CN108644124A - 一种使用抑制生物生长新材料的双动力长轴消防泵 - Google Patents
一种使用抑制生物生长新材料的双动力长轴消防泵 Download PDFInfo
- Publication number
- CN108644124A CN108644124A CN201810405232.3A CN201810405232A CN108644124A CN 108644124 A CN108644124 A CN 108644124A CN 201810405232 A CN201810405232 A CN 201810405232A CN 108644124 A CN108644124 A CN 108644124A
- Authority
- CN
- China
- Prior art keywords
- pump
- parts
- fire
- fire pump
- long axis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及消防设备制造领域，具体关于一种使用抑制生物生长新材料的双动力长轴消防泵；其主要部件包括消防泵、动力系统、控制柜和扬水管；所述的消防泵由泵头和泵体组成；所述的消防泵泵头、动力系统和控制柜安装于地坪基础上，扬水管及泵体部分立式安装于泵组基础下方；所述的消防泵为长轴单级离心泵；所述泵轴分成几段；本方案设计的双动力长轴消防泵设备工作稳定可靠，有效防止水中各种生物附着在消防泵上，避免消防泵的功能参数降低或失效。
Description
技术领域
本发明涉及消防设备制造领域，具体关于一种使用抑制生物生长新材料的双动力长轴消防泵。
背景技术
随着我国经济的持续发展,越来越多的工程项目相继开工，,不管是工业项目还是民用项目，其中的一项重要设施就是消防系统，而作为消防系统的核心---消防泵尤为关键。
CN203081681U公开了一种新型消防泵，其特征在于，包括：电机、主泵电机、备用消防泵、多级泵、柴油机、中开消防泵、主管网、控制柜、逆变器，所述一种新型柴油机消防泵，在柴油机上设有中开消防泵，其中开消防泵有高效等特点，所述中开消防泵是柴油机，除迅速启动多级泵、备用消防泵外，直接采用启动高效的中开消防泵，是一种先进、性能可靠的消防设备。
CN106382197A公开了一种移动式两用消防泵，包括消防泵挡板、消防泵本体和防炸保护层，所述消防泵本体的内部固定安装有增压泵，所述增压泵的下方通过连接杆与固定底座连接，所述增压泵的左侧通过防炸保护层与出水管单向控制阀固定连接，所述保护壳上嵌套安装有限位凹槽和挂壁器。该发明，首先在消防泵的下方固定安装有可以收缩式的万向自锁轮，使得该消防泵既可以固定安装有某个地方进行使用，也可以将该消防泵进行车载携带，从而处理紧急情况，其次在该消防泵的出水管单向控制阀处设置有防炸保护层，可以防止增压泵压力过大造成出水口的炸裂现象，使得该消防泵的使用安全性更高。
CN102322412A一种采用电机带动真空泵的消防泵，包括动力装置、真空泵、泵体，泵体设有进水管和出水管，真空泵连接有电动机。由于该发明利用电动机直接带动真空泵，不需要皮带传动，其可靠性大大提高，大大地有利于消防救火。
消防泵常常要使用自然水源作为消防介质，但是由于消防泵长期浸泡在海洋，湖泊，江河等水域自然水域中，水中各种生物，如海草、贝类、软体动物等的附着，致使消防泵结构受到严重的污损，造成消防泵的功能参数降低或失效。
发明内容
为了解决上述问题，本发明提供了一种使用抑制生物生长新材料的双动力长轴消防泵。
一种使用抑制生物生长新材料的双动力长轴消防泵，其技术方案如下：
其主要部件包括消防泵、动力系统、控制柜和扬水管；所述的消防泵由泵头和泵体组成；所述的消防泵泵头、动力系统和控制柜安装于地坪基础上，扬水管及泵体部分立式安装于泵组基础下方；所述的长轴消防泵通过扬水管将泵体及吸入口垂直延伸到水面以下，实现水泵倒灌进水；所述的消防泵为长轴单级离心泵；所述的动力系统与消防泵通过泵轴相连接且能驱动消防泵工作，其特征在于，所述泵轴分成几段，分为动力轴、叶轮轴、传动轴三部分；其特征在于所述的消防泵泵体、吸入管、以及扬水管过流部件表面全部使用抑制生物生长新材料制备而成。所述的动力系统为柴油机和电机组成的双动力系统。
