CN104788874A - 一种强弹性耐寒热塑性橡胶皮筋及其制备方法 - Google Patents
一种强弹性耐寒热塑性橡胶皮筋及其制备方法 Download PDFInfo
- Publication number
- CN104788874A CN104788874A CN201510218909.9A CN201510218909A CN104788874A CN 104788874 A CN104788874 A CN 104788874A CN 201510218909 A CN201510218909 A CN 201510218909A CN 104788874 A CN104788874 A CN 104788874A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber band
- preparation
- sbs
- heat resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种强弹性耐寒热塑性橡胶皮筋及其制备方法，它由下述重量份原料制成：SBS 80-120份，钛白粉3-6份，色母胶5-10份，抗光老化剂1-3份、煤矸石粉5-7份、竹叶提取物3-5份。制备方法：(1)配料：按上述重量份比例配料；(2)投料：先将SBS放入搅拌机内，加入煤矸石粉、竹叶提取物充分搅拌，然后加入其它原料搅拌，得混合料；(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100-110℃、120-130℃、160-170℃；(4)冷却，切断；(5)烘干，包装，入库。本发明的强弹性耐寒热塑性橡胶皮筋弹性好，耐寒性能好，在低温下仍然保持良好的弹性，制备方法简单。
Description
技术领域
本发明涉及橡皮筋技术领域，尤其涉及一种强弹性耐寒热塑性橡胶皮筋及其制备方法。
背景技术
橡皮筋具有弹性好、质量轻等特点被广泛应用于日常生活中。目前的橡皮筋耐寒极限为-20℃，当温度低于-20℃时，会出现变硬甚至裂痕的现象。
发明内容
本发明的目的是克服现有技术的不足，提供一种强弹性耐寒热塑性橡胶皮筋及其制备方法，制备的橡胶皮筋弹性好，耐寒性能好，在低温下仍然保持良好的弹性。
为了实现上述目的本发明采用如下技术方案：
一种强弹性耐寒热塑性橡胶皮筋，它由下述重量份的原料制成：SBS 80-120份，钛白粉3-6份，色母胶5-10份，抗光老化剂1-3份、煤矸石粉5-7份、竹叶提取物3-5份。
所述竹叶提取物的提取方法为：将竹叶绞碎后，用0.6mol/L的盐酸溶液浸泡1-2天，然后分别用95％的乙醇溶液和醋酸乙酯提取，旋蒸去掉乙酸乙酯后，将提取物烘干即可。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入煤矸石粉、竹叶提取物充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100-110℃、120-130℃、160-170℃；
(4)冷却，切断；
(5)烘干，包装，入库。
与已有技术相比，本发明的有益效果如下：
本发明的强弹性耐寒热塑性橡胶皮筋弹性好，耐寒性能好，在低温下仍然保持良好的弹性，制备方法简单。
具体实施方式
以下结合实施例对本发明作进一步的说明，但本发明不仅限于这些实施例，在未脱离本发明宗旨的前提下，所作的任何改进均落在本发明的保护范围之内。
实施例1：
一种强弹性耐寒热塑性橡胶皮筋，它由下述重量份的原料制成：SBS 80份，钛白粉3份，色母胶5份，抗光老化剂1份、煤矸石粉5份、竹叶提取物5份。
所述竹叶提取物的提取方法为：将竹叶绞碎后，用0.6mol/L的盐酸溶液浸泡1天，然后分别用95％的乙醇溶液和醋酸乙酯提取，旋蒸去掉乙酸乙酯后，将提取物烘干即可。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入煤矸石粉、竹叶提取物充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100℃、120℃、160℃；
(4)冷却，切断；
(5)烘干，包装，入库。
实施例2：
一种强弹性耐寒热塑性橡胶皮筋，它由下述重量份的原料制成：SBS 100份，钛白粉5份，色母胶6份，抗光老化剂2份、煤矸石粉6份、竹叶提取物4份。
所述竹叶提取物的提取方法为：将竹叶绞碎后，用0.6mol/L的盐酸溶液浸泡2天，然后分别用95％的乙醇溶液和醋酸乙酯提取，旋蒸去掉乙酸乙酯后，将提取物烘干即可。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入煤矸石粉、竹叶提取物充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在105℃、125℃、165℃；
(4)冷却，切断；
(5)烘干，包装，入库。
实施例3：
一种强弹性耐寒热塑性橡胶皮筋，它由下述重量份的原料制成：SBS 120份，钛白粉6份，色母胶10份，抗光老化剂3份、煤矸石粉7份、竹叶提取物3份。
所述竹叶提取物的提取方法为：将竹叶绞碎后，用0.6mol/L的盐酸溶液浸泡2天，然后分别用95％的乙醇溶液和醋酸乙酯提取，旋蒸去掉乙酸乙酯后，将提取物烘干即可。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入煤矸石粉、竹叶提取物充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在110℃、130℃、170℃；
(4)冷却，切断；
(5)烘干，包装，入库。
Claims (3)
1.一种强弹性耐寒热塑性橡胶皮筋，其特征在于：它由下述重量份的原料制成：SBS 80-120份，钛白粉3-6份，色母胶5-10份，抗光老化剂1-3份、煤矸石粉5-7份、竹叶提取物3-5份。
2.根据权利要求1所述的强弹性耐寒热塑性橡胶皮筋，其特征在于：所述竹叶提取物的提取方法为：将竹叶绞碎后，用0.6mol/L的盐酸溶液浸泡1-2天，然后分别用95％的乙醇溶液和醋酸乙酯提取，旋蒸去掉乙酸乙酯后，将提取物烘干即可。
3.一种如权利要1所述的耐化学腐蚀热塑橡胶皮筋的制备方法，其特征在于：包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入煤矸石粉、竹叶提取物充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100-110℃、120-130℃、160-170℃；
(4)冷却，切断；
(5)烘干，包装，入库。