CN110181064A - WC-Co预烧回收料的压模方法 - Google Patents
WC-Co预烧回收料的压模方法 Download PDFInfo
- Publication number
- CN110181064A CN110181064A CN201910435924.7A CN201910435924A CN110181064A CN 110181064 A CN110181064 A CN 110181064A CN 201910435924 A CN201910435924 A CN 201910435924A CN 110181064 A CN110181064 A CN 110181064A
- Authority
- CN
- China
- Prior art keywords
- burning
- reclaimed materials
- wet
- parts
- milling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (8)