所述的抑制生物生长新材料按照以下技术方案制备：
按质量份数，将20-35份环氧树脂E-51、0.5-2份有机硅季铵盐改性水合三醋酸铽、0.8-1.5份的10,10-氧代双吩恶砒、3-7份石英粉、1-5份的聚丙烯酰胺甲基亚苄基樟脑、5-10份的二甲苯、0.1-0.5份的流平剂、0.05-0.10份的水合乙酰丙酮钐和0.3-0.7份的五(二甲氨基)钽混合制成中间产物A；按照质量份数，将5-15份环氧固化剂、0.1-0.5份的促进剂辛酸亚锡、5-10份的二甲苯和1-5份的异丙醇比例将上述物质混合制成中间产物B；使用时将所述的中间产物A和中间产物B按照质量比3.5-6.5:1的比例均匀混合，然后熟化30-40min后即可使用。
所述的环氧固化剂为聚酰胺环氧固化剂或二氨甲基环已基甲烷或2-甲基咪唑与环氧丙烷异辛基醚加成物。
所述的有机硅季铵盐改性水合三醋酸铽按照以下技术方案制备：
按照质量份数，将25-30份的β-（3,4环氧环己基）乙基三甲氧基硅烷、28-35份的十六烷基二甲基叔胺、100-150份的乙醇溶剂和0.1-0.5份的碘化钠加入到反应釜中；在氮气保护下，加热到70-80℃，使溶剂回流，反应20-30h后停止反应，冷却后过滤，减压蒸馏除去乙醇，然后将100-150份的水合三醋酸铽和500-600份的去离子水加入到反应釜中，在常温下低速混合搅拌150-180min，然后在搅拌状态下逐滴加入1.0-1.5mol/L草酸溶液，将溶液pH值调节到3-4，然后静置18-24h后，过滤，在100-120℃下干燥3-7h，研磨过筛后即可得到一种有机硅季铵盐改性水合三醋酸铽。
本发明提供的一种使用抑制生物生长新材料的双动力长轴消防泵，本方案设计的长轴消防泵设备工作稳定可靠，在有电或无电的情况下，都能实现送水；使用一种防生物附着新材料，有效防止水中各种生物附着在消防泵上，防止消防泵结构受到污损，避免消防泵的功能参数降低或失效。
具体实施方式
下面通过具体实施例对该发明作进一步说明：
实施例1
其主要部件包括消防泵、动力系统、控制柜和扬水管；所述的消防泵由泵头和泵体组成；所述的消防泵泵头、动力系统和控制柜安装于地坪基础上，扬水管及泵体部分立式安装于泵组基础下方；所述的长轴消防泵通过扬水管将泵体及吸入口垂直延伸到水面以下，实现水泵倒灌进水；所述的消防泵为长轴单级离心泵；所述的动力系统与消防泵通过泵轴相连接且能驱动消防泵工作，其特征在于，所述泵轴分成几段，分为动力轴、叶轮轴、传动轴三部分；其特征在于所述的消防泵泵体、吸入管、以及扬水管过流部件表面全部使用抑制生物生长新材料制备而成。所述的动力系统为柴油机和电机组成的双动力系统。
所述的抑制生物生长新材料按照以下技术方案制备：
按质量份数，将27份环氧树脂E-51、1份有机硅季铵盐改性水合三醋酸铽、1.2份的10,10-氧代双吩恶砒、5份石英粉、3份的聚丙烯酰胺甲基亚苄基樟脑、7份的二甲苯、0.3份的流平剂、0.08份的水合乙酰丙酮钐和0.5份的五(二甲氨基)钽混合制成中间产物A；按照质量份数，将10份环氧固化剂、0.3份的促进剂辛酸亚锡、8份的二甲苯和3份的异丙醇比例将上述物质混合制成中间产物B；使用时将所述的中间产物A和中间产物B按照质量比4.5:1的比例均匀混合，然后熟化35min后即可使用。
所述的环氧固化剂为聚酰胺环氧固化剂或二氨甲基环已基甲烷或2-甲基咪唑与环氧丙烷异辛基醚加成物。
所述的有机硅季铵盐改性水合三醋酸铽按照以下技术方案制备：
按照质量份数，将28份的β-（3,4环氧环己基）乙基三甲氧基硅烷、31份的十六烷基二甲基叔胺、130份的乙醇溶剂和0.3份的碘化钠加入到反应釜中；在氮气保护下，加热到75℃，使溶剂回流，反应25h后停止反应，冷却后过滤，减压蒸馏除去乙醇，然后将130份的水合三醋酸铽和550份的去离子水加入到反应釜中，在常温下低速混合搅拌160min，然后在搅拌状态下逐滴加入1.3mol/L草酸溶液，将溶液pH值调节到3.5，然后静置22h后，过滤，在110℃下干燥5h，研磨过筛后即可得到一种有机硅季铵盐改性水合三醋酸铽。
