采用喷涂或刷涂的方法将涂料涂覆在试件表面，然后将涂覆涂料的试件放在使用温度以上20-30℃中烘烧40分钟左右，则可在试件表面形成一层高效、保温、隔热涂层。

Claims (2)

1.一种短时高效隔热涂料，其特征在于：该涂料由有机硅树脂作为基料，并以多种保温材料作为填料，其填料成份为(以涂料的重量为100％计)：15-25％石棉粉，6-10％二氧化锆，2-4％硅酸铝粉、2-4％除硅酸铝外的其它硅酸盐粉，基料和填料的配比为2∶1。
2.一种权利1的短时高效隔热涂料的制备方法，其特征在于：其步骤如下：
(1)将基料和填料按2∶1配置成涂料；
(2)将涂料搅拌均匀；
(3)采用喷涂或刷涂的方法涂覆在试件表面；
(4)在使用温度以上20℃～30℃烘烧0.5-1小时。
CN 98117687 1998-09-09 1998-09-09 一种短时高效隔热涂料 Expired - Fee Related CN1117827C (zh)