CN104804359A - 一种耐化学腐蚀热塑橡胶皮筋及其制备方法 - Google Patents
一种耐化学腐蚀热塑橡胶皮筋及其制备方法 Download PDFInfo
- Publication number
- CN104804359A CN104804359A CN201510219364.3A CN201510219364A CN104804359A CN 104804359 A CN104804359 A CN 104804359A CN 201510219364 A CN201510219364 A CN 201510219364A CN 104804359 A CN104804359 A CN 104804359A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber band
- chemical
- preparation
- thermoplastic rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐化学腐蚀热塑橡胶皮筋及其制备方法，它由下述重量份的原料制成：SBS 80-120份，钛白粉3-6份，色母胶5-10份，抗光老化剂1-3份、滑石粉3-6份、鱼骨粉1-3份。制备方法：(1)配料：按上述重量份比例配料；(2)投料：先将SBS放入搅拌机内，加入滑石粉、鱼骨粉充分搅拌，然后加入其它原料搅拌，得混合料；(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100-110℃、120-130℃、160-170℃；(4)冷却，切断；(5)烘干，包装，入库。本发明的耐化学腐蚀热塑橡胶皮筋，弹性好、耐老化性高、耐化学腐蚀性好，而且制备方法简单。
Description
技术领域
本发明涉及橡皮筋技术领域，尤其涉及一种耐化学腐蚀热塑橡胶皮筋及其制备方法。
背景技术
橡皮筋具有弹性好、质量轻等特点被广泛应用于日常生活中，目前的橡胶橡皮筋耐老化性低，随着温度的升高会加速老化，而且耐化学腐蚀性低，不能满足化学腐蚀程度高的场所的应用。
发明内容
本发明的目的是克服现有技术的不足，提供一种耐化学腐蚀热塑橡胶皮筋及其制备方法，制备的橡胶皮筋弹性好、耐老化性高、耐化学腐蚀性好。
为了实现上述目的本发明采用如下技术方案：
一种耐化学腐蚀热塑橡胶皮筋，它由下述重量份的原料制成：SBS 80-120份，钛白粉3-6份，色母胶5-10份，抗光老化剂1-3份、滑石粉3-6份、鱼骨粉1-3份。
优选地，所述的耐化学腐蚀热塑橡胶皮筋，它由下述重量份的原料制成：SBS100份，钛白粉5份，色母胶8份，抗光老化剂2份、滑石粉5份、鱼骨粉2份。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，其特征在于：包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入滑石粉、鱼骨粉充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100-110℃、120-130℃、160-170℃；
(4)冷却，切断；
(5)烘干，包装，入库。
与已有技术相比，本发明的有益效果如下：
本发明的耐化学腐蚀热塑橡胶皮筋，弹性好、耐老化性高、耐化学腐蚀性好，而且制备方法简单。
具体实施方式
以下结合实施例对本发明作进一步的说明，但本发明不仅限于这些实施例，在未脱离本发明宗旨的前提下，所作的任何改进均落在本发明的保护范围之内。
实施例1：
一种耐化学腐蚀热塑橡胶皮筋，它由下述重量份的原料制成：SBS 80份，钛白粉3份，色母胶5份，抗光老化剂1份、滑石粉3份、鱼骨粉3份。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，其特征在于：包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入滑石粉、鱼骨粉充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100℃、120℃、160℃；
(4)冷却，切断；
(5)烘干，包装，入库。
实施例2：
一种耐化学腐蚀热塑橡胶皮筋，它由下述重量份的原料制成：SBS 100份，钛白粉5份，色母胶8份，抗光老化剂2份、滑石粉5份、鱼骨粉2份。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，其特征在于：包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入滑石粉、鱼骨粉充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在105℃、125℃、165℃；
(4)冷却，切断；
(5)烘干，包装，入库。
实施例3：
一种耐化学腐蚀热塑橡胶皮筋，它由下述重量份的原料制成：SBS 120份，钛白粉6份，色母胶10份，抗光老化剂3份、滑石粉6份、鱼骨粉1份。
所述的耐化学腐蚀热塑橡胶皮筋的制备方法，其特征在于：包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入滑石粉、鱼骨粉充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在110℃、130℃、170℃；
(4)冷却，切断；
(5)烘干，包装，入库。
Claims (3)
1.一种耐化学腐蚀热塑橡胶皮筋，其特征在于：它由下述重量份的原料制成：SBS 80-120份，钛白粉3-6份，色母胶5-10份，抗光老化剂1-3份、滑石粉3-6份、鱼骨粉1-3份。
2.根据权利要求1所述的耐化学腐蚀热塑橡胶皮筋，其特征在于：它由下述重量份的原料制成：SBS 100份，钛白粉5份，色母胶8份，抗光老化剂2份、滑石粉5份、鱼骨粉2份。
3.一种如权利要1所述的耐化学腐蚀热塑橡胶皮筋的制备方法，其特征在于：包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将SBS放入搅拌机内，加入滑石粉、鱼骨粉充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在100-110℃、120-130℃、160-170℃；
(4)冷却，切断；
(5)烘干，包装，入库。