CN1114640C - 适用于制备收缩趋势减少的高回弹性软泡沫的聚（氧化丙烯/氧化乙烯）无规多醇及由其制备的泡沫 - Google Patents

适用于制备收缩趋势减少的高回弹性软泡沫的聚（氧化丙烯/氧化乙烯）无规多醇及由其制备的泡沫 Download PDF

Info

Publication number
CN1114640C
CN1114640C CN97191859A CN97191859A CN1114640C CN 1114640 C CN1114640 C CN 1114640C CN 97191859 A CN97191859 A CN 97191859A CN 97191859 A CN97191859 A CN 97191859A CN 1114640 C CN1114640 C CN 1114640C
Authority
CN
China
Prior art keywords
polyol
polyvalent alcohol
foam
polyols
ethylene oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN97191859A
Other languages
English (en)
Chinese (zh)
Other versions
CN1209820A (zh
Inventor
S·黑格
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Koth A Ltd By Share Ltd
Link Chemical Technologies
Bayer Antwerpen NV
Original Assignee
Arco Chemical Technology LP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arco Chemical Technology LP filed Critical Arco Chemical Technology LP
Publication of CN1209820A publication Critical patent/CN1209820A/zh
Application granted granted Critical
Publication of CN1114640C publication Critical patent/CN1114640C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
    • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
    • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
    • C08G65/2642—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the catalyst used
    • C08G65/2645—Metals or compounds thereof, e.g. salts
    • C08G65/2663—Metal cyanide catalysts, i.e. DMC's
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/4009—Two or more macromolecular compounds not provided for in one single group of groups C08G18/42 - C08G18/64
    • C08G18/4072—Mixtures of compounds of group C08G18/63 with other macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4833—Polyethers containing oxyethylene units
    • C08G18/4837—Polyethers containing oxyethylene units and other oxyalkylene units
    • C08G18/485—Polyethers containing oxyethylene units and other oxyalkylene units containing mixed oxyethylene-oxypropylene or oxyethylene-higher oxyalkylene end groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4866—Polyethers having a low unsaturation value
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
    • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
    • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
    • C08G65/2696—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the process or apparatus used
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0008—Foam properties flexible
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0041—Foam properties having specified density
    • C08G2110/005—< 50kg/m3
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0083—Foam properties prepared using water as the sole blowing agent

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Toxicology (AREA)
  • Polyurethanes Or Polyureas (AREA)
  • Polyethers (AREA)
CN97191859A 1996-01-26 1997-01-23 适用于制备收缩趋势减少的高回弹性软泡沫的聚（氧化丙烯/氧化乙烯）无规多醇及由其制备的泡沫 Expired - Lifetime CN1114640C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US08/592,087 US5605939A (en) 1996-01-26 1996-01-26 Poly(oxypropylene/oxyethylene) random polyols useful in preparing flexible high resilience foam with reduced tendencies toward shrinkage and foam prepared therewith
US08/592,087 1996-01-26

Publications (2)

Publication Number Publication Date
CN1209820A CN1209820A (zh) 1999-03-03
CN1114640C true CN1114640C (zh) 2003-07-16

Family

ID=24369232

Family Applications (1)

Application Number Title Priority Date Filing Date
CN97191859A Expired - Lifetime CN1114640C (zh) 1996-01-26 1997-01-23 适用于制备收缩趋势减少的高回弹性软泡沫的聚（氧化丙烯/氧化乙烯）无规多醇及由其制备的泡沫

Country Status (12)

Country Link
US (2) US5605939A (enExample)
EP (1) EP0876416B1 (enExample)
JP (1) JP3895385B2 (enExample)
CN (1) CN1114640C (enExample)
AR (1) AR005528A1 (enExample)
AU (1) AU1544897A (enExample)
BR (1) BR9706974A (enExample)
CA (1) CA2241627C (enExample)
DE (1) DE69700406T2 (enExample)
ES (1) ES2135287T3 (enExample)
TW (1) TW440577B (enExample)
WO (1) WO1997027236A1 (enExample)

