ES2135287T3 - Polioles aleatorios de poli(oxipropileno/oxietileno) utiles para preparar espuma flexible de elevada resiliencia con poca tendencia a la contraccion y espuma preparada con ellos. - Google Patents

Polioles aleatorios de poli(oxipropileno/oxietileno) utiles para preparar espuma flexible de elevada resiliencia con poca tendencia a la contraccion y espuma preparada con ellos.

Info

Publication number
ES2135287T3
ES2135287T3 ES97901596T ES97901596T ES2135287T3 ES 2135287 T3 ES2135287 T3 ES 2135287T3 ES 97901596 T ES97901596 T ES 97901596T ES 97901596 T ES97901596 T ES 97901596T ES 2135287 T3 ES2135287 T3 ES 2135287T3
Authority
ES
Spain
Prior art keywords
oxyethylene
oxypropylene
foam
contraction
poly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES97901596T
Other languages
English (en)
Spanish (es)
Inventor
Stanley Hager
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lyondell Chemical Technology LP
Original Assignee
Arco Chemical Technology LP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arco Chemical Technology LP filed Critical Arco Chemical Technology LP
Application granted granted Critical
Publication of ES2135287T3 publication Critical patent/ES2135287T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
    • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
    • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
    • C08G65/2642—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the catalyst used
    • C08G65/2645—Metals or compounds thereof, e.g. salts
    • C08G65/2663—Metal cyanide catalysts, i.e. DMC's
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/4009—Two or more macromolecular compounds not provided for in one single group of groups C08G18/42 - C08G18/64
    • C08G18/4072—Mixtures of compounds of group C08G18/63 with other macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4833—Polyethers containing oxyethylene units
    • C08G18/4837—Polyethers containing oxyethylene units and other oxyalkylene units
    • C08G18/485—Polyethers containing oxyethylene units and other oxyalkylene units containing mixed oxyethylene-oxypropylene or oxyethylene-higher oxyalkylene end groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4866—Polyethers having a low unsaturation value
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
    • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
    • C08G65/26—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds
    • C08G65/2696—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers and other compounds characterised by the process or apparatus used
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0008—Foam properties flexible
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0041—Foam properties having specified density
    • C08G2110/005—< 50kg/m3
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G2110/00—Foam properties
    • C08G2110/0083—Foam properties prepared using water as the sole blowing agent

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Toxicology (AREA)
  • Polyurethanes Or Polyureas (AREA)
  • Polyethers (AREA)
ES97901596T 1996-01-26 1997-01-23 Polioles aleatorios de poli(oxipropileno/oxietileno) utiles para preparar espuma flexible de elevada resiliencia con poca tendencia a la contraccion y espuma preparada con ellos. Expired - Lifetime ES2135287T3 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US08/592,087 US5605939A (en) 1996-01-26 1996-01-26 Poly(oxypropylene/oxyethylene) random polyols useful in preparing flexible high resilience foam with reduced tendencies toward shrinkage and foam prepared therewith

Publications (1)

Publication Number Publication Date
ES2135287T3 true ES2135287T3 (es) 1999-10-16

Family

ID=24369232

Family Applications (1)

Application Number Title Priority Date Filing Date
ES97901596T Expired - Lifetime ES2135287T3 (es) 1996-01-26 1997-01-23 Polioles aleatorios de poli(oxipropileno/oxietileno) utiles para preparar espuma flexible de elevada resiliencia con poca tendencia a la contraccion y espuma preparada con ellos.

Country Status (12)

Country Link
US (2) US5605939A (enExample)
EP (1) EP0876416B1 (enExample)
JP (1) JP3895385B2 (enExample)
CN (1) CN1114640C (enExample)
AR (1) AR005528A1 (enExample)
AU (1) AU1544897A (enExample)
BR (1) BR9706974A (enExample)
CA (1) CA2241627C (enExample)
DE (1) DE69700406T2 (enExample)
ES (1) ES2135287T3 (enExample)
TW (1) TW440577B (enExample)
WO (1) WO1997027236A1 (enExample)