实施例2
一种使用抑制生物生长新材料的双动力长轴消防泵，其技术方案如下：
其主要部件包括消防泵、动力系统、控制柜和扬水管；所述的消防泵由泵头和泵体组成；所述的消防泵泵头、动力系统和控制柜安装于地坪基础上，扬水管及泵体部分立式安装于泵组基础下方；所述的长轴消防泵通过扬水管将泵体及吸入口垂直延伸到水面以下，实现水泵倒灌进水；所述的消防泵为长轴单级离心泵；所述的动力系统与消防泵通过泵轴相连接且能驱动消防泵工作，其特征在于，所述泵轴分成几段，分为动力轴、叶轮轴、传动轴三部分；其特征在于所述的消防泵泵体、吸入管、以及扬水管过流部件表面全部使用抑制生物生长新材料制备而成。所述的动力系统为柴油机和电机组成的双动力系统。
所述的抑制生物生长新材料按照以下技术方案制备：
按质量份数，将20份环氧树脂E-51、0.5份有机硅季铵盐改性水合三醋酸铽、0.8份的10,10-氧代双吩恶砒、3份石英粉、1份的聚丙烯酰胺甲基亚苄基樟脑、5份的二甲苯、0.1份的流平剂、0.05份的水合乙酰丙酮钐和0.3份的五(二甲氨基)钽混合制成中间产物A；按照质量份数，将5份环氧固化剂、0.1份的促进剂辛酸亚锡、5份的二甲苯和1份的异丙醇比例将上述物质混合制成中间产物B；使用时将所述的中间产物A和中间产物B按照质量比3.5:1的比例均匀混合，然后熟化30min后即可使用。
所述的环氧固化剂为二氨甲基环已基甲烷或2-甲基咪唑。
所述的有机硅季铵盐改性水合三醋酸铽按照以下技术方案制备：
按照质量份数，将25份的β-（3,4环氧环己基）乙基三甲氧基硅烷、28份的十六烷基二甲基叔胺、100份的乙醇溶剂和0.1份的碘化钠加入到反应釜中；在氮气保护下，加热到70℃，使溶剂回流，反应20h后停止反应，冷却后过滤，减压蒸馏除去乙醇，然后将100份的水合三醋酸铽和500份的去离子水加入到反应釜中，在常温下低速混合搅拌150min，然后在搅拌状态下逐滴加入1.0mol/L草酸溶液，将溶液pH值调节到3，然后静置18h后，过滤，在100℃下干燥3h，研磨过筛后即可得到一种有机硅季铵盐改性水合三醋酸铽。
实施例3
一种使用抑制生物生长新材料的双动力长轴消防泵，其技术方案如下：
其主要部件包括消防泵、动力系统、控制柜和扬水管；所述的消防泵由泵头和泵体组成；所述的消防泵泵头、动力系统和控制柜安装于地坪基础上，扬水管及泵体部分立式安装于泵组基础下方；所述的长轴消防泵通过扬水管将泵体及吸入口垂直延伸到水面以下，实现水泵倒灌进水；所述的消防泵为长轴单级离心泵；所述的动力系统与消防泵通过泵轴相连接且能驱动消防泵工作，其特征在于，所述泵轴分成几段，分为动力轴、叶轮轴、传动轴三部分；其特征在于所述的消防泵泵体、吸入管、以及扬水管过流部件表面全部使用抑制生物生长新材料制备而成。所述的动力系统为柴油机和电机组成的双动力系统。
所述的抑制生物生长新材料按照以下技术方案制备：
按质量份数，将35份环氧树脂E-51、2份有机硅季铵盐改性水合三醋酸铽、1.5份的10,10-氧代双吩恶砒、7份石英粉、5份的聚丙烯酰胺甲基亚苄基樟脑、10份的二甲苯、0.5份的流平剂、0.10份的水合乙酰丙酮钐和0.7份的五(二甲氨基)钽混合制成中间产物A；按照质量份数，将15份环氧固化剂、0.5份的促进剂辛酸亚锡、10份的二甲苯和5份的异丙醇比例将上述物质混合制成中间产物B；使用时将所述的中间产物A和中间产物B按照质量比6.5:1的比例均匀混合，然后熟化40min后即可使用。
所述的环氧固化剂为聚酰胺环氧固化剂。
所述的有机硅季铵盐改性水合三醋酸铽按照以下技术方案制备：