Families Citing this family (86)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5670601A (en) * 1995-06-15 1997-09-23 Arco Chemical Technology, L.P. Polyurethane elastomers having improved green strength and demold time and polyoxyalkylene polyols suitable for their preparation
US5700847A (en) * 1995-12-04 1997-12-23 Arco Chemical Technology, L.P. Molded polyurethane foam with enhanced physical properties
US5668191A (en) * 1995-12-21 1997-09-16 Arco Chemical Technology, L.P. One-shot cold molded flexible polyurethane foam from low primary hydroxyl polyols and process for the preparation thereof
US5958994A (en) * 1997-02-25 1999-09-28 Arco Chemical Technology, L.P. Method for decreasing the propensity for phase-out of the high molecular weight component of double metal cyanide-catalyzed high secondary hydroxyl polyoxypropylene polyols
US6066683A (en) * 1998-04-03 2000-05-23 Lyondell Chemical Worldwide, Inc. Molded and slab polyurethane foam prepared from double metal cyanide complex-catalyzed polyoxyalkylene polyols and polyols suitable for the preparation thereof
US6008263A (en) * 1998-04-03 1999-12-28 Lyondell Chemical Worldwide, Inc. Molded and slab polyurethane foam prepared from double metal cyanide complex-catalyzed polyoxyalkylene polyols and polyols suitable for the preparation thereof
DE19840585A1 (de) † 1998-09-05 2000-03-09 Basf Ag Verfahren zur Herstellung von Polyetherolen durch ringöffnende Polymerisation von Alkylenoxiden
DE69906819T2 (de) * 1998-12-29 2004-02-05 Dow Global Technologies, Inc., Midland Polyurethanschäume hergestellt aus mechanisch aufgeschaumten polyurethandispersionen
JO2132B1 (en) * 1999-01-19 2002-08-07 شل انترناشونال ريسيرتش ماتستشابيج بي في Method for preparing flexible polyurethane foams
DE19917897A1 (de) * 1999-04-20 2000-10-26 Basf Ag Verfahren zur Herstellung von Polyurethanen
DE19918727A1 (de) * 1999-04-24 2000-10-26 Bayer Ag Langkettige Polyetherpolyole mit hohem Anteil primärer OH-Gruppen
DE19928156A1 (de) * 1999-06-19 2000-12-28 Bayer Ag Aus Polyetherpolyolen hergestellte Polyurethan-Weichschäume
DE19944762A1 (de) * 1999-09-17 2001-03-22 Basf Ag Verfahren zur Herstellung von Blockweichschaumpolyolen
DE19960148A1 (de) 1999-12-14 2001-06-21 Basf Ag Verfahren zur Herstellung von Polyetheralkoholen
AU772300B2 (en) 2000-04-14 2004-04-22 Asahi Glass Company Limited Process for producing flexible polyurethane foam
US6642171B2 (en) 2000-04-28 2003-11-04 Synuthane International, Inc. Double metal cyanide catalysts containing polyglycol ether complexing agents
US6201035B1 (en) * 2000-05-24 2001-03-13 Basf Corporation Use of low unsaturated polyether polyols in high resilience slabstock foam applications
US6344494B1 (en) * 2000-05-24 2002-02-05 Basf Corporation Use of low unsaturated polyether polyols in slabstock foam applications
US6372812B1 (en) * 2001-02-20 2002-04-16 Foamex L.P. Higher support, lower density cushioning foams
DE10111823A1 (de) * 2001-03-13 2002-09-26 Basf Ag Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen
CN1208364C (zh) * 2001-05-24 2005-06-29 三井武田化学株式会社 生产软聚氨酯泡沫的方法
JP4122874B2 (ja) * 2001-07-18 2008-07-23 旭硝子株式会社 ポリオールおよびポリマー分散ポリオールの製造方法
KR100873594B1 (ko) * 2001-07-18 2008-12-11 아사히 가라스 가부시키가이샤 폴리올 및 폴리머 분산 폴리올의 제조방법
JP2008095122A (ja) * 2001-08-06 2008-04-24 Asahi Glass Co Ltd 軟質ポリウレタンフォーム、その製造方法およびその製造用原料システム液
JP4601894B2 (ja) * 2001-08-06 2010-12-22 旭硝子株式会社 自動車シート用軟質ポリウレタンフォーム
JP3909598B2 (ja) * 2001-12-21 2007-04-25 旭硝子株式会社 低反発軟質ポリウレタンフォームの製造方法
EP1329469A1 (de) * 2002-01-18 2003-07-23 Sika Schweiz AG Polyurethanzusammensetzung
DE10226415A1 (de) * 2002-06-13 2003-12-24 Basf Ag Verfahren zur Herstellung von Polyetheralkoholen
