CN109112581A - 一种镀铬溶液 - Google Patents
一种镀铬溶液 Download PDFInfo
- Publication number
- CN109112581A CN109112581A CN201710478314.6A CN201710478314A CN109112581A CN 109112581 A CN109112581 A CN 109112581A CN 201710478314 A CN201710478314 A CN 201710478314A CN 109112581 A CN109112581 A CN 109112581A
- Authority
- CN
- China
- Prior art keywords
- plating bath
- sulfate
- glycerine
- surplus
- methanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于金属表面处理技术领域,尤其涉及一种镀铬溶液。本发明所要解决的技术问题是提供一种稳定性较好的溶液,尤其是硬度和耐高温性方面较好。本发明所提供的技术问题是:一种镀铬溶液,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬30~40%,硫酸钾2~5%,硫酸硅2~5%,硫酸亚铁2~5%,1,5‑萘二磺酸钠盐10~20%,甲醇2~8%,氯化钠3~5%,丙三醇1~3%,余量为去离子水。本发明的有益效果在于:实用本发明生产的镀铬层,其硬度可持久维持在900~1100HV之间;600℃以内不会出现氧化变色。
Description
技术领域
本发明属于金属表面处理技术领域,尤其涉及一种镀铬溶液。
背景技术
铬是在做金属表面处理是所用常用的一种材料。镀铬层具有硬度高和耐高温性好的特点。而镀铬层性能的好坏主要有两个影响因素,一是镀铬溶液的配比,二是镀铬工艺。其中,镀铬溶液的配比尤为重要。现有镀铬溶液稳定性方面仍有不足。
发明内容
本发明所要解决的技术问题是提供一种稳定性较好的溶液,尤其是硬度和耐高温性方面较好。
本发明所提供的技术问题是:
一种镀铬溶液,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬30~40%,硫酸钾2~5%,硫酸硅2~5%,硫酸亚铁2~5%,1,5-萘二磺酸钠盐10~20%,甲醇2~8%,氯化钠3~5%,丙三醇1~3%,余量为去离子水。
优选的,所述溶液包括硫酸铬30~35%,硫酸钾2~3%,硫酸硅2~3%,硫酸亚铁2~3%,1,5-萘二磺酸钠盐10~15%,甲醇2~5%,氯化钠3~5%,丙三醇1~3%,余量为去离子水。
优选的,所述溶液包括硫酸铬35~40%,硫酸钾3~5%,硫酸硅3~5%,硫酸亚铁3~5%,1,5-萘二磺酸钠盐15~20%,甲醇5~8%,氯化钠3~5%,丙三醇1~3%,余量为去离子水。
本发明的有益效果在于:实用本发明生产的镀铬层,其硬度可持久维持在900~1100HV之间;600℃以内不会出现氧化变色。
具体实施方式
为了更清楚、完整说明本发明的内容,下面提供最优实施方式来说明本发明构思。
实施例1
一种镀铬溶液,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬30%,硫酸钾2%,硫酸硅5%,硫酸亚铁3%,1,5-萘二磺酸钠盐10%,甲醇4%,氯化钠4%,丙三醇1%,余量为去离子水。
实施例2
一种镀铬溶液,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬33%,硫酸钾2%,硫酸硅3%,硫酸亚铁5%,1,5-萘二磺酸钠盐12%,甲醇2%,氯化钠3%,丙三醇2%,余量为去离子水。
实施例3
一种镀铬溶液,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬35%,硫酸钾4%,硫酸硅2%,硫酸亚铁3%,1,5-萘二磺酸钠盐15%,甲醇7%,氯化钠5%,丙三醇3%,余量为去离子水。
实施例4
一种镀铬溶液,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬37%,硫酸钾3%,硫酸硅3%,硫酸亚铁2%,1,5-萘二磺酸钠盐18%,甲醇6%,氯化钠4%,丙三醇2%,余量为去离子水。
实施例5
一种镀铬溶液,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬40%,硫酸钾5%,硫酸硅2%,硫酸亚铁4%,1,5-萘二磺酸钠盐20%,甲醇8%,氯化钠5%,丙三醇1%,余量为去离子水。
当然,所提供的是实施例旨在说明本发明的构思,并不是本发明设计方案的全部,更不应该视为本发明设计内容的局限。在所提供的实施方式的启示下,所作出的任何方案均属于本发明的保护范围。
Claims (3)
1.一种镀铬溶液,其特征在于,所述镀铬溶液的组分及重量百分比,其特征在于,所述溶液包括硫酸铬30~40%,硫酸钾2~5%,硫酸硅2~5%,硫酸亚铁2~5%,1,5-萘二磺酸钠盐10~20%,甲醇2~8%,氯化钠3~5%,丙三醇1~3%,余量为去离子水。
2.根据权利要求1所述的溶液,其特征在于,所述溶液包括硫酸铬30~35%,硫酸钾2~3%,硫酸硅2~3%,硫酸亚铁2~3%,1,5-萘二磺酸钠盐10~15%,甲醇2~5%,氯化钠3~5%,丙三醇1~3%,余量为去离子水。
3.根据权利要求1所述的溶液,其特征在于,所述溶液包括硫酸铬35~40%,硫酸钾3~5%,硫酸硅3~5%,硫酸亚铁3~5%,1,5-萘二磺酸钠盐15~20%,甲醇5~8%,氯化钠3~5%,丙三醇1~3%,余量为去离子水。