按照质量份数，将30份的β-（3,4环氧环己基）乙基三甲氧基硅烷、35份的十六烷基二甲基叔胺、150份的乙醇溶剂和0.5份的碘化钠加入到反应釜中；在氮气保护下，加热到80℃，使溶剂回流，反应30h后停止反应，冷却后过滤，减压蒸馏除去乙醇，然后将150份的水合三醋酸铽和600份的去离子水加入到反应釜中，在常温下低速混合搅拌180min，然后在搅拌状态下逐滴加入1.5mol/L草酸溶液，将溶液pH值调节到4，然后静置24h后，过滤，在120℃下干燥7h，研磨过筛后即可得到一种有机硅季铵盐改性水合三醋酸铽。
对比例1
不加有机硅季铵盐改性水合三醋酸铽，其它同实施例1。
对比例2
不加10,10-氧代双吩恶砒，其它同实施例1。
对比例3
不对水合三醋酸铽进行改性，其它同实施例1。
对比例4
不加聚丙烯酰胺甲基亚苄基樟脑，其它同实施例1。
对比例5
不加水合乙酰丙酮钐，其它同实施例1。
对比例6
不加五(二甲氨基)钽，其它同实施例1。
表：不同工艺做出的样品性能比较。
| 编号 | 抑菌率（%） | 紫贻贝致死率（%） |
| 实施例1 | 95.89 | 100 |
| 实施例2 | 95.07 | 100 |
| 实施例3 | 96.72 | 100 |
| 对比例1 | 77.61 | 86 |
| 对比例2 | 81.89 | 91 |
| 对比例3 | 85.31 | 94 |
| 对比例4 | 90.12 | 92 |
| 对比例5 | 89.32 | 97 |
| 对比例6 | 88.58 | 95 |
Claims (4)
1.一种使用抑制生物生长新材料的双动力长轴消防泵，其技术方案如下：
其主要部件包括消防泵、动力系统、控制柜和扬水管；所述的消防泵由泵头和泵体组成；所述的消防泵泵头、动力系统和控制柜安装于地坪基础上，扬水管及泵体部分立式安装于泵组基础下方；所述的长轴消防泵通过扬水管将泵体及吸入口垂直延伸到水面以下，实现水泵倒灌进水；所述的消防泵为长轴单级离心泵；所述的动力系统与消防泵通过泵轴相连接且能驱动消防泵工作，其特征在于，所述泵轴分成几段，分为动力轴、叶轮轴、传动轴三部分；其特征在于所述的消防泵泵体、吸入管、以及扬水管过流部件表面全部使用抑制生物生长新材料制备而成;
所述的抑制生物生长新材料按照以下技术方案制备：
按质量份数，将20-35份环氧树脂E-51、0.5-2份有机硅季铵盐改性水合三醋酸铽、0.8-1.5份的10,10-氧代双吩恶砒、3-7份石英粉、1-5份的聚丙烯酰胺甲基亚苄基樟脑、5-10份的二甲苯、0.1-0.5份的流平剂、0.05-0.10份的水合乙酰丙酮钐和0.3-0.7份的五(二甲氨基)钽混合制成中间产物A；按照质量份数，将5-15份环氧固化剂、0.1-0.5份的促进剂辛酸亚锡、5-10份的二甲苯和1-5份的异丙醇比例将上述物质混合制成中间产物B；使用时将所述的中间产物A和中间产物B按照质量比3.5-6.5:1的比例均匀混合，然后熟化30-40min后即可使用。
2.根据权利要求1所述的一种使用抑制生物生长新材料的双动力长轴消防泵，其特征在于：所述的动力系统为柴油机和电机组成的双动力系统。
3.根据权利要求1所述的一种使用抑制生物生长新材料的双动力长轴消防泵，其特征在于：所述的环氧固化剂为聚酰胺环氧固化剂或二氨甲基环已基甲烷或2-甲基咪唑与环氧丙烷异辛基醚加成物。
4.根据权利要求1所述的一种使用抑制生物生长新材料的双动力长轴消防泵，其特征在于：所述的有机硅季铵盐改性水合三醋酸铽按照以下技术方案制备：
按照质量份数，将25-30份的β-（3,4环氧环己基）乙基三甲氧基硅烷、28-35份的十六烷基二甲基叔胺、100-150份的乙醇溶剂和0.1-0.5份的碘化钠加入到反应釜中；在氮气保护下，加热到70-80℃，使溶剂回流，反应20-30h后停止反应，冷却后过滤，减压蒸馏除去乙醇，然后将100-150份的水合三醋酸铽和500-600份的去离子水加入到反应釜中，在常温下低速混合搅拌150-180min，然后在搅拌状态下逐滴加入1.0-1.5mol/L草酸溶液，将溶液pH值调节到3-4，然后静置18-24h后，过滤，在100-120℃下干燥3-7h，研磨过筛后即可得到一种有机硅季铵盐改性水合三醋酸铽。