CN1107120C - 特别适用于汽车应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金 - Google Patents

特别适用于汽车应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金 Download PDF

Info

Publication number
CN1107120C
CN1107120C CN99801195A CN99801195A CN1107120C CN 1107120 C CN1107120 C CN 1107120C CN 99801195 A CN99801195 A CN 99801195A CN 99801195 A CN99801195 A CN 99801195A CN 1107120 C CN1107120 C CN 1107120C
Authority
CN
China
Prior art keywords
weight
magnesium
magnesium alloy
scandium
aluminium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN99801195A
Other languages
English (en)
Chinese (zh)
Other versions
CN1274391A (zh
Inventor
B·兰克佐斯基
V·叶拉金
R·拉友
V·萨克哈罗夫
Y·费拉托夫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Airbus Operations GmbH
Original Assignee
DaimlerChrysler AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DaimlerChrysler AG filed Critical DaimlerChrysler AG
Publication of CN1274391A publication Critical patent/CN1274391A/zh
Application granted granted Critical
Publication of CN1107120C publication Critical patent/CN1107120C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Preventing Corrosion Or Incrustation Of Metals (AREA)
  • Powder Metallurgy (AREA)
  • Prevention Of Electric Corrosion (AREA)
  • Arc Welding In General (AREA)
  • Forging (AREA)
  • Conductive Materials (AREA)
  • Extrusion Of Metal (AREA)
  • Pressure Welding/Diffusion-Bonding (AREA)
CN99801195A 1998-08-21 1999-08-10 特别适用于汽车应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金 Expired - Lifetime CN1107120C (zh)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19838015A DE19838015C2 (de) 1998-08-21 1998-08-21 Gewalztes, stranggepreßtes, geschweißtes oder geschmiedetes Bauteil aus einer schweißbaren, korrosionsbeständigen hochmagnesiumhaltigen Aluminium-Magnesium-Legierung
DE19838015.1 1998-08-21

Publications (2)

Publication Number Publication Date
CN1274391A CN1274391A (zh) 2000-11-22
CN1107120C true CN1107120C (zh) 2003-04-30

Family

ID=7878284

Family Applications (1)

Application Number Title Priority Date Filing Date
CN99801195A Expired - Lifetime CN1107120C (zh) 1998-08-21 1999-08-10 特别适用于汽车应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金

Country Status (10)

Country Link
US (1) US6315948B1 (enExample)
EP (1) EP1025270B1 (enExample)
JP (1) JP2002523621A (enExample)
CN (1) CN1107120C (enExample)
AT (1) ATE216735T1 (enExample)
CA (1) CA2306726C (enExample)
DE (2) DE19838015C2 (enExample)
ES (1) ES2173759T3 (enExample)
RU (1) RU2226567C2 (enExample)
WO (1) WO2000011231A1 (enExample)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN100445019C (zh) * 2006-09-14 2008-12-24 中国航空工业第一集团公司北京航空材料研究院 Al-Mg-Sc系焊丝
CN107363122A (zh) * 2017-06-14 2017-11-21 飞龙精工科技(苏州)有限公司 铝镁合金丝的制备工艺
CN111378878A (zh) * 2018-12-29 2020-07-07 嘉丰工业科技（惠州）有限公司 一种高延展性非热处理压铸铝合金及其制备方法

