CN109592651A - 一种碲化铅薄膜 - Google Patents

一种碲化铅薄膜 Download PDF

Info

Publication number
CN109592651A
CN109592651A CN201811463950.2A CN201811463950A CN109592651A CN 109592651 A CN109592651 A CN 109592651A CN 201811463950 A CN201811463950 A CN 201811463950A CN 109592651 A CN109592651 A CN 109592651A
Authority
CN
China
Prior art keywords
lead
solution
thin film
telluride thin
lead telluride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811463950.2A
Other languages
English (en)
Inventor
孙喜桂
石磊
王建鹏
张云瑞
张艺宁
乔雪
巩鑫宇
沈向丞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Jianzhu University
Original Assignee
Shandong Jianzhu University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Jianzhu University filed Critical Shandong Jianzhu University
Priority to CN201811463950.2A priority Critical patent/CN109592651A/zh
Publication of CN109592651A publication Critical patent/CN109592651A/zh
Withdrawn legal-status Critical Current

Abstract

本发明涉及一种碲化铅薄膜，属于半导体材料的制备领域。本发明采用的是醋酸铅和碲粉，分别为铅源和碲源，以碲粉和亚硫酸钠为原料制备碲代硫酸钠，以柠檬酸钠为络合剂，通过氢氧化钾调节pH值，将沉积液放置水浴锅中，在75℃下加热4小时，干燥后得到的碲化铅薄膜。本发明合成方法中所用的原料易得，工艺简便，成本低、收率高和能大规模生产薄膜的优点，因此该方法具有非常广阔的应用前景。