Families Citing this family (86)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5670601A (en) * 1995-06-15 1997-09-23 Arco Chemical Technology, L.P. Polyurethane elastomers having improved green strength and demold time and polyoxyalkylene polyols suitable for their preparation
US5700847A (en) * 1995-12-04 1997-12-23 Arco Chemical Technology, L.P. Molded polyurethane foam with enhanced physical properties
US5668191A (en) * 1995-12-21 1997-09-16 Arco Chemical Technology, L.P. One-shot cold molded flexible polyurethane foam from low primary hydroxyl polyols and process for the preparation thereof
US5958994A (en) * 1997-02-25 1999-09-28 Arco Chemical Technology, L.P. Method for decreasing the propensity for phase-out of the high molecular weight component of double metal cyanide-catalyzed high secondary hydroxyl polyoxypropylene polyols
US6008263A (en) * 1998-04-03 1999-12-28 Lyondell Chemical Worldwide, Inc. Molded and slab polyurethane foam prepared from double metal cyanide complex-catalyzed polyoxyalkylene polyols and polyols suitable for the preparation thereof
US6066683A (en) * 1998-04-03 2000-05-23 Lyondell Chemical Worldwide, Inc. Molded and slab polyurethane foam prepared from double metal cyanide complex-catalyzed polyoxyalkylene polyols and polyols suitable for the preparation thereof
DE19840585A1 (de) † 1998-09-05 2000-03-09 Basf Ag Verfahren zur Herstellung von Polyetherolen durch ringöffnende Polymerisation von Alkylenoxiden
AU760247B2 (en) * 1998-12-29 2003-05-08 Dow Global Technologies Inc. Polyurethane foams prepared from mechanically frothed polyurethane dispersions
JO2132B1 (en) * 1999-01-19 2002-08-07 شل انترناشونال ريسيرتش ماتستشابيج بي في Method for preparing flexible polyurethane foams
DE19917897A1 (de) 1999-04-20 2000-10-26 Basf Ag Verfahren zur Herstellung von Polyurethanen
DE19918727A1 (de) 1999-04-24 2000-10-26 Bayer Ag Langkettige Polyetherpolyole mit hohem Anteil primärer OH-Gruppen
DE19928156A1 (de) 1999-06-19 2000-12-28 Bayer Ag Aus Polyetherpolyolen hergestellte Polyurethan-Weichschäume
DE19944762A1 (de) * 1999-09-17 2001-03-22 Basf Ag Verfahren zur Herstellung von Blockweichschaumpolyolen
DE19960148A1 (de) 1999-12-14 2001-06-21 Basf Ag Verfahren zur Herstellung von Polyetheralkoholen
EP1273605B1 (en) * 2000-04-14 2006-06-07 Asahi Glass Company Ltd. Process for producing flexible polyurethane foam
WO2001083107A2 (en) 2000-04-28 2001-11-08 Synuthane International, Inc. Double metal cyanide catalysts containing polyglycol ether complexing agents
US6201035B1 (en) * 2000-05-24 2001-03-13 Basf Corporation Use of low unsaturated polyether polyols in high resilience slabstock foam applications
US6344494B1 (en) 2000-05-24 2002-02-05 Basf Corporation Use of low unsaturated polyether polyols in slabstock foam applications
US6372812B1 (en) * 2001-02-20 2002-04-16 Foamex L.P. Higher support, lower density cushioning foams
DE10111823A1 (de) * 2001-03-13 2002-09-26 Basf Ag Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen
WO2002100916A1 (en) * 2001-05-24 2002-12-19 Mitsui Takeda Chemicals, Inc. Process for producing flexible polyurethane foams and apparatus for producing flexible polyurethane foams
JP4122874B2 (ja) * 2001-07-18 2008-07-23 旭硝子株式会社 ポリオールおよびポリマー分散ポリオールの製造方法
CN1257928C (zh) * 2001-07-18 2006-05-31 旭硝子株式会社 多元醇和聚合物分散多元醇的制造方法
JP2008095122A (ja) * 2001-08-06 2008-04-24 Asahi Glass Co Ltd 軟質ポリウレタンフォーム、その製造方法およびその製造用原料システム液
JP4601894B2 (ja) * 2001-08-06 2010-12-22 旭硝子株式会社 自動車シート用軟質ポリウレタンフォーム
JP3909598B2 (ja) * 2001-12-21 2007-04-25 旭硝子株式会社 低反発軟質ポリウレタンフォームの製造方法
EP1329469A1 (de) * 2002-01-18 2003-07-23 Sika Schweiz AG Polyurethanzusammensetzung