US6740687B2 (en) * 2002-08-14 2004-05-25 Foamex L.P. Latex replacement polyurethane foams with improved flame retardancy
US20040064001A1 (en) * 2002-09-30 2004-04-01 Stephan Ehlers Processes for preparing ethylene oxide-capped polyols
US7094811B2 (en) * 2002-10-03 2006-08-22 Bayer Corporation Energy absorbing flexible foams produced in part with a double metal cyanide catalyzed polyol
US6855742B2 (en) * 2003-01-28 2005-02-15 Bayer Antwerp, N.V. Agents for reducing the force-to-crush (FTC) of high support flexible foams
US6716890B1 (en) 2003-01-30 2004-04-06 Foamex L.P. Polyurethane foams with fine cell size
US20040154718A1 (en) * 2003-02-06 2004-08-12 Doesburg Van I. Polyurethane filled tire and method of making same
US20050038132A1 (en) * 2003-03-19 2005-02-17 Raghuram Gummaraju Composition for forming a foamed article and an article of furniture having the foamed article disposed therein
US6784218B1 (en) * 2003-03-19 2004-08-31 Basf Corporation Method of forming high resilience slabstock polyurethane foam displaying latex-like characteristics
US6797736B1 (en) * 2003-03-19 2004-09-28 Basf Corporation Method of forming high resilience slabstock polyurethane foam
US7005552B2 (en) 2003-11-03 2006-02-28 Bayer Materialscience Llc Single reactor synthesis of KOH-capped polyols based on DMC-synthesized intermediates
US20050101681A1 (en) * 2003-11-07 2005-05-12 Kaushiva Bryan D. Molded polyurethane foam with property enhancements for improved comfort and greater durability
US20060029788A1 (en) * 2004-08-04 2006-02-09 Foamex L.P. Lower density, thermoformable, sound absorbing polyurethane foams
DE102004047406A1 (de) * 2004-09-28 2006-03-30 Basf Ag Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen
DE102004047524A1 (de) * 2004-09-28 2006-03-30 Basf Ag Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen
RU2375945C2 (ru) * 2004-10-25 2009-12-20 Дау Глобал Текнолоджиз, Инк. Полиуретановая основа коврового покрытия, полученная с использованием гидроксиметилированных (сложный полиэфир) полиолов
WO2006047431A1 (en) * 2004-10-25 2006-05-04 Dow Global Technologies, Inc. Aqueous polyurethane dispersions made from hydroxymethyl containing polyester polyols derived from faty acids
MY148439A (en) * 2004-10-25 2013-04-30 Dow Global Technologies Inc Polymer polyols and polymer dispersions made from vegetable oil-based hydroxyl-containing materials
MX2007004933A (es) * 2004-10-25 2007-06-12 Dow Global Technologies Inc Prepolimeros preparados a partir de poliester polioles que contienen hidroximetilo derivados de acidos grasos.
MY158063A (en) * 2004-10-25 2016-08-30 Dow Global Technologies Inc Polyurethanes made from hydroxy-methyl containing fatty acids or alkyl esters of such fatty acids
WO2006054657A1 (ja) * 2004-11-18 2006-05-26 Asahi Glass Company, Limited 軟質ポリウレタンフォームの製造方法
KR20080018171A (ko) * 2005-05-25 2008-02-27 아사히 가라스 가부시키가이샤 연질 폴리우레탄폼 및 그 제조 방법, 그 연질폴리우레탄폼을 이용한 자동차용 시트
DE102005041142A1 (de) * 2005-08-30 2007-03-01 Basf Ag Verfahren zur Herstellung von Polyetheralkoholen
TW200801060A (en) * 2006-02-28 2008-01-01 Asahi Glass Co Ltd Flexible polyurethane foam and process for producing the same
US20090292147A1 (en) * 2006-06-23 2009-11-26 Basf Se Process for the continuous production of polyether alcohols
US20070299153A1 (en) * 2006-06-23 2007-12-27 Hager Stanley L Viscoelastic foams with slower recovery and improved tear
CN100588671C (zh) * 2006-11-28 2010-02-10 王伟松 丁醇聚醚的合成方法
CN100588669C (zh) * 2006-11-28 2010-02-10 王伟松 烯丙醇无规聚醚的制备方法
CN100588668C (zh) * 2006-11-28 2010-02-10 王伟松 甘油聚醚的合成方法
CN100588672C (zh) * 2006-11-28 2010-02-10 王伟松 烯丙醇无规聚醚的合成方法