Families Citing this family (40)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10248594B4 (de) * 2001-12-14 2006-04-27 Eads Deutschland Gmbh Verfahren zum Herstellen eines Scandium (Sc)- legierten Aluminiumblechmaterials mit hoher Risszähigkeit
US20040156739A1 (en) 2002-02-01 2004-08-12 Song Shihong Gary Castable high temperature aluminum alloy
AT501867B1 (de) * 2005-05-19 2009-07-15 Aluminium Lend Gmbh & Co Kg Aluminiumlegierung
US7875132B2 (en) * 2005-05-31 2011-01-25 United Technologies Corporation High temperature aluminum alloys
US7584778B2 (en) * 2005-09-21 2009-09-08 United Technologies Corporation Method of producing a castable high temperature aluminum alloy by controlled solidification
WO2009062866A1 (en) 2007-11-15 2009-05-22 Aleris Aluminum Koblenz Gmbh Al-mg-zn wrought alloy product and method of its manufacture
US7875131B2 (en) * 2008-04-18 2011-01-25 United Technologies Corporation L12 strengthened amorphous aluminum alloys
US8409373B2 (en) * 2008-04-18 2013-04-02 United Technologies Corporation L12 aluminum alloys with bimodal and trimodal distribution
US20090263273A1 (en) * 2008-04-18 2009-10-22 United Technologies Corporation High strength L12 aluminum alloys
US7811395B2 (en) * 2008-04-18 2010-10-12 United Technologies Corporation High strength L12 aluminum alloys
US7879162B2 (en) * 2008-04-18 2011-02-01 United Technologies Corporation High strength aluminum alloys with L12 precipitates
US7875133B2 (en) 2008-04-18 2011-01-25 United Technologies Corporation Heat treatable L12 aluminum alloys
US8002912B2 (en) * 2008-04-18 2011-08-23 United Technologies Corporation High strength L12 aluminum alloys
US20090260724A1 (en) * 2008-04-18 2009-10-22 United Technologies Corporation Heat treatable L12 aluminum alloys
US8017072B2 (en) * 2008-04-18 2011-09-13 United Technologies Corporation Dispersion strengthened L12 aluminum alloys
US7871477B2 (en) * 2008-04-18 2011-01-18 United Technologies Corporation High strength L12 aluminum alloys
US8778099B2 (en) * 2008-12-09 2014-07-15 United Technologies Corporation Conversion process for heat treatable L12 aluminum alloys
US20100143177A1 (en) * 2008-12-09 2010-06-10 United Technologies Corporation Method for forming high strength aluminum alloys containing L12 intermetallic dispersoids
US8778098B2 (en) * 2008-12-09 2014-07-15 United Technologies Corporation Method for producing high strength aluminum alloy powder containing L12 intermetallic dispersoids
US20100226817A1 (en) * 2009-03-05 2010-09-09 United Technologies Corporation High strength l12 aluminum alloys produced by cryomilling
RU2393073C1 (ru) * 2009-03-17 2010-06-27 Федеральное Государственное Унитарное Предприятие "Центральный Научно-Исследовательский Институт Конструкционных Материалов "Прометей" (Фгуп "Цнии Км "Прометей") Состав сварочной проволоки на основе алюминия
US20100252148A1 (en) * 2009-04-07 2010-10-07 United Technologies Corporation Heat treatable l12 aluminum alloys
US20100254850A1 (en) * 2009-04-07 2010-10-07 United Technologies Corporation Ceracon forging of l12 aluminum alloys
US9611522B2 (en) * 2009-05-06 2017-04-04 United Technologies Corporation Spray deposition of L12 aluminum alloys
US9127334B2 (en) * 2009-05-07 2015-09-08 United Technologies Corporation Direct forging and rolling of L12 aluminum alloys for armor applications
DE102010020268A1 (de) 2009-05-12 2010-11-18 Aleris Aluminum Duffel Bvba Aluminium-Magnesium-Legierungsprodukt für geformte Autmobilteile
US20110044844A1 (en) * 2009-08-19 2011-02-24 United Technologies Corporation Hot compaction and extrusion of l12 aluminum alloys
US8728389B2 (en) * 2009-09-01 2014-05-20 United Technologies Corporation Fabrication of L12 aluminum alloy tanks and other vessels by roll forming, spin forming, and friction stir welding
US8409496B2 (en) * 2009-09-14 2013-04-02 United Technologies Corporation Superplastic forming high strength L12 aluminum alloys
US20110064599A1 (en) * 2009-09-15 2011-03-17 United Technologies Corporation Direct extrusion of shapes with l12 aluminum alloys
US9194027B2 (en) * 2009-10-14 2015-11-24 United Technologies Corporation Method of forming high strength aluminum alloy parts containing L12 intermetallic dispersoids by ring rolling
US8409497B2 (en) * 2009-10-16 2013-04-02 United Technologies Corporation Hot and cold rolling high strength L12 aluminum alloys
US20110091346A1 (en) * 2009-10-16 2011-04-21 United Technologies Corporation Forging deformation of L12 aluminum alloys
US20110091345A1 (en) * 2009-10-16 2011-04-21 United Technologies Corporation Method for fabrication of tubes using rolling and extrusion
CN102699564B (zh) * 2012-04-27 2015-04-22 浙江宇光铝材有限公司 铝合金自动焊丝
AU2016218269B2 (en) 2015-02-11 2019-10-03 Scandium International Mining Corporation Scandium-containing master alloys and methods for making the same
CN105499832A (zh) * 2016-01-28 2016-04-20 东北大学 一种铝镁铈焊丝及其制备方法
CN106624428A (zh) * 2016-12-16 2017-05-10 吴中区穹窿山天仲高分子材料技术研究所 一种环保型焊接合金材料及其制备方法
RU2663446C1 (ru) * 2017-12-06 2018-08-06 Общество с ограниченной ответственностью "Опытный завод "Авиаль" (ООО "ОЗА") Сплав на основе алюминия для сварочной проволоки
CN110029252B (zh) * 2019-04-12 2021-08-24 范卫忠 一种5g手机中板用高强高韧抗氧化铝镁合金材料及其制备方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5055257A (en) * 1986-03-20 1991-10-08 Aluminum Company Of America Superplastic aluminum products and alloys
US5624632A (en) * 1995-01-31 1997-04-29 Aluminum Company Of America Aluminum magnesium alloy product containing dispersoids

