CN109645555A - 一种用于新型加热不燃烧烟草中的果香香线的制备方法和应用 - Google Patents
一种用于新型加热不燃烧烟草中的果香香线的制备方法和应用 Download PDFInfo
- Publication number
- CN109645555A CN109645555A CN201910091010.3A CN201910091010A CN109645555A CN 109645555 A CN109645555 A CN 109645555A CN 201910091010 A CN201910091010 A CN 201910091010A CN 109645555 A CN109645555 A CN 109645555A
- Authority
- CN
- China
- Prior art keywords
- parts
- spice
- line
- preparation
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种用于新型加热不燃烧烟草中的果香香线的制备方法和应用，其制备方法如下：将含香微胶囊、聚乳酸、共混材料、增塑剂混合均匀后，用熔融纺丝机进行纺丝。所述含香微胶囊、聚乳酸、共混材料及增塑剂的质量比为(0.05‑0.15)：1：(0.1‑0.15)：(0.02‑0.08)。本发明采用复凝聚法将沸点在200‑300℃的香精包裹于微胶囊内，含香微胶囊再与成丝基材进行熔融纺丝，在纺丝过程中香料不直接受热，可抑制加工过程中香料受热分解，减少香料散失，烟气通过时微囊壁上的微隙可缓释香味，从而使加热不燃烧卷烟香味持久。
Description
技术领域
本发明属于新型烟草领域，具体是一种用于加热不燃烧烟草中的果香香线制备和应用。
背景技术
加热不燃烧烟草是通过特殊的加热源对烟丝进行加热，加热时烟丝中的尼古丁及香味物质通过挥发产生烟气来满足吸烟者需求的一种新型烟草制品。与传统卷烟相比，加热不燃烧卷烟的重大变化之一在于消费过程中烟草材料所处的环境温度较低。传统卷烟的燃烧锥温度最高可达950℃，卷烟烟丝可通过蒸馏、裂解和燃烧等复杂的反应途径形成几千种产物；对于加热不燃烧卷烟，消费者使用时烟草材料所处温度一般低于500℃，且主要通过烟草材料的热解反应产生烟气。因此，消费者生理满足感不强，香气丰富性不够，是目前新型烟草制品相对于传统卷烟而言普遍存在的问题。
通过加香加料技术提升消费者抽吸加热不燃烧烟草制品时的生理满足感和香气丰富性，是行之有效的手段。传统的加香工艺是将香料按一定比例均匀喷洒到烟丝中，然而由于加热不燃烧卷烟独特的抽吸方式，在抽吸过程中，前几口风味充足，而后几口香味已非常淡薄，香料的释放不均匀、不持久。
香线材料一般采用棉纤维或香烟中允许使用的一些合成纤维，将香线浸泡在香精香料溶液中通过纤维丝束的物理吸附将其固定在香线上。当烟气通过时利用烟气的高温将香精香料释放出来。通过调节香精香料的配方和添加量来控制其在烟气中的释放量和释放速度。专利CN201810901367.9公开了一种果香风格的烟草组合物、发烟段以及加热不燃烧卷烟烟棒，将烟草组合物加入烟棒的烟草原料中，但加热不燃烧烟草制品的烟草原料吸收能力较差，加入到烟草原料中的香料很容易因机械挤压而流失。专利CN105595415A公开了一种利用荔枝花蜜制备蜜香卷烟香线的方法，将植物短纤维浸泡在荔枝花蜜香料液中，风干得到蜜香卷烟香线。通过浸泡法制得的香线，在滤嘴的成型过程中会有部分的香精香料提早释放出来造成损失。在香烟的存储和运输过程中，由于没有有效的屏蔽，也会有香精香料部分逸出造成吸味达不到要求。
更为稳定的添加和释放香精香料是香线亟待解决的问题。目前的一个研究发展趋势就是纺丝法制备香线。通过纺丝技术一次成型或对所纺丝线进行后处理，使制备的香线具有稳定的添加和释放香精香料的能力，并通过纺丝的过程对香精香料的释放达到可控的目的。
发明内容
针对上述现有技术的不足，本发明提供一种用于加热不燃烧烟草中的果香香线制备和应用，制备的香线具有稳定的添加和释放香精香料的能力，用于新型烟草中，香味持久，吸味和感觉效果很好。
