CN110282962A - 一种玉石装饰的陶瓷制品及其制备工艺 - Google Patents

一种玉石装饰的陶瓷制品及其制备工艺 Download PDF

Info

Publication number
CN110282962A
CN110282962A CN201910687572.4A CN201910687572A CN110282962A CN 110282962 A CN110282962 A CN 110282962A CN 201910687572 A CN201910687572 A CN 201910687572A CN 110282962 A CN110282962 A CN 110282962A
Authority
CN
China
Prior art keywords
parts
ceramic
jade
raw material
jade decorated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910687572.4A
Other languages
English (en)
Inventor
孙建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Dehua County Sannuo Ceramics Co Ltd
Original Assignee
Fujian Dehua County Sannuo Ceramics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Dehua County Sannuo Ceramics Co Ltd filed Critical Fujian Dehua County Sannuo Ceramics Co Ltd
Priority to CN201910687572.4A priority Critical patent/CN110282962A/zh
Publication of CN110282962A publication Critical patent/CN110282962A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种玉石装饰的陶瓷制品及其制备工艺，包括陶瓷胚体，所述陶瓷胚体的表面设置有釉层，所述釉层的表面设置有玉石装饰件，包括以下步骤：步骤1：按照重量份数硼砂80份、长石80份、石英55份、高岭土35份、硅30份、铅丹15份取各原料；步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨。本发明在制备时不需要对陶瓷坯体表面进行破坏，在陶瓷烧制时将玉石装饰件与陶瓷坯体连接，其制作工艺简单、成本低、成品率高，且通过玉石装饰件对陶瓷坯体进行装饰，将玉石装饰件的原料引入釉料中，使玉石装饰件与陶瓷坯体成为一个整体，使的玉石装饰件连接紧固性更强，美观性好，有利于人们的使用。

