CN1090330A - 牛皮擦色金属效应革及其生产方法 - Google Patents
牛皮擦色金属效应革及其生产方法 Download PDFInfo
- Publication number
- CN1090330A CN1090330A CN 93120634 CN93120634A CN1090330A CN 1090330 A CN1090330 A CN 1090330A CN 93120634 CN93120634 CN 93120634 CN 93120634 A CN93120634 A CN 93120634A CN 1090330 A CN1090330 A CN 1090330A
- Authority
- CN
- China
- Prior art keywords
- leather
- minutes
- rotated
- water
- hide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及“制革业”技术,对牛皮加工方法中,
采用擦色金属效应技术而制成高档次皮革。其特点
是在对复鞣、复鞣之后诸道工序的成分、配方、工艺进
行了设计,如涂饰(封革里、填充、刷色)、喷涂(喷底
层、中层、效应层、光亮层、顶层),所生产出皮革:革身
丰满柔软有弹性、革面平滑光亮、耐磨、防水、易保养,
经蜡质擦拭抛光后,革面呈现出色泽艳丽、光泽闪烁
的珠光金属效应等特点。对低档次牛皮加工亦能提
高皮革档次。其革用于加工各式男女时装鞋、歌舞厅
鞋、时装箱包、包袋。
Description
本发明涉及制革业技术领域,尤其为一种对牛皮进行加工以及用化工原料进行处理的高档次皮革及其生产方法。
社会发展,人们生活水平提高,国际国内市场对皮革及其制品的需求量越来越大,尤其对皮革业的要求是向着高质量、高档次方面发展,是向着舒适、美观艺术、豪华型发展,而当前的皮革在“革身丰满柔软有弹性、革面平滑光亮、耐磨、防水、易保养方面性能较差,尤其对皮革进行腊质擦试抛光后,革面在呈现色彩艳丽、光泽闪烁的珠光金属效应方面性能差,这样便满足不了改革开放年代,人们进行广泛“社交”及生活的需要。
本发明的目的在于克服以上已有技术中的不足之处,而提供一种耐折、耐拉、革身丰满有弹性、革面平滑光亮、耐磨、防水、易保养,经腊质擦试抛光后,革面能呈现出色彩艳丽、光泽闪烁的珠光金属效应等特点的牛皮皮革及其生产方法。
生产工艺见附图-生产工艺流程图;复鞣以前的工艺与河南省沁阳市光华制革厂的黄牛皮全粒面革工艺相同。所说:“擦色金属效应革”意为:其革经腊质擦试抛光后,革面能呈现色彩艳丽的金属亮光。这种牛皮擦色金属效应革的生产工艺、配方及操作规程为:
1、复鞣
称重:取削匀后的革,作为复鞣至染色、加脂工艺用料的依据,
水洗:流水洗30-40分钟
复鞣:水系数 1-1.5倍
温度 40-45℃
树脂型复鞣剂
PT-A:4%,加水稀释,转动40分钟
醋酸钠:1.5-2%,转动30分钟
树脂型复鞣剂
KS-1:3%,转动60分钟
铬鞣剂:8%,转动90分钟
小苏打:0.6-0.7%,加水稀释,转动60分钟
2、中和
(1)水洗:流水洗30分钟
(2)中和:水系数1.5倍
温度:38±1℃
碳酸铵:2.5%,加水稀释
醋酸钠:0.8%
扩散剂:0.2%
时间:40-60分钟
(3)水洗:流水洗30-40分钟
3、染色:水系数:2.5倍
温度:60-65℃
平平加:0.3%,转动5分钟
氨水:0.2%,转动5分钟
染料:1.5-2%,转动30-40分钟
甲酸:0.5%,加水稀释,转动20分钟
4、加脂:水系数:1.5倍
温度:60-65℃
SE加脂剂:6%
硫化油:2%
KS-1:2%,转动40分钟
丰满鱼油:1%
楷光浆:1.5%(用水稀释加入)转动20分钟
5、填充:水系数:1-1.5倍
温度:34-35℃
落叶松:3%
渗透剂:0.3%
时间:40分钟
填充树脂:3%
渗透剂:0.2%
时间:转动40-50分钟
6、干燥、整理(贴板、真空干燥、挂晾、振软、真空干燥),
7、磨革:该工序与一般修饰不同,要求磨合达到绒细而短、不呈现乳头层,因此需要:240#-600#-除尘、净面
8、涂饰
(1)封革里:丙烯酸树酯:15,水:60
(2)填充:填充树脂:40,水:60
渗透剂J、F、C:7
(3)刷色:黑色膏(9202):200,腊剂(4350):25,填充剂(4601):50,水:150,树酯乳液(2350):150,树酯乳液(2019):200,树脂乳液(2912):100,晾干-烫平,(90℃/100kg)-意为烫平板压力为100kg,温度为90℃
9、喷涂
喷涂工艺、成份、配方(组分比):
(1)喷底层
颜料膏:200,填充剂:50,乳化腊:25,水:150,中硬树脂:150,中软树脂:300,重喷1次-烘干-烫平(90℃/100kg)
