CN108558449A - A kind of production method of fluorescence ceramic tile - Google Patents
A kind of production method of fluorescence ceramic tile Download PDFInfo
- Publication number
- CN108558449A CN108558449A CN201810125972.1A CN201810125972A CN108558449A CN 108558449 A CN108558449 A CN 108558449A CN 201810125972 A CN201810125972 A CN 201810125972A CN 108558449 A CN108558449 A CN 108558449A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- weight
- parts
- adobe
- fluorescence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of fluorescence ceramic tile production method, is related to ceramic tile technical field, and raw material crushes；Make powder；Adobe is made, stalk ball is mixed and is poured into tile mould after being added in powder, adobe is pressed into using press；It is laid with reflective layer, and centre position is laid with dotted ceramic tile coagulating agent above adobe surface layer, microprism is fixed above ceramic tile coagulating agent, the quantity of microprism is 3~5, adobe surface layer is flattened using press；Dry glazing uses bell-jar spray to carry out glazing for adobe；It fires；Polishing preserves.Fluorescence ceramic tile is made of following parts by weight of component, 100~120 parts by weight of porcelain stone china clay, 2~8 parts by weight of stalk ball, 300~350 parts by weight of water, 4~10 parts by weight of ceramic tile coagulating agent, 2~6 parts by weight of microprism, 10~20 parts by weight of glaze.Permeability of the present invention is good, has more comfortable reflecting effect, and level is abundant, has unique fragrance, while having good repelling effect.
Description
Technical field
The present invention relates to ceramic tile technical field, specially a kind of production method of fluorescence ceramic tile.
Background technology
Ceramic tile is metal oxide and half-metal oxide with fire resisting, via grinding, mixing, compacting, glazing, sintering
Process, and a kind of porcelain of acid and alkali-resistance of formation or the building of stone matter etc. or the material of decoration, total referred to as ceramic tile, former material
Material is mostly mixed by clay, quartz sand etc., and before B.C. 4000, Mesopotamia area has also discovered ceramic tile, this
Kind ceramic tile achievees the purpose that decoration with the striped of blue and white, occurs more kinds of style and color later, and China is pottery
The center of porcelain art, early in the abundant period (B.C. 1523-1028) of quotient, China just produces a kind of white stoneware of fineness, it
The glaze of Chinese early stage has been used to be whitewashed, since several centuries, decorative effect the changing with ceramic tile production method of ceramic tile
And then improve, for example, in Islamic period, the trailing of all ceramic tiles has reached peak in Persian, then, the utilization of ceramic tile
The gradual whole world prevailing, in many countries and cities, the production of ceramic tile and decoration have reached vertex, in the historical progress of ceramic tile
In, Spain and Portuguese mosaic, the floor tile in the Italian renaissance period, the glazed tile of Antwerp, Dutch ceramic tile
The development of illustration and the ceramic tile of Germany all have landmark meaning, and in ancient times, ceramic tile is all hand-made, that is,
It says, each block of ceramic tile is all offhand, hand colouring, therefore each block of ceramic tile is all a unique art work, and ceramic tile is several
It is used the every aspect of building, for example：Wall, ground, ceiling, fireplace, mural painting and building exterior wall etc., nowadays,
In worldwide, ceramic tile is no longer hand-made, hand colouring, but uses the production technology of automation, and the hand of people is
For ceramic tile is installed, as the past, indoor and outdoor is all decorated using ceramic tile, for example：Ground, metope, table top, wall
Stove, fountain and exterior wall etc., in the current constantly age of seeking change and innovation, requirement of the people to decorating ceramic tile is increasingly
Height, this just forces ceramic tile production firm to accelerate the paces of new product development, constantly puts out a new product, to adapt to the difference of consumer
It needs, occurred five kinds of fashions trend in the market in international ceramic tile in recent years, first, the type that surprises the world, this ceramic tile largely uses
Weight tone, such as gold and black, bud green and purplish red, the pattern and color of every block of ceramic tile have different surprising places, are pursued very much
The architect of individual character and consumer welcome；Second is that conservative of missing old times or old friends, this ceramic tile with apricot and it is light blue be adjusted to master, design updip
To in the church pattern of 13, trecento, the portrait etc. of European imperial palace pseudo-classic finery pattern and ancient Greek, from being patterned onto color and luster
All generous proper, the customer of purchase belongs to the conservative middle class of personality more, they, which seek for seeking rule, steps square, will not exceed the bounds；Three
It is type of vivaciously keeping forging ahead.This ceramic tile focuses on sense of the times very much, and for pattern based on wrinkle cloth line, tone uses claret, bottle green and depth
Blue etc., with the indoor light that can adjust coloration is closed, can generate very strong solid under especially more concave-convex line designs
Therefore sense is firmly got and focuses on fraicheur two, 30 years old young man's favor；Fourth, gentle gynecoid type, this ceramic tile is mostly with soft
Powder it is blue, it is pink be homophony, pattern matches lining feathers with colored series, absolutely womanlike, receives mature women and is especially
The favor of female middle-aged；Fifth, young administration type.The design comparison of this ceramic tile is resistance to be seen, tone is biased to soft pink colour or shallower
Color system, books taste is heavier, less noticeable, can coordinate the identity of the young management level of one's late 30s, them is made to fall in love at first sight.But
Existing ceramic tile is all without fluorescent functional, and the internal layer reflecting power difference of ceramic tile causes ceramic tile to seem that comparison is dim, while ceramic tile
Do not have beautiful pattern yet.