DE10226415A1 (de) * 2002-06-13 2003-12-24 Basf Ag Verfahren zur Herstellung von Polyetheralkoholen
US6740687B2 (en) * 2002-08-14 2004-05-25 Foamex L.P. Latex replacement polyurethane foams with improved flame retardancy
US20040064001A1 (en) * 2002-09-30 2004-04-01 Stephan Ehlers Processes for preparing ethylene oxide-capped polyols
US7094811B2 (en) * 2002-10-03 2006-08-22 Bayer Corporation Energy absorbing flexible foams produced in part with a double metal cyanide catalyzed polyol
US6855742B2 (en) * 2003-01-28 2005-02-15 Bayer Antwerp, N.V. Agents for reducing the force-to-crush (FTC) of high support flexible foams
US6716890B1 (en) 2003-01-30 2004-04-06 Foamex L.P. Polyurethane foams with fine cell size
US20040154718A1 (en) * 2003-02-06 2004-08-12 Doesburg Van I. Polyurethane filled tire and method of making same
US6784218B1 (en) * 2003-03-19 2004-08-31 Basf Corporation Method of forming high resilience slabstock polyurethane foam displaying latex-like characteristics
US20050038132A1 (en) * 2003-03-19 2005-02-17 Raghuram Gummaraju Composition for forming a foamed article and an article of furniture having the foamed article disposed therein
US6797736B1 (en) * 2003-03-19 2004-09-28 Basf Corporation Method of forming high resilience slabstock polyurethane foam
US7005552B2 (en) 2003-11-03 2006-02-28 Bayer Materialscience Llc Single reactor synthesis of KOH-capped polyols based on DMC-synthesized intermediates
US20050101681A1 (en) * 2003-11-07 2005-05-12 Kaushiva Bryan D. Molded polyurethane foam with property enhancements for improved comfort and greater durability
US20060029788A1 (en) * 2004-08-04 2006-02-09 Foamex L.P. Lower density, thermoformable, sound absorbing polyurethane foams
DE102004047406A1 (de) * 2004-09-28 2006-03-30 Basf Ag Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen
DE102004047524A1 (de) * 2004-09-28 2006-03-30 Basf Ag Verfahren zur Herstellung von Polyurethan-Weichschaumstoffen
RU2418813C2 (ru) * 2004-10-25 2011-05-20 Дау Глобал Текнолоджиз Инк. Форполимеры, полученные из гидроксиметилсодержащих полиэфирполиолов на основе сложного эфира, полученных из жирных кислот
CA2579766C (en) * 2004-10-25 2013-12-17 Dow Global Technologies Inc. Polymer polyols and polymer dispersions made from vegetable oil-based hydroxyl-containing materials
CN101039977B (zh) * 2004-10-25 2011-10-12 陶氏环球技术有限责任公司 由含羟甲基的脂肪酸或这种脂肪酸的烷基酯制成的聚氨酯
CN100554303C (zh) * 2004-10-25 2009-10-28 陶氏环球技术公司 使用羟甲基化聚酯多元醇制成的聚氨酯地毯背衬
WO2006047431A1 (en) * 2004-10-25 2006-05-04 Dow Global Technologies, Inc. Aqueous polyurethane dispersions made from hydroxymethyl containing polyester polyols derived from faty acids
JP4910702B2 (ja) 2004-11-18 2012-04-04 旭硝子株式会社 軟質ポリウレタンフォームの製造方法
KR20080018171A (ko) * 2005-05-25 2008-02-27 아사히 가라스 가부시키가이샤 연질 폴리우레탄폼 및 그 제조 방법, 그 연질폴리우레탄폼을 이용한 자동차용 시트
DE102005041142A1 (de) * 2005-08-30 2007-03-01 Basf Ag Verfahren zur Herstellung von Polyetheralkoholen
TW200801060A (en) * 2006-02-28 2008-01-01 Asahi Glass Co Ltd Flexible polyurethane foam and process for producing the same
US20070299153A1 (en) * 2006-06-23 2007-12-27 Hager Stanley L Viscoelastic foams with slower recovery and improved tear
EP2035479B1 (de) * 2006-06-23 2010-07-07 Basf Se Verfahren zur kontinuierlichen herstellung von polyetheralkoholen
CN100588669C (zh) * 2006-11-28 2010-02-10 王伟松 烯丙醇无规聚醚的制备方法
CN100588671C (zh) * 2006-11-28 2010-02-10 王伟松 丁醇聚醚的合成方法
CN100588668C (zh) * 2006-11-28 2010-02-10 王伟松 甘油聚醚的合成方法
CN100588672C (zh) * 2006-11-28 2010-02-10 王伟松 烯丙醇无规聚醚的合成方法
US20090012195A1 (en) * 2007-07-05 2009-01-08 Neff Raymond A Resin composition for use in forming a polyurethane article with increased comfort