Description

一种玉石装饰的陶瓷制品及其制备工艺
技术领域
本发明涉及陶瓷制品技术领域，具体为一种玉石装饰的陶瓷制品及其制备工艺。
背景技术
用陶土烧制的器皿叫陶器，用瓷土烧制的器皿叫瓷器，陶瓷则是陶器，炻器和瓷器的总称，古人称陶瓷为瓯，凡是用陶土和瓷土这两种不同性质的粘土为原料，经过配料、成型、干燥、焙烧等工艺流程制成的器物都可以叫陶瓷，陶瓷是以天然粘土以及各种天然矿物为主要原料经过粉碎混炼、成型和煅烧制得的材料的各种制品，人们把用陶土制作成的在专门的窑炉中高温烧制的物品称作陶瓷。
陶瓷的传统概念是指所有以粘土等无机非金属矿物为原料的人工工业产品，它包括由粘土或含有粘土的混合物经混炼，成形，煅烧而制成的各种制品，由最粗糙的土器到最精细的精陶和瓷器都属于它的范围，陶与瓷的区别在于原料土的不同和温度的不同，在制陶的温度基础上再添火加温，陶就变成了瓷，陶器的烧制温度在800-1000度，瓷器则是用高岭土在1300-1400度的温度下烧制而成，陶瓷制品的品种繁多，它们之间的化学成分，矿物组成，物理性质，以及制造方法，常常互相接近交错，无明显的界限，而在应用上却有很大的区别。
陶瓷的主要原料是取之于自然界的硅酸盐矿物，因此与玻璃、水泥、搪瓷、耐火材料等工业，同属于“硅酸盐工业”的范畴，陶瓷因其质地坚硬、细密、耐高温、釉色丰富等特点，广泛应用于食器、装饰等领域，随着人们生活水平的不断提高，审美需求也在不断的变化，传统的技术对陶瓷装饰主要是通过釉料效果的改变，这种装饰方式生产的陶瓷制品美观性差，缺乏创新，难以适应消费者求新求变的需求，不利于人们的使用。
发明内容
本发明的目的在于提供一种玉石装饰的陶瓷制品及其制备工艺，具备玉石装饰的陶瓷制品便于使用的优点，解决了陶瓷制品使用不方便的问题。
为实现上述目的，本发明提供如下技术方案：一种玉石装饰的陶瓷制品，包括陶瓷胚体，所述陶瓷胚体的表面设置有釉层，所述釉层的表面设置有玉石装饰件。
优选的，所述陶瓷胚体由以下重量份数的原料组成：硼砂80-100份、长石80-100份、石英50-65份、高岭土30-50份、硅20-30份、铅丹15-30份。
优选的，所述釉层由以下重量份数的原料组成：着色剂10-20份、基础釉料60-80份、玉石原料10-20份。
优选的，所述玉石装饰件为水晶、玛瑙、琥珀和绿松石制成，所述玉石装饰件与玉石原料为同一物质。
一种玉石装饰的陶瓷制品制备工艺，包括以下步骤：
步骤1：按照重量份数硼砂80份、长石80份、石英55份、高岭土35份、硅30份、铅丹15份取各原料；
步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；
步骤3：取高岭土40份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；
步骤4：取基础釉料60份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂12份、玉石原料15份进行混合搅拌，得到釉层；
步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
优选的，所述在步骤2中研磨机的转速为800r/min，所述研磨机的研磨时间为3-10min，所述研磨后的混合物粒径为300目。
优选的，所述在步骤3中陶瓷胚体的晾干时间为24-36h。
优选的，所述在步骤4中研磨机的转速为1400r/min，所述研磨后的粒径为140目，所述研磨时间为5-10min。
优选的，所述在步骤5中窖炉的烧制时间为8-12h，所述窖炉的烧制温度为800-1200℃。
与现有技术相比，本发明的有益效果如下：本发明在制备时不需要对陶瓷坯体表面进行破坏，在陶瓷烧制时将玉石装饰件与陶瓷坯体连接，其制作工艺简单、成本低、成品率高，且通过玉石装饰件对陶瓷坯体进行装饰，将玉石装饰件的原料引入釉料中，使玉石装饰件与陶瓷坯体成为一个整体，使的玉石装饰件连接紧固性更强，美观性好，有利于人们的使用。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
一种玉石装饰的陶瓷制品，包括陶瓷胚体，陶瓷胚体的表面设置有釉层，釉层的表面设置有玉石装饰件。
一种玉石装饰的陶瓷制品制备工艺，包括以下步骤：
步骤1：按照重量份数硼砂80份、长石80份、石英55份、高岭土35份、硅30份、铅丹15份取各原料；
步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；
步骤3：取高岭土40份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；
步骤4：取基础釉料60份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂12份、玉石原料15份进行混合搅拌，得到釉层；
步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
实施例1
一种玉石装饰的陶瓷制品，包括陶瓷胚体，陶瓷胚体由以下重量份数的原料组成：硼砂80份、长石80份、石英55份、高岭土35份、硅30份、铅丹15份，陶瓷胚体的表面设置有釉层，釉层由以下重量份数的原料组成：着色剂12份、基础釉料60份、玉石原料15份，釉层的表面设置有玉石装饰件，玉石装饰件为水晶、玛瑙、琥珀和绿松石制成，玉石装饰件与玉石原料为同一物质。
一种玉石装饰的陶瓷制品制备工艺，包括以下步骤：步骤1：按照重量份数硼砂80份、长石80份、石英55份、高岭土35份、硅30份、铅丹15份取各原料；步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；步骤3：取高岭土40份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；步骤4：取基础釉料60份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂12份、玉石原料15份进行混合搅拌，得到釉层；步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
实施例2
在实施例1中，在加入以下步骤：
在步骤2中研磨机的转速为800r/min，研磨机的研磨时间为3-10min，研磨后的混合物粒径为300目。
一种玉石装饰的陶瓷制品，包括陶瓷胚体，陶瓷胚体由以下重量份数的原料组成：硼砂88份、长石85份、石英60份、高岭土35份、硅25份、铅丹17份，陶瓷胚体的表面设置有釉层，釉层由以下重量份数的原料组成：着色剂10份、基础釉料66份、玉石原料20份，釉层的表面设置有玉石装饰件，玉石装饰件为水晶、玛瑙、琥珀和绿松石制成，玉石装饰件与玉石原料为同一物质。
一种玉石装饰的陶瓷制品制备工艺，包括以下步骤：步骤1：按照重量份数硼砂88份、长石88份、石英60份、高岭土35份、硅25份、铅丹17份取各原料；步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；步骤3：取高岭土35份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；步骤4：取基础釉料66份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂10份、玉石原料20份进行混合搅拌，得到釉层；步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
实施例3
在实施例2中，在加入以下步骤：
在步骤3中陶瓷胚体的晾干时间为24-36h。
一种玉石装饰的陶瓷制品，包括陶瓷胚体，陶瓷胚体由以下重量份数的原料组成：硼砂100份、长石100份、石英50份、高岭土35份、硅30份、铅丹25份，陶瓷胚体的表面设置有釉层，釉层由以下重量份数的原料组成：着色剂15份、基础釉料80份、玉石原料10份，釉层的表面设置有玉石装饰件，玉石装饰件为水晶、玛瑙、琥珀和绿松石制成，玉石装饰件与玉石原料为同一物质。
一种玉石装饰的陶瓷制品制备工艺，包括以下步骤：步骤1：按照重量份数硼砂100份、长石100份、石英50份、高岭土35份、硅30份、铅丹25份取各原料；步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；步骤3：取高岭土35份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；步骤4：取基础釉料80份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂15份、玉石原料10份进行混合搅拌，得到釉层；步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
实施例4
在实施例3中，在加入以下步骤：
在步骤4中研磨机的转速为1400r/min，研磨后的粒径为140目，研磨时间为5-10min。
一种玉石装饰的陶瓷制品，包括陶瓷胚体，陶瓷胚体由以下重量份数的原料组成：硼砂90份、长石90份、石英65份、高岭土30份、硅20份、铅丹30份，陶瓷胚体的表面设置有釉层，釉层由以下重量份数的原料组成：着色剂10份、基础釉料68份、玉石原料17份，釉层的表面设置有玉石装饰件，玉石装饰件为水晶、玛瑙、琥珀和绿松石制成，玉石装饰件与玉石原料为同一物质。
一种玉石装饰的陶瓷制品制备工艺，包括以下步骤：步骤1：按照重量份数硼砂90份、长石90份、石英65份、高岭土30份、硅20份、铅丹30份取各原料；步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；步骤3：取高岭30份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；步骤4：取基础釉料68份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂10份、玉石原料17份进行混合搅拌，得到釉层；步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
实施例5
在实施例4中，在加入以下步骤：
在步骤5中窖炉的烧制时间为8-12h，窖炉的烧制温度为800-1200℃。
一种玉石装饰的陶瓷制品，包括陶瓷胚体，陶瓷胚体由以下重量份数的原料组成：硼砂95份、长石82份、石英57份、高岭土45份、硅22份、铅丹19份，陶瓷胚体的表面设置有釉层，釉层由以下重量份数的原料组成：着色剂18份、基础釉料72份、玉石原料10份，釉层的表面设置有玉石装饰件，玉石装饰件为水晶、玛瑙、琥珀和绿松石制成，玉石装饰件与玉石原料为同一物质。
一种玉石装饰的陶瓷制品制备工艺，包括以下步骤：步骤1：按照重量份数硼砂95份、长石82份、石英57份、高岭土45份、硅22份、铅丹19份取各原料；步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；步骤3：取高岭土45份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；步骤4：取基础釉料72份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂18份、玉石原料10份进行混合搅拌，得到釉层；步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
综上所述：该玉石装饰的陶瓷制品及其制备工艺，解决了陶瓷制品使用不方便的问题。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (9)