Invention content
Technical problem to be solved by the present invention lies in providing one kind having fluorescent functional, stereovision is strong, has better
Good reflecting power is provided simultaneously with the production method of the fluorescence ceramic tile of beautiful pattern.
A kind of production method of fluorescence ceramic tile, includes the following steps,
(1), it is laid with functional layer, the groove of regular shape is opened up in the both sides on adobe surface, is filled in inside grooves enough
Inorganic fluorescent material, be laid with after the completion of adobe surface is flattened using press；
(2), prepare glaze, by feldspar, quartz, Western Hills pond sludge and zinc oxide, by glaze raw material be put into blender and stirred to
It is proportionally mixed after crushing enough, pours into blender and stir again after addition enough water；
(3), adobe is put into drying in dry kiln, pressure is used after detecting the moisture content qualification of ceramic tile original brick by dry glazing
Power formula glaze spraying is that adobe carries out glazing；
(4), it fires, by adobe kiln-firing, the firing time should be 70~80 minutes, and firing temperature should be 1200 DEG C；
(5), polishing molding will be handled after the ceramic tiles in advance baked by edge polisher, beveler and polishing machine；
(6), finished product detection is detected the quality, size and colouring of ceramic tile, removes underproof ceramic tile, will be qualified
Ceramic tile be packed into carton preserve.
The present invention, which has been laid with inorganic fluorescent material, makes ceramic tile be provided with fluorescent functional, increases while realizing ceramic tile beauty
The interest for having added ceramic tile makes ceramic tile that can have certain illumination functions under dark surrounds, while people can be given pleasantly surprised,
It brightens everyone's eyes when boring, while ceramic tile makes ceramic tile after the completion of firing by edging, chamfering and polishing many more manipulations
Details it is more perfect, ceramic tile gap smaller when fitting is more beautiful, and last inspection has been carried out after ceramic tile polishing
It looks into, removes underproof ceramic tile, ensure that the perfection of ceramic tile, it is ensured that the quality of ceramic tile.
The fluorescence ceramic tile is made of following parts by weight of component, 100~120 parts by weight of adobe, 6~10 weight of ceramic tile coagulating agent
Measure part, 2~6 parts by weight of microprism, 10~20 parts by weight of inorganic fluorescent material, 2~6 parts by weight of feldspar, quartzy 1~5 parts by weight,
0.5~1.5 parts by weight of 1~3 parts by weight of Western Hills pond sludge and zinc oxide.
It is preferred that being made of following parts by weight of component, 110 parts by weight of adobe, 8 parts by weight of ceramic tile coagulating agent, 4 weight of microprism
Part, 15 parts by weight of inorganic fluorescent material, 4 parts by weight of feldspar, quartzy 3 parts by weight, 1 weight of 2 parts by weight of Western Hills pond sludge and zinc oxide
Part.