JP5303885B2 (ja) * 2007-09-18 2013-10-02 旭硝子株式会社 軟質ポリウレタンフォームの製造方法および軟質ポリウレタンフォーム
EP2095832A1 (de) * 2008-02-28 2009-09-02 Bayer MaterialScience AG Polyharnstoff-Systeme und deren Anwendung als postoperative Adhäsionsbarrieren, Filme und Verbundteile.
WO2010105966A1 (de) * 2009-03-17 2010-09-23 Basf Se POLYURETHANFORMKÖRPER MIT VERBESSERTER WEITERREIßFESTIGKEIT UND VERBESSERTEM DAUERBIEGEVERHALTEN
DE102009033710A1 (de) 2009-07-18 2011-01-20 Evonik Goldschmidt Gmbh Verwendung von Metallsalzen einer Carbonsäure bei der Herstellung von Polyurethansystemen
BR112012015946A2 (pt) * 2009-12-29 2020-09-08 Dow Global Technologies Llc mistura de óxidos de polipropileno capeados com oxido de etileno, processo para preparar um poliuretano e processo para preparar uma espuma de poliuretano resiliente e flexivel
US9115246B2 (en) 2010-04-30 2015-08-25 Basf Se Polyether polyols, process for preparing polyether polyols and their use for producing polyurethanes
EP2563839B1 (de) 2010-04-30 2014-12-17 Basf Se Polyetherpolyole, verfahren zur herstellung von polyetherpolyolen, sowie deren verwendung zur herstellung von polyurethanen
JP5902719B2 (ja) * 2011-02-14 2016-04-13 ダウ グローバル テクノロジーズ エルエルシー 低密度ポリウレタンフォーム
US10066047B2 (en) 2012-02-02 2018-09-04 Covestro Llc Polyurethane foams with decreased aldehyde emissions, a process for preparing these foams and a method for decreasing aldehyde in polyurethane foams
KR20150070220A (ko) * 2012-10-10 2015-06-24 바스프 에스이 점탄성 폴리우레탄 발포체
CN103087292B (zh) * 2013-02-04 2015-01-07 苏州井上高分子新材料有限公司 一种用于校车挡板的聚氨酯高回弹泡沫组合物
US9840603B2 (en) * 2013-09-13 2017-12-12 Dow Global Technologies Llc PIPA based combustion-modified flexible foam
TWI518000B (zh) 2014-08-26 2016-01-21 溫芫鋐 自行車用液壓刹車器
EP3280752A1 (en) * 2015-04-08 2018-02-14 Shell Internationale Research Maatschappij B.V. Improvements relating to polyols and polyurethanes
BR112017028016B1 (pt) * 2015-06-30 2022-02-22 Dow Global Technologies Llc Polímero aleatório de poli(óxido de propileno-co-óxido de etileno), método para produzir uma espuma de poliuretano e processo para a preparação de um poliéter poliol
US10829584B2 (en) 2015-09-29 2020-11-10 Basf Se High-resiliency polyurethane foam
CN108137773B (zh) * 2015-10-08 2021-10-15 陶氏环球技术有限责任公司 由具有主要仲羟基的高官能度、高当量多元醇制备的高弹性聚氨基甲酸酯泡沫
LT3394137T (lt) * 2015-12-21 2021-06-10 Shell Internationale Research Maatschappij B.V. Poliuretano putplasčio gamybos būdas
US11312811B2 (en) 2016-04-26 2022-04-26 Covestro Llc Flexible foam using polymer polyols produced via DMC catalyzed polyols
WO2018022368A1 (en) 2016-07-29 2018-02-01 Resinate Materials Group, Inc. Sustainable polyester polyol compositions
US10155837B2 (en) 2016-07-29 2018-12-18 Resinate Materials Group, Inc. Sustainable polyester polyol compositions
KR102718684B1 (ko) 2017-11-06 2024-10-18 쉘 인터내셔날 리써취 마트샤피지 비.브이. 높은 에틸렌 옥시드 함량을 갖는 폴리에테르 폴리올의 제조 방법
US10766998B2 (en) 2017-11-21 2020-09-08 Covestro Llc Flexible polyurethane foams
JP7158903B2 (ja) * 2018-06-13 2022-10-24 シーカ・ハマタイト株式会社 ２液ウレタン系接着剤組成物
US11572433B2 (en) 2021-03-12 2023-02-07 Covestro Llc In-situ formed polyols, a process for their preparation, foams prepared from these in-situ formed polyols and a process for their preparation
CN115232257B (zh) * 2021-04-22 2023-09-29 中国石油化工股份有限公司 一种低粘度聚合物多元醇的制备方法及得到的聚合物多元醇与应用
US11718705B2 (en) 2021-07-28 2023-08-08 Covestro Llc In-situ formed polyether polyols, a process for their preparation, and a process for the preparation of polyurethane foams
WO2025128192A1 (en) * 2023-12-15 2025-06-19 Dow Global Technologies Llc High-resiliency polyurethane foam and method of making

