CN110438546A - 一种在钛合金表面微弧氧化制备分级结构多孔涂层的电解液 - Google Patents

一种在钛合金表面微弧氧化制备分级结构多孔涂层的电解液 Download PDF

Info

Publication number
CN110438546A
CN110438546A CN201910775468.0A CN201910775468A CN110438546A CN 110438546 A CN110438546 A CN 110438546A CN 201910775468 A CN201910775468 A CN 201910775468A CN 110438546 A CN110438546 A CN 110438546A
Authority
CN
China
Prior art keywords
tetraborate
coating
titanium
arc oxidation
electrolyte
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910775468.0A
Other languages
English (en)
Other versions
CN110438546B (zh
Inventor
王伟强
齐民
李亚达
关世伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian University of Technology
Original Assignee
Dalian University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian University of Technology filed Critical Dalian University of Technology
Priority to CN201910775468.0A priority Critical patent/CN110438546B/zh
Publication of CN110438546A publication Critical patent/CN110438546A/zh
Priority to US16/962,761 priority patent/US20210156046A1/en
Priority to PCT/CN2020/077111 priority patent/WO2021031548A1/zh
Application granted granted Critical
Publication of CN110438546B publication Critical patent/CN110438546B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种在钛合金表面微弧氧化制备分级结构多孔涂层的电解液，属于材料表面改性技术领域。基于本发明的电解液，采用微弧氧化法，能够在钛合金表面制备具有高孔隙度分级结构的二氧化钛涂层，该电解液由0.07–0.15mol/L四硼酸盐和0.10–0.40mol/L强碱组成。四硼酸盐包含四硼酸锂、四硼酸钠和四硼酸钾中的一种。强碱选自氢氧化钾和氢氧化钠中的一种。该电解液制备的涂层具有相互连通的微米沟槽或微米孔洞和随机分布的纳米孔构成的分级结构、内部孔洞和外层孔槽构成的分层结构、高孔隙度和超亲水性，可用于骨科材料和牙种植体等领域的表面改性。