The adobe makes by the following method
1), raw material crushes：It is put into jaw crushing crusher machine after collected porcelain stone china clay is tentatively removed impurity, when being crushed
Between should be 3 hours, after broken plus water pours into ball mill, and Ball-milling Time should be 12 hours；
2), prepare colorant：Color needed for adobe prepares having colors；
3) powder, is made：The mixture of porcelain stone particle and water after ball milling is poured into blender, in whipping process not
It is disconnected that material colorant is added until stirring fully, pours into spray dryer, powder is obtained after spray-dried；
4) adobe, is made：It is pressed into adobe using press after powder is poured into tile mould, with mold on adobe surface
The shape that stamp needs, pattern is delineated with pigment on adobe surface.
The ceramic tile raw material is detected using preceding needs, ceramic tile raw material is dried in baker, drying temperature should be
It 100~110 DEG C, detects the front and back mass ratio of ceramic tile raw material after drying by high temperature sintering and the method for immersion respectively, removes matter
The underproof ceramic tile raw material of amount ratio.
It needs to carry out frosted processing to the shape of stamp after the shape that the adobe is needed with die imprint.
It is intermediate above the adobe coat of colo(u)r to be laid with dotted ceramic tile coagulating agent, microprism is fixed above ceramic tile coagulating agent,
The quantity of microprism is 3~5.
The inorganic fluorescent material should carry out Screening Treatment before laying, and the mesh number of selected sieve should be 100 mesh, the nothing
Machine fluorescent material should be fixed after being laid with using fixative.
The feldspar, quartz, Western Hills pond sludge and zinc oxide mixed proportion should be 4:3:2:1.
The ceramic tile should be wrapped up with foam on the outside before being packed into carton.
Centre position of the present invention below ceramic tile glaze layer has been laid with microprism, increases the hierarchy of ceramic tile, while one
As ceramic tile reflective function it is all poor, or the surface of ceramic tile have stronger reflective function, can seem it is showy and not substantial simultaneously
Class is relatively low, and the present invention increases the reflective function of ceramic tile below glaze layer, while reflective position is the graininess being laid with immediately,
Make ceramic tile part regularity is presented the strong phenomenon of luminescent properties, increases the aesthetic measure of ceramic tile, while improving ceramic tile
Class.
Ceramic tile background color of the present invention is more graceful after adding pigment, at the same feature below glaze layer special shape and
Pattern keeps ceramic tile more beautiful.Ceramic tile raw material of the present invention have passed through test before use, eliminate underproof raw material, from source
The first quality for having controlled ceramic tile, improves the quality of ceramic tile.
The beneficial effects of the invention are as follows：Invention increases unique fluorescent functionals, and reflecting effect is strong, and layer of structure is rich
Richness, more beautiful, quality is more guaranteed.
Specific implementation mode
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment one
A kind of production method of fluorescence ceramic tile, includes the following steps,
(1), it is laid with functional layer, the groove of regular shape is opened up in the both sides on adobe surface, is filled in inside grooves enough
Inorganic fluorescent material, be laid with after the completion of adobe surface is flattened using press；
(2), prepare glaze, by feldspar, quartz, Western Hills pond sludge and zinc oxide, by glaze raw material be put into blender and stirred to
It is proportionally mixed after crushing enough, pours into blender and stir again after addition enough water；
(3), adobe is put into drying in dry kiln, pressure is used after detecting the moisture content qualification of ceramic tile original brick by dry glazing
Power formula glaze spraying is that adobe carries out glazing；
(4), it fires, by adobe kiln-firing, the firing time should be 70 minutes, and firing temperature should be 1200 DEG C；
(5), polishing molding will be handled after the ceramic tiles in advance baked by edge polisher, beveler and polishing machine；
(6), finished product detection is detected the quality, size and colouring of ceramic tile, removes underproof ceramic tile, will be qualified
Ceramic tile be packed into carton preserve.
Fluorescence ceramic tile is made of following parts by weight of component, 100 parts by weight of adobe, 6 parts by weight of ceramic tile coagulating agent, microprism 2
Parts by weight, 10 parts by weight of inorganic fluorescent material, 2 parts by weight of feldspar, quartzy 1 parts by weight, 1 parts by weight of Western Hills pond sludge and zinc oxide
0.5 parts by weight.