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3461086A (en) * 1964-03-05 1969-08-12 Dow Chemical Co Polyether urethane foams from certain heteric polyethers
US3829505A (en) * 1970-02-24 1974-08-13 Gen Tire & Rubber Co Polyethers and method for making the same
US4143004A (en) * 1974-10-02 1979-03-06 Berol Kemi Ab Process for the preparation of polyurethane foam
US4690955A (en) * 1986-06-30 1987-09-01 Union Carbide Corporation Polyether silicone copolymers with mixed hydroxy alkoxy capping for stabilizing high solid content, molded, flexible urethane foam
US5171759A (en) * 1988-07-12 1992-12-15 Arco Chemical Technology, L.P. Polymer polyol compositions and their use in the preparation of polyurethane foams
WO1990004613A1 (fr) * 1988-10-25 1990-05-03 Asahi Glass Company Ltd. Mousse de polyurethane elastique et procede de production
US5114619A (en) * 1989-07-14 1992-05-19 The Dow Chemical Company Production of polyether polyols with reduced unsaturation
CN1033093C (zh) * 1988-11-18 1996-10-23 陶氏化学公司 一种制备聚氨酯聚合物的方法
US5010117A (en) * 1989-06-16 1991-04-23 Dow Chemical Company Flexible polyurethane foams prepared using low unsaturation polyether polyols
US5391722A (en) * 1990-03-30 1995-02-21 Olin Corporation Acid-catalyzed fabrication of precursors for use in making polyols using double metal cyanide catalysts
US5177119A (en) * 1990-04-25 1993-01-05 Arco Chemical Technology, L.P. Polyurethane foams blown only with water
US5235114A (en) * 1991-04-29 1993-08-10 Olin Corporation Process for purifying and end-capping polyols made using double metal cyanide catalysts
US5144093A (en) * 1991-04-29 1992-09-01 Olin Corporation Process for purifying and end-capping polyols made using double metal cyanide catalysts
US5157056A (en) * 1991-07-17 1992-10-20 Arco Chemical Technology, L.P. High resiliency polyurethane foams with improved static fatigue properties
US5158922A (en) * 1992-02-04 1992-10-27 Arco Chemical Technology, L.P. Process for preparing metal cyanide complex catalyst
US5357038A (en) * 1992-08-03 1994-10-18 Olin Corporation Process and composition for providing double metal cyanide catalyzed polyols having enhanced reactivity
GB9301995D0 (en) * 1993-02-02 1993-03-17 Ici Plc Process for making flexible foams
US5364906A (en) * 1993-08-20 1994-11-15 Arco Chemical Technology, L.P. Low viscosity polymer polyols with improved dispersion stability