Description

一种在钛合金表面微弧氧化制备分级结构多孔涂层的电解液
技术领域
本发明属于材料表面改性技术领域，涉及一种在钛合金表面制备二氧化钛(TiO2)涂层的微弧氧化电解液。
背景技术
钛和钛合金广泛用于人体硬组织植入或替代材料，但是钛和钛合金表面缺乏生物活性，通过表面改性技术构建表面微结构是提高钛和钛合金表面生物活性的主要途径。
微弧氧化(又称阳极火花氧化或等离子体电解氧化)是一种适用于钛和钛合金的表面改性技术，通过微弧氧化处理能够在钛和钛合金表面原位生长出氧化物涂层。
目前，使用微弧氧化在钛和钛合金表面制备的多孔氧化物涂层多为火山口状或分立的多孔状结构。这种表面结构孔洞之间相互独立，缺乏连通性，对孔隙度的提高和亲水性的改善较为有限。同时，这些涂层通常结构尺度较为单一，不具有分级结构特征。相互连通的孔洞或沟槽和不同尺度复合的分级结构以及高亲水性均有利于提高材料表面的生物活性。为提高微结构的连通性和亲水性，同时构建分级结构，专利CN201210096780.5使用四硼酸盐作为电解液，在钛表面制备了一种超亲水性褶皱孔槽状TiO2涂层。该涂层具有分级结构和超亲水性，能够显著改善钛表面的生物活性。
Ti–6Al–4V(牌号TC4)和Ti–6Al–7Nb(牌号TC20)是常用的钛合金材料。仅使用四硼酸盐电解液不足以在其表面制备出均匀的孔槽状TiO2涂层。本发明在此基础上，通过调整电解液成分，在Ti–6Al–4V和Ti–6Al–7Nb表面制备出均匀的孔槽状TiO2涂层。
发明内容
本发明针对目前钛合金微弧氧化涂层在生物活性上的局限性，提出一种二氧化钛微弧氧化涂层电解液。该电解液通过在四硼酸盐电解液中添加强碱，能够在钛合金(如Ti–6Al–4V、Ti–6Al–7Nb)表面通过微弧氧化制备出具有分级结构和高孔隙度的多孔二氧化钛涂层，使其表面获得高亲水性，提高其表面的生物活性。
为了达到上述目的，本发明的技术方案为：
一种在钛合金表面微弧氧化制备多孔涂层的电解液，基于本发明的电解液，采用微弧氧化法，能够在钛合金表面制备出二氧化钛涂层，包含溶剂和溶质两部分；其中，所述的溶剂为去离子水；所述的溶质为四硼酸盐和强碱，其中四硼酸盐摩尔浓度为0.07–0.15mol/L，强碱摩尔浓度为0.10–0.40mol/L。
所述四硼酸盐选自四硼酸锂(Li2B4O7)、四硼酸钠(Na2B4O7)、四硼酸钾(K2B4O7)中的一种，所述强碱选自氢氧化钾(KOH)和氢氧化钠(NaOH)中的一种。
基于上述微弧氧化电解液，采用微弧氧化法，可在钛合金表面制备出二氧化钛涂层，该涂层具有均匀分布并相互连通的微米孔或沟槽，同时具有随机分布的纳米孔，是一种典型的分级结构表面。并且该涂层表面结构具有一定内部孔洞，形成一种分层结构。上述表面结构使该涂层具有高孔隙度和超亲水性。
本发明所述的微弧氧化电解液，可采用本领域常规方法进行制备，将四硼酸盐和强碱按配比加入去离子水中，搅拌均匀并使其充分溶解。
本发明的有益效果是：
(1)本发明的微弧氧化电解液能够在钛合金表面制备出二氧化钛涂层。
(2)本发明的微弧氧化电解液在钛合金表面制备的涂层具有高孔隙度和超亲水性，具有分级结构的特征——均匀分布的微米孔或沟槽和随机分布的纳米孔，其表面孔洞和沟槽相互连通，并具有一定的内部孔洞和分层结构。
附图说明
图1为实施例1所制备涂层的扫描电子显微镜表面形貌(3000X)；
图2为实施例1所制备涂层的扫描电子显微镜表面形貌(5000X)；
图3为实施例1所制备涂层表面的水接触角图像；
图4为实施例2所制备涂层的扫描电子显微镜表面形貌(5000X)；
图5为实施例3所制备涂层的扫描电子显微镜表面形貌(5000X)。
具体实施方式
下面结合具体实施例对本发明进行进一步的说明，本发明的具体实施例及其说明仅用于解释本发明，并不对本发明的范围进行限定。
将抛光后的Ti–6Al–4V或Ti–6Al–7Nb钛合金用于微弧氧化，微弧氧化参数如下：
电源：微弧氧化电源
阳极：抛光钛合金片(长15mm，宽15mm，厚度2mm)
阴极：不锈钢电解槽
微弧氧化控制方式：恒定电压或恒定电流
微弧氧化脉冲方式：单向脉冲
微弧氧化频率：600Hz
微弧氧化占空比：9％