Adobe makes by the following method
1), raw material crushes：It is put into jaw crushing crusher machine after collected porcelain stone china clay is tentatively removed impurity, when being crushed
Between should be 3 hours, after broken plus water pours into ball mill, and Ball-milling Time should be 12 hours；
2), prepare colorant：Color needed for adobe prepares having colors；
3) powder, is made：The mixture of porcelain stone particle and water after ball milling is poured into blender, in whipping process not
It is disconnected that material colorant is added until stirring fully, pours into spray dryer, powder is obtained after spray-dried；
4) adobe, is made：It is pressed into adobe using press after powder is poured into tile mould, with mold on adobe surface
The shape that stamp needs, pattern is delineated with pigment on adobe surface.
Ceramic tile raw material is detected using preceding needs, ceramic tile raw material is dried in baker, drying temperature should be 100
DEG C, detect the front and back mass ratio of ceramic tile raw material after drying by high temperature sintering and the method for immersion respectively, removal mass ratio is not
Qualified ceramic tile raw material.
It needs to carry out frosted processing to the shape of stamp after the shape that adobe is needed with die imprint.
It is intermediate above adobe coat of colo(u)r to be laid with dotted ceramic tile coagulating agent, microprism, micro- rib are fixed above ceramic tile coagulating agent
The quantity of mirror is 3.
Inorganic fluorescent material should carry out Screening Treatment before laying, and the mesh number of selected sieve should be 100 mesh, described inorganic glimmering
Luminescent material should be fixed after being laid with using fixative.
Feldspar, quartz, Western Hills pond sludge and zinc oxide mixed proportion should be 4:3:2:1.
Ceramic tile should be wrapped up with foam on the outside before being packed into carton.
Embodiment two
A kind of production method of fluorescence ceramic tile, includes the following steps,
(1), it is laid with functional layer, the groove of regular shape is opened up in the both sides on adobe surface, is filled in inside grooves enough
Inorganic fluorescent material, be laid with after the completion of adobe surface is flattened using press；
(2), prepare glaze, by feldspar, quartz, Western Hills pond sludge and zinc oxide, by glaze raw material be put into blender and stirred to
It is proportionally mixed after crushing enough, pours into blender and stir again after addition enough water；
(3), adobe is put into drying in dry kiln, pressure is used after detecting the moisture content qualification of ceramic tile original brick by dry glazing
Power formula glaze spraying is that adobe carries out glazing；
(4), it fires, by adobe kiln-firing, the firing time should be 75 minutes, and firing temperature should be 1200 DEG C；
(5), polishing molding will be handled after the ceramic tiles in advance baked by edge polisher, beveler and polishing machine；
(6), finished product detection is detected the quality, size and colouring of ceramic tile, removes underproof ceramic tile, will be qualified
Ceramic tile be packed into carton preserve.
Fluorescence ceramic tile is preferably made of following parts by weight of component, 110 parts by weight of adobe, 8 parts by weight of ceramic tile coagulating agent, micro- rib
4 parts by weight of mirror, 15 parts by weight of inorganic fluorescent material, 4 parts by weight of feldspar, quartzy 3 parts by weight, 2 parts by weight of Western Hills pond sludge and oxidation
1 parts by weight of zinc.
Adobe makes by the following method
1), raw material crushes：It is put into jaw crushing crusher machine after collected porcelain stone china clay is tentatively removed impurity, when being crushed
Between should be 3 hours, after broken plus water pours into ball mill, and Ball-milling Time should be 12 hours；
2), prepare colorant：Color needed for adobe prepares having colors；
3) powder, is made：The mixture of porcelain stone particle and water after ball milling is poured into blender, in whipping process not
It is disconnected that material colorant is added until stirring fully, pours into spray dryer, powder is obtained after spray-dried；
4) adobe, is made：It is pressed into adobe using press after powder is poured into tile mould, with mold on adobe surface
The shape that stamp needs, pattern is delineated with pigment on adobe surface.
Ceramic tile raw material is detected using preceding needs, ceramic tile raw material is dried in baker, drying temperature should be 105
DEG C, detect the front and back mass ratio of ceramic tile raw material after drying by high temperature sintering and the method for immersion respectively, removal mass ratio is not
Qualified ceramic tile raw material.
It needs to carry out frosted processing to the shape of stamp after the shape that adobe is needed with die imprint.