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SU439535A1 (ru) * 1972-07-04 1974-08-15 Предприятие П/Я Р-6209 Сплав на основе алюмини
SU480513A1 (ru) * 1973-04-28 1975-08-15 Предприятие П/Я М-5539 Сплав дл сварочной проволоки на основе алюмини
JPS59159961A (ja) * 1983-02-28 1984-09-10 Mitsubishi Alum Co Ltd 超塑性Ａｌ合金
JPS63179040A (ja) 1987-01-20 1988-07-23 Showa Alum Corp 表面平滑性に優れたシリンダ用アルミニウム合金
JPS63248593A (ja) * 1987-03-31 1988-10-14 Showa Alum Corp アルミニウム合金溶加材
JP3286982B2 (ja) * 1990-04-25 2002-05-27 菱化マックス株式会社 金型素材
JPH07145441A (ja) * 1993-01-27 1995-06-06 Toyota Motor Corp 超塑性アルミニウム合金およびその製造方法
FR2717827B1 (fr) 1994-03-28 1996-04-26 Jean Pierre Collin Alliage d'aluminium à hautes teneurs en Scandium et procédé de fabrication de cet alliage.
RU2082809C1 (ru) * 1995-07-25 1997-06-27 Акционерное общество открытого типа "Всероссийский институт легких сплавов" Деформируемый термически неупрочняемый сплав на основе алюминия
KR100469929B1 (ko) * 1997-02-10 2005-02-02 알코아 인코포레이티드 알루미늄 합금 및 그로부터 제조된 항공기 부품
PT918095E (pt) * 1997-11-20 2003-06-30 Alcan Tech & Man Ag Processo para a obtencao de um componente estrutural a partir de uma liga de aluminio de moldagem sob pressao

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5055257A (en) * 1986-03-20 1991-10-08 Aluminum Company Of America Superplastic aluminum products and alloys
US5624632A (en) * 1995-01-31 1997-04-29 Aluminum Company Of America Aluminum magnesium alloy product containing dispersoids

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN100445019C (zh) * 2006-09-14 2008-12-24 中国航空工业第一集团公司北京航空材料研究院 Al-Mg-Sc系焊丝
CN107363122A (zh) * 2017-06-14 2017-11-21 飞龙精工科技(苏州)有限公司 铝镁合金丝的制备工艺
CN107363122B (zh) * 2017-06-14 2018-12-14 飞龙精工科技(苏州)有限公司 铝镁合金丝的制备工艺
CN111378878A (zh) * 2018-12-29 2020-07-07 嘉丰工业科技（惠州）有限公司 一种高延展性非热处理压铸铝合金及其制备方法
CN111378878B (zh) * 2018-12-29 2021-10-26 嘉丰工业科技（惠州）有限公司 一种高延展性非热处理压铸铝合金及其制备方法