US20090012195A1 (en) * 2007-07-05 2009-01-08 Neff Raymond A Resin composition for use in forming a polyurethane article with increased comfort
JP5303885B2 (ja) 2007-09-18 2013-10-02 旭硝子株式会社 軟質ポリウレタンフォームの製造方法および軟質ポリウレタンフォーム
EP2095832A1 (de) * 2008-02-28 2009-09-02 Bayer MaterialScience AG Polyharnstoff-Systeme und deren Anwendung als postoperative Adhäsionsbarrieren, Filme und Verbundteile.
EP2408841B1 (de) * 2009-03-17 2014-11-19 Basf Se POLYURETHANFORMKÖRPER MIT VERBESSERTER WEITERREIßFESTIGKEIT UND VERBESSERTEM DAUERBIEGEVERHALTEN
DE102009033710A1 (de) 2009-07-18 2011-01-20 Evonik Goldschmidt Gmbh Verwendung von Metallsalzen einer Carbonsäure bei der Herstellung von Polyurethansystemen
JP5763674B2 (ja) * 2009-12-29 2015-08-12 ダウ グローバル テクノロジーズ エルエルシー 吸音及び吸振用低密度ポリウレタンフォームの製造方法
SG185102A1 (en) 2010-04-30 2012-12-28 Basf Se Polyether polyols, process for preparing polyether polyols and their use for producing polyurethanes
US9115246B2 (en) 2010-04-30 2015-08-25 Basf Se Polyether polyols, process for preparing polyether polyols and their use for producing polyurethanes
US9228047B2 (en) * 2011-02-14 2016-01-05 Dow Global Technologies Llc Low density polyurethane foams
US10066047B2 (en) 2012-02-02 2018-09-04 Covestro Llc Polyurethane foams with decreased aldehyde emissions, a process for preparing these foams and a method for decreasing aldehyde in polyurethane foams
MX2015004380A (es) 2012-10-10 2015-06-10 Basf Se Espuma de poliuretano viscoelastica.
CN103087292B (zh) * 2013-02-04 2015-01-07 苏州井上高分子新材料有限公司 一种用于校车挡板的聚氨酯高回弹泡沫组合物
EP3044244B1 (en) * 2013-09-13 2020-06-10 Dow Global Technologies LLC Pipa polyol based conventional flexible foam
TWI518000B (zh) 2014-08-26 2016-01-21 溫芫鋐 自行車用液壓刹車器
US20180072838A1 (en) * 2015-04-08 2018-03-15 Shell Oil Company Improvements relating to polyols and polyurethanes
KR102575283B1 (ko) * 2015-06-30 2023-09-07 다우 글로벌 테크놀로지스 엘엘씨 이중 금속 시아나이드 촉매를 사용한 프로필렌 옥사이드/에틸렌 옥사이드 코폴리머를 제조하는 방법 및 그렇게 제조된 코폴리머
MX2018004006A (es) 2015-09-29 2018-05-23 Basf Se Espuma de poliuretano de alta resiliencia.
ES2819507T3 (es) * 2015-10-08 2021-04-16 Dow Global Technologies Llc Espumas de poliuretano de alta resiliencia hechas con polioles de alto peso equivalente, alta funcionalidad, con grupos hidroxilo principalmente secundarios
SG11201804524TA (en) 2015-12-21 2018-07-30 Shell Int Research Process for the production of polyurethane foams
US11312811B2 (en) 2016-04-26 2022-04-26 Covestro Llc Flexible foam using polymer polyols produced via DMC catalyzed polyols
US10155837B2 (en) 2016-07-29 2018-12-18 Resinate Materials Group, Inc. Sustainable polyester polyol compositions
WO2018022368A1 (en) 2016-07-29 2018-02-01 Resinate Materials Group, Inc. Sustainable polyester polyol compositions
SG11202003718XA (en) 2017-11-06 2020-05-28 Shell Int Research Process for preparing a polyether polyol with a high ethylene oxide content
US10766998B2 (en) * 2017-11-21 2020-09-08 Covestro Llc Flexible polyurethane foams
JP7158903B2 (ja) * 2018-06-13 2022-10-24 シーカ・ハマタイト株式会社 ２液ウレタン系接着剤組成物
US11572433B2 (en) 2021-03-12 2023-02-07 Covestro Llc In-situ formed polyols, a process for their preparation, foams prepared from these in-situ formed polyols and a process for their preparation
CN115232257B (zh) * 2021-04-22 2023-09-29 中国石油化工股份有限公司 一种低粘度聚合物多元醇的制备方法及得到的聚合物多元醇与应用
US11718705B2 (en) 2021-07-28 2023-08-08 Covestro Llc In-situ formed polyether polyols, a process for their preparation, and a process for the preparation of polyurethane foams
WO2025128192A1 (en) * 2023-12-15 2025-06-19 Dow Global Technologies Llc High-resiliency polyurethane foam and method of making