Also Published As

Publication number Publication date
JP2000517347A (ja) 2000-12-26
AU1544897A (en) 1997-08-20
US5605939A (en) 1997-02-25
BR9706974A (pt) 1999-04-06
JP3895385B2 (ja) 2007-03-22
CN1209820A (zh) 1999-03-03
TW440577B (en) 2001-06-16
EP0876416B1 (en) 1999-08-11
EP0876416A1 (en) 1998-11-11
CA2241627C (en) 2006-08-29
DE69700406D1 (de) 1999-09-16
WO1997027236A1 (en) 1997-07-31
AR005528A1 (es) 1999-06-23
CA2241627A1 (en) 1997-07-31
CN1114640C (zh) 2003-07-16
US5648559A (en) 1997-07-15
DE69700406T2 (de) 2000-03-23

Similar Documents

Publication Publication Date Title
ES2135287T3 (es) Polioles aleatorios de poli(oxipropileno/oxietileno) utiles para preparar espuma flexible de elevada resiliencia con poca tendencia a la contraccion y espuma preparada con ellos.
ES2142823T3 (es) Espumas hidrofilas y procedimiento para su fabricacion.
ES2099094T3 (es) Metodos y composiciones para tratamiento de interacciones hidrofobas patologicas en fluidos biologicos.
MXPA03005694A (es) Composicion de agente de soplado y espuma polimerica conteniendo un hidrofluorocarburo normalmente liquido y dioxido de carbono.
TR28386A (tr) Silikonsuz yüzeyaktif maddeler iceren terkiplerden hazirlanan poliizosiyanata dayanan polimerler ve bunlarin hazirlanmasi icin yöntem.
ES2101108T3 (es) Un procedimiento para preparar un elastomero de poliuretano microcelular a partir de un prepolimero con terminacion de isocianato con &#34;segmento blando&#34; y elastomero de poliuretano microcelular obtenido a partir del mismo.
FR2531093B1 (fr) Suspensions concentrees pompables de polymeres hydrosolubles
AR002489A1 (es) Metodo para preparar elastomeros de poliuretano que tienen propiedades mejoradas de resistencia en crudo y tiempo de desmoldeo, un prepolimero ypolioles de polioxialquileno adecuados para la preparacion de estos elastomeros, elastomero de poliuretano, y suela de zapatos.
BRPI0407373A (pt) Espuma hidro-alcoólica formando espuma em filme
CO4940388A1 (es) Composiciones limpiadoras suaves antimicrobianas que se qui- tan enjuagando
MXPA02012937A (es) Combinaciones de productos activos con propiedades insecticidas y acaricidas.
PE20000721A1 (es) Articulo absorbente que incluye un agente modificador de heces basado en calcio
SE8402372D0 (sv) Water soluble, modified polyurethane
BR0112080A (pt) Vetores particulados para aperfeiçoamento da absorção oral de principios ativos
AR030966A1 (es) Composiciones y metodos para limpiar lentes de contacto
CA2368505A1 (fr) Materiau elastomere silicone hydrophile utilisable notamment pour la prise d&#39;empreintes dentaires
ES2183917T3 (es) Espumas moldeadas de poliuretano de muy baja densidad via prepolimeros terminados en isocianatos.
HN1999000135A (es) Formulacion liquida.
AR047270A1 (es) Una barra de tocador masajeadora conaglomerados desintegrables.
BR9911108A (pt) Catalisadores de complexo de cianeto de metal duplo sililado
AR005178A1 (es) Proceso para la preparacion de elastomeros de poliuretano microcelulares basados en prepolimeros terminados en isocianato, elastomeros de poliuretanomicrocelulares de baja densidad basados en prepolimeros terminados en isocianatos, y la suela de calzado preparada con dicho elastomero microcelular
ES2105873T3 (es) Espumas de poliuretano modificadas con tensioactivos no ionicos.
DE69916643D1 (de) Verwendung von hyaluronsäure zur behandlung der bestrahlungs-blasenentzündung
AR008609A1 (es) Proceso para elaborar espumas rigidas de poliuretano modificado con isocianurato, dicha espuma rigida y composicion isocianato-reactiva, y uso dela espuma.
AR037434A1 (es) Mejoras referidas a barras detergentes

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 876416

Country of ref document: ES