实施例1
抛光的Ti–6Al–4V作为阳极。按摩尔浓度称量各组分并混合搅拌配置成电解液。溶剂为：去离子水；溶质为：四硼酸钠(Na2B4O7)0.10mol/L，氢氧化钾(KOH)0.25mol/L。电源控制方式为恒定电压，设置值为300V，处理时长为10min。扫描电子显微镜图像显示该涂层具有由微米沟槽与纳米孔构成的分级结构和内部孔洞与外层孔槽构成的分层结构；X射线衍射分析显示制备的微弧氧化涂层主要由金红石相二氧化钛和锐钛矿相二氧化钛组成；能谱显示制备的微弧氧化涂层铝元素的原子百分比为0.06％，钒元素的原子百分比为0.3％；接触角测试显示制备的微弧氧化涂层水接触角为10.2°，表明该涂层具有超亲水性。
实施例2
抛光的Ti–6Al–4V作为阳极。按摩尔浓度称量各组分并混合搅拌配置成电解液。溶剂为：去离子水；溶质为：四硼酸锂(Li2B4O7)0.07mol/L，氢氧化钠(NaOH)0.10mol/L。电源控制方式为恒定电流，设置值为4A，处理时长为30min。扫描电子显微镜图像显示该涂层具有由微米沟槽与纳米孔构成的分级结构和内部孔洞与外层孔槽构成的分层结构；X射线衍射分析显示制备的微弧氧化涂层主要由金红石相二氧化钛和锐钛矿相二氧化钛组成；能谱显示制备的微弧氧化涂层铝元素的原子百分比为0.64％，钒元素的原子百分比为0.52％；接触角测试显示制备的微弧氧化涂层水接触角为10.5°，表明该涂层具有超亲水性。
实施例3
抛光的Ti–6Al–7Nb作为阳极。按摩尔浓度称量各组分并混合搅拌配置成电解液。溶剂为：去离子水；溶质为：四硼酸钾(K2B4O7)0.15mol/L，氢氧化钾(KOH)0.40mol/L。电源控制方式为恒定电流，设置值为5A，处理时长为10min。扫描电子显微镜图像显示该涂层具有由微米沟槽与纳米孔构成的分级结构和内部孔洞与外层孔槽构成的分层结构；X射线衍射分析显示制备的微弧氧化涂层主要由金红石相二氧化钛和锐钛矿相二氧化钛组成；能谱显示制备的微弧氧化涂层铝元素的原子百分比为0.05％，铌元素的原子百分比为1％；接触角测试显示制备的微弧氧化涂层水接触角为9.3°，表明该涂层具有超亲水性。
通过以上实施例可以说明本发明能够通过在四硼酸盐溶液中添加强碱在Ti–6Al–4V或Ti–6Al–7Nb钛合金表面制备出二氧化钛微弧氧化涂层，本发明在钛合金表面制备出的二氧化钛涂层具有由相互连通的微米沟槽或微米孔洞和随机分布的纳米孔构成的分级结构，同时具有内部孔洞与外层孔槽构成的分层结构。该涂层表面孔隙度较高，表面结构分布均匀，微孔洞之间具有一定连通性，并具有超亲水性特征。
与以往研究相比，使用本发明制备的二氧化钛涂层具有分级结构和分层结构并且涂层表面结构均匀平整，能够有效提高微弧氧化涂层孔隙度、孔洞连通性和亲水性，从而提高钛合金表面的生物活性。
以上所述实施例仅表达本发明的实施方式，但并不能因此而理解为对本发明专利的范围的限制，应当指出，对于本领域的技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些均属于本发明的保护范围。

Claims (3)

1.一种在钛合金表面微弧氧化制备多孔涂层的电解液，其特征在于，基于该电解液，采用微弧氧化法能够在钛合金表面制备具有高孔隙度、超亲水性且具有分级结构的二氧化钛涂层，该涂层具有均匀分布并相互连通的微米孔或沟槽；所述的电解液包含溶剂和溶质两部分；其中，所述的溶剂为去离子水；所述的溶质为四硼酸盐和强碱，其中四硼酸盐摩尔浓度为0.07–0.15mol/L，强碱摩尔浓度为0.10–0.40mol/L。
2.根据权利要求1所述的一种在钛合金表面微弧氧化制备多孔涂层的电解液，其特征在于，所述四硼酸盐选自四硼酸锂Li2B4O7、四硼酸钠Na2B4O7、四硼酸钾K2B4O7中的一种。
3.根据权利要求2所述的一种在钛合金表面微弧氧化制备多孔涂层的电解液，其特征在于，所述强碱选自氢氧化钾KOH和氢氧化钠NaOH中的一种。
CN201910775468.0A 2019-08-21 2019-08-21 一种在钛合金表面微弧氧化制备分级结构多孔涂层的电解液 Active CN110438546B (zh)