CN1097376A - 高弹性皮筋及其制备方法 - Google Patents

高弹性皮筋及其制备方法 Download PDF

Info

Publication number
CN1097376A
CN1097376A CN 94104469 CN94104469A CN1097376A CN 1097376 A CN1097376 A CN 1097376A CN 94104469 CN94104469 CN 94104469 CN 94104469 A CN94104469 A CN 94104469A CN 1097376 A CN1097376 A CN 1097376A
Authority
CN
China
Prior art keywords
rubber band
parts
agent
sections
section
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 94104469
Other languages
English (en)
Other versions
CN1047125C (zh
Inventor
万青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN94104469A priority Critical patent/CN1047125C/zh
Publication of CN1097376A publication Critical patent/CN1097376A/zh
Application granted granted Critical
Publication of CN1047125C publication Critical patent/CN1047125C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明属于用热塑弹性体为原料，经挤出成型而 制成的供娱乐用的皮筋。其特点为弹性高，强度大， 弹性伸长率可达500％，即拉长5倍后仍可恢复原 状，不易老化，寿命长，不易断裂伤人，安全性好，可制 成单色或多色，横截面形状也可多样，外表美观。

Description

本发明属于用热塑弹性体为原料，经挤出成型而制成的供娱乐用的皮筋。
“跳皮筋”一直是中国孩子们的传统游戏项目之一，它健身于娱乐之中，虽简单却百玩不厌，但这一简单的产品，却一直没有工业化生产，故孩子们只能用皮筋一根根套起来或用衣服上的松紧带来代用。这类皮筋不是连续生产，而且材料为橡胶，故弹性小，强度低，易老化发粘，使用寿命短，玩时也易断裂伤人。
本发明的目的就是针对现有技术的不足之处，采用热弹性体为原料，用工业化生产方式连续生产高弹性皮筋，供孩子们娱乐，以增强他们的体质。
本发明的技术解决方案为以热塑弹性体为原料，经挤出成型而制成，主要原料为SBS（苯乙烯-丁二烯-苯乙烯嵌段共聚物）、RUR弹性体、高聚合度PVC、乙烯类弹性体如EPDM等。其配方如下（以重量份计）：
一、用SBS生产皮筋
SBS  100份
环烷油  0～100份
抗氧剂  0～1份
光稳定剂  0～1份
着色剂  0～1份
珠光剂  0～3份
二、用高聚合度PVC生产皮筋
高聚合度PVC[P（平均聚合度）=2500～4000]  100份
DOP（邻苯二甲酸二辛酯）  80～150份
DBP（邻苯二甲酸二丁酯）  0～80份
透明稳定剂  2～6份
润滑剂  0.1～1份
着色剂  0～1份
珠光剂  0～5份
本发明的工艺流程为：原料称量→混合均匀→挤出机成型→
挤出机各段温度为：一段50℃～80℃，二段100℃～130℃，三段160℃～180℃，四段160℃～180℃，机头160℃～190℃，冷却水温20℃～50℃，挤出机螺杆转速10～120rpm，挤出线速度0.1m/min～30m/min。
本发明可制成单色或多色，用不同的机头尺寸和形状可制成任何尺寸利任何截面的形状。
本发明由于采用热塑弹性体原料制成，故产品弹性高，强度大，弹性伸长率可达500%，即拉长5倍后仍可恢复原状，长期使用不易老化，皮筋沿长度方向上每一点横截面积都相同，没有缺陷，强度、弹性均一，不易断裂伤人，安全性好，寿命长，产品可制成单色或多色，横截面形状多样，因而外表美观，符合孩子们心理。
本发明实施例：
一、用SBS生产皮筋
实施例1：SBS（国产）  100份
环烷油  50份
抗氧剂（B215）  0.1份
光稳定剂（GW-540）  0.1份
着色剂（萤光绿）  0.1份
珠光剂（云母钛）  1份
将上述物料混合均匀，入挤出机，用直径3mm～5mm的圆孔机头挤出成型，挤出机各段的温度为一段50℃，二段100℃，三段160℃，四段160℃，机头160℃，挤出机螺杆转速10rpm，挤出线速度0.1m/min，经水冷，水温20℃，收卷，检验，分切，包装，成品。
实施例2：SBS（进口）  100份
环烷油  100份
抗氧剂（B225）  0.8份
光稳定剂（GW-544）  0.8份
着色剂（酞普兰）  0.8份
珠光剂（云母钛）  3份
工艺步骤同例1，挤出机各段的温度为一段80℃，二段130℃，三段180℃，四段180℃，机头190℃，挤出机螺杆转速120rpm，挤出线速度30m/min，冷却水温50℃。
二、用高聚合度PVC生产皮筋
实施例3：高聚合度PVC（P=2500）  100份
DOP  80份
DBP  70份
透明稳定剂（有机锡）  2份
润滑剂（石蜡）  0.1份
着色剂（耐晒黄）  0.1份
珠光剂（云母钛）  1份
工艺步骤同例1。
实施例4：高聚合度PVC（P=4000）  100份
DOP  130份
DBP  10份
透明稳定剂（金属皂）  6份
润滑剂（硬脂酸）  1份
着色剂（立索尔宝红）  1份
珠光剂（云母钛）  5份
工艺步骤同例2。

Claims (5)

1、一种高弹性皮筋，其特征在于配方成份如下(以重量份计)：
(1)SBS    100份；
环烷油    0～100份；
抗氧剂    0～1份；
光稳定剂  0～1份；
着色剂    0～1份；
珠光剂    0～3份；
(2)高聚合度PVC( P=2500～4000) 100份；
DOP                            80～150份；
DBP                            0～80份；
透明稳定剂                     2～6份；
润滑剂                         0.1～1份；
着色剂                         0～1份；
珠光剂                         0～5份。
2、根据权利要求1所述的皮筋，其特征在于抗氧剂为B215、B225；光稳定剂为GW-540和GW-544；透明稳定剂为有机锡和金属皂；润滑剂为石蜡和硬脂酸。
3、根据权利要求1所述的皮筋、其特征在于皮筋的颜色为单色和多色；尺寸和截面可以各式各样。
4、根据权利要求1所述的皮筋，其特征在于沿长度方向各点横截面积相同。
5、一种高弹性皮筋的制备方法，其特征在于工艺流程为：
原料称量→混合→挤出成型→冷却→收卷→
Figure 941044696_IMG1
挤出各段温度为：一段50℃～80℃；二段100℃～130℃；三段160℃～180℃；四段160℃～180℃；机头160℃～190℃；冷却水温为20℃～50℃；挤出机螺杆转速为10～120rpm；挤出线速度为0.1～20m/min。
CN94104469A 1994-05-07 1994-05-07 高弹性皮筋及其制备方法 Expired - Fee Related CN1047125C (zh)