(2)喷中层,按(1)中混合液:重喷1-2次
(3)喷效应层
乳化腊:25,中软树脂:350,络合染料:5,珠光粉:150,水:300,轻喷2-3次,晾干
(4)喷光亮层
光油:100,醋酸丁酯:100,将混合液重喷1次-晾干-烫平(90℃/100kg)
(5)喷顶层
络合染料:5,高光光油:65,黑色光油:35,抛光剂:10,消光剂:20,醋酸丁酯:300,轻喷2次-晾干。
上述的“填充5”工艺亦可采用“部分复鞣,填充剂搭配”工艺,试验情况为:
材料名称、用量 | 实现的坯革性状 | ||||
丰满度 | 弹性 | 延伸率 | 粒面细度 | 全张革身软硬 | |
FR-1:2%PFB:4%栲胶:2.5%填充剂:3%J、F、C:0.3% | 5 | 5 | 4 | 5 | 4 |
试验表中看出:整体指标较好,特别是采用FR-1后,使革的部位差缩小,丰满有弹性,全张革软硬较一致,解决“革的边浅空松”效果好。
表中:FR-1为树脂复鞣剂,PFB为合成丹宁鞣剂,J、F、C为渗透剂。
按照上述工艺、配方生产出来的黄牛皮擦色金属效应革,对内部测试,成品革的理化性能指标如下:
抗张强度:(N/mm2):27.6
伸长率(在抗张强度为10N/mm2)%:43.0
撕裂强度(N/mm):107.0
崩裂强度(N/mm):483.7
崩裂高度:(N/mm):8.0
收缩温度:(℃) >95
颜色磨擦牢度(干/湿)级:4.5/4.5
耐折牢度(次):10000
水份及其它挥发物(%):15.75
二氯甲烷萃取物(%):7.8
三氧化二铬(%):4.6
酸碱值(PH):5.5
所制成的皮革:革身丰满柔软有弹性,革面平滑光亮,耐磨、防水、易保养,经腊质擦试抛光后,革面能呈现色泽艳丽、光泽闪烁的珠光金属效应等特点。
采用上述生产方法,对于低档次牛皮加工,亦能提高皮革档次,也就是对提高低档原料皮使用价值找到了一条出路。这种牛皮擦色金属效应革用于加工男女各式时装鞋、歌舞厅鞋、或时装箱包、包袋。
附件材料:
1、河南省科技情报所联机检索报告单,1993.5.20
2、河南省皮革质检中心站成品理化测试报告,1993.5.12
Claims (2)
1、一种牛皮擦色金属效应革的生产方法,要经过:原牛皮分档、浸水回软、去肉里、脱毛浸灰、去肉里、片皮、初鞣、片皮、削匀、复鞣以及用化工原料混合液、涂饰、喷涂等工序,其特征在于生产过程中部分工序的成份、配方、操作规程为:
(1)复鞣
水系数:1-1.5倍,温度40-45℃,PT-A:4%,加水稀释,转动40分钟,醋酸钠:1.5-2%,转动30分钟,KS-1:3%,转动60分钟,铬鞣剂:8%,转动90分钟,小苏打:0.6-0.7%,加水稀释,转动60分钟,
(2)中和
水系数:1.5倍,温度:38±1℃,碳酸铵:2.5%,加水稀释,醋酸钠:0.8%,扩散剂:0.2%,时间40-60分钟,流水洗:30-40分钟,
(3)染色
水系数:2.5倍,温度:60-65℃,平平加:0.3%,转动5分钟,氨水:0.2%,转动5分钟,染料:1.5-2%,30-40分钟,甲酸:0.5%,加水稀释,转动20分钟,
(4)加脂:
水系数:1.5倍,温度:60-65℃,SE:6%,硫化油:2%,丰满鱼油:1%,KS-1:2%,转动40分钟,楷光浆:1.5%,
加水稀释,转动20分钟,
(5)填充
水系数:1-1.5倍,温度:34-35℃,落叶松:3%:渗透剂:0.3%,时间:40分钟,填充树脂:3%,渗透剂:0.2%,时间:转动40-50分钟,
(6)磨革
240#砂-600#砂-除尘、净面
(7)涂饰
(1)封革里:丙烯酸树酯:15,水:60
(2)填充:填充树酯:40,水:60,J、F、C:7
(3)刷色:黑色膏(9202):200,腊剂(4350):25,填充剂(4601):50,水:150,树酯乳液(2350):150,树酯乳液(2019):200,树酯乳液(2912):100,晾干-烫平
(8)喷涂
喷涂工艺、成份、配方(组分比):
a、喷底层:颜料膏:200,填充剂:50,乳化腊:25,水:150,中硬树脂:150,中软树脂:300,重喷1次-烘干-烫平
b、喷中层:按(1)中的混合液重喷1-2次
c、喷效应层:乳化腊:25,中软树脂:350,络化染料:5,珠光粉:150,水:300,轻喷2-3次,晾干
d、喷光亮层:光油:100,醋酸丁酯:100,将混合液重喷1次-晾干-烫平
e、喷丁层:络合颜料:5,高光光油:65,黑色光油:35,抛光剂:10,消光剂:20,醋酸丁酯:300,重喷2次-晾干。
2、据权利要求1所述的牛皮擦色金属效应革的生产方法,其特征在于所说的“填充”(5)的工艺亦可采用“部分复鞣、填充剂搭配”工艺:FR-1:2%,PFB:4%,栲胶:2.5%,填充剂:3%,J、F、C:0.3%。