CN104817778A - 一种抗老化的热塑橡胶皮筋及其制备方法 - Google Patents
一种抗老化的热塑橡胶皮筋及其制备方法 Download PDFInfo
- Publication number
- CN104817778A CN104817778A CN201510217879.XA CN201510217879A CN104817778A CN 104817778 A CN104817778 A CN 104817778A CN 201510217879 A CN201510217879 A CN 201510217879A CN 104817778 A CN104817778 A CN 104817778A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber band
- resistant thermoplastic
- ageing
- thermoplastic rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗老化的热塑橡胶皮筋及其制备方法，它由下述重量份原料制成：苯乙烯类弹性体80-120份，色母胶5-10份，复合型抗光老化剂1-2份、纳米碳酸钙3-5份、白炭黑5-8份、硅酮3-5份、玻璃纤维1-3份、植物香料0.2-0.3份、巴西蜡0.8-1.5份。制备方法：(1)配料；(2)投料：先将苯乙烯类弹性体放入搅拌机内，加入纳米碳酸钙、白炭黑、硅酮、玻璃纤维、巴西蜡充分搅拌，然后加入其它原料搅拌，得混合料；(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在190-200℃、200-210℃、225-235℃；(4)冷却，切断；(5)烘干，包装，入库。本发明的抗老化的热塑橡胶皮筋具有良好的抗老化性能，弹性好，物理性能强，气味芳香。
Description
技术领域
本发明涉及橡胶制品技术领域，尤其涉及一种抗老化的热塑橡胶皮筋及其制备方法。
背景技术
热塑性弹性体TPE/TPR，又称人造橡胶或合成橡胶，其产品既具备传统交联硫化橡胶的高弹性、耐老化、耐油性各项优异性能，同时又具备普通塑料加工方便、加工方式广的特点，可采用注塑、挤出、吹塑等加工方式生产，既简化加工过程，又降低加工成本，因此热塑性弹性体TPE/TPR材料已成为取代传统橡胶制备成橡皮筋的最新材料，其环保、无毒、手感舒适、外观精美。但是，通常的热塑性弹性体材料制备的橡皮筋耐老化性差，耐高温性能低，长期在高温环境中使用时，会出现开裂、弯曲、收缩等现象，影响外形及性能，另外，味道刺鼻，直接接触皮肤，易出现过敏、瘙痒等现象，具有一定的刺激性，不适合长期使用。
发明内容
本发明的目的是克服现有技术的不足，提供一种抗老化的热塑橡胶皮筋及其制备方法，制备的橡胶皮筋具有良好的抗老化性能，弹性好，物理性能强，气味芳香，其拉伸强度可达到16MPa,在热老化箱中，于120℃下保持120小时，再次测试拉伸强度，其拉伸强度保留值可以达到98％以上。
为了实现上述目的本发明采用如下技术方案：
一种抗老化的热塑橡胶皮筋，它由下述重量份的原料制成：苯乙烯类弹性体80-120份，色母胶5-10份，复合型抗光老化剂1-2份、纳米碳酸钙3-5份、白炭黑5-8份、硅酮3-5份、玻璃纤维1-3份、植物香料0.2-0.3份、巴西蜡0.8-1.5份。
所述的抗老化的热塑橡胶皮筋的制备方法，包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将苯乙烯类弹性体放入搅拌机内，加入纳米碳酸钙、白炭黑、硅酮、玻璃纤维、巴西蜡充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在190-200℃、200-210℃、225-235℃；
(4)冷却，切断；
(5)烘干，包装，入库。
与已有技术相比，本发明的有益效果如下：
本发明的抗老化的热塑橡胶皮筋具有良好的抗老化性能，弹性好，物理性能强，气味芳香，其拉伸强度可达到16MPa,在热老化箱中，于120℃下保持120小时，再次测试拉伸强度，其拉伸强度保留值可以达到98％以上。
具体实施方式
以下结合实施例对本发明作进一步的说明，但本发明不仅限于这些实施例，在未脱离本发明宗旨的前提下，所作的任何改进均落在本发明的保护范围之内。
实施例1：
一种抗老化的热塑橡胶皮筋，它由下述重量份的原料制成：苯乙烯类弹性体100份，色母胶6份，复合型抗光老化剂1.5份、纳米碳酸钙5份、白炭黑8份、硅酮3份、玻璃纤维3份、植物香料0.3份、巴西蜡1.2份。
所述的抗老化的热塑橡胶皮筋的制备方法，包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将苯乙烯类弹性体放入搅拌机内，加入纳米碳酸钙、白炭黑、硅酮、玻璃纤维、巴西蜡充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在190-200℃、200-210℃、225-235℃；
(4)冷却，切断；
(5)烘干，包装，入库。
Claims (2)
1.一种抗老化的热塑橡胶皮筋，其特征在于：它由下述重量份的原料制成：苯乙烯类弹性体80-120份，色母胶5-10份，复合型抗光老化剂1-2份、纳米碳酸钙3-5份、白炭黑5-8份、硅酮3-5份、玻璃纤维1-3份、植物香料0.2-0.3份、巴西蜡0.8-1.5份。
2.一种如权利要1所述的抗老化的热塑橡胶皮筋的制备方法，其特征在于：包括以下制备步骤：
(1)配料：按上述重量份比例配料；
(2)投料：先将苯乙烯类弹性体放入搅拌机内，加入纳米碳酸钙、白炭黑、硅酮、玻璃纤维、巴西蜡充分搅拌，然后加入其它原料搅拌，得混合料；
(3)升温挤出：将混合料加入挤出机挤出，挤出时挤出机的机头、过渡段、口模三个部位的温度分别控制在190-200℃、200-210℃、225-235℃；
(4)冷却，切断；
(5)烘干，包装，入库。