本发明提供的技术方案：一种用于新型加热不燃烧烟草中的果香香线的制备方法，包括如下步骤：
(1)将含香微胶囊、聚乳酸、共混材料、增塑剂以质量比为(0.05-0.15)：1：(0.1-0.15)：(0.02-0.08)的比例混合均匀；
(2)采用熔融纺丝机进行纺丝得到果香香线，其中熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为170-190℃、160-180℃、150-160℃，纺丝速率为1000-2000m/min，热定温度为60-70℃，牵伸速度200-300m/min，牵伸倍数2.8-3.2,纺丝直径为0.8-1.5mm。
其中含香微胶囊的制备方法为：
A.50-65℃搅拌条件下，将明胶及多糖作为微胶囊壁材溶解于水中，壁材浓度为0.5％-2.0％，
B.加入香精，在500-800rpm的连续搅拌下乳化10-15min，其中香精与壁材的质量比为1：(0.4-1.5)；
C.保持溶液温度35±5℃，加入10％柠檬酸溶液缓慢调节pH至3.5-4.2，在400-500rpm下恒温搅拌15-30min；
D.冰水浴降低溶液温度至10±3℃，加入固化剂，用5％NaOH溶液调节pH至6.0-7.0，其中固化剂与明胶的质量比为(0.01-0.2):1；
E.体系水浴加热升温至35±5℃，固化1-4h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得含香微胶囊。
进一步的，所述步骤B中香精是由以下重量份数的物质混合而成：丙酸香叶酯15份、香兰素10份、茉莉酮20份、苯甲酸异戊酯15份、乙酸乙酯5份。
进一步的，所述步骤(1)中共混材料包括聚苯乙烯、聚乙烯、聚丙烯、聚酯树脂中的一种或多种。
进一步的，所述步骤(1)中增塑剂包括甘油、聚乙二醇、聚乙烯醇、ε-己内酯、马来酸酐中的一种或多种。
进一步的，所述步骤A中明胶与多糖的质量比为1：(1.0-1.5)。
进一步的，所述步骤A中多糖包括果糖、鼠李糖、羧甲基壳聚糖、海藻酸钠、环糊精、改性淀粉中的一种或多种。
进一步的，所述步骤D中固化剂包括戊二醛、乙二醛、转谷氨酰胺酶(TG酶)的一种或多种，或茶多酚、葡多酚、苹果多酚、可可多酚的一种或多种。
进一步的，一种用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：
将丙酸香叶酯15份、香兰素10份、茉莉酮20份、苯甲酸异戊酯15份、乙酸乙酯5份配置成香精备用；将明胶50份、羧甲基壳聚糖20份、海藻酸钠45份溶解于55℃热水中，溶液浓度为1.2％，加入110份香精，在750rpm的连续搅拌下乳化15min，保持溶液温度35℃，加入10％柠檬酸溶液缓慢调节pH至4.0，在500rpm下恒温搅拌25min；冰水浴降低溶液温度至10℃，加入转谷氨酰胺酶(TG酶)6份，用5％NaOH溶液调节pH至7.0；体系水浴加热升温至35℃，固化2.5h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得含香微胶囊；
将含香微胶囊、聚乳酸、聚乙烯、聚丙烯、甘油按质量比0.1:1:0.08:0.04：0.05混合均匀后，用熔融纺丝机进行纺丝得到果香香线，其中熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、160℃，纺丝速率为1200m/min，热定温度为70℃，牵伸速度240m/min，牵伸倍数3.0，纺丝直径为1.2mm。
一种用于新型加热不燃烧烟草中的果香香线的应用，其特征在于：将上述方法制备的果香香线添加到加热不燃烧卷烟滤棒中醋纤段，用于缓释香味，从而使加热不燃烧卷烟香味持久。
本发明采用复凝聚法将沸点在200-300℃的香精包裹于微胶囊内，含香微胶囊再与成丝基材进行熔融纺丝，在纺丝过程中香料不直接受热，可抑制加工过程中香料受热分解，减少香料散失，烟气通过时微囊壁上的微隙可缓释香味，从而使加热不燃烧卷烟香味持久。