Also Published As

Publication number Publication date
DE19838015C2 (de) 2002-10-17
CA2306726A1 (en) 2000-03-02
CN1274391A (zh) 2000-11-22
WO2000011231A1 (de) 2000-03-02
JP2002523621A (ja) 2002-07-30
US6315948B1 (en) 2001-11-13
CA2306726C (en) 2008-07-29
ES2173759T3 (es) 2002-10-16
DE59901293D1 (de) 2002-05-29
RU2226567C2 (ru) 2004-04-10
EP1025270B1 (de) 2002-04-24
EP1025270A1 (de) 2000-08-09
DE19838015A1 (de) 2000-03-02
ATE216735T1 (de) 2002-05-15

Similar Documents

Publication Publication Date Title
CN1107120C (zh) 特别适用于汽车应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金
CN1103828C (zh) 特别适用于交通运输的、可焊、耐腐蚀铝－镁合金
CN1103827C (zh) 特别适用于航空应用的、新的可焊、耐腐蚀、高镁含量的铝－镁合金
JP4554088B2 (ja) 耐剥離性アルミニウム−マグネシウム合金
RU2000112644A (ru) Обладающие свариваемостью, коррозионностойкие алюминиево-магниевые сплавы, прежде всего для применения в транспортном машиностроении
US7108042B2 (en) Aluminum diecasting alloy
CA2663605C (en) Magnesium gadolinium alloys
RU2000112645A (ru) Новый обладающий свариваемостью, коррозионностойкий алюминиево-магниевый сплав с высоким содержанием магния, прежде всего для применения в автомобилестроении
RU2000112642A (ru) Обладающий свариваемостью, коррозионностойкий алюминиево-магниевый сплав с высоким содержанием магния, прежде всего для применения в авиастроении
EP3437789B1 (en) Aluminum alloy cladding material and production method for aluminum alloy cladding material
EP3202933A1 (en) Aluminum alloy brazing sheet
JPS61238937A (ja) 押出性および応力腐食割れ性に優れた溶接構造材用高強度アルミニウム合金
US20080056931A1 (en) Aluminum Alloy And Brazing Sheet Manufactured Therefrom
JPH11310842A (ja) シーム溶接性に優れた燃料タンク用アルミニウム合金板およびその製造方法
JP3396523B2 (ja) ろう付け後強度およびろう付け性に優れたＡｌ合金フィン材
JP7690701B1 (ja) アルミニウム合金展伸材
JP7690700B1 (ja) アルミニウム合金展伸材
JP2002012935A (ja) 犠牲防食アルミニウム合金板及びその複合材
JP2004068122A (ja) 熱交換器用アルミニウム合金クラッド材及びその製造方法、並びにチューブ
JP5268824B2 (ja) アルミニウム合金材およびアルミニウム合金ブレージングシート
JP3396521B2 (ja) ろう付け後強度およびろう付け性に優れたＡｌ合金フィン材
JP2001026831A (ja) 押出チューブ
KR20130104740A (ko) 충격 흡수성 및 열적 안정성이 우수한 고강도 알루미늄 합금
JPS6289838A (ja) 圧延加工性に優れた高強度アルミニウム合金
JPH0432534A (ja) 耐応力腐食割れ性に優れた溶接用アルミニウム合金

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
ASS Succession or assignment of patent right

Owner name: AIRBUS GMBH (DE)

Free format text: FORMER OWNER: DAIMLER-KLINSLER AG

Effective date: 20130927

C41 Transfer of patent application or patent right or utility model
TR01 Transfer of patent right

Effective date of registration: 20130927

Address after: hamburg

Patentee after: Airbus GMBH (DE)

Address before: Stuttgart, Germany

Patentee before: Daimler-Benz AG

CX01 Expiry of patent term

Granted publication date: 20030430

CX01 Expiry of patent term