CN110078120B - 一种基于超临界分散焙烧的氧化钇稳定氧化锆粉体的制备方法 - Google Patents
一种基于超临界分散焙烧的氧化钇稳定氧化锆粉体的制备方法 Download PDFInfo
- Publication number
- CN110078120B CN110078120B CN201910394719.0A CN201910394719A CN110078120B CN 110078120 B CN110078120 B CN 110078120B CN 201910394719 A CN201910394719 A CN 201910394719A CN 110078120 B CN110078120 B CN 110078120B
- Authority
- CN
- China
- Prior art keywords
- yttria
- stabilized zirconia
- precursor
- precursor material
- zirconia powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (6)