1.一种玉石装饰的陶瓷制品，包括陶瓷胚体，其特征在于：所述陶瓷胚体的表面设置有釉层，所述釉层的表面设置有玉石装饰件。
2.根据权利要求1所述的一种玉石装饰的陶瓷制品，其特征在于：所述陶瓷胚体由以下重量份数的原料组成：硼砂80-100份、长石80-100份、石英50-65份、高岭土30-50份、硅20-30份、铅丹15-30份。
3.根据权利要求1所述的一种玉石装饰的陶瓷制品，其特征在于：所述釉层由以下重量份数的原料组成：着色剂10-20份、基础釉料60-80份、玉石原料10-20份。
4.根据权利要求1和3所述的一种玉石装饰的陶瓷制品，其特征在于：所述玉石装饰件为水晶、玛瑙、琥珀和绿松石制成，所述玉石装饰件与玉石原料为同一物质。
5.一种玉石装饰的陶瓷制品制备工艺，其特征在于：包括以下步骤：
步骤1：按照重量份数硼砂80份、长石80份、石英55份、高岭土35份、硅30份、铅丹15份取各原料；
步骤2：将硼砂、长石、石英和硅放入研磨机内进行研磨，然后在混合料内加入铅丹，得到混合物；
步骤3：取高岭土40份，将步骤2中得到混合物渗入高岭土内，以高岭土为原料制胚，得到粗胚，然后将得到的粗胚放入转盘中，通过手工制得陶瓷胚体，最后将陶瓷胚体晾干；
步骤4：取基础釉料60份，通过研磨机对基础釉料进行研磨，然后加水，加入着色剂12份、玉石原料15份进行混合搅拌，得到釉层；
步骤5：然后将混合后的玉石装饰件放入陶瓷胚体上预先开好的槽孔内，将得到的釉层通过毛刷均匀的涂抹在陶瓷胚体的表面，然后将涂抹釉层的陶瓷胚体放入窖炉中进行烧制，得到玉石装饰的陶瓷制品。
6.根据权利要求5所述的一种玉石装饰的陶瓷制品制备工艺，其特征在于：所述在步骤2中研磨机的转速为800r/min，所述研磨机的研磨时间为3-10min，所述研磨后的混合物粒径为300目。
7.根据权利要求5所述的一种玉石装饰的陶瓷制品制备工艺，其特征在于：所述在步骤3中陶瓷胚体的晾干时间为24-36h。
8.根据权利要求5所述的一种玉石装饰的陶瓷制品制备工艺，其特征在于：所述在步骤4中研磨机的转速为1400r/min，所述研磨后的粒径为140目，所述研磨时间为5-10min。
9.根据权利要求5所述的一种玉石装饰的陶瓷制品制备工艺，其特征在于：所述在步骤5中窖炉的烧制时间为8-12h，所述窖炉的烧制温度为800-1200℃。
CN201910687572.4A 2019-07-29 2019-07-29 一种玉石装饰的陶瓷制品及其制备工艺 Pending CN110282962A (zh)