具体实施方式
为了更好地解释本发明，以下结合具体实施例对本发明作进一步的详细说明，但它们不对本发明构成限定。
将丙酸香叶酯15份、香兰素10份、茉莉酮20份、苯甲酸异戊酯15份、乙酸乙酯5份配置成香精备用。
对比例一：
将普通棉线浸泡在上述香精中30min，常温风干得到香线样品一，将香线一加入滤棒中卷制得到加热不燃烧卷烟样品一。
实施例1：
将明胶50份、羧甲基壳聚糖20份、海藻酸钠45份溶解于55℃热水中，溶液浓度为1.2％，加入110份香精，在750rpm的连续搅拌下乳化15min，保持溶液温度35℃，加入10％柠檬酸溶液缓慢调节pH至4.0，在500rpm下恒温搅拌25min；冰水浴降低溶液温度至10℃，加入转谷氨酰胺酶(TG酶)6份，用5％NaOH溶液调节pH至7.0；体系水浴加热升温至35℃，固化2.5h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得粉末状样品。
将上述方法制备的含香微胶囊、聚乳酸、聚乙烯、聚丙烯、甘油按质量比0.1:1:0.08:0.04：0.05混合均匀后，用熔融纺丝机进行纺丝，熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、160℃，纺丝速率为1200m/min，热定温度为70℃，牵伸速度240m/min，牵伸倍数3.0，纺丝直径为1.2mm，得到香线样品二，将香线二加入滤棒中卷制得到加热不燃烧卷烟样品二。
实施例2：
将明胶50份、鼠李糖15份、改性淀粉35份溶解于50℃热水中，溶液浓度为1％，加入130份香精，在650rpm的连续搅拌下乳化15min，保持溶液温度38℃，加入10％柠檬酸溶液缓慢调节pH至3.8，在400rpm下恒温搅拌30min；冰水浴降低溶液温度至10℃，加入戊二醛0.8份，用5％NaOH溶液调节pH至6.8；体系水浴加热升温至40℃，固化1.5h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得粉末状样品。
将上述方法制备的含香微胶囊、聚乳酸、聚苯乙烯、马来酸酐按质量比0.06:1:0.1：0.06混合均匀后，用熔融纺丝机进行纺丝，熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、160℃，纺丝速率为1200m/min，热定温度为70℃，牵伸速度240m/min，牵伸倍数3.0，纺丝直径为1.2mm，得到香线样品三，将香线三加入滤棒中卷制得到加热不燃烧卷烟样品三。
对比例2：
将上述香精按质量分数15％加入新型烟草卷烟薄片涂布液中，制得加热不燃烧卷烟样品四。
香线热稳定性测试：将香线样品分别在30℃、50℃、80℃、100℃四种不同的温度下，加热8h时，测试其香精的挥发质量(单位：毫克)。
逐口烟气中香精含量测试：利用加热不燃烧产品加热器具在10孔道直线型吸烟机上对添加香线的卷烟进行逐口烟气抽吸，具体抽吸参数：抽吸容量50mL，抽吸持续时间2s，抽吸间隔30s，测试主流烟气中的香精含量(单位：微克)。
从结果可知，采用本技术方案制备的香线(香线二、三)在热稳定性较好，香料散失较少，同时在抽吸时释放香气更均匀、持久。
以上所述，仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何属于本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求的保护范围为准。
Claims (9)
1.一种用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于包括如下步骤：
(1)将含香微胶囊、聚乳酸、共混材料、增塑剂以质量比为(0.05-0.15)：1：(0.1-0.15)：(0.02-0.08)的比例混合均匀；