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0394487A1 (en) * 1988-10-25 1990-10-31 Asahi Glass Co., Ltd. Elastic polyurethane foam and process for its production
US5114619A (en) * 1989-07-14 1992-05-19 The Dow Chemical Company Production of polyether polyols with reduced unsaturation
US5158922A (en) * 1992-02-04 1992-10-27 Arco Chemical Technology, L.P. Process for preparing metal cyanide complex catalyst
CN1077463A (zh) * 1988-11-18 1993-10-20 陶氏化学公司 一种制备聚氨酯聚合物的方法

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3461086A (en) * 1964-03-05 1969-08-12 Dow Chemical Co Polyether urethane foams from certain heteric polyethers
US3829505A (en) * 1970-02-24 1974-08-13 Gen Tire & Rubber Co Polyethers and method for making the same
US4143004A (en) * 1974-10-02 1979-03-06 Berol Kemi Ab Process for the preparation of polyurethane foam
US4690955A (en) * 1986-06-30 1987-09-01 Union Carbide Corporation Polyether silicone copolymers with mixed hydroxy alkoxy capping for stabilizing high solid content, molded, flexible urethane foam
US5171759A (en) * 1988-07-12 1992-12-15 Arco Chemical Technology, L.P. Polymer polyol compositions and their use in the preparation of polyurethane foams
US5010117A (en) * 1989-06-16 1991-04-23 Dow Chemical Company Flexible polyurethane foams prepared using low unsaturation polyether polyols
US5391722A (en) * 1990-03-30 1995-02-21 Olin Corporation Acid-catalyzed fabrication of precursors for use in making polyols using double metal cyanide catalysts
US5177119A (en) * 1990-04-25 1993-01-05 Arco Chemical Technology, L.P. Polyurethane foams blown only with water
US5235114A (en) * 1991-04-29 1993-08-10 Olin Corporation Process for purifying and end-capping polyols made using double metal cyanide catalysts
US5144093A (en) * 1991-04-29 1992-09-01 Olin Corporation Process for purifying and end-capping polyols made using double metal cyanide catalysts
US5157056A (en) * 1991-07-17 1992-10-20 Arco Chemical Technology, L.P. High resiliency polyurethane foams with improved static fatigue properties
US5357038A (en) * 1992-08-03 1994-10-18 Olin Corporation Process and composition for providing double metal cyanide catalyzed polyols having enhanced reactivity
GB9301995D0 (en) * 1993-02-02 1993-03-17 Ici Plc Process for making flexible foams
US5364906A (en) * 1993-08-20 1994-11-15 Arco Chemical Technology, L.P. Low viscosity polymer polyols with improved dispersion stability