It is intermediate above adobe coat of colo(u)r to be laid with dotted ceramic tile coagulating agent, microprism, micro- rib are fixed above ceramic tile coagulating agent
The quantity of mirror is 4.
Inorganic fluorescent material should carry out Screening Treatment before laying, and the mesh number of selected sieve should be 100 mesh, described inorganic glimmering
Luminescent material should be fixed after being laid with using fixative.
Feldspar, quartz, Western Hills pond sludge and zinc oxide mixed proportion should be 4:3:2:1.
Ceramic tile should be wrapped up with foam on the outside before being packed into carton.
Embodiment three
A kind of production method of fluorescence ceramic tile, includes the following steps,
(1), it is laid with functional layer, the groove of regular shape is opened up in the both sides on adobe surface, is filled in inside grooves enough
Inorganic fluorescent material, be laid with after the completion of adobe surface is flattened using press；
(2), prepare glaze, by feldspar, quartz, Western Hills pond sludge and zinc oxide, by glaze raw material be put into blender and stirred to
It is proportionally mixed after crushing enough, pours into blender and stir again after addition enough water；
(3), adobe is put into drying in dry kiln, pressure is used after detecting the moisture content qualification of ceramic tile original brick by dry glazing
Power formula glaze spraying is that adobe carries out glazing；
(4), it fires, by adobe kiln-firing, the firing time should be 80 minutes, and firing temperature should be 1200 DEG C；
(5), polishing molding will be handled after the ceramic tiles in advance baked by edge polisher, beveler and polishing machine；
(6), finished product detection is detected the quality, size and colouring of ceramic tile, removes underproof ceramic tile, will be qualified
Ceramic tile be packed into carton preserve.
Fluorescence ceramic tile is made of following parts by weight of component, 120 parts by weight of adobe, 10 parts by weight of ceramic tile coagulating agent, microprism 6
Parts by weight, 20 parts by weight of inorganic fluorescent material, 6 parts by weight of feldspar, quartzy 5 parts by weight, 3 parts by weight of Western Hills pond sludge and zinc oxide
1.5 parts by weight.
Adobe makes by the following method
1), raw material crushes：It is put into jaw crushing crusher machine after collected porcelain stone china clay is tentatively removed impurity, when being crushed
Between should be 3 hours, after broken plus water pours into ball mill, and Ball-milling Time should be 12 hours；
2), prepare colorant：Color needed for adobe prepares having colors；
3) powder, is made：The mixture of porcelain stone particle and water after ball milling is poured into blender, in whipping process not
It is disconnected that material colorant is added until stirring fully, pours into spray dryer, powder is obtained after spray-dried；
4) adobe, is made：It is pressed into adobe using press after powder is poured into tile mould, with mold on adobe surface
The shape that stamp needs, pattern is delineated with pigment on adobe surface.
Ceramic tile raw material is detected using preceding needs, ceramic tile raw material is dried in baker, drying temperature should be 110
DEG C, detect the front and back mass ratio of ceramic tile raw material after drying by high temperature sintering and the method for immersion respectively, removal mass ratio is not
Qualified ceramic tile raw material.
It needs to carry out frosted processing to the shape of stamp after the shape that adobe is needed with die imprint.
It is intermediate above adobe coat of colo(u)r to be laid with dotted ceramic tile coagulating agent, microprism, micro- rib are fixed above ceramic tile coagulating agent
The quantity of mirror is 5.
Inorganic fluorescent material should carry out Screening Treatment before laying, and the mesh number of selected sieve should be 100 mesh, described inorganic glimmering
Luminescent material should be fixed after being laid with using fixative.
Feldspar, quartz, Western Hills pond sludge and zinc oxide mixed proportion should be 4:3:2:1.
Ceramic tile should be wrapped up with foam on the outside before being packed into carton.