(2)采用熔融纺丝机进行纺丝得到果香香线，其中熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为170-190℃、160-180℃、150-160℃，纺丝速率为1000-2000m/min，热定温度为60-70℃，牵伸速度200-300m/min，牵伸倍数2.8-3.2,纺丝直径为0.8-1.5mm。
其中含香微胶囊的制备方法为：
A.50-65℃搅拌条件下，将明胶及多糖作为微胶囊壁材溶解于水中，壁材浓度为0.5％-2.0％，
B.加入香精，在500-800rpm的连续搅拌下乳化10-15min，其中香精与壁材的质量比为1：(0.4-1.5)；
C.保持溶液温度35±5℃，加入10％柠檬酸溶液缓慢调节pH至3.5-4.2，在400-500rpm下恒温搅拌15-30min；
D.冰水浴降低溶液温度至10±3℃，加入固化剂，用5％NaOH溶液调节pH至6.0-7.0，其中固化剂与明胶的质量比为(0.01-0.2):1；
E.体系水浴加热升温至35±5℃，固化1-4h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得含香微胶囊。
2.根据权利要求1所述的用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：所述步骤B中香精是由以下重量份数的物质混合而成：丙酸香叶酯15份、香兰素10份、茉莉酮20份、苯甲酸异戊酯15份、乙酸乙酯5份。
3.根据权利要求1所述的用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：所述步骤(1)中共混材料包括聚苯乙烯、聚乙烯、聚丙烯、聚酯树脂中的一种或多种。
4.根据权利要求1所述的用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：所述步骤(1)中增塑剂包括甘油、聚乙二醇、聚乙烯醇、ε-己内酯、马来酸酐中的一种或多种。
5.根据权利要求1所述的用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：所述步骤A中明胶与多糖的质量比为1：(1.0-1.5)。
6.根据权利要求1所述的用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：所述步骤A中多糖包括果糖、鼠李糖、羧甲基壳聚糖、海藻酸钠、环糊精、改性淀粉中的一种或多种。
7.根据权利要求1所述的用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：所述步骤D中固化剂包括戊二醛、乙二醛、转谷氨酰胺酶(TG酶)的一种或多种，或茶多酚、葡多酚、苹果多酚、可可多酚的一种或多种。
8.根据权利要求1-7任一项所述的用于新型加热不燃烧烟草中的果香香线的制备方法，其特征在于：
将丙酸香叶酯15份、香兰素10份、茉莉酮20份、苯甲酸异戊酯15份、乙酸乙酯5份配置成香精备用；将明胶50份、羧甲基壳聚糖20份、海藻酸钠45份溶解于55℃热水中，溶液浓度为1.2％，加入110份香精，在750rpm的连续搅拌下乳化15min，保持溶液温度35℃，加入10％柠檬酸溶液缓慢调节pH至4.0，在500rpm下恒温搅拌25min；冰水浴降低溶液温度至10℃，加入转谷氨酰胺酶(TG酶)6份，用5％NaOH溶液调节pH至7.0；体系水浴加热升温至35℃，固化2.5h，停止搅拌，静置，抽滤，洗去微囊表面残留的固化剂，室温下干燥得含香微胶囊；
将含香微胶囊、聚乳酸、聚乙烯、聚丙烯、甘油按质量比0.1:1:0.08:0.04：0.05混合均匀后，用熔融纺丝机进行纺丝得到果香香线，其中熔融纺丝螺杆挤出温度、箱体组件、喷丝板温度分别为190℃、180℃、160℃，纺丝速率为1200m/min，热定温度为70℃，牵伸速度240m/min，牵伸倍数3.0，纺丝直径为1.2mm。
9.根据权利要求1-7任一项所述方法制得的用于新型加热不燃烧烟草中的果香香线的应用，其特征在于：将上述方法制备的果香香线添加到加热不燃烧卷烟滤棒中醋纤段，用于缓释香味，从而使加热不燃烧卷烟香味持久。