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0394487A1 (en) * 1988-10-25 1990-10-31 Asahi Glass Co., Ltd. Elastic polyurethane foam and process for its production
CN1077463A (zh) * 1988-11-18 1993-10-20 陶氏化学公司 一种制备聚氨酯聚合物的方法
US5114619A (en) * 1989-07-14 1992-05-19 The Dow Chemical Company Production of polyether polyols with reduced unsaturation
US5158922A (en) * 1992-02-04 1992-10-27 Arco Chemical Technology, L.P. Process for preparing metal cyanide complex catalyst

Also Published As

Publication number Publication date
EP0876416B1 (en) 1999-08-11
DE69700406D1 (de) 1999-09-16
EP0876416A1 (en) 1998-11-11
US5648559A (en) 1997-07-15
DE69700406T2 (de) 2000-03-23
JP2000517347A (ja) 2000-12-26
JP3895385B2 (ja) 2007-03-22
AR005528A1 (es) 1999-06-23
BR9706974A (pt) 1999-04-06
WO1997027236A1 (en) 1997-07-31
TW440577B (en) 2001-06-16
CA2241627C (en) 2006-08-29
CA2241627A1 (en) 1997-07-31
AU1544897A (en) 1997-08-20
US5605939A (en) 1997-02-25
ES2135287T3 (es) 1999-10-16
CN1209820A (zh) 1999-03-03

Similar Documents

Publication Publication Date Title
CN1114640C (zh) 适用于制备收缩趋势减少的高回弹性软泡沫的聚（氧化丙烯/氧化乙烯）无规多醇及由其制备的泡沫
CN1116329C (zh) 物理性质有改进的模制聚氨酯泡沫塑料
US8299138B2 (en) Process for producing flexible polyurethane foam
CN100391997C (zh) 双金属氰化物催化的散布的环氧乙烷型聚氧亚丙基多元醇的应用
CN1152902C (zh) 从双金属氰化物配合物催化的多元醇制备的模塑料和块料聚氨酯泡沫体
CN1221584C (zh) 软质聚氨酯泡沫材料及其制造方法
CN1320016C (zh) 用于降低高支撑柔性泡沫的压破力的试剂
HK1039956A1 (en) Dispersion polyols for hypersoft polyurethane foam
EP1316571A1 (en) Flexible polyurethane foam and method for its production
CN101802047A (zh) 软质聚氨酯泡沫的制造方法
US20130345331A1 (en) High-concentration polymer polyol and method for its production
HK1047441A1 (en) Polyisocyanate compositions and a process for the production of low-density flexible foams with low humid aged compression sets from these polyisocyanate compositions
CN101410430A (zh) 聚氨酯泡沫体制造方法
US6395798B1 (en) Low density microcellular elastomers based on isocyanate-terminated prepolymers
US11572433B2 (en) In-situ formed polyols, a process for their preparation, foams prepared from these in-situ formed polyols and a process for their preparation
JP4412116B2 (ja) 低反発性軟質ポリウレタンフォームおよびその製造方法
CN117881714A (zh) 用于制备高回弹性聚氨酯泡沫的方法
TW201313765A (zh) 軟質聚胺甲酸酯發泡體之製造方法
JP5151461B2 (ja) 軟質ポリウレタンフォームの製造方法およびその用途
JP4182733B2 (ja) 軟質ポリウレタンフォームおよびその製造方法
KR20070063002A (ko) Ｐｉｐａ-폴리올의 제조 방법
HK1068359B (en) Process for the production of polyol blends
HK1068359A1 (en) Process for the production of polyol blends

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
C41 Transfer of patent application or patent right or utility model
C56 Change in the name or address of the patentee
CP01 Change in the name or title of a patent holder

Address after: American Delaware

Patentee after: Link chemical technologies

Address before: American Delaware

Patentee before: ARCO CHEMICAL TECHNOLOGY, L.P.

TR01 Transfer of patent right

Effective date of registration: 20161013

Address after: Antwerp

Patentee after: Koth a Limited by Share Ltd.

Address before: Antwerp

Patentee before: Bayer Antwerp

Effective date of registration: 20161013

Address after: Antwerp

Patentee after: Bayer Antwerp

Address before: American Delaware

Patentee before: Link chemical technologies

CX01 Expiry of patent term

Granted publication date: 20030716

EXPY Termination of patent right or utility model