The embodiment of the present invention and the common ceramic tile table of comparisons
From above table as can be seen that compared with ceramic tile commonly in the market, there is the present invention apparent reflective degree to relax
Suitable feature, while there is fluorescent effect, it is more bonded between ceramic tile, stereovision is more abundant, and shape is more beautiful.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (10)
1. a kind of production method of fluorescence ceramic tile, it is characterised in that：Include the following steps,
(1), it is laid with functional layer, the groove of regular shape is opened up in the both sides on adobe surface, enough nothings is filled in inside grooves
Machine fluorescent material is flattened adobe surface using press after the completion of being laid with；
(2), prepare glaze glaze raw material is put into blender and stirred feldspar, quartz, Western Hills pond sludge and zinc oxide to enough to
It is proportionally mixed after crushing, pours into blender and stir again after addition enough water；
(3), adobe is put into drying in dry kiln, pressure type is used after detecting the moisture content qualification of ceramic tile original brick by dry glazing
Glaze spraying is that adobe carries out glazing；
(4), it fires, by adobe kiln-firing, the firing time should be 70~80 minutes, and firing temperature should be 1200 DEG C；
(5), polishing molding will be handled after the ceramic tiles in advance baked by edge polisher, beveler and polishing machine；
(6), finished product detection is detected the quality, size and colouring of ceramic tile, removes underproof ceramic tile, by qualified porcelain
Brick is packed into carton and preserves.
2. a kind of production method of fluorescence ceramic tile according to claim 1, it is characterised in that：The fluorescence ceramic tile is by following
Parts by weight of component is made, 100~120 parts by weight of adobe, 6~10 parts by weight of ceramic tile coagulating agent, 2~6 parts by weight of microprism, inorganic
10~20 parts by weight of fluorescent material, 2~6 parts by weight of feldspar, quartzy 1~5 parts by weight, 1~3 parts by weight of Western Hills pond sludge and zinc oxide
0.5~1.5 parts by weight.
3. a kind of production method of fluorescence ceramic tile according to claim 1, it is characterised in that：The fluorescence ceramic tile preferably by
Following parts by weight of component is made, 110 parts by weight of adobe, 8 parts by weight of ceramic tile coagulating agent, 4 parts by weight of microprism, inorganic fluorescent material
15 parts by weight, 4 parts by weight of feldspar, quartzy 3 parts by weight, 1 parts by weight of 2 parts by weight of Western Hills pond sludge and zinc oxide.
4. a kind of production method of fluorescence ceramic tile according to claim 1, it is characterised in that：The adobe is by the following method
It makes
1), raw material crushes：It is put into jaw crushing crusher machine after collected porcelain stone china clay is tentatively removed impurity, the broken time answers
It it is 3 hours, after broken plus water pours into ball mill, and Ball-milling Time should be 12 hours；
2), prepare colorant：Color needed for adobe prepares having colors；
3) powder, is made：The mixture of porcelain stone particle and water after ball milling is poured into blender, is constantly added in whipping process
Enter material colorant until stirring fully, pours into spray dryer, powder is obtained after spray-dried；
4) adobe, is made：It is pressed into adobe using press after powder is poured into tile mould, is stamped on adobe surface with mold
The shape needed delineates pattern with pigment on adobe surface.
5. a kind of production method of fluorescence ceramic tile according to claim 4, it is characterised in that：Before the ceramic tile raw material use
It needs to be detected, ceramic tile raw material is dried in baker, drying temperature should be 100~110 DEG C, pass through height after drying respectively
The method of warm calcination and immersion detects the front and back mass ratio of ceramic tile raw material, removes the underproof ceramic tile raw material of mass ratio.
6. a kind of production method of fluorescence ceramic tile according to claim 4, it is characterised in that：The adobe die imprint
It needs to carry out frosted processing to the shape of stamp after the shape needed.
7. a kind of production method of fluorescence ceramic tile according to claim 1, it is characterised in that：Above the adobe coat of colo(u)r
Centre is laid with dotted ceramic tile coagulating agent, microprism is fixed above ceramic tile coagulating agent, the quantity of microprism is 3~5.
8. a kind of production method of fluorescence ceramic tile according to claim 1, it is characterised in that：The inorganic fluorescent material exists
Screening Treatment should be carried out before laying, the mesh number of selected sieve should be 100 mesh, and the inorganic fluorescent material should be used after being laid with and be fixed
Agent is fixed.
9. a kind of production method of fluorescence ceramic tile according to claim 1, it is characterised in that：The feldspar, quartz, Western Hills
The mixed proportion of pond sludge and zinc oxide should be 4:3:2:1.
10. a kind of production method of fluorescence ceramic tile according to claim 1, it is characterised in that：The ceramic tile is being packed into paper
It should be wrapped up on the outside with foam before case.