Description

一种碲化铅薄膜
技术领域
本发明涉及一种碲化铅薄膜，该方法简便易行，无毒环保，具有普适性，能够在实验室中进行快速有效的制备，属于半导体材料的制备领域。
背景技术
碲化铅薄膜是一类重要的热电变换材料，具有窄的禁带宽度(0.27eV, 300K)。因为其介电常数较大，折射率高达5.5，折射率温度系数也达到-0.002K-1，透明波段宽，短波吸收限为3.4μm，在4μm到16μm的吸收系数小，且易沉积，可以制成很好的红外滤光电镀膜材料，在机械、电子、光学、航空、建材、轻工等工业部门得到广泛应用，特别在电子技术领域得到了广泛的应用。光电摄像器件，各种集成电路器件、各种显示器件、太阳电池及磁头磁带的各种转换传感都应用薄膜。高科技产业的需求推动下，该材料在国防及工、农业建设中得到了大规模应用，近几十年来受到了科学界的广泛重视。
制备碲化铅薄膜的方法有很多，如电化学沉积法（ ECD ）、分子束外延法（MBE）、真空气相沉积法（VPD），原子层沉积法（ALD），溅射沉积法等。与这些制备方法比较，化学液相法从性能价格比上来说具有明显的优势，是广泛应用的一种方法。在相对较低的温度下，不需要任何特殊的设置和任何复杂的仪器，且制备的薄膜晶粒更加紧密，表面更加光滑。化学液相法具有成本低、收率高和能大规模生产薄膜等特点，在合成金属碲族化物晶体时有很大前景。
发明内容
本发明采用的是化学液相法，其中醋酸铅和碲粉，分别为铅源和碲源，以碲粉和亚硫酸钠为原料制备碲代硫酸钠，以柠檬酸钠为络合剂，通过氢氧化钾调节pH值，将沉积液放置水浴锅中，在75℃下加热4小时，干燥后得到的碲化铅薄膜。本发明合成方法中所用的原料易得，工艺简便，成本低、收率高和能大规模生产薄膜的优点，因此该方法具有非常广阔的应用前景。
化学液相法制备碲化铅薄膜的实验原理如下：
PbTe + Na2SO3 → Na2TeSO3
(TeSO3)2- + 2OH- → Te2- + SO4 2- + H2O
Pb2+ + Te2- → PbTe↓
此种碲化铅半导体薄膜的制备方法的步骤是：
（1）制备前对衬底进行去油、去污清洗，即放入无水乙醇中经过超声波清洗15~20min，再放入无水乙醇中浸泡，以便沉积时使用；
（2）配制出0.2mol/L的醋酸铅溶液、1 mol/L柠檬酸钠溶液和0.2 mol/L碲代硫酸钠溶液；
（3）将上述三种溶液混合，并使用氢氧化钾溶液调节pH值至11.0~12.0，加入去离子水至100mL；
（4）将衬底吹干后，放入沉积液中，沉积液放入75℃恒温水浴锅中，4小时后取出，使用吹风机冷风吹干，得到碲化铅薄膜。
上述步骤（2）中碲代碲酸钠溶液是通过将5g碲粉和12g亚硫酸钠放入烧杯中，加蒸馏水至100mL，在90℃下边搅拌边加热24h，过滤除去未反应的碲粉和碲酸盐后制备出的。
上述步骤（3）中三种溶液的混合，是边搅拌边将20mL的柠檬酸钠溶液缓慢地倒入30mL的醋酸铅溶液中，此为柠檬酸钠的络合过程，再将6~8mL的碲代硫酸钠溶液倒入二者的混合溶液中，以沉积液的颜色变化，由浅棕色变至棕色再变至咖啡色最后至黑色，来判断碲代硫酸钠的具体用量。
利用X射线衍射分析了所得碲化铅薄膜的相结构，结果如图1所示；利用金相显微镜分析了所得碲化铅薄膜的形貌图，结果如图2所示。所得结果表明晶核分布比较均匀，薄膜较为致密且外观平整，已稳定成完全多晶结构，其密度得到改善。
与现有技术相比，本发明中所使用的化学液相法具有成本低、收率高和能大规模生产薄膜等特点，该方法简便易行，无毒环保，能够在实验室中进行快速有效的制备，具有普适性。
附图说明
图1是碲化铅薄膜的XRD衍射图谱。
图2是碲化铅薄膜的金相显微镜图：(a) 沉积时间3.0h，(b) 沉积时间3.5h，(c)沉积时间4.0h。
具体实施方式
制备前对衬底进行去油、去污清洗，放入无水乙醇中经过超声波清洗后，再放入无水乙醇中浸泡，沉积时使用；配制出0.2mol/L的醋酸铅溶液，1mol/L的柠檬酸钠溶液和0.2mol/L碲代硫酸钠溶液；边搅拌边将30mL的醋酸铅溶液、20mL的柠檬酸钠溶液和6~8mL碲代硫酸钠溶液混合，再使用氢氧化钾溶液调节pH值至11.0~12.0，加入去离子水至100mL；准备三个衬底，吹干后放入75℃恒温水浴锅中的沉积液中，分别在3小时后，3.5小时后，4小时后取出衬底，得到碲化铅薄膜。
从图1可以看出制备出了碲化铅薄膜，从图2可以看出晶核分布比较均匀，薄膜较为致密，衬底表面被完全覆盖，且外观平整。
由上述实施例可以看出，采用化学液相法制备的碲化铅薄膜成膜质量较高，无毒环保，工艺操作简单，能大规模生产，生产条件没有限制，有很大的应用前景。

Claims (1)

1.一种碲化铅薄膜，其主要特征在于，包括0.2mol/L醋酸铅、1 mol/L柠檬酸钠、5g碲粉、12g亚硫酸钠、氢氧化钾，其余为水；其制备过程如下：制备前对衬底进行去油、去污清洗，放入无水乙醇中经过超声波清洗后，再放入无水乙醇中浸泡，沉积时使用；配制出0.2mol/L的醋酸铅溶液，1mol/L的柠檬酸钠溶液和0.2mol/L碲代硫酸钠溶液；边搅拌边将30mL的醋酸铅溶液、20mL的柠檬酸钠溶液和6~8mL碲代硫酸钠溶液混合，再使用氢氧化钾溶液调节pH值至11.0~12.0，加入去离子水至100mL；吹干后放入75℃的沉积液中，4小时后取出衬底。
CN201811463950.2A 2018-12-03 2018-12-03 一种碲化铅薄膜 Withdrawn